SCC Susceptibility of Steel 16Mn in Nitrate Solution and Its Mechanism

The SCC (stress corrosion cracking) susceptibility of steel l6Mn in nitrate solution was studied. The results showed that applied potential polarization would accelerate(anodic polarization) or retard (cathodic polarization) the SCC process. The study on phase electrochemistry revealed that there was significant difference in electrochemical performance between ferrite and pearlite of steel 16Mn. Pearlite preferentially corroded under the action of galvanic cell. The observation on time and in situ showed that corrosion started first at the phaseboundary between ferrite and pearlite, and the pearlite gradually corroded until disappeared, and then corrosion crossed the phase boundary extending into the ferrite phase. According to this, an anodic dissolution mechanism of SCC was proposed, on which pre-existing sting active path and phase electrochemistry (PEAP-PEC) jointly came into action (SCC mechanism of PEAP-PEC).     

钼对低合金钢硝酸盐体系应力腐蚀的影响

以高风温热风炉用钢的沿晶应力腐蚀开裂问题为背景,研究了Ｍｏ对低合金钢在硝酸盐溶液中的应力腐蚀行为。结果表明,低合金钢中加入合金元素将使钢中贝氏体和／或珠光体含量增大,从而提高了材料的稳定性和抗ＳＣＣ耐蚀性。提出了低合金钢／硝酸盐溶液体系的“温度－钼含量－ＳＣＣ图”。     

铁素体/珠光体界面对耐酸管线钢氢致开裂敏感性的影响

利用OM、SEM、EBSD、TEM等手段,分别对热轧态和退火态耐酸管线钢的微观组织、晶界分布、位错及析出相进行表征,测试了不同组织管线钢的氢致开裂(HIC)敏感性,计算分析了有效氢扩散系数、氢陷阱密度及其对不同组织的氢捕获效率,重点探讨了铁素体/珠光体(F/P)界面对耐酸管线钢HIC敏感性的影响。结果表明,随着管线钢珠光体含量的增加,F/Fe_3C界面及F/P界面越多,二者作为不可逆氢陷阱会阻碍氢的扩散,提高氢的捕获效率,有效氢扩散系数降低,管线钢的HIC敏感性提高;F/P界面附近位错的聚集会加速氢原子向高界面能的F/P界面聚集,使氢致裂纹起始于F/P界面处,并沿着F/P界面扩展。     

初始组织形态对中碳钢温变形组织演变的影响

中碳钢温变形过程的组织演变包含铁素体动态回复、再结晶和渗碳体的析出球化等过程.采用Gleeble1500热模拟试验机研究了初始组织形态对含碳0.48%(质量分数)的中碳钢在温变形中上述复杂过程的影响.结果表明:初始组织为珠光体 先共析铁素体的试样在温加工变形中渗碳体层片发生了扭折、溶断到逐渐球化的过程,在铁素体回复再结晶的同时伴随着细小弥散的渗碳体颗粒从过饱和铁素体中析出,得到微米级铁素体晶粒和颗粒状渗碳体弥散分布的复相组织,但等轴状铁素体晶粒与弥散的渗碳体颗粒沿变形方向呈带状不均匀分布.温加工变形促进初始组织为马氏体的中碳钢中渗碳体析出和铁素体回复与再结晶.由于初始条件下碳的分布在微观尺度下相对均匀,变形后获得细小等轴铁素体与均匀分布颗粒状渗碳体的组织.     

超声无损表征30Mn2SiV钢复杂混合组织探讨

采用超声水浸线聚焦技术和频谱分析方法,研究了控轧控冷工艺生产的非调质D级抽油杆用钢30Mn2SiV复杂混合组织状态的超声无损表征方法,确定了不同质量分数的珠光体、铁素体及上贝氏体混合组织的相对衰减系数和相对相速度.含大量上贝氏体组织、珠光体 铁素体组织以及珠光体球化组织,相对衰减系数按照由大到小顺序变化,而相对相速度则依次增大.利用该方法可以无损区分30Mn2SiV钢的复杂混合组织.     

铁素体球铁和珠光体球铁疲劳断口形貌的研究

借助于扫描电镜,对铁素体球铁、珠光体球铁常温下旋转弯曲疲劳断口进行了大量观察和分析,确认“穿晶疲劳组织特征”是球铁疲劳断口的显著形貌特征;滑移线条是“穿晶疲劳组织特征”的主要细节形态。     

