乙醇脱水对聚丙烯酸水凝胶pH敏感性的影响

以丙烯酸和无水乙醇为原料,N,N’-亚甲基双丙烯酰胺为交联剂,过硫酸钾和亚硫酸氢钠为引发剂制备了聚丙烯酸水凝胶,并研究了不同pH值的缓冲溶液对水凝胶溶胀度的影响。结果表明,水凝胶在酸性条件下的溶胀度比在碱性条件下大,pH值为4时的溶胀度最大,可达40倍。乙醇脱水干燥水凝胶的溶胀度和溶胀速率都得到了明显提高,且具有良好的温度敏感性和稳定性。     

PVA水凝胶的制备及其性能研究

以聚乙烯醇(PVA)为原料合成了PVA水凝胶膜,同时以水杨酸(SA)为抗菌剂合成了具有抗菌作用的PVA/SA水凝胶膜,表征了其结构与性能,发现其透明度均达95％以上,在15℃时,纯PVA水凝胶溶胀度达33.64％以上,加入SA后溶胀度为29.66％.这两种膜具有一定的透气性,其透气系数均在0.4～0.5 m2/S·kPa之间,两种膜没有抗紫外线性能,紫外线透过率均高达95％以上.PVA/SA水凝胶膜抗菌性远远优于PVA水凝胶.考察了PVA水凝胶膜和PVA膜的缓释性能,发现PVA水凝胶膜的药物释放速度相对于PVA膜而言,释放速度更加平稳,明显优于PVA膜的缓释性能.     

壳聚糖基水凝胶的制备及溶胀性能研究

壳聚糖(CS)具有良好的生物相容性,易生物降解,无毒,是一种很有发展前景的医药材料。壳聚糖基水凝胶作为一种新型的可注射给药载体,药物的控制释放具有易控性、靶向性。以壳聚糖(CS)为基材,聚乙烯醇为第2组分,戊二醛为交联剂,制备了一系列壳聚糖基水凝胶,研究该水凝胶在水中的溶胀行为、溶胀动力学以及相关影响因素。结果表明,所制备的一系列壳聚糖基水凝胶的溶胀度均随着溶胀时间的增加而增大,至溶胀4.5h时,凝胶的溶胀度基本达到最大。溶胀动力学为一级动力学。随着CS/PVA凝胶质量百分比的增加,该类水凝胶溶胀速率和饱和溶胀度呈现出3个性质明显不同的区域。     

PVA/TEOS/GA杂化膜的制备及溶胀吸附性能

采用溶胶-凝胶法(sol-gel)制备了PVA/TEOS/GA有机/无机杂化膜,比较杂化膜在3种不同温度下在乙醇/水全浓度范围的溶胀性能,分析无机相和交联剂对PVA膜溶胀性能的影响.比较不同溶胶-凝胶反应条件及不同热处理条件对膜溶胀度和溶解选择性的影响.用FTIR和XRD对杂化膜结构进行分析表征.结果表明PVA与无机相(TEOS)发生溶胶-凝胶反应生成氢键和共价键Si-O-Si,形成交联有机聚合物/无机杂化体系,使杂化膜的结晶度减少,控制了膜的溶胀,提高膜的溶解选择性能,但膜的溶胀减少会使通量有所下降.加入GA后,使PVA杂化膜溶胀度和溶解选择性都有所提高,表明PVA杂化有利于控制膜在乙醇/水溶液中的溶胀,从而提高膜的分离性能.     

医用聚乙烯醇水凝胶的制备及性能

采用反复冷冻、融化的方法制备了不同浓度、相同循环次数的聚乙烯醇(PVA)水凝胶和相同浓度、不同循环次数的PVA水凝胶。测试了PVA水凝胶的拉伸性能、溶胀率,再溶胀动力学。结果表明,拉伸强度随PVA含量的增加而增加;当浓度相同、循环次数不同时,再溶胀率随循环次数的增加而增加;当达到一个峰值时,随循环次数的增加而降低;当循环次数相同、浓度不同时,再溶胀率随浓度的增加而增加;当达到一个峰值时,随浓度的增加而降低。用物理交联和化学交联的方法制备了PVA/PAA互穿网络水凝胶,测试再溶胀行为,发现PVA/PAA互穿网络水凝胶具有温度敏感性。     

PEG致孔快速响应pH/温度双重敏感性PNIPAM/SA水凝胶的制备与性能

以聚乙二醇(PEG)为致孔剂,以海藻酸钠(SA)和N-异丙基丙烯酰胺(NIPAM)为原料,制备出具有温度和pH双重敏感性的快速响应水凝胶.研究温度、pH值对凝胶溶胀度,以及PEG用量和分子量对凝胶溶胀速率的影响.结果表明,海藻酸钠的加入能够赋于PNIPAM pH敏感性能,所制备水凝胶的溶胀度随着pH值的改变而改变.在酸性条件下,凝胶溶胀度随SA用量的增加而减小;在碱性条件下,凝胶溶胀度随SA用量的增加而增大.在酸性和碱性条件下,水凝胶溶胀度都随着PEG用量的增多和PEG分子量的增大而增大,且与传统水凝胶相比,溶胀速率有较大程度的提高.     

