固溶处理对TC16钛合金显微组织和拉伸性能的影响

通过金相显微镜和室温拉伸性能测试,研究固溶处理对TC16钛合金棒材显微组织和拉伸性能的影响.结果表明:TC16钛合金低于800℃进行固溶处理,初始组织为初生α相和亚稳态β相,随着固溶温度的升高,亚稳态β相会发生α"马氏体转变,温度达到900℃时,α"马氏体析出晶界完整的β相,出现过烧组织,抗拉强度和屈服强度先降后升,温度对塑性影响不大.该合金固溶处理后,冷镦性能差,不同的冷却速度使钛合金有不同的α和β相比率,冷却速度决定β→α转变反应中间相的形成条件,水淬、空冷、炉冷后的TC16钛合金显微组织和拉伸性能差异较大.     

热等静压316L不锈钢致密体的组织与性能

采用热等静压方法对气雾化316L奥氏体不锈钢粉末致密化,用箱式电阻炉对致密体进行了固溶处理,研究了固溶前后致密体的显微组织和力学性能,并对其拉伸断口形貌进行了分析．结果表明：热等静压态致密体密度接近理论全致密,内部组织为细小的奥氏体,存在较多的碳化物,抗拉强度、屈服强度分别达到595．3MPa和263．3MPa,延伸率为58．3％,硬度为HBS152．3;固溶处理使致密体强度和硬度降低,塑性增加,且随着固溶温度的提高,强度迅速降低,塑性明显提高,最佳固溶温度为1050℃;在固溶温度为1050℃和水冷的情况下,最佳保温时间为20min;固溶处理前后拉伸试样断口呈现明显的韧性断裂,固溶韧性好于固溶前的,均高于热轧态产品的韧性．     

Ti-22Nb-6Zr合金的耐蚀性和超弹性研究

采用电化学方法研究固溶处理后Ti-22Nb-6Zr形状记忆合金在0.9%NaC l溶液中的腐蚀行为,研究固溶处理温度对合金耐蚀性的影响;用拉伸法测定900℃固溶处理后合金的超弹性和形状记忆效应.结果表明:固溶处理后Ti-22Nb-6Zr合金的室温组织为单一的β相,晶粒尺寸随固溶处理温度升高而增大.合金的腐蚀电流随着固溶处理温度的升高而降低.耐蚀性逐渐提高.900℃固溶处理后的合金在室温下拉伸变形,应变为5%时,总的最大回复应变达4.12%,其中超弹性回复应变为3.91%,记忆回复应变为0.21%.     

黄铜的超塑性研究

本文研究Cu-Zn合金的超塑性条件。用工业用的Hpb59—1和H62铜棒,机加工成拉伸试样,经热处理,得到超塑性的微细组织。试样在高温拉伸机上以不同的温度和变形速度进行拉伸。试验表明,Hpb59—1黄铜在温度为620℃,拉伸速度为0.3毫米/分,出现了超塑性,延伸率达500％,未断;H62黄铜在温度为750℃,拉伸速度为0.2毫米/分时,出了超塑性,延伸率达624％,未断。本文还研究了Hpb 59—1和H 62黄铜的温度与拉伸速度之间的关系,并用金相显微镜和扫描电镜观察了试样变形前后显微组织的变化。     

固溶温度对Ag2205双相不锈钢组织与性能的影响

通过添加Cu–Ag合金颗粒制备Ag2205双相不锈钢,并分别在1 050,1 075,1 100,1 125和1 150℃对其进行固溶处理;利用光学显微镜、扫描电子显微镜、拉伸试验、电化学工作站及覆膜法等研究固溶温度对Ag2205双相不锈钢组织、力学性能、耐蚀性能及抗菌性能的影响,并与母材2205及Cu2205不锈钢的实验结果进行对比分析。研究结果表明:随着固溶温度的升高,Ag2205材料内γ相体积分数逐渐降低且γ相先变粗后细化,而α相体积分数逐渐提高;此外,微米级的含Ag相主要分布于α基体及α/γ相界处,升高固溶温度会促进Ag相溶解;随着固溶温度的升高,含Ag材料洛氏硬度和抗拉强度均先降低后升高,但伸长率持续增大,当固溶温度为1150℃时,Ag2205综合力学性能最佳且优于母材与含Cu2205材料的力学性能;Ag的加入会降低2205材料的耐蚀性,但提高固溶温度可改善其耐蚀性能,且在1125℃固溶后,其耐蚀性已优于母材耐蚀性;3种材料中,Cu2205材料的耐蚀性最好;当固溶温度大于等于1 075℃时含Ag材料具有优异的抗菌性能,Cu2205材料及母材则不具备抗菌效果。     

