Reinforcing effect of graphene on the mechanical properties of Al2O3/TiC ceramics

Multilayer graphene (MLG)-reinforced Al2O3/TiC ceramics were fabricated through hot pressing sintering, and the reinforcingef-fect of MLG on the microstructure and mechanical properties of the composites was investigated by experiment and simulation. The simula-tion of dynamic crack initiation and propagation was investigated based on the cohesive zone method. The results show that the composite added with 0.2wt% MLG has excellent flexural strength and high fracture toughness. The major reinforcing mechanisms are the synergistic effect by strong and weak bonding interfaces, MLG pull-out, and grain refinement resulting from the addition of MLG. In addition, the ag-gravating of crack deflection, branching, blunting, and bridging have indispensable contribution to the improvement of the as-designed mate-rials.     

Effects of BN content on the mechanical properties of nanocrystalline 3Y-TZP/Al_2O_3/BN dental ceramics

3 Y-TZP/3 wt% Al_2O_3 powder was coated with varying amounts of BN using the urea and borate reaction sintering method, and then multiphase ceramics were prepared by hot pressing sintering. The micro-topography and the compositional analysis of synthesized ceramics were conducted through scanning electron microscopy, transmission electron microscopy and X-ray diffraction. A mechanical tester was used to analyze the Vickers hardness, fracture toughness, and bending strength of the synthesized ceramics. The results showed that the ceramic with a BN content of 12 wt% showed the best processability, but had diminished mechanical properties(such as fracture toughness and bending strength). The ceramic with a BN content of 9 wt% showed better processability than those with 3 wt% and 6 wt% BN. However, the fracture toughness was affected by the addition of 9 wt% BN, making this ceramic only usable as a base material for a three-unit fixed bridge. In contrast, the ceramics with a BN content of 3 wt% or 6 wt% fulfilled the criteria for use in multi-unit restoration, but their low processability made them unsuitable for milling after sintering.     

铝热法制备的ZrO_2/Al_2O_3复相陶瓷材料组织和力学性能

通过铝热反应制备ZrO2/Al2O3复相陶瓷材料,研究ZrO2含量对复相陶瓷显微组织与力学性能的影响.结果表明:复相陶瓷的相组成为ZrO2和Al2O3.随着ZrO2含量增加,ZrO2在基体中的分布越均匀,维氏硬度为8～15GPa,在ZrO2质量分数为41.5%时呈现最大值为14.85GPa;断裂韧性先增加后降低,在ZrO2质量分数为30%时呈现最大值8.01MPa.m1/2.     

Reinforcing effect of graphene on the mechanical properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>/TiC ceramics

Multilayer graphene (MLG)-reinforced Al₂O₃/TiC ceramics were fabricated through hot pressing sintering, and the reinforcing effect of MLG on the microstructure and mechanical properties of the composites was investigated by experiment and simulation. The simulation of dynamic crack initiation and propagation was investigated based on the cohesive zone method. The results show that the composite added with 0.2wt% MLG has excellent flexural strength and high fracture toughness. The major reinforcing mechanisms are the synergistic effect by strong and weak bonding interfaces, MLG pull-out, and grain refinement resulting from the addition of MLG. In addition, the aggravating of crack deflection, branching, blunting, and bridging have indispensable contribution to the improvement of the as-designed materials.     

Al_2O_3／nano－SiC复相陶瓷力学性能及显微结构

研究了热压烧结Ａｌ２Ｏ３／ｎａｎｏ－ＳｉＣ复相陶瓷的力学性能及显微结构。研究表明,纳米ＳｉＣ的引入显著地改善了材料的力学性能,在ＳｉＣ添加体积分数为１０％时,Ａｌ２Ｏ３／ｎａｎｏ－ＳｉＣ复相陶瓷抗弯强度σｆ达峰值为８６９ＭＰａ,断裂韧性ＫＩｃ也达峰值为６．７ＭＰａ·ｍ０．５,比纯Ａｌ２Ｏ３基体材料分别提高１３８％和８１％。ＴＥＭ观察表明：纳米ＳｉＣ晶粒主要存在于Ａｌ２Ｏ３基体晶粒内部,形成独特的“晶内型”结构。当受外力作用时,既能因弥散的纳米颗粒诱发穿晶断裂,且穿晶断裂时,还能因晶内存在第二相颗粒而引起裂纹偏转,起到增强增韧作用。     

Nb对Ti/Al_2O_3复合材料力学性能的影响

研究了热压烧结条件下Nb元素对Ti/ [φ(Al2 O3 ) =80 % ]复合材料相对密度、抗弯强度、断裂韧性及维氏硬度等力学性能的影响 ,分析了其影响机理。结果表明 ,在Ti/ [φ(Al2 O3 ) =80 % ]的Al2 O3 复合材料中掺入Nb元素 ,材料的微观组织形貌得以细化 ,性能有了较大提高。随Nb掺量的增加 ,材料的相对密度、维氏硬度与抗弯强度先增大后减小 ,当掺量为 φ =1.5 %时 ,其相对密度、抗弯强度、维氏硬度达到最高 ,分别为 98.13%、5 0 1.0 6MPa和 2 0 .31GPa ,断裂韧性随Nb掺量的增加而增大 ,当掺量为 φ =2 %时 ,其断裂韧性为5 .2 4MPa·m1/ 2 。     