铁素体珠光体球铁强度和延伸率的计算细观力学分析

本文基于计算细观力学方法,用有限元网格模拟球铁细观结构,将搞拉强度判据和延伸率判据引入轴对称弹塑性大应变有限元程序,计算了在球墨体积百分数为12.566％、球化良好、分布均匀条件下。不同细观结构球铁的抗拉强度和延伸率。结果表明:(1)铁素体含量是影响铁素体球光体球铁抗拉强度的主要因素,其关系可用线性或双线性公式表示:(2)当球铁中铁素体含量在50％以上时,延伸率随铁素体含量增加而迅速增大;(3)当铁素体含量在50％以下时,延伸率主要由球光体组织性能控制,并受到铁素体分布形态的较大影响,以铁素体呈破碎状分布为优;(4)在一定尺寸范围内,球墨直径增大,将使铁素体球铁抗拉强度和延伸率提高;对球光体球铁,则使延伸率略为下降(小于1％),而抗拉强度提高。     

Bagaryatsky取向的铁素体/渗碳体相界结构模拟

近似重位点阵模拟的结果表明,具Bagaryatsky取向的铁素体／渗碳体界面上的台阶并非本征结构,即台阶无特定宽度与高度．这种结构台阶不仅导致两相界面能可在一定范围内波动,而且导致铁素体／渗碳体无宏观的惯习面,有利于珠光体在生长时根据动力学条件发生弯曲．     

CuPCr钢显微组织对全浸海水腐蚀行为的影响

为考察CuPCr型耐海水腐蚀钢不同显微组织的腐蚀行为,采用热轧后不同冷却方式分别获得贝氏体和铁素体+珠光体组织,进行模拟海水腐蚀的全浸加速腐蚀实验,并利用失重法测量腐蚀速率,采用SEM,XRD和电化学方法评价钢的腐蚀行为.结果表明:贝氏体组织能够在更短时间内形成比较致密的锈层,其耐蚀性能明显优于铁素体和珠光体组织.碳元素在贝氏体中的均匀分布减少了微电池数量,因而能够降低钢的腐蚀电流密度.     

中碳钢温变形的力学特性

利用Gleeble-3500热模拟实验机对中碳钢铁素体+珠光体组织进行温变形压缩试验,研究其在不同变形温度(500～700 ℃)和应变率(0.001～10 s-1)条件下的流变行为及其主导机制. 研究结果表明:温变形过程先从铁素体变形开始,而后珠光体开始变形,渗碳体片层结构被破坏;铁素体晶粒细化至1～2 μm;珠光体片层被破坏使流变应力形成峰值;温变形流变应力曲线特征具有显著差异性,对工件塑性成形、工模具载荷分布及变形产生重要影响.      

控轧控冷对低碳铆螺钢力学性能的影响

对低碳铆螺钢采用两次控轧控冷试验,结果表明,铁素体晶粒尺寸比珠光体形态对低碳铆螺钢力学性能的影响要大.低温轧制较常规轧制后控冷可以获得更好的力学性能.在奥氏体化工艺参数非常合理的条件下,通过控轧控冷使铁素体晶粒细化的同时,避免魏氏组织产生,能够获得最佳的力学性能.采用控轧控冷,有可能实现以低碳代替中碳免热处理490 MPa级铆螺钢的实际生产.     

共析钢经表面研磨处理后微观组织的演化

利用表面研磨处理(SMAT)在共析钢上制备出具有纳米晶体结构的表面层,并利用X射线衍射和透射电镜分析了纳米表面层的微观组织结构及其演变.结果表明:原始组织为层片状铁素体 渗碳体两相复合组织的共析钢经过SMAT后,铁素体晶粒由于位错产生、位错缠结形成位错胞,然后分割晶粒使铁素体细化至纳米尺度,而渗碳体在强烈塑性变形下,经历弯曲、断裂,最终分解成体心立方铁素体和底心正交的石墨.     

基于热膨胀法与相体积计算模型研究连铸坯冷却过程中奥氏体相变行为

采用热膨胀仪测试研究了Q450NQR1钢连铸坯5℃·min-1及20℃·min-1冷却速率下的线性热膨胀(△L/L0)和热膨胀系数随温度的变化规律.在此基础上,建立了一种基于平均原子体积的相体积计算模型,量化研究了奥氏体相变过程中各相体积分数的变化规律,并在将计算结果与显微组织观察结果对比分析基础上,讨论了连铸冷却速率对铸坯奥氏体相变过程的影响.结果表明：该计算模型可以较为准确地描述铸坯的奥氏体相变过程,适用于多相连续析出相变;随着冷却速率的增大,铸坯热膨胀曲线中对应于铁素体和珠光体析出的两个变化峰向低温区移动,峰值明显增大;冷却速率由5℃·min-1上升至20℃·min-1时,铁素体及珠光体起始析出温度分别降低约32℃和37℃,最终体积分数分别由0.894和0.106变为0.945和0.055.     