热循环频率对铸态Zn-Al合金相变超塑性的影响

用恒载荷蠕变法研究了热循环频率对质量分数为 5 %的铝的铸态Zn Al合金相变超塑性的影响。研究结果表明 ,在温度为 2 0～ 35 0℃循环条件下进行拉伸时 ,铸态Zn Al合金的延伸率能超过 10 0 % ,呈现相变超塑性特征。改变热循环频率对铸态Zn Al合金的相变超塑性有很大影响。若保持循环温度和外加载荷不变 ,随着热循环频率的提高 ,铸态Zn Al合金的相变超塑性延伸率增大 ,而准稳态蠕变阶段的应变速率则有所降低。Zn Al铸态合金的这种相变超塑性与共析相变过程中新、旧相间的界面行为有很大关系 ,相变过程中产生的内应力在外应力的偏置作用下使新、旧相界面间的Zn Al合金发生牛顿粘滞性流动 ,而界面间的原子扩散对热循环中Zn Al合金的变形起着重要的协调作用。     

用铝合金中间层连接Si_3N_4和低碳钢

利用Thermorestor-W焊接热模拟试验机,采用适当的焊接参数和工艺,能够用铝合金中间层固相扩散连接Si_3N_4和低碳钢。在连接温度下,铝合金Si_3N_4进入孔洞中形成机械连接,而铝合金与Si_3N_4连接的主要机理是铝与Si_3N_4发生固相反应生成AlN。当温度大于530℃时,铝合金/Si_3N_4界面Al,Si扩散层厚度基本上不随温度升高而变化。Si_3N_4/铝合金/低碳钢接头的剪切强度取决于铝合金/钢界面强度,且随扩散连接温度上升而增加。     

热循环频率对铸态Zn-Al合金相变超塑性的影响

用恒载荷蠕变法研究了热循环频率对质量分数为5％的铝的铸态Zn-Al合金相变超塑性的影响。研究结果表明，在温度为20～350℃循环条件下进行拉伸时，铸态Zn—Al合金的延伸率能超过100％，呈现相变超塑性特征。改变热循环频率对铸态Zn-Al合金的相变超塑性有很大影响。若保持循环温度和外加载荷不变，随着热循环频率的提高，铸态Zn-Al合金的相变超塑性延伸率增大，而准稳态蠕变阶段的应变速率则有所降低。Zn-Al铸态合金的这种相变超塑性与共析相变过程中新、旧相间的界面行为有很大关系，相变过程中产生的内应力在外应力的偏置作用下使新、旧相界面间的Zn-Al合金发生牛顿粘滞性流动，而界面间的原子扩散对热循环中Zn-Al合金的变形起着重要的协调作用。     

一种单晶高温合金中g?相的析出行为

研究了固溶冷却速度和时效时间对一种镍基单晶高温合金中γ′相的析出的影响。合金经1 250℃固溶处理4 h,从炉中快速取出,分别进行空冷、油冷和水冷,以考察冷却速度对γ′相析出的影响。随后对固溶处理后试样进行时效处理,以考察时效时间和固溶冷却速度对γ′相长大的影响。结果表明,合金在固溶处理后,γ′相尺寸随固溶冷却速率的升高而下降。在时效处理时,γ′相尺寸的增大率随固溶冷却速度的增大而减小;随着时效时间的增加,γ′相的尺寸增加。     

涂层烧结及热处理工艺对GH202合金组织性能的影响

研究了涂层烧结及热处理工艺对GH2 0 2合金基材组织性能的影响 .运用电子拉伸机、扫描电镜及光学显微镜 ,测定了拉伸试样的力学性能 ,并分析了试样的显微组织和拉伸断口 .试验结果表明 ,GH2 0 2合金在 115 0℃固溶处理 5h后 ,合金表面进行高温涂层与烧结 ,在 85 0℃时效 6h出炉空冷 ,合金基体晶粒细小 ,均匀 ;强化相γ'弥散分布 ;合金强度提高 ,塑性改善 ,拉伸断口为韧性断裂 .     

