Eu_（1－x）Sr_xFeO_（3－y）的~（57）Fe Mossbauer谱

报导Ｅｕ＿（１－ｘ）Ｓｒ＿ｘＦｅＯ＿（３－ｙ）（ｘ＝０．０～１．０）的固相反应法合成，测量了其Ｘ射线衍射及室温下的￣５７ＦｅＭｏｓｓｂａｕｅｒ谱。实验结果表明，Ｓｒ掺入了ＥｕＦｅＯ＿３晶格，结构变化与掺杂量密切相关。室温下￣５７ＦｅＭｏｓｓｂａｕｅｒ谱由一套反铁磁六线谱、一套顺磁双线谱和一套顺磁单线谱组成（Ｘ＝０．２，０．４，０．６）．处于立方相的Ｆｅ离子的ＩＳ介于Ｆｅ￣３＋和Ｆｅ￣４＋之间，可能参与电子跳跃。     

电弧法制备了Fe—C合金超微粒的分析

用电弧法制备了以Ｆｅ和Ｃ为原材料的超微粒,通过Ｘ射线衍射,Ｘ射线光电子能谱,电子显微镜和电子衍射观测和分析了样品的形态,结构和成分,并与以Ｆｅ为原材料制备的微粒进行了对比分析,结果表明,用电弧法能够制备出含有ＦｅｘＣ１－ｘ相的合金超微粒,较Ｆｅ超微粒而言,含ＦｅｘＣ１－ｘ相的合金超微粒抗氧化能力有所增强。     

纺锤型γ－FeOOH的合成及其热分析研究

采用空气氧化ＦｅＳＯ４与Ｎａ２ＣＯ３作用生成的Ｆｅ（ＣＯ３）ｘ（ＯＨ）２（１－ｘ）悬浮液体系，通过稀土离子Ｙ３＋的掺杂合成出均匀纺锤型铁黄γ－ＦｅＯＯＨ微晶．由ＤＴＡ－ＴＧ和ＸＲＤ分析得出γ－ＦｅＯＯＨ随温度升高，发生如下相变过程：γ－ＦｅＯＯＨ→γ－Ｆｅ２Ｏ３→α－Ｆｅ２Ｏ３．本文还对γ－ＦｅＯＯＨ的脱水过程机制和以γ－ＦｅＯＯＨ为中间体经热处理制备的纺锤形γ－Ｆｅ２Ｏ３磁性能作了初步探讨．     

Sm2Fel7-xGaxCy化合物磁晶各向异性的晶场分析

用单离子模型晶场理论计算了Ｓｍ２Ｆｅ１７－ｘＧａｘＣｙ化合物的磁晶各向异性场随温度和Ｇａ、Ｃ含量的变化关系,讨论了不同晶位的Ｇａ原子和间隙位Ｃ原子对磁晶各向异性的贡献。从而解释了Ｇａ原子对Ｓｍ２Ｆｅ１７－ｘＧａｘ和Ｓｍ２Ｆｅ１７－ｘＧａｘＣｙ化合物磁晶各向异性的影响。     

电弧法制备Fe-C合金超微粒的分析

用电弧法制备了以Ｆｅ和Ｃ为原材料的超微粒．通过Ｘ射线衍射、Ｘ射线光电子能谱、电子显微镜和电子衍射观测和分析了样品的形态、结构和成分,并与以Ｆｅ为原材料制备的微粒进行了对比分析．结果表明,用电弧法能够制备出含有ＦｅｘＣ１－ｘ相的合金超微粒．较Ｆｅ超微粒而言,含ＦｅｘＣ１－ｘ相的合金超微粒抗氧化能力有所增强．     

红外光谱中溶剂效应机理研究（Ⅴ）：有机锡络合物红外光谱的溶…

用Ｃｙ２ＢｕＳｎＯ２Ｃ－Ｃ６Ｈ４－ｘ，Ｃｙ２ＭｅＳｎＯ２Ｃ－Ｃ６Ｈ４－ｘ，ＣｙＢｕ２ＳｎＯ２Ｃ－Ｃ６Ｈ４－ｘ（ｘ＝Ｈ，ｐ－ＣＨ３，ｐ－ＣＨ３Ｏ，ｐ－ＮＯ２，ｐ－Ｆ，ｐ－Ｃｌ，ｐ－Ｉ，ｐ－ＯＨ，ｐ－ＮＨ，ｍ－ＮＯ２，ｍ－ＣＨ３Ｏ）３个系列共１８种取代苯甲酸配位的有机锡络合物在１３种有机溶剂（环己烷、正庚烷、四氯化碳、苯、甲苯、乙醚、氯仿、二氯甲烷、１，２－二氯乙烷、四氢呋喃、对二氧六环、乙腈）中的羰     

