Effects of deposition parameters on the properties of VO2 thin films

The vanadium oxide thin films are deposited for microbolometers by radio frequency reactive sputtering method at room temperature. The effects of the oxygen partial pressure on the deposition rate, electrical properties and compositions of the films are discussed. The as-deposited VO_x thin films with x value of nearly 2 are deposited by adjusting the oxygen partial pressure. After oxidation annealing of these films in air, the VO₂ films with high temperature coefficients of resistivity (about -4%/℃) and low resistivity can be obtained. The square resistances of the films are in the range of 100 kΩ/squ?300 kΩ/squ. All films are deposited at room temperature and annealed at 400℃, in which the compatibility between VO_x deposition process and MEMS (micro electromechanical systems) is greatly improved.     

Effects of deposition parameters on the properties of VO_2 thin films

Up to now, much attention has been paid tovanadiumoxide (VOx) thinfil ms due to their exten-sive applications in the infrared microbolometers .Incontrast tothe conventional photon detectors ,the mi-crobolometer using VOxthinfil ms as sensitive materi-als can offer decreased systemcost ,i mproved reliabil-ity,low power-consumption and high sensitivity inthe spectral range of 8—14μm.Vanadiumoxides have various crystal structuresand valency states ,such as VO, V2O3, VO2, V2O5,whichleads tol…     

H2/(Ar+H2)流量比对AZO薄膜结构及光电性能的影响

在Ar+H2气氛下,用RF磁控溅射法在室温下制备Al掺杂的ZnO(AZO)薄膜,研究H2/(Ar+H2)流量比对薄膜结构和光电性能的影响。结果表明,在沉积气氛中引入H2可以提高AZO薄膜的结晶质量,降低AZO薄膜的电阻率,提高其霍尔迁移率和载流子浓度;H2/(Ar+H2)流量比为5%时,AZO薄膜的最小电阻率为1.58×10-3Ω.cm,最大霍尔迁移率和载流子浓度分别为13.17cm2.(V.s)-1和3.01×1020 cm-3;AZO薄膜在可见光范围内平均透光率大于85.7%。     

氮气分压比对硼碳氮薄膜的组分及光学带隙的影响

采用射频磁控溅射方法以不同的氮气分压比(1/10～2/3)制备出一组硼碳氮薄膜.傅里叶变换红外光谱(FTIR)和X射线光电子能谱(XPS)测量发现样品的组成原子之间均实现了原子级化合.XPS测量结果表明,所有样品中的B、N原子比近似为1:1,其化学配比为BCx N(0.16＜x＜1.46).紫外/可见/近红外分光光度计用于测量样品的吸收光谱.由吸收谱线在低能区域(2.0～3.0 eV)的光吸收,利用关系作图法求出光学带隙Eopt范围为0.17～0.83 eV.氮气分压比对薄膜的组分和光学带隙有很大影响,其通过改变薄膜组分而影响光学带隙,并且碳原子数小的样品具有较宽的光学带隙.以氮气分压比为1/3条件下制备的样品中碳原子数最小,它的光学带隙最宽为0.83 eV.     

DC反应磁控溅射制备VO2薄膜及XPS分析

文章通过改变玻璃基温度和靶基间距,采用m(O2)/m(Ar)为112.5,溅射功率为190 W,工作真空度为2.2 Pa,用DC磁控溅射法在玻璃基上沉积VO2薄膜,并经真空退火处理,制备的试样通过XPS测试分析薄膜表面的元素组成及成分.测试分析结果表明,基片温度在室温或超过350℃,易于生成VO2薄膜,真空退火可以显著改善制备薄膜的氧缺陷,提高V与O的化学计量比.     

Influence of O2/Ar ratio on the properties of transparent conductive niobium-doped ZnO films

Niobium-doped ZnO transparent conductive films are deposited on glass substrates by radio frequency sputtering at 300℃. The influence of O2/Ar ratio on the structural, electrical and optical properties of the as-deposited films is investigated by X-ray diffraction, Hall measurement and optical transmission spectroscopy. The lowest resistivity of 4.0×10^-4Ω· cm is obtained from the film deposited at the O2/Ar ratio of 1/12. The average optical transmittance of the films is over 90%.     