高性能铜铝复合排的制备及界面研究

采用固-液法浇注和铸轧工艺制备铝/铜复合材料.研究不同工艺对铜/铝复合排界面结合强度的影响,并对铜/铝复合排界面结构和复合机理进行分析.结果表明:当进行300°C×1h热处理时,所得复合排的结合强度最高,多次热循环后复合排界面结合强度有所增加.电子探针能谱扫描分析(EDS)和X射线衍射分析(XRD)表明铜/铝复合界面上生成金属间化合物Al2Cu,Al4Cu9和AlCu相,从而使得界面层硬度增大.采用该方法制备的铜/铝复合排,整体拉伸强度达98MPa,电阻率为0.021 6×10-6Ω.m.     

AISI304/低碳钢真空扩散焊接头组织和性能

采用真空扩散焊接方法连接AISI304奥氏体不锈钢和低碳钢异种材料.在焊接温度和焊接压力恒定的条件下,研究焊接时间对ASTM304/低碳钢异种材料扩散焊接头组织和性能的影响.研究结果表明:在焊接温度850℃,焊接压力10 MPa,焊接时间60 min条件下AISI304奥氏体不锈钢/低碳钢异种材料实现了良好的扩散结合,其强度和韧性均超过低碳钢母材水平.接头抗拉强度达到440 MPa,拉伸断裂发生在低碳钢一侧.在扩散焊高温环境下,界面附近有碳化物偏析现象,析出相为脆硬的Cr23C6,脆硬相的出现导致界面韧性下降,延长焊接时间可有效避免有害化合物Cr23C6的析出,冲击韧性达到120.5 J/cm2,冲击断口在低碳钢一侧.     

多级热处理对TC21钛合金组织和力学性能的影响

Duplex-structured TC21 alloy samples were first solution-treated at a higher temperature in the α + β region (940°C) with furnace cooling (FC), air cooling (AC), and water cooling (WC), followed by a second-stage solution treatment at a lower temperature in the α + β region (900°C), and then finally aged at 590°C. The effects of the morphology and quantity of α phases on the structure and properties of the TC21 alloy after the different heat treatments were analyzed. The in-situ tensile deformation process and crack propagation behavior were observed using scanning electron microscopy (SEM). The quantity of equiaxed α phases as well as the thickness of lamellar α phases reduced, the tensile strength increased firstly and then decreased, the elongation decreased with the increasing cooling rate after the first-stage solution treatment. The amount and size of lamellar α phases increased after the second-stage solution treatment because of sufficient diffusion of the alloying elements, thereby leading to increased tensile strength. The amount of dispersed α phases increased after the third-stage aging treatment owing to the increase in the nucleation rate, resulting in a noteworthy strengthening effect. After the third-stage aging treatment, the first-stage FC sample exhibited better mechanical properties because it contained more equiaxed α and β_trans phases than the first-stage AC and WC samples.     

原位观察铜网格增强Al/Cu复合材料的断裂行为

将一种按正交法编织的铜网格作为增强体引入到铝基体中制备了Al/Cu复合材料,再借助原位拉伸扫描电镜(SEM),观察了铝铜复合材料的组织演变,研究了其断裂机理与力学性能之间的关系.结果表明:在相同轧制变形量下,25 ℃冷轧和400 ℃热轧均可破碎增强体铜网格,并使其均匀分布于基体铝板.复合板原位拉伸下的载荷-位移曲线均表现出明显的弹性阶段、塑性阶段和失效阶段,微裂纹在Cu颗粒周围和应力集中处萌生,主裂纹及其扩展主要是Cu颗粒周围界面分层开裂与微裂纹沿滑移线方向的扩展共同作用下形成的,并且最终沿滑移线的断裂路径与单轴拉伸方向呈45°.发生在Al层的塑性断裂和Al/Cu结合界面上的界面分层断裂是Al/Cu复合板两种主要的失效方式.     