pH敏感性水凝胶的制备及其性能研究

以聚乙烯醇(PVA)和丙烯酸(AA)为原料,过硫酸铵(APS)为引发剂,N,N′-亚甲基双丙烯酰胺(MBA)为交联剂,通过化学引发聚合制备了具有互穿网络结构的聚乙烯醇/丙烯酸(PVA/PAA)水凝胶.用红外光谱(FT-IR)、热重分析(TG-DTA)、扫描电镜(SEM)对其结构、热稳定性和形貌进行了表征.研究了溶胀动力学,探讨了pH及盐浓度对水凝胶溶胀性能的影响,考察了该凝胶在不同pH介质中对药物异烟肼的控制释放行为.结果表明,PVA/PAA水凝胶具有良好的pH敏感性和离子强度敏感性,其在pH=1.20的缓冲溶液中对异烟肼的累积释放率明显大于在pH=7.40和pH=6.86的缓冲溶液中.     

CS/PVA水凝胶的制备与性能研究

以聚乙烯醇(PVA)为基体,以壳聚糖(CS)为功能性添加剂,采用冻融法与辐射法相结合的工艺技术制备出CS/PVA水凝胶.分别研究了吸收剂量和制备工艺对PVA水凝胶性能和SEM形貌的影响;研究了壳聚糖浓度和制备工艺对CS/PVA水凝胶溶胀性能和力学性能的影响;研究了CS/PVA水凝胶对大肠杆菌的抑菌效果.结果表明:采用先冻融后辐射方法制备PVA水凝胶,该制备工艺既解决了冻融法合成水凝胶不透明的问题,又解决了辐射法合成水凝胶起泡和强度较弱的问题. CS的添加,不仅提高了PVA水凝胶的溶胀性能,而且使得CS/PVA水凝胶对大肠杆菌具有较好的抑菌作用.     

pH敏感性壳聚糖/聚乙烯基吡咯烷酮水凝胶的制备及其性能

合成了pH敏感性壳聚糖/聚乙烯基吡咯烷酮水凝胶,研究了室温下该水凝胶在不同pH介质中的溶胀比.结果表明,在酸性溶液中凝胶的溶胀比远大于碱性溶液中的溶胀比,且其在不同pH溶液中重复可逆溶胀收缩.     

PVA/淀粉接枝P(AA-AM)互穿网络水凝胶的合成与性能研究

以马铃薯淀粉、丙烯酸(AA)、丙烯酰胺(AM)和聚乙烯醇(PVA)为原料,过硫酸钾为引发剂,三氯化铝为交联剂,利用水溶液法制备PVA/淀粉接枝AA、AM互穿网络水凝胶(PVA/St-g-P(AA-AM)IPN)。红外光谱(FT-IR)分析表明,PVA与St-g-P(AA-AM)间形成较强的氢键或部分共聚反应。X射线衍射(XRD)分析表明,当PVA用量较少时,PVA能均匀的穿插于凝胶网络中,形成完善的互穿网络结构;当PVA用量过多时,有部分的PVA结晶出现。水凝胶性能测试结果表明,随PVA用量增加水凝胶的吸水率先增大后减小,抗压缩强度不断升高,压缩应变持续降低,对蒸馏水的最大吸水率为650 g.g-1,在60min内达到溶胀平衡,保水性良好;水凝胶在pH<4时几乎不发生溶胀,在pH=12附近出现体积突变,表现出敏感的pH响应性。     

聚乙烯醇水凝胶与人关节软骨摩擦特性比较

利用自行研制的振子式摩擦仪测定了聚乙烯醇水凝胶自摩擦副、人关节软骨/聚乙烯醇水凝胶摩擦副的摩擦因数,并根据其Stribeck曲线对其摩擦润滑机理进行初步探讨.实验结果表明,在透明质酸润滑条件下,聚乙烯醇水凝胶与人关节软骨具有相似的摩擦学特性,且聚乙烯醇水凝胶自摩擦副的摩擦因数略小于聚乙烯醇水凝胶/人软骨的摩擦因数,由其Stribeck曲线初步判定其润滑机制为液膜润滑.     

Salt effects on formation of microcrystallites in poly(vinyl alcohol) gels prepared by cast-drying method

The preparation method of poly(vinyl alcohol)(PVA) gels by a simple cast-drying technique using salt solutions was reported in the present investigation.The effects of the salt concentration on the macro- and microscopic properties were examined in detail,and the relationships between macroscopic properties,such as swelling ratio,mechanical strength,and the network microstaicture were presented.It was found that the swelling ratio of PVA cast gel increased largely by adding a small amount of salt, and de...     