Co含量对Fe1—xCox—SiO2纳米合金颗粒体晶体结构和磁性的…

利用溶胶法制备了Ｆｅ１－ｘＣｏｘ－ＳｉＯ２纳米颗粒体材料，并首次利用Ｘ射线衍射仪，透射电子显微镜和振动样品磁强计研究了这种材料中Ｃｏ含量对晶体结构和磁性的影响。结果表明，样品中Ｆｅ－Ｃｏ合金微粒的晶体结构与Ｃｏ含量的关系和大块Ｆｅ－Ｃｏ合金相似；合金微粒的比饱和磁化强度σｓ随Ｃｏ含量的变化规律与粉状纯Ｆｅ－Ｃｏ合金相似。     

红外光谱中溶剂效应机理研究（Ⅴ）──有机锡络合物红外光谱的溶剂效应

用Ｃｙ２ＢｕＳｎＯＣ－Ｃ６Ｈ４－ｘ，Ｃｙ２ＭｅＳｎＯ２Ｃ－Ｃ６Ｈ４－ｘ，ＣｙＢｕ２ＳｎＯ２Ｃ－Ｃ６Ｈ４－ｘ（Ｘ＝Ｈ、ｐ－ＣＨ３、ｐＣＨ３Ｏ、ｐ－ＮＯ２、ｐ－Ｆ、ｐ－Ｃｌ、ｐ－Ｉ、ｐ－ＯＨ、Ｐ－ＮＨ２、ｍ－ＮＯ２、ｍ－ＣＨ３Ｏ）３个系列共１８种取代苯甲酸配位的有机锡络合物在１３种有机溶剂（环己烷、正己烷、正庚烷、四氯化碳、苯、甲苯、乙醚、氯伤、二氯甲烷、１，２－二氯乙烷、四氢呋喃、对二氧六环、乙腈）中的羰基伸缩振动波数（以下简写为ｖｃ＝０）和氯仿在７种溶剂（硝基甲烷、乙腈、乙酸乙酯、四氯化碳、环乙烷、对二氧六环、四氢呋喃）中的ｖｃ－ｃ１的溶剂效应，验证了先前提出的经验方程．     

R2Fe17—xCrx（R=Y,Dy,x≤3）化合物的磁交换作用

利用Ｘ射线衍射的方法及磁性测量手段研究了Ｒ２Ｆｅ１７－ｘＣｒｘ（Ｒ＝Ｙ,Ｄｙ,ｘ≤３）化合物,给出了其居里点的变化情况,即随ｘ的增大,居里温度增大,在ｘ近似为１．０时达到最大值。利用分子场理论计算了磁交换作用系数并从磁交换作用出,对其居里温度的变化情况进行了分析。     

针形α—Fe磁粉表面氧化处理研究

采用针形铁黄（α－ＦｅＯＯＨ）还原制备得到针形α－Ｆｅ金属磁粉，然后将其浸入甲苯中，慢速空气氧化制得样品．用透射电子显微镜（ＴＥＭ）观察其表面形貌，采用Ｘ－射线衍射（ＸＲＤ），Ｘ－射线光电子能谱（ＸＰＳ）分析其组成与结构．提出α－Ｆｅ粒子表面双层缺陷氧化膜（内层Ｆｅ３Ｏ４，外层γ－Ｆｅ２Ｏ３）的模型，用热处理的方法证实了它的存在，并得出有序氧化物结构可改善α－Ｆｅ磁粉稳定性的有益结果     

合金成分对Nd2Fe14B/α-Fe纳米双相复合稀土永磁材料结构和性能的影响

采用熔体直接快淬(DRQ)工艺制备了成分为NdxFe94-xB6(x=7,8,9,10at%)和Nd8Dy1Fe85-xNbxB6(x=0,0.5,1,1.5at%)两组合金的最佳快淬薄带.用X射线衍射(XRD)和振动样品磁强计(VSM)测量了薄带的相结构和磁性能.结果表明:NdxFe94-xB6(x=7,8,9,10)合金在x=8时综合磁性能最佳;同时添加少量的Dy和Nb元素,可有效的提高纳米双相复合永磁合金的磁性能.     

