THE ADSORPTION OF STARCHES ON PRESSURE-SENSITIVE ADHESIVE MATERIAL AND ITS IMPACT ON AGGLOMERATION

Pressure sensitive adhesive (PSA) particles, or stickies, will self-agglomerate in water with agitation.Under certain conditions, it was found that some starches and Poly-Diallyldimethylammonium Chloride prevent this agglomeration. Both cationic and neutral starches were found to adsorb onto the surface of the negatively charged stickies. This was determined by infra-red spectroscopy, UV spectroscopy, contact angle measurements and charge titration methods. Cationic charge promotes the adsorption of starch onto the surface of stickies and cationic starches adsorbed on the PSA film do not desorb when exposed for 15 minutes to deionized water at room temperature. Cationic starches were found to prevent the agglomeration of stickies at lower concentrations relative to neutral starches.Stickies compete with fibers for the cationic charge in the system. Over the molecular weight (MW)range studied, the MW of the starch has no effect on the prevention of agglomeration of stickies.     

磷酸型两性淀粉糊化性质的研究

运用Brabender粘度计对磷酸型两性淀粉的粘度曲线进行了测定，研究考察了不同阴、阳离子取代度不同pH值对磷酸型两性淀粉糊化性质的影响，并同原淀粉及阳离子淀粉的糊化性质作了比较。结果表明：磷酸型两性淀粉经阳离子淀粉具有较高的热稳定性和冷粘稳定性；阳离子取代度及阴阳离子比对磷酸型两性淀粉的糊化性质有很大的影响；磷酸型两性淀粉还具有一定的抗酸降解能力，在pH值为9．0的稀碱溶液中，碱对磷酸型两性淀粉的糊化没有明显的促进作用。     

阳离子淀粉在草浆上的吸附行为

研究了阳离子淀粉在不同种类的草浆上的吸附行为。结果表明,草浆比木浆更有利于原淀粉的吸附;阳离子淀粉的吸附速率和吸附率由草浆种类所决定;原淀粉在麦草化学 的吸附率随打浆度升高而降低,而阳离子淀粉的情况则与此相反;原淀粉和阳离子淀粉在渣机械浆上的吸附率都较低。不同浆种的纤维形态特征和表面电荷密度的差异可解释上述结果。     

无机电解质对淀粉在纸浆上吸附的影响

考察了无机电解质 Na Cl、Na2 SO4 和 Al2 ( SO4 ) 3 对淀粉在混合木浆和麦草浆上吸附的影响 .实验结果表明 :在使用的盐浓度范围内 ,无机盐的存在可促进原淀粉在两种浆上的吸附 ,但大幅减小阳离子淀粉的吸附率 .三种无机电解质对淀粉吸附的影响也各不相同 .这些结果能被氢键作用机理、邻位水层模型和DLVO理论解释     

球磨-酯化复合改性槟榔芋淀粉对Pickering乳液形成的影响

为了提高淀粉颗粒的乳化能力,以球磨-酯化复合改性槟榔芋淀粉为颗粒乳化剂,大豆油为油相,制备水包油型Pickering乳液。采用激光粒度仪、研究级正置显微镜、流变仪等对Pickering乳液外观、液滴粒径、显微形态及动态流变特性进行表征,考察淀粉颗粒质量浓度(1、5、10、20、30mg/mL)和油相体积分数(10%、20%、30%、40%、50%)对乳液稳定性和流变特性的影响。研究发现:增加颗粒质量浓度导致乳化相体积增加,液滴粒径减小;随着油相体积分数的增加,乳化相体积增加,液滴粒径增大。当颗粒质量浓度为20mg/mL,油相体积分数为40%时,乳液的乳析现象明显改善。球磨-酯化复合改性槟榔芋淀粉颗粒吸附在油/水界面,有效抵抗了液滴聚结,使乳液在储存30d后仍表现出良好的稳定性。流变特性表明:乳液内部存在弹性凝胶网络结构,随着颗粒质量浓度和油相体积分数的增加,液滴间堆积变得更紧密,从而增加了乳液黏度和凝胶强度,使其抵抗形变能力增强。球磨-酯化复合改性槟榔芋淀粉颗粒具有良好的作为Pickering乳液稳定剂的潜力。     

AKD-LT中性/碱性造纸施胶剂的研制

系统分析和讨论了阳离子树脂型ＡＫＤ施胶剂的制备工艺和影响乳液性能的多种因素。发现ＡＫＤ乳化温度和时间、分散剂的选择和树脂的阳离子度对ＡＫＤ胶的粒径、乳液稳定性及施胶效能有较大的影响。结果表明树脂型ＡＫＤ胶具有更高的阳电荷密度、更长的有效贮存期和更好的施胶效能，且不易霉变。     