Al_2O_3/TiC纳米复合陶瓷刀具材料的氧化行为

研究Al2O3/TiC纳米和微米复合陶瓷刀具材料在800℃、1000℃和1250℃下的氧化行为,分析其氧化机理,并对其氧化产物进行了XRD分析.试验表明在同等氧化条件下纳米复合材料的氧化程度较微米复合材料严重.氧化后的残余强度测试表明:Al2O3/TiC纳米复合陶瓷刀具材料在800℃下氧化50h后其抗弯强度虽有降低,但仍能满足切削刀具的要求,但在1000℃和1250℃下氧化50h后,其抗弯强度有很大的下降,材料遭到破坏.     

添加Al_2O_3对95W-Ni-Fe合金微观组织与力学性能的影响

针对钨合金作为预制破片战斗部穿甲后的易碎性,研究了添加不同粒径Al2O3对95W合金微观组织与性能的影响.结果表明,随着添加的Al2O3粒径的减小,钨合金中钨颗粒的平均直径尺寸减小 获得的新型95W合金的静态抗拉强度和延伸率均低于传统95W合金,并且新型95W合金的强度和延伸率随着添加Al2O3初始粉末粒径的降低而增加 添加Al2O3初始粉末粒径的减小增大了新型95W合金的抗压强度 新型钨合金由于Al2O3的存在引发了大量初始裂纹并在承受冲击载荷时导致应力集中,微裂纹迅速连结并扩展后形成裂纹.     

铝热反应制备YAG/Al2O3复相陶瓷的组织和性能

利用铝热反应熔化法制备YAG/Al2O3复相陶瓷材料,研究配料中Y2O3含量对复相陶瓷显微组织和力学性能的影响.结果表明:复相陶瓷的相组成为YAG和Al2O3,合有少量的Fe相.随着Y2O3含量的增大,Al2O3颗粒分布越均匀,复相陶瓷的维氏硬度先减小后增加,而相对密度是增加的,在x=0.90时达到最大值分别10.9 ...     

Preparation and radar-absorbing properties of Al_2O_3/TiO_2/Fe_2O_3/Yb_2O_3 composite powder

Al_2O_3/Ti O_2/Fe_2O_3/Yb_2O_3 composite powder was synthesized via the sol–gel method. The structure,morphology,and radar-absorption properties of the composite powder were characterized by transmission electron microscopy,X-ray diffraction analysis and RF impedance analysis. The results show that two types of particles exist in the composite powder. One is irregular flakes(100–200 nm) and the other is spherical Al_2O_3 particles(smaller than 80 nm). Electromagnetic wave attenuation is mostly achieved by dielectric loss. The maximum value of the dissipation factor reaches 0.76(at 15.68 GHz) in the frequency range of 2–18 GHz. The electromagnetic absorption of waves covers 2–18 GHz with the matching thicknesses of 1.5–4.5 mm. The absorption peak shifts to the lower-frequency area with increasing matching thickness. The effective absorption band covers the frequency range of 2.16–9.76 GHz,and the maximum absorption peak reaches-20.18 d B with a matching thickness of 3.5 mm at a frequency of 3.52 GHz.     

Ni/Al2O3、Co /Al2O3和Ni-Co /Al2O3催化剂催化乙醇水蒸气重整制氢的性能

利用浸渍法制备Ni/Al2O3、Co/Al2O3、Ni-Co/Al2O3催化剂,考察催化剂对乙醇水蒸气重整反应的催化性能,对催化剂进行x射线衍射(XRD)表征.实验结果表明,Ni/Al2O3催化剂具有较好的低温活性,Co/Al2O3催化剂具有较高的氢气选择性和较低的甲烷选择性,而Ni-Co/Al2O3催化剂表现出良好的催化性能,有较高的低温活性,较高的氢气、二氧化碳选择性,较低的一氧化碳、甲烷选择性,450 ℃时乙醇转化率达到100%, 氢气选择性为79.8%,二氧化碳选择性为91.9%.     