基于双亚点阵模型对H13钢中初生碳氮化物的研究

实验证明H13钢中存在三类初生碳氮化物,包括富V和C的(Vx,Mo1x)(Cy,N1-y)、富Ti和N的(Tix,V1x)(Cy,N1-y)及富V和C的(Tix,V1-x)(Cy,N1-y),部分存在形核核心.基于双亚点阵模型和凝固偏析模型分析计算H13钢凝固过程中元素含量变化,考虑初生碳氮化物中元素间的相互作用,根据三类碳氮化物中合金元素含量和C/N比值不同,对各碳氮化物的生成自由能进行分析.理论研究指出富Ti和N的(Tix,V1-x)(Cy,N1-y)在固相率为0.90时即可生成,而富V和C的(Tix,V1-x)(Cx,N1-y)在固相率大于0.96才可生成,两类碳氮化物的临界生成固相率fP均随固溶Ti和N含量的增加而减小.(Vx,Mo1-x)(Cy,N1-y)的临界生成固相率与x值密切相关,x减小时fP降低,粒子尺寸增加,实验与理论分析吻合良好.根据错配度分析氧化物和碳氮化物对H13钢中初生碳氮化物异质形核的作用.     

Nd4.5-xTbxFe75.5B20(x=0;1)纳米晶的磁性

利用熔体快淬和晶化热处理法制备了成分为N d4.5-xT bxF e75.5B20(x=0;1)的纳米晶复合永磁合金,采用x射线衍射及V SM分析研究了材料的显微结构与磁性.结果显示,退火工艺对两种合金磁性能的影响显著,且原子分数为1%的稀土元素T b掺杂明显提高了材料的磁性.     

Tunable and enhanced luminescence of Ba2−xCaxSiO4−yN2/3y:Eu2+ phosphors for white light-emitting diodes

Color tuning and luminescence enhancement are predominant challenges for improving the performance of white light emitting diodes(LEDs) toward commercial application. In this paper, a novel promising Ba_(2-x)Ca_xSiO_(4-y)N_(2/3y):Eu~(2+) tphosphors with tunable and enhanced luminescence for phosphors converted LEDs(pc-LEDs) have been successfully synthesized by a direct gas-reduction nitridation method. The effects of Ca and N doping on the phase purity, morphology and optical properties of Ba_(2-x)Ca_xSiO_(4-y)N_(2/3y):Eu~(2+) tphosphors were also systematically investigated. The optical results show that Ba_(2-x)Ca_xSiO_(4-y)N_(2/3y):Eu~(2+) tphosphors can be actively excited over a broad range from 250 to430 nm. With the adding of different concentrations of Ca~(2+) tions in phosphors, the emission color wavelength can be tailored from 501 to 441 nm by a 375 nm NUV LED excitation source. Furthermore, it has been found that the emission and absorption of Ba_(2-x)Ca_xSiO_(4-y)N_(2/3y) tphosphor can be significantly improved when N~(3-) ions were introduced into the host lattices. The intensity of Ba_(1.5)Ca_(0.5)SiO_(4-y)N_(2/3y):Eu~(2+) tphosphor was 3.4 times higher than the phosphor without N doping. The fabrication and characterization of pc-LEDs using Ba_(2-x)Ca_xSiO_(4-y)N_(2/3y):Eu~(2+) tphosphors-silica gel as the coating layer onto 375 nm-emitting In Ga N LED caps demonstrated the superior optical and current tolerant properties,making it a promising and competitive candidate for commercial utilization in white LED applications.     

Bi4－xNdxTi3O12单晶的光谱学特性研究

使用自助熔生长法生长Bi4－xNdxTi3O12（BNdT,x=0,0．5,0．85）单晶,研究了Nd掺杂对BNdT单晶光谱学特性的影响．常温拉曼光谱结果表明：随Nd含量的增加,BNdT中TiO6八面体振动模式有所增强;Nd含量增加到一定值,BNdT单晶可能在常温下发生铁电-N电相转变;位于（Bi2O2）^2＋层的Bi-O振动模式随Nd掺杂量增加而减弱,表明Nd含量较低时,Nd^3＋离子仅仅取代伪钙钛矿层的Bi^3＋离子,当Nd含量较高时,有部分Nd^3＋离子开始替换（Bi2O2）^2＋层中的Bi^3＋离子．紫外-可见光谱结果表明,BNdT单晶具有间接带隙跃迁的特点,而且单晶的禁带宽度随Nd掺杂含量的增加而减小。     

Study of transport behavior for Fe-doping La(0.67)Ca(0.33)MnO3 perovskite manganese

Systematic studies of the transport properties of La0.67Ca0.33Mn1-xFexO3 (x=0-0.3) systems showed that with increasing Fe-doping content x the resistance increases and the insulator-metal transition temperature moves to lower temperature. For small doping content, the transport property satisfies metal transport behavior below the transition temperature, and above the transition temperature it satisfies the small polaron model. This behavior can be explained by Fe^3 doping, which easily forms Fe^3 -O^2- -Mn^4 channel, suppressing the double exchange Mn^3 -O^2- -Mn^4 channel and enhancing the spin scattering of Mn ions induced by antiferromagnetic clusters of Fe ions.     