变性淀粉在赤铁矿阳离子反浮选脱硅中的抑制性能

以十二胺为捕收剂,木薯原淀粉、取代度为0.026和0.21的羧甲基淀粉和取代度为0.0065和0.055的磷酸酯淀粉作为抑制剂,考察了赤铁矿与石英的可浮性,重点研究了基团取代度对变性淀粉抑制性能的影响.结果表明:原淀粉、取代度0.026的羧甲基淀粉和取代度0.0065的磷酸酯淀粉对赤铁矿有良好的抑制作用,而取代度0.21的羧甲基淀粉和取代度0.055的磷酸酯淀粉对赤铁矿的抑制能力较弱;原淀粉和取代度0.026的羧甲基淀粉对石英有较强抑制作用,其他3种淀粉对石英抑制能力较弱.可见,低取代度的磷酸酯淀粉,在赤铁矿阳离子反浮选脱硅中可作为较高选择性的抑制剂.Zeta电位测定结果表明,特征基团取代度相对较高的变性淀粉,与赤铁矿和石英作用后,矿物Zeta电位负值较大.变性淀粉的取代度越高,其伸展向溶液中荷负电的基团越多,使阳离子捕收剂通过静电作用吸附于矿物表面,减弱了变性淀粉的抑制能力.     

Alkyl Ketene Dimer (AKD) Paper Sizing Efficiency in Term of Fiber Surface Charge

The charge density of cellulose fibers is a key parameter in the papermaking systems,and this is particularly true for the Alkyl Ketene Dimer( AKD) paper sizing.Zeta potential and cationic demand are often used to characterize these charges.Generally,a similar sizing performance would be obtained when the fibers with similar morphology and charge characteristics are used.However,in a mill trial,it was shown that three bleached birch pulp samples,with similar fiber morphology,and zeta potential,had different AKD sizing behaviors.In this study,the surface charges of these pulp samples,measured using the polyelectrolyte titration methods,were investigated.The results showed that lower sizing efficiency of fibers were due to their lower surface charges.It was concluded that the direct measurement of surface charge of cellulose fibers can be more appropriate to evaluate the AKD paper sizing efficiency.     

Influences of Electrolytes on Soap-Free P（ST-MMA-AA） Emulsion Polymerization

1 Introduction Functional polymer microspheres are kinds of polymer particles with special structures, morphologies or functional groups~([1]), and have been gained much attention because of their specific properties and their application since 1980s. Although some researches have investigated that the latex particle size and its distribution, as well as the stability of polymerization and the resultant latex were strongly influenced by introducing electrolyte into the emulsion polymerization …     

pH值对淀粉酯化反应的影响

用化学分析方法和红外光谱法测定了在不同pH值下制备的一系列醋酸酯淀粉的取代度和乙酰基含量,获得了pH值对淀粉酯化反应的影响规律,并解释了该规律。     

乳液粒子的性能对最低成膜温度的影响

讨论了乳液粒子的粒度，形态以及单体的亲水性对乳液最低成膜温度的影响。乳液粒子粒度大，ＭＦＴ高，反之则低。ＭＦＴ随乳液体系的多分散性变化而变化。乳液粒子的形态影响ＭＦＴ，粒子外壳为硬聚合物的，ＭＦＴ高，反之则低，新水性单体倾向于留在乳液粒子的外壳层，因而ＭＦＴ的取值依赖于亲水单体的性能。     

阳离子微粒聚合物在造纸工业中的应用

采用乳剂和溶液的聚合技术制备了不同电荷密度和胶体性质的阳离子微粒聚合物(CPMP)。论文探讨了阳离子微粒聚合物在造纸工业中的应用。研究表明用阳离子或阴离子的聚合物与阳离子微粒聚合物联合使用可以改善纸张的匀度和留着率。其机理可能是由干阳离子微粒聚合物的加入产生了更有效的架桥絮聚。另外阳离子微粒聚合物也是一种良好的施胶剂，研究结果表明施胶效果与聚合物添加量．电荷密度和微粒尺寸有关。通过施胶张可以获得更好的光学和物理性能。     

改性气相SiO2和膨润土稳定环氧树脂水基乳液的研制

采用物理方法对SiO2粒子进行表面改性,并用改性纳米粉体气相SiO2和膨润土分别作乳化稳定剂,通过转相乳化法制备环氧树脂水基乳液,结果表明:通过对气相SiO2表面改性或向膨润土中添加亲水性微粒均能促成乳状液的转相跃迁.气相SiO2的表面润湿性对这种水基乳液的稳定性产生影响的主要原因体现在两个方面:一是用做改性剂的阳离子...     

高取代度阳离子淀粉电荷性质

采用胶体滴定法对高取代度阳离子淀粉的电荷性质进行研究．研究结果表明,高取代度阳离子淀粉的电荷性质受pH值和贮存时间的影响较大,热糊化和冷糊化对其电荷性质影响不大,采用胶体滴定和凯氏定氮两种方法测定高取代度阳离子淀粉的取代度试验结果相差较大．     