Influence of diffusion time on property of steel-aluminum solid to liquid bonding

The bonding of solid steel to liquid aluminum was conducted using rapid solidification. The influence of diffusion time on interfacial shear strength was studied. The results show that when the temperature of aluminum liquid is 700℃ and the preheat temperature of steel plate is 250℃, the relationship between diffusion time (t) and interfacial shear strength (σ) is (σ=15.1+8.14t(037t2 +0.005t3, and the maximum interfacial shear strength is 71.1 MPa.     

5 Cr9 Si3钢的高温变形行为及流变应力异常变化机理

通过不同热加工参数下的热压缩试验,研究了新型阀门钢5Cr9Si3的高温变形行为.5Cr9Si3钢在850~900℃和1000~1100℃温度区间内峰值应力分别随温度的升高而减小,而在900~1000℃温度区间内出现峰值应力随温度升高而增大的异常现象.进一步的微观组织及相结构演化分析表明：5Cr9Si3钢在900~1000℃温度区间内发生了由铁素体向奥氏体的转变,产生奥氏体相变强化;同时,随着变形温度的提高,碳化物的回溶造成碳元素和铬元素对5Cr9Si3基体固溶强化效果增强.相变强化和固溶强化是导致5Cr9Si3在900~1000℃温度区间内流变应力异常变化的主要原因.     

Zr基非晶合金准静态压缩下的多重剪切带行为

利用IUTM和SEM研究了Zr-Ti-Ni-Cu块状非晶合金的准静态单轴压缩变形和断裂行为. 研究表明:该合金的室温压缩变形过程主要表现为弹性和塑性变形,塑性变形阶段没有加工硬化现象. 在准静态压缩条件下Zr基非晶合金表现出多重剪切效应,提高了塑性. 微观研究证明,剪切带的滑移分枝与相互交叉是非晶合金塑性提高的主要机制. 沿着剪切带发现了微空洞和微裂纹,剪切带的形成与自由体积的合并有关. 塑性变形过程中形成脉纹状断口形貌,受力状态的不同脉状花纹表现为不同的形式.     

TiC颗粒增强钛基复合材料的热变形行为及加工图

在Gleeble-1500热模拟实验机上对原位生成TiC颗粒增强钛基复合材料进行热压缩实验,研究变形温度为700～950℃,应变速率为0.001～1s-1时的热变形行为.研究结果表明:变形温度和应变速率对流变应力有显著影响,流变应力随变形温度的升高而降低,随应变速率的增加而升高.原位生成钛基复合材料在(α+β)相区激活能为357.09kJ/mol,β相区激活能为227.18k.J/mol,采用Zener-Hollomon参数法构建其高温塑性变形的本构关系.根据动态材料模型,建立原位生成钛基复合材料的加工图,并确定热变形的流变失稳区域.     

应力状态对AZ31镁合金最佳成形温度的影响

在20～250℃温度范围内,对AZ31镁合金薄板进行了单向拉伸、筒形件拉深以及胀形试验,并用金相显微镜观察了试验后试件的显微组织。分析了AZ31镁合金在不同工艺所对应的应力状态下塑性变形特点及其最佳成形温度。结果表明,变形过程中所受应力状态对AZ31镁合金最佳成形温度的影响很大,AZ31镁合金在成形过程中受单向拉应力时,其总延伸率随成形温度的升高而增加;应力状态主要为压应力时,最佳成形温度应在tr=1以下;而应力状态主要为双向拉应力时,其最佳成形温度应在tr=1以上。     

SA508-Ⅲ钢的氢致脆性行为

采用高温高压气相热充氢方法,将氢充入SA508-Ⅲ钢.在常温下,研究了氢与SA508-Ⅲ钢的拉伸变形行为的交互作用,以澄清钢的氢致脆性机理,为核电用钢的安全设计提供理论依据.结果表明,充氢使钢的屈服强度略升高,而钢的断面收缩率明显降低.充氢后钢的拉伸断口由纯微孔聚集型断口转变为韧窝加河流花样复合型断口.钢的屈服强度升高主要归因于在弹性变形阶段氢对位错的钉扎,从而阻碍了位错开动.然而在塑性变形阶段,氢随可动位错迁移并不断富集于碳化物与基体界面处,当氢浓度达到一定值时,造成碳化物与基体之间的结合强度降低,从而引起钢的塑性降低.