BaxSr(1-x)TiO3弛豫铁电体的制备及性能研究

用传统的固相反应法制备Ba0．5Sr0.5TiO3和Ba0.7Sr0.3TiO3 2种Ba,Sr比的BST陶瓷体．并研究了其介电性和弛豫性,由频谱关系和温谱关系了解到,A位取代的BST复合钙钛矿结构仍具有和铅系B位取代陶瓷相类似的弛豫性。     

Tb_(0.3)Dy_(0.7-x)Pr_x(Fe_(0.9)Al_(0.1))_(1.95)合金的磁性、磁致伸缩和穆斯堡尔谱

系统研究了室温下Tb0.3Dy0.7-xPrx(Fe0.9Al0.1)1.95(x=0,0.1,0.2,0.25,0.3,0.35)合金中稀土元素Pr替代Dy对磁性、磁晶各向异性、磁致伸缩和穆斯堡尔谱的影响.对磁化强度和磁致伸缩的测量发现,少量Pr替代有助于降低磁晶各向异性;随着替代量x的增多磁致伸缩减小,x>0.2时超磁致伸缩效应消失.然而,x=0.1时合金的磁致伸缩略大于没有替代的,而且磁致伸缩随磁场更易趋于饱和;同时发现,随着Pr替代量x的增加,饱和磁化强度和Curie温度单调下降,而内禀磁致伸缩急剧增大.多功能磁性测量系统PPMS的研究和Mossbauer效应表明,随着Pr含量的增加,合金中的易磁化轴可能在{110}面上绕主对称轴作微小转动,发生自旋重取向.与Al元素替代效应相比,Pr替代Dy对自旋重取向的影响相对较小.     

Cu低掺杂对La0.7Ca0.3MnO3电阻及磁电阻的影响

用溶胶凝胶法制备了Cu低掺杂的La0.7Ca0.3Mn1-xCuxO3(x=0%,1%,2%,3%,4%,5%)系列多晶材料.采用振动样品磁强计测量了系列样品的热磁曲线并获得了相应的居里温度,实验结果表明居里温度随着Cu掺杂量的增加而减少.在77~350 K温度范围内测量了样品的电阻和磁电阻,结果表明样品电阻率与温度的关系均具有明显的电阻峰结构.当x=5%时,开始出现双电阻峰结构;掺杂量x为1%,2%,3%,5%的样品在外场为0.4 T时存在较大的磁电阻极大值,分别为30.5%,25.4%,22.4%,18.8%,均大于未掺杂(x=0%)的13.5%.双交换(DE)模型简单地解释了Cu低掺杂对电阻及磁电阻行为的影响.     

高温时H13钢中初生碳氮化物的分解研究

利用光学显微镜、扫描电镜和电子探针研究了H13钢中初生碳氮化物高温分解时的形貌、尺寸、成分变化规律.原始初生碳氮化物主要为10~30μm的长条状(Vx,Mo1-x)(Cy,N1-y)及少量方形的(Tix,V1-x)(Cy,N1-y).在1200℃保温2.5 h后碳氮化物边缘变为凹凸不平的锯齿状,然后形成细小的分解颗粒,10 h后碳氮化物平均长度减小为12.9μm,主要为(Tix,V1-x)(Cy,N1-y).当经过1250℃ ×5 h保温后87%的碳氮化物发生分解,(Vx,Mo1-x)(Cy,N1-y)溶解消失,碳氮化物长度在20μm以下,当保温时间延长到10 h后碳氮化物长度均在10μm以下,70%为方形并且93%分解形成细小颗粒,未分解的碳氮化物为(Tix,V1-x)(Cy,N1-y).电子探针分析(Tix,V1-x)(Cy,N1-y)的分解与Fe元素扩散有关,高温时Fe在(Tix,V1-x)(Cy,N1-y)中含量逐渐增加而Ti、V减少,优先在边部曲率半径较小部位或缺陷处分解,形成0.1~1μm的细小分解颗粒,并由外向内以区域溶解方式使原始碳氮化物逐渐消失.双亚点阵模型分析两种碳氮化物的平衡溶解温度和组成有关,试样中大部分(Tix,V1-x)(Cy,N1-y)平衡溶解温度在1200~1246℃之间,与实验吻合较好.