热模拟平面应变条件下的热轧织构研究

以微合金钢为材料,采用光学显微镜和EBSD,研究热模拟平面应变实验条件下再结晶奥氏体和变形奥氏体的织构演变.研究发现,在热模拟平面应变实验的压缩过程中,试样的两个自由端限制了变形区金属的宽向流动,达到了很好的平面应变状态.对于再结晶奥氏体相变工艺,由于相变前奥氏体发生再结晶,无畸变保留,奥氏体分解为仿晶界铁素体、贝氏体和少量的珠光体,织构为{100}011α;对于变形奥氏体相变工艺,未再结晶区的变形促进了铁素体相变,使奥氏体分解为铁素体和珠光体组织,织构为{332}113α和{113}110α.此两种工艺条件下的织构,皆为平面应变条件下的奥氏体相变织构,即热模拟平面应变实验可以达到很好的平面应变状态,可用于研究热轧过程的织构演变.     

基于OpenCL并行的挡板对珠光体生长的相场法模拟

建立了耦合相场和溶质场的KKSO模型,采用OpenCL并行计算模拟了Fe-C合金共析生长过程,研究了不同形状和不同位置的挡板对层片状珠光体协同生长的影响.结果表明:GPU计算效率相对于串行CPU,最高可达88倍的加速比,并且随着模拟规模的增大,GPU的加速性能越高;挡板的存在直接影响珠光体的形貌演化,其使挡板下方的珠光...     

Research and Development of X70 with an Acicular Ferrite Microstructure for West-East Pipeline Project

It is introduced in this paper that a high strength and high toughness X70 pipeline steel with an ultra-low acicular ferrite microstructure has been researched and developed at Baosteel according to the requirements of the West-East Gas Pipeline(WEGTP) project. The developed steel has higher strength, higher toughness, lower ductile-brittle transition temperature and higher dynamic tear-resistance than the conventional X70 with ferrite and pearlite microstructure. The excellent properties of the steel are benefited from ultralow carbon acicular ferrite consisting of interaction of very fine precipitated particles and high-density dislocation. And the steel has been applied on the WEGTP in China.     

超快冷下X65管线钢微观组织演变及强化机制分析

基于热连轧生产线开发了X65管线钢超快冷新工艺，系统表征了该工艺下实验钢的微观组织特征，并进一步讨论了其强化机制.结果表明，超快冷下X65管线钢微观组织为细小针状铁素体(AF)+准多边形铁素体(QPF)+M/A岛+弱化珠光体(DP)混合组织，有效晶粒尺寸为2.93μm，大角晶界百分比为31.5%;实验钢组织亚结构为细小的块状铁素体，铁素体尺寸分布在200~1000nm;在铁素体基体上析出了大量尺寸＜10nm的Nb(C，N)粒子;实验钢各项力学性能均满足API SPEC 5L标准要求.超快冷工艺下X65管线钢的主要强化机制为细晶强化、固溶强化、位错强化及纳米析出强化的耦合强化，其中纳米析出强化强度贡献值为96.1MPa.     

微合金化非调质钢35MnVN低温冲击韧性研究

本研究通过对35MnVN钢低温系列冲击韧性值测定,金相组织分析、断口形貌与二次裂纹扩展途径观察,初步揭示了其低温冲击韧性的变化规律及影响因素。结果表明:铁素体晶粒尺寸及相对量、原奥氏体晶粒大小、珠光体团尺寸对低温冲击韧性值有较大影响;铁素体晶粒尺寸为较敏感因素;温度降低,晶界有弱化趋势。本文还讨论了改善低温冲击韧性的途径。     

奥氏体变形对耐候钢相变行为及显微组织的影响

在MMS-100热力模拟实验机上采用热膨胀法结合硬度测试,对耐候钢进行了未变形和变形后的连续冷却的实验研究,建立了未变形和变形奥氏体的CCT曲线.利用光学显微镜、扫描电镜分析研究了冷却速度、变形条件对显微组织的影响.实验结果表明,从未变形到变形的过程,多边形铁素体相变开始温度升高,相变区左移,获得铁素体加珠光体混合组织的临界冷速增大.变形奥氏体的位错缠结抑制贝氏体长大,从而细化转变后的显微组织.     

Microstructural and mechanical characteristics of Al-alloyed ductile iron upon casting and annealing

Ductile iron containing 6.16wt% Al was developed to investigate the effects of aluminum on both its microstructure and hardness. It was found that aluminum not only increases the nodule count and pearlite content but also improves the hardness in both sand mold and metal mold castings. Annealing treatments were conducted to attain a homogenous microstructure and improve high-temperature serviceability. A ferrite/carbide or ferritic matrix was gained depending on the annealing temperature. It is also discovered that annealing has inverse influences on the hardness of the bulk alloy and the ferrite phase. Although it causes a small decrease in the bulk hardness of the specimens, it leads to an increase in the microhardness of the ferrite. Micro-segregation of the alloying elements was also investigated by means of electron probe micro-analysis for the specimens with different annealing durations and the as-cast specimen as well. An optimum annealing time was proposed to result in the least amount of micro-segregation of aluminum and silicon between graphite nodules.