玉米秸秆还原浸出高铁低品位锰矿研究

采用"玉米秸秆硫酸预处理—浸出"工艺处理含Mn 9.63%(质量分数)的朝阳锰矿.通过试验考察用硫酸对玉米秸秆进行预处理的时间、秸秆用量、温度、硫酸浓度和浸出温度对锰浸出率的影响.试验表明,在秸秆用量2.5 g、时间10 min、硫酸浓度1.2 mol/L、温度80℃时预处理秸秆,浸出温度为90℃的条件下,锰的浸出率达92%,杂质铁溶出率仅为20%.玉米秸秆处理前后FTIR分析结果表明,对秸秆进行硫酸预处理能够破坏难降解的木质素结构,有利于提高锰的浸出效果.     

芦丁还原浸出低品位软锰矿的研究

为了研究糖蜜酒精废液中有机物还原浸出软锰矿的机理,采用芦丁为还原剂,在酸性介质中直接浸出低品位软锰矿。通过正交实验和单因素实验,研究了芦丁浓度、硫酸浓度、反应温度、浸出时间等因素对锰浸出率的影响,并对反应过程机理进行了初步探讨。实验结果表明,影响锰浸出率的主要因素依次为反应温度、硫酸浓度、浸出时间和芦丁浓度;当硫酸初始浓度2.35 mol/L,芦丁初始浓度0.041 mol/L,反应温度90℃,浸出时间90 m in时,锰浸出率达94.9%。     

Reductive leaching of manganese from low-grade pyrolusite ore in sulfuric acid using pyrolysis-pretreated sawdust as a reductant

Manganese (Mn) leaching and recovery from low-grade pyrolusite ore were studied using sulfuric acid (H₂SO₄) as a leachant and pyrolysis-pretreated sawdust as a reductant. The effects of the dosage of pyrolysis-pretreated sawdust to pyrolusite ore, the concentration of sulfuric acid, the liquid/solid ratio, the leaching temperature, and the leaching time on manganese and iron leaching efficiencies were investigated. Analysis of manganese and iron leaching efficiencies revealed that a high manganese leaching efficiency was achieved with low iron extraction. The optimal leaching efficiency was determined to be 20wt% pyrolysis-pretreated sawdust and 3.0 mol/L H₂SO₄ using a liquid/ solid ratio of 6.0 mL/g for 90 min at 90℃. Other low-grade pyrolusite ores were tested, and the results showed that they responded well with manganese leaching efficiencies greater than 98%.     

硫酸中香蕉皮还原低品位锰矿的浸出行为及动力学模型

Manganese was leached from a low-grade manganese ore (LGMO) using banana peel as the reductant in a dilute sulfuric acid medium. The effects of banana peel amount, H₂SO₄ concentration, reaction temperature, and time on Mn leaching from the complex LGMO were studied. A leaching efficiency of ~98% was achieved at a leaching time of 2 h, banana peel amount of 4 g, leaching temperature of 120°C, manganese ore amount of 5 g, and sulfuric acid concentration of 15vol%. The phase, microstructural, and chemical analyses of LGMO samples before and after the leaching process confirmed the successful leaching of manganese. Furthermore, the leaching process followed the shrinking core model and the leaching rate was controlled by a surface chemical reaction (1 ? (1 ? x)1/3 = kt) mechanism with an apparent activation energy of 40.19 kJ·mol?1.     

用还原焙烧法从硫铁矿烧渣中提取铁的研究

研究了高温还原焙烧、硫酸浸取提取硫铁矿烧渣中的铁。用碳作还原剂,800℃以上温度、反应时间约20min时铁的提取率达90%以上,得到的还原渣可以在温和条件下浸出。得到的FeSO4提取液不需再经还原,便于净化,适于作透明氧化铁颜料、磁性铁氧体等高档用品的原料。     

Preparation of manganese sulfate from low-grade manganese carbonate ores by sulfuric acid leaching

In this study, a method for preparing pure manganese sulfate from low-grade ores with a granule mean size of 0.47 mm by direct acid leaching was developed. The effects of the types of leaching agents, sulfuric acid concentration, reaction temperature, and agitation rate on the leaching efficiency of manganese were investigated. We observed that sulfuric acid used as a leaching agent provides a similar leaching efficiency of manganese and superior selectivity against calcium compared to hydrochloric acid. The optimal leaching conditions in sulfuric acid media were determined; under the optimal conditions, the leaching efficiencies of Mn and Ca were 92.42% and 9.61%, respectively. Moreover, the kinetics of manganese leaching indicated that the leaching follows the diffusion-controlled model with an apparent activation energy of 12.28 kJ·mol-1. The purification conditions of the leaching solution were also discussed. The results show that manganese dioxide is a suitable oxidant of ferrous ions and sodium dimethyldithiocarbamate is an effective precipitant of heavy metals. Finally, through chemical analysis and X-ray diffraction analysis, the obtained product was determined to contain 98% of MnSO₄·H₂O.     