内氧化工艺对Al_2O_3/Cu复合材料中Al_2O_3颗粒分布的影响

采用压块加入法和分别加入法两种内氧化工艺 ,将 Cu O和 Al粉末加入到 Ar气保护的铜液中制备 Al2 O3/ Cu复合材料 ,在光学显微镜、扫描电镜及 X射线衍射仪上观察分析了Al2 O3颗粒的数量、分布及材料的相组成。结果表明 ,压块加入法生成的 Al2 O3颗粒呈枝晶状分布 ,最佳保温时间为 30～ 45 min;分别加入法生成的 Al2 O3颗粒呈弥散状分布 ,最佳保温时间为 45～ 6 0 mi     

Microstructure and properties of mullite-based porous ceramics produced from coal fly ash with added Al_2O_3

Using coal fly ash slurry samples supplemented with different amounts of Al_2O_3,we fabricated mullite-based porous ceramics via a dipping-polymer-replica approach,which is a popular method suitable for industrial application.The microstructure,phase composition,and compressive strength of the sintered samples were investigated.Mullite was identified in all of the prepared materials by X-ray diffraction analysis.The microstructure and compressive strength were strongly influenced by the content of Al_2O_3.As the Al/Si mole ratio in the starting materials was increased from 0.84 to 2.40,the amount of amorphous phases in the sintered microstructure decreased and the compressive strength of the sintered samples increased.A further increase in the Al_2O_3 content resulted in a decrease in the compressive strength of the sintered samples.The mullite-based porous ceramic with an Al/Si molar ratio of 2.40 exhibited the highest compressive strength and the greatest shrinkage among the investigated samples prepared using coal fly ash as the main starting material.     

Effects of metal binder on the microstructure and mechanical properties of Al_2O_3-based micro-nanocomposite ceramic tool material

The Al_2O_3-(W,Ti)C composites with Ni and Mo additions varying from 0vol% to 12vol% were prepared via hot pressing sintering under 30 MPa. The microstructure was investigated via X-ray diffraction(XRD) and scanning electron microscopy(SEM) equipped with energy dispersive spectrometry(EDS). Mechanical properties such as flexural strength, fracture toughness, and Vickers hardness were also measured. Results show that the main phases A12O3 and(W,Ti)C were detected by XRD. Compound Mo Ni also existed in sintered nanocomposites. The fracture modes of the nanocomposites were both intergranular and transgranular fractures. The plastic deformation of metal particles and crack bridging were the main toughening mechanisms. The maximum flexural strength and fracture toughness were obtained for 9vol% and 12vol% additions of Ni and Mo, respectively. The hardness of the composites reduced gradually with increasing content of metals Ni and Mo.     

氧化铝、莫来石增强白水泥熟料基质复相陶瓷材料性能

研究了氧化铝、莫来石颗粒增强白水泥熟料基质复相陶瓷材料的常温力学性能。采用干混、冷等静压成型、常压烧结等方法，制备复相陶瓷。结果表明：这种材料具有良好的烧结性能，氧化铝、莫来石颗粒可以显著地提高材料的常压力学性能。     

CuCrW(Al_2O_3) nanocomposite: mechanical alloying,microstructure, and tribological properties

The effect of alumina nanoparticle addition on the microstructure and tribological properties of a CuCrW alloy was investigated in this work. Mechanical alloying was carried out in a satellite ball mill. The tribological properties of the samples were evaluated using pin-on-disk wear tests with different pins(alumina, tungsten carbide, and steel pins). The results indicated that the tungsten carbide pin had a lower coefficient of friction than the alumina and steel pins because of its high hardness and low surface roughness. In addition, when the sliding rate was decreased, the weight-loss rate increased. The existence of alumina nanoparticles in the nanocomposite led to a lower weight-loss rate and to a change in the wear mechanism from adhesive to abrasive.     

噻吩在Mo－Ni－Co／Al_2O_3催化剂上的加氢脱硫动力学

应用微型催化反应－色谱装置，在总压１～２ＭＰａ、温度４７３～５７３Ｋ、氢油体积比５００、质量空速１～３０ｈ￣（－１）的范围内，研究了噻吩在Ｍｏ－Ｎｉ－Ｃｏ／Ａｌ_２Ｏ_３催化剂上的加氢脱硫动力学。根据加氢脱硫反应具有极限转化率的特点；用类二级反应的数学模型描述噻吩脱硫的动力学行为，求得活化能为７６．２１ｋＪ／ｍｏｌ，频率因子为３．６７×１０８。     

SiCw／Al_2O_3复合材料的研究现状与发展趋势

本文介绍了国内外对ＳｉＣｗ／Ａｌ＿Ｏ＿３复合材料研究现状，并从工艺的角度，分析了影响复合材料性能的主要因素。     

烧成温度对Al_2O_3-Fe_2O_3复合材料性能的影响

以煅烧α-Al2O3粉、氧化铁为原料,采用MgO为添加剂,控制配料的Al2O3/Fe2O3的摩尔比为1、3、5,MgO引入量质量百分数分别为2%、4%、6%,成型压强为100 MPa,烧结温度为1500℃、1550℃、1600℃,保温3小时可获得Al2O3-Fe2O3复合材料,对烧后试样了烧结与抗热震性能研究。结果表明：控制Al2O3-Fe2O3复合材料试样AF34-2的Al2O3/Fe2O3摩尔比为3,MgO引入量为4%,烧成温度为1550℃保温3小时的工艺条件,可以制备出较高致密度、常温抗折强度及抗热震性能的Al2O3-Fe2O3复合材料。该复合材料试样AF34-2的SEM显微结构照片显示出材料晶粒间结合紧密,形成具有直接结合的镶嵌结构。