Nd掺杂对ZnO薄膜结构及室温光致发光特性的影响

通过射频磁控溅射技术在Si（111）衬底上制备了不同含量的Nd掺杂ZnO薄膜.XRD和AFM分析表明,Nd掺杂没有改变ZnO薄膜的结构,薄膜为纳米多晶结构,未掺杂ZnO沿c择优生长.Nd掺杂使ZnO薄膜表面粗糙,起伏较大,薄膜中随Nd掺杂量的增加颗粒减小.室温光致发光谱显示,薄膜出现了395nm的强紫光峰和495nm的弱绿光峰,同时,Nd掺杂不改变PL谱的峰位置,Nd含量对PL谱的峰强度产生了一定影响.     

氧气流量对TiO_x薄膜结构和光学特性的影响

用直流反应磁控溅射法在未加热的玻璃基片上制备出晶态TiOx(x2)薄膜,研究关键工艺因素即氧气流量对薄膜的沉积速率、表面形貌、显微结构和光学特性的影响。研究结果表明:随着氧气流量增加,薄膜的沉积速率从38.54nm/min下降到3.28nm/min,溅射模式也从转变模式过渡到氧化模式,薄膜表面均方根粗糙度逐渐减小,表面更趋平整;当氧气流量≤5mL/min时,得到不透明的晶态TiOx(x2)薄膜;当氧气流量5mL/min时,所沉积的TiOx薄膜呈透明非晶态,薄膜平均透射率高于80%。     

射频反应溅射纳米SnO2薄膜气敏特性研究

采用射频反应溅射在瓷管上制备了SnO2气敏薄膜元件,以及用传统方法制备了SnO2厚膜元件.两种元件经测试表现出对乙醇较高的灵敏度,对两种元件进行了性能对比测试.测试表明,无论在灵敏度、响应恢复时间,还是在检测浓度范围上,SnO2气敏薄膜元件都比传统的厚膜元件性能优越.SnO2气敏薄膜元件经过表面修饰,在200×10-6体积浓度下接近30.对薄膜元件加热温度及选择性进行了研究,初步探讨了元件稳定性及其敏感机理.     

磁控溅射制备TiO_2薄膜及其光学特性研究

采用直流反应磁控溅射法在玻璃衬底上制备TiO2薄膜.用紫外-可见光分光光度计和AFM分别表征了薄膜的透射率和表面形貌,用包络线法详细研究了不同衬底温度下TiO2薄膜的光学特性.结果表明:薄膜在可见光波段有很高的透明度,且随着衬底温度的升高,薄膜的透射率略有增加,薄膜的折射率和吸收系数增大,薄膜的光学带隙减小;同时,薄膜表面粗糙度减小,薄膜变得平整.     

氧分压对射频磁控溅射制备氧化锌薄膜光电学性质的影响

利用射频磁控溅射在石英基片上沉积ZnO薄膜.为了研究氧分压对ZnO薄膜的结构和光电学性质的影响,在氧分压0.00,2.54,5.06,7.57 mPa的条件下制备了4个样品.样品的微结构、表面形貌和光电学性质分别用X射线衍射仪、原子力显微镜、分光光度计和Van der Pauw方法进行测量.结果表明,所有样品的主要衍射...     

负偏压对反应磁控溅射AlN薄膜的影响

利用反应磁控溅射制备AlN薄膜,研究了基底负偏压对薄膜结构及其性能的影响.XRD和SEM结果表明:用此方法获得的AlN薄膜呈晶态,负偏压对AlN择优取向产生一定的影响,随着偏压的增大,薄膜表面晶粒尺寸有长大趋势.根据透射谱测试和包络线计算结果可知,薄膜在可见光和红外区域透射率高,随着偏压的增大,薄膜的折射率也随之增大.     

溅射功率对氧化铝薄膜结构和光学性能的影响

采用射频反应磁控溅射法,在K9双面抛光玻璃基底上制备了一系列不同溅射功率的Al2O3薄膜,并对部分薄膜进行退火处理.利用X线衍射法对Al2O3薄膜退火前后的晶体结构进行分析,采用椭圆偏振光谱仪对薄膜的厚度、折射率和消光系数进行测试和拟合.实验结果表明:测射功率在100~300 W时,沉积的Al2O3薄膜退火前后均为非晶态;薄膜在可见光范围内具有良好的透光性能,透射率接近90%,为透明膜;薄膜的沉积速率随溅射功率的增大而增大;薄膜在可见光波段的折射率n随波长的增大而减小,平均值随溅射功率的增大呈现出先增大后减小的变化趋势;薄膜消光系数k的平均值亦随溅射功率的增大呈现先增大后减小的变化趋势.     