玉米杆制草酸中水解技术的研究

玉米杆属植物纤维废料,研究玉米杆制草酸的目的在于寻求一条玉米杆的合理利用新途径,并寻找制草酸价廉宜得的原料。本研究采用独特的水解技术把玉米杆水解成含糖液体,再进一步氧化、结晶制取草酸。结晶过程中产生的含酸废液全部用于玉米杆水解。水解产生的废渣加工成粉末状的混合肥料。因此,独特的玉米杆水解技术不仅使草酸生产过程无废液和废渣排放,而且使草酸成本大幅度下降,为植物纤维废料的利用开辟新途径。     

Reductive recovery of manganese from low-grade manganese dioxide ore using toxic nitrocellulose acid wastewater as reductant

The hydrometallurgical strategy of extracting Mn from low-grade Mn ores has attracted attention for the production of electrolytic manganese metal (EMM). In this work, the reductive dissolution of low-grade MnO₂ ores using toxic nitrocellulose acidic wastewater (NAW) as a reductant was investigated for the first time. Under the optimized conditions of an MnO₂ ore dosage of 100 g·L-1, an ore particle size of -200 mesh, concentrated H₂SO₄-to-NAW volume ratio of 0.12, reaction temperature of 90℃, stirring speed at 160 r·min-1, and a contact time of 120 min, the reductive leaching efficiency of Mn and the total organic carbon (TOC) removal efficiency of NAW reached 97.4% and 98.5%, respectively. The residual TOC of 31.6 mg·L-1 did not adversely affect the preparation of EMM. The current process offers a feasible route for the concurrent realization of the reductive leaching of Mn and the treatment of toxic wastewater via a simple one-step process.     

浸取环境对电解锰废渣中锰浸取的影响

在电解锰废渣中掺入锰矿粉,以提高锰废渣品位,探讨锰废渣中锰的硫酸法浸取回收效果.用单因素实验考察了矿渣比、液固比、浸取pH值、浸取温度和浸取时间等因素对锰浸取率的影响.实验结果表明,最佳浸取条件为：矿渣质量比3∶1、液固比3∶1（g/mL）、浸取液pH值2.0、浸取温度60 ℃和浸取时间3 h.最佳浸取条件下,锰浸取率达42.38%,与不加锰矿粉的浸取方法比较,锰浸取率提高了1.01倍.     

粉煤灰酸浸提铝试验条件的优化

 为优化酸浸法从粉煤灰中提取氧化铝的试验条件,提高酸溶过程浸出率,降低氟化物掺量,采用正交试验,对影响浸出率的各种因素进行研究。通过优化试验条件,提高铝的浸出率,大大降低环境污染。当溶出温度达沸腾硫酸浓度为12 mol/L固液比为1：3溶出时间为120 min、KF 和粉煤灰的质量比为4：100 时,铝的浸出率可达91.2%。在没有降低浸出率的前提下,有毒氟化物的掺量约减少一半。     

Sulfuric acid leaching of high iron-bearing zinc calcine

Sulfuric acid leaching of high iron-bearing zinc calcine was investigated to assess the effects of sulfuric acid concentration, liquid-to-solid ratio, leaching time, leaching temperature, and the stirring speed on the leaching rates of zinc and iron. The results showed that the sulfuric acid concentration, liquid-to-solid ratio, leaching time, and leaching temperature strongly influenced the leaching of zinc and iron, whereas stirring speed had little influence. Zinc was mainly leached and the leaching rate of iron was low when the sulfuric acid concentration was less than 100 g/L. At sulfuric acid concentrations higher than 100 g/L, the leaching rate of iron increased quickly with increasing sulfuric acid concentration. This behavior is attributed to iron-bearing minerals such as zinc ferrite in zinc calcine dissolving at high temperatures and high sulfuric acid concentrations but not at low temperatures and low sulfuric acid concentrations.     

蛭石在低浓度盐酸和硫酸中的溶出性比较研究

蛭石作为三八面体层状硅酸盐矿物,由于其独特的层状结构被广泛应用于各领域．酸处理蛭石能提高蛭石的比表面积,改变层电荷数,达到增加表面活性官能团的目的．以新疆尉犁蛭石为原料,在低浓度盐酸和硫酸界面进行溶出性比较研究,对原料及酸浸后样品的物相、结构、微观形貌以及浸出液中各离子浓度进行表征分析．结果表明：在酸浓度较低时盐酸和硫酸对蛭石的酸蚀程度相当,在酸浓度稍微增加时硫酸对蛭石的酸蚀速度快于盐酸．两种酸的蛭石结构中各金属离子浸出的难易顺序一致,均为：层间物>八面体片>四面体片．Ca²⁺作为层间阳离子在酸浸前4h的溶出速率远大于八面体阳离子Mg²⁺和四面体阳离子Al³⁺,且层间物中Ca²⁺相比于K⁺更容易浸出．适当的酸处理可以提高蛭石的阳离子交换容量．本文对于蛭石的利用开发具有一定意义．     