重组草酸青霉生淀粉糖化酶的酶学特性鉴定

【目的】了解在毕赤酵母中表达的来源于草酸青霉(Penicillium oxalicum)GXU20的重组生淀粉糖化酶的酶学特性。【方法】用3,5-二硝基水杨酸法测定pH值、温度、金属离子和化学试剂对纯化的重组生淀粉糖化酶的活力的影响,同时测定酶的底物特异性、酶对生淀粉的吸附能力以及酶对不同生淀粉的水解效率等,用高效液相色谱法对该酶水解生木薯淀粉的产物进行分析鉴定,用扫描电子显微镜观察重组酶对不同生淀粉颗粒的水解方式。【结果】重组生淀粉糖化酶rPoGA15A的最适pH值为4.5,最适温度为65℃,在pH值为2.0~10.0时,重组酶具有较好的pH耐受性,温度小于50℃时,酶的稳定性好。除Ag~+、Cu~(2+)和SDS之外,其他大部分金属离子和化学试剂对重组酶的酶活力影响不大。重组生淀粉糖化酶对大米和玉米生淀粉的活性较高,对木薯和马铃薯生淀粉的活性次之,重组生淀粉糖化酶rPoGA15A对不同生淀粉的吸附能力与其对相应不同生淀粉的水解活性大小呈正相关。扫描电子显微镜观察表明重组生淀粉糖化酶对不同生淀粉颗粒的降解作用明显,水解方式各有特点。高效液相色谱分析表明该重组生淀粉糖化酶水解生木薯淀粉的产物仅有葡萄糖。重组生淀粉糖化酶rPoGA15A在40℃下对大米和玉米生淀粉水解72h后水解率分别达到86.5%和71.9%。【结论】重组生淀粉糖化酶具有广泛的pH耐受性,对生淀粉具有高水解活性,在生淀粉的水解和生料同步糖化发酵生产酒精中有一定的应用潜力。     

新型阳离子淀粉的研究

对两类新型阳离子淀粉——阳离子羟乙基淀粉和阳离子苄基淀粉的合成方法进行了研究．通过元素分析和红外光谱对其进行了初步表征．元素分析表明，所得产物取代度小于０．２；红外光谱分析表明在阳离子淀粉中引入了羟乙基和苄基，与预期结构相符．此外，对两类新型阳离子淀粉的某些使用性能如絮凝性、破乳性进行了初步探讨，并与普通阳离子淀粉进行了比较．试验表明，阳离子羟乙基淀粉具有较好的絮凝性能；阳离子羟乙基淀粉、阳离子苄基淀粉对破乳剂有增效作用，且可改善脱出水的水质．两种新型阳离子淀粉比普通阳离子淀粉具有更好的使用性能．     

St/BA/DBMPA无皂阳离子共聚物乳胶粒研究

选用苯乙烯（St)、丙烯酸丁酯（BA）和少量的反应性阳离子共聚单体N,N－二甲基,N－丁基,N－（3－甲基丙烯酰胺基）丙基溴化铵（DBMPA）,以阳离子自由基型引发剂引发进行无皂乳液聚合,合成了稳定的无皂阳离子共聚物St/BA/DBMPA乳液。研究结果表明：增大阳离子单体浓度、引发剂浓度和主单体St/BA体积比,共聚物乳胶粒粒径减小,粒子数目增大;增大离子强度,粒径呈现一个增大－减小－增大的变化过程;粒子的表面电荷密度也由以上4个因素决定。所合成的乳液表面张力小,耐电解质和耐有机溶剂性能好,说明该乳液具有很高的化学稳定性。胶膜经高温处理后,耐水性大大提高。     

聚季铵盐絮凝剂的合成及其性能的研究

本文以二叔胺与二卤代烃为原料合成了十四种聚季铵盐,讨论了不同原料对缩聚反应以及缩聚物结构对其絮凝性能的影响。通过絮凝效应的测定,探讨了这些聚季铵盐的絮凝特性和Zeta电位变化等。结果表明,对悬浮颗粒的电荷中和是聚季铵盐具有絮凝效应的重要原因之一。聚季铵盐和其它高分子絮凝剂类似,在溶液中对悬浮颗粒也具有架桥作用,因此,聚季铵盐分子量大小对絮凝效果也有一定影响。这类絮凝剂在中性、弱碱性且电解质浓度不高的溶液中絮凝效果较好。聚季铵盐化合物有可能成为具有实际应用价值的一类阳离子型有机絮凝剂。     

功能型丙烯酸乳液的合成及其性能

以一种阴离子表面活性剂与辛烷基酚聚氧乙烯醚为复合乳化剂，在基体配方中加入多种功能单体，采用半连续滴加方法制备了室温自交联型丙烯酸乳液，讨论了功能单体丙烯酸含量、单体滴加时间对丙烯酸乳液的流变性能、乳胶膜的交联度及耐水性的影响。结果表明：随着丙烯酸含量增加，其乳液粘度上升，乳胶膜交联度增加、吸水率先下降后上升；增加单体滴加时间，可使乳胶粒平均粒径变小，分布变窄，相应生成的乳液粘度变小，同时其乳胶膜交联度上升，吸水率下降。     

阳离子聚丙烯酰胺表征及其阳离子度测定方法

采用反相微乳法，合成丙烯酰胺(AM)和甲基丙烯酰氧乙基三甲基氯化铵(DMC)的阳离子聚合物，并采用胶体滴定法测试聚合物的阳离子度，分析了溶液pH值、指示剂用量、滴定速度及残余乳化剂对阳离子度测试准确性的影响，并用红外光谱法确定了聚合物阳离子链节的存在。