Compatibility of Soybean Protein and Poly (vinyl alcohol)

IntroductionTheuseofsoybean ,peanut,zeinandothervegetableproteinsasinexpensivefibermaterialstoreplacewoolandsilkcanbetracedbackto 1930s.Earlyin 1935 ,theItalianfirm ,SniaViscosa ,beganlarge scaleproductionofcaseinfibers[1] .Shortlyafterward ,ICIinEngland produced peanut proteinfibersknownasArdil.CoCornProductRefiningmanufacturedzeinproteinfiberin 1939.Theseusesofseedmealsintoindustryenhancethevalueoftheagriculturematerial.Thelargeintroductionofpetroleum basedfibersduring 194 0sand 195 0s…     

人工软骨材料-聚乙烯醇水凝胶的研制

聚乙烯醇溶液经反复冷冻-融化、真空脱水及辐照交联处理后,制得一种人工软骨材料PVA-水凝胶．通过光学显微镜和扫描电镜观察PVA-水凝胶的微观形貌;通过差示扫描量热法（DSC）及相应的力学性能试验研究反复冷冻-融化、真空脱水和辐照交联对PVA-水凝胶结晶和力学性能的影响．该PVA-水凝胶的力学性能与人关节软骨相近,可望用于人工软骨材料．     

壳聚糖/聚乙烯醇/氧氟沙星共混无纺布的制备及体外释放研究

以静电纺丝法制备了具有抗菌性能的壳聚糖/聚乙烯醇/氧氟沙星共混无纺布,测定了共混无纺布的力学性能,通过红外光谱(FT-IR) 、X-射线衍射(XRD)和扫描电子显微镜(SEM)对其结构性能进行了表征,选出了载药量较大、力学性能较好(壳聚糖/聚乙烯醇质量比为7,氧氟沙星质量分数为4%)的共混无纺布,在不同pH值的缓冲溶液中对其进行了体外药物释放实验。结果表明,所得的无纺布纤维直径均匀,平均为200nm。聚乙烯醇可以改善氧氟沙星/壳聚糖/聚乙烯醇共混无纺布的力学性能;氧氟沙星在壳聚糖/聚乙烯醇共混膜中有良好的相容性;氧氟沙星在pH为7.40的缓冲溶液中达到释放平衡时需要6h。     

透明低温凝胶力学性能的研究

采用低温处理方法，制得了含液量在８５％以上，透光度高达９９％且具有较高强度和模量的“ＰＶＡ－ＤＭＳＯ－水”凝胶，用单向压缩和单向拉伸法研究了其力学性能，实验发现，该低温凝胶的弹性模量随两混合溶剂配比的不同而发生变化，在ＷＨ２Ｏ／ＷＤＭＳＤ＝２０／８０时，弹性模量最大，此时该凝胶的透明性最好，随着低温处理时间的增长，凝胶模量也增大，同时凝胶模量也随着体系中聚合物浓度的增大而增大。     

Swelling Studies of Chitosan-Gelatin Films Cross-Linked by Sulfate

0　IntroductionChitosanisadeacetylatedderivativeofchitin ,containinginitsstructure glucosamineandacetylglucosamine joinedthroughβ (1→ 4 )linkages.ItisinsolubleinwaterandcommonorganicsolventsbutsolubleatapHunder 6 .5acidicmedia.Duetoitsexcellentbiodegradableandbiocompatiblecharacter,chi tosanhasbeenexaminedextensivelyinthepharmaceuticalindus tryforitspotentialinthedevelopmentofdrugdeliverysys tems[1 ,2 ] .Gelatinisabiodegradablepolymerofwidesafety ,pro ducedfromcollagen ,themostabundantprote…     

原位聚合法制备聚苯胺/ 聚乙烯醇导电材料的研究

采用原位聚合方法合成了聚苯胺／聚乙烯醇导电复合材料,研究了反应体系中聚苯胺的质量分数和反应时间对复合材料电导率的影响,并且通过红外光谱和热重分析对其结构和稳定性进行了表征和分析．     

高强度物理-化学混杂双网络水凝胶的制备及性质

以聚乙烯醇（polyvinyl alcohol, PVA）和丙烯酰胺（acrylamide, AM）为原料, 采用“一锅煮”及紫外辐照结合冷冻 解冻两步聚合法制备聚乙烯醇/聚丙烯酰胺(PVA/PAM)混杂双网络水凝胶, 并对水凝胶的力学性能、 溶胀性能、 失水性能以及自愈合性进行测试和分析. 结果表明, PVA/PAM混杂双网络水凝胶具有较高的力学强度, 其拉伸强度为428 kPa, 失水速率和单网络水凝胶相比较慢, 具有一定的自愈合性.     

海藻酸-羧甲基壳聚糖/聚乙烯醇水凝胶的制备及对蛋白药物释放的探讨简

以牛血清白蛋白（BSA）为模型药物,制备了海藻酸-羧甲基壳聚糖（CMCS）/聚乙烯醇（PVA）复合水凝胶,考察了海藻酸水凝胶微球的粒径和微球在水凝胶基质中的分散性,分析了复合水凝胶基质的结构、溶解分数以及水凝胶在不同pH值下的溶胀率和药物释放。结果表明,药物的累积释放率（犆R）随pH值的升高而升高,当pH值为1．2时CR 为32％,当pH值为6．8时犆R 为53％,当pH值为8．0时CR 达到70％,表明该复合水凝胶的释药性能受pH值的影响较大。