Reductive leaching of indium from the neutral leaching residue using oxalic acid in sulfuric acid solution

The present study evaluates the reductive leaching of indium from indium-bearing zinc ferrite using oxalic acid as a reducer in sulfuric acid solution. The effect of main factors affecting the process rate, including the oxalic-acid-to-sulfuric-acid ratio, stirring rate, grain size,temperature, and the initial concentration of synergic acid, was precisely evaluated. The results confirmed the acceptable efficiency of dissolving indium in the presence of oxalic acid. The shrinking-core model with a chemical-reaction-controlled step can correctly describe the kinetics of indium dissolution. On the basis of an apparent activation energy of 44.55 k J/mol and a reaction order with respect to the acid concentration of 1.14, the presence of oxalic acid was found to reduce the sensitivity to temperature changes and to increase the effect of changes in acid concentration. Finally, the equation of the kinetic model based on the factors under study is presented.     

LiCoO2的化学分解浸取过程

废旧锂离子电池中钴的含量较高．钴具有较强的毒性,且资源稀少．为此,研究了废旧锂离子电池的湿法回收工艺过程,并分析了废旧锂离子电池中钴和锂在硫酸溶液中的漫取过程动力学．采用了解体电池塑料外壳、钢壳、正负极材料、N-甲基吡咯烷酮(NMP)分离铝箔与正极活性材料以及硫酸浸取钴与锂的回收工艺．结果表明,铝片的回收率接近100％,钴和锂的浸取率均超过99．6％,同时分析了漫取过程中的工艺参数对钴和锂的漫取率的影响．     

微生物浸出深海多金属结核中有价金属

对氧化亚铁硫杆菌浸出深海多金属结核中有价金属的可行性进行了,着重研究了矿浆浓度、接种量、温度、浸出过程中ＰＨ值对结核中有价金属钴和镍浸出率的影响,同时对氧化亚铁硫杆菌进行了驯化。实验表明,采用Ｌｅａｔｈｅｎ培养基,加入适量黄铁矿作为菌种的营养基质和浸出过程中的还原剂、多金属结核,在常温、酸性环境下,可直接浸出金属铜、钴、镍、锰和铁。     

黄钾铁矾法炼锌矿渣中锌的提取条件试验

传统湿法分析过程中采用两段或多段浸出的流程,存在浸出率低的问题.该文研究对国内某厂黄钾铁矾法炼锌所产生的矿渣进行了浸出试验,采用浓硫酸浸出其中的锌,浸出条件为:液固比4:1,浸出温度160℃,时间6h.最后锌的浸出率达98%以上,达到预期要求,操作更简单,对现实很有指导意义和参考价值.     

A primary study of simultaneous leaching of silver containing manganese ore and a sphalerite concentrate

It is demonstrated that a low grade, silver containing manganese deposit can be exploited by reaction with a ZnS concentrate. In the process, Mn（IV） is reduced to Mn（II） and the ZnS converted to ZnSO4. In the process, Mn and Zn are solubilized. By studying the effects of quantity of reducing agent and sulfuric acid added and of time, temperature and liquid-to-solid ratio on the leaching process, the optimum technological conditions have been achieved un- der which the amount of manganese leached was 98 %. The silver can be removed from remaining solids by adding ammonia liquor. Then by adding hydrazine hydrate, sponge silver with purity up to 99 % can be obtained with a recovery of 87 %.     

低温稀酸预处理玉米秸秆的研究

本文采用低温稀酸法预处理玉米秸秆,利用正交实验方法考察了反应时间、反应温度、硫酸浓度三个因素对预处理效果的影响,以水解液中木糖浓度和葡萄糖浓度比值和预处理后的物料酶解液中葡萄糖的浓度作为评价指标。实验结果表明：在固液质量比1:5时,硫酸浓度2 ％,温度90 ℃,反应时间12 h为最佳处理条件,此时水解液中木糖浓度和葡萄糖比值为4.43,酶解液中葡萄糖的浓度为2.76%。     

氧化铝赤泥酸浸提取镓的新工艺研究

研究了拜耳法赤泥硫酸浸出镓的过程。硫酸浸出镓的溶液,用氢氧化钠反应生成沉淀,再用盐酸溶解沉淀提取镓的过程。采用正交试验考察浸出过程中温度、时间、液固比、浓度对镓浸出率的影响的主次顺序以及最佳条件。结果表明,该方法比单纯用盐酸浸出镓的浸出率高。镓的高浸出率是保证高的回收率的基础。     

陇东地区玉米秆制取糠醛研究

以甘肃陇东地区玉米秆为原料,采用改良硫酸法制取糠醛,并用紫外分光光度法测定了糠醛含量,出醛率为2.76%.