TiO2薄膜表面形貌的多重分形分析

采用原子力显微镜(AFM)对不同电泳时间生成的纳米二氧化钛(TiO2)薄膜进行了观测。经过图像处理得到对应的二值化黑白图,基于构型熵这一指标考虑了多重分形分析时标度区间这一重要因素的影响。讨论了TiO2薄膜的表面形貌与多重分形特征,使得不同生长时间的薄膜表面可以较为明显地定量区分开来。随着电泳时间的增大,薄膜的多重分形谱宽Δα逐渐增大,说明对应的表面粗糙度逐渐增大,薄膜的表面形貌逐渐变差。最后得出电泳镀膜的生长效果在电泳时间为50s时较优,并且通过甲醛降解实验得到进一步验证了其光催化效果,为进一步研究薄膜的催化特性提供了较好的定量评价方法。     

衬底偏压对ZnO：Zr薄膜结构及光电性能的影响

以Zn：Zr（Zr片贴在金属Zn靶上面）为溅射靶材,利用直流反应磁控溅射法在Ar／O_2混合气氛中制备Zr掺杂ZnO（ZnO：Zr）薄膜．在制备ZnO：Zr薄膜时,衬底偏压在0～60V之间变化．研究结果表明,衬底偏压对薄膜的结构、光学及电学性能有很大影响．当衬底偏压从0增大到60V时,薄膜的平均光学透过率和平均折射率都单调增大,而薄膜的晶粒尺寸先增大后减小．ZnO：Zr薄膜电阻率的变化规律与晶粒尺寸相反．     

衬底温度对射频磁控溅射制备ZnO薄膜结构的影响

采用射频磁控溅射法在玻璃衬底上制备ZnO薄膜.用X射线衍射仪(XRD)、扫描电镜(SEM)对不同衬底温度下制备薄膜的相结构和表面形貌进行分析.结果表明,在衬底温度为400℃时制备的ZnO薄膜表面光滑,晶粒尺寸均匀,结构致密,且沿c轴择优生长.     

Preparation of CuInSe2 thin films by four-step process

A simple process for the deposition of CulnSe₂ thin films was described. The CulnSe₂ compound was prepared by selenization of Cu-In alloy precursors, which were electrodeposited at a constant current. The selenized precursors were compacted and then annealed. The films were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The results indicate that single-phase CulnSe₂ is formed at 250℃ and its crystallinity of this phase is improved as the annealing temperature rises. The losses of In occur in selenization process. The dense CulnSe₂ film with comparatively smooth surface can be obtained by compaction under the pressure of 200 MPa.     

衬底温度对CdTe/ZnTe多层薄膜制备的影响

采用射频磁控溅射法制备了CdTe/ZnTe多层薄膜,并在制备单层CdTe薄膜和ZnTe薄膜的基础上,研究了衬底温度对CdTe/ZnTe多层薄膜性质的影响;通过XRD和透过谱、吸收谱的分析,对其结构进行了研究.结果表明在185 ℃下制备的CdTe/ZnTe多层膜中,CdTe和ZnTe均沿（111）晶面择优取向生长,尤其是ZnTe沿（111）晶面择优取向明显,衍射强度极大. 通过比较不同衬底温度,发现185 ℃生长的样品衍射峰强度最高,成膜质量较好;通过吸收谱图分析,185 ℃下沉积的样品对光有较好的吸收性.     

Si83Ge17／Si压应变衬底上HfO2栅介质薄膜的电学性能

本文用射频磁控溅射方法在p-si83Ge17／Si压应变衬底上沉积制备Hf02栅介质薄膜,研究其后退火处理前后的电学性能,并与相同条件沉积在无应变p-Si衬底上Hf02薄膜的电学性能进行对比研究．物性测试分析结果表明,沉积Hf02薄膜为单斜相（m-Hf02）多晶薄膜,薄膜介电常数的频率依赖性较小,1MHz时薄膜介电常数k约为23．8．在相同的优化制备条件下,沉积在si83Ge17／si衬底上的Hf02薄膜电学性能明显优于沉积在Si衬底上的薄膜样品：薄膜累积态电容增加;平带电压‰骤减至-0．06V;电容．电压滞后回线明显减小;-1V栅电压下漏电流密度,减小至2．51 x 10-5A·cm-2．实验对比结果表明Si83Ge17应变层能有效地抑制Hf02与si之间的界面反应,改善HfO2／Si界面性质,从而提高薄膜的电学性能．