利用置换溶液型优化计算了ＹＯ１．５－ＣｅＯ２二元系的相图，并得到了估算的热力学参数，结合以前优化的ＺｒＯ２－ＣｅＯ２和ＺｒＯ２－ＹＯ１．５二元系，并根据Ｂｏｎｎｉｅｒ方法进行外推，估算了ＺｒＯ２－ＹＯ１．５－ＣｅＯ２三元系在１９７３Ｋ和１８７３Ｋ下的等温截面相图，基结果与试验结果吻合。     

热障涂层陶瓷材料La_2(Zr_(0.7)Ce_(0.3))_2O_7的制备和性能

研究了La2(Zr0.7Ce0.3)2O7(LZ7C3)的合成动力学及相结构,并根据合成过程中的损失对初始成分进行了设计,最终制备出符合原子比La∶Zr∶Ce为10∶7∶3的LZ7C3粉末.用X射线衍射仪和场发射扫描电镜研究了样品的相成分和微观组织,用激光脉冲法和推杆法测量了样品的热导率和热膨胀系数.结果表明:LZ7C3是由烧绿石结构的La2Zr2O7(LZ)固溶体和萤石结构的La2Ce2O7(LC)固溶体组成,其中LZ固溶体是主相;热导率随着温度的升高而逐渐降低,在1473 K时为0.79 W.m-1.K-1,较LZ降低了50%左右;热膨胀系数在1473 K时为11.6×10-6 K-1,比LZ提高了20%左右.这些优越的性能表明LZ7C3是一种具有较大应用前景的新型热障涂层陶瓷材料.     

CuMn_2O_4/Ce(Zr)O_2/cord催化剂对CO-O_2和CO-NO_x反应的研究

用共沉淀法和溶胶凝胶法制备了以CuMn2O4尖晶石为主相的Cu-Mn复合氧化物粉体,并制成负载型CuMn2O4/(Ce(Zr)O2)/cord催化剂,同时测定了CO-O2和CO-NOx的反应活性即λ特性和温度特性,发现空速≤3000h-1情况下,富氧条件下(λ>1.02)溶胶凝胶法制备的CuMn2O4/(Ce(Zr)O2)/cord催化剂的NOx转化率高于Pd/Ce(Zr)O2/cord.     

CuMn2O4/Ce(Zr)O2/cord催化剂对CO-O2和CO-NOx反应的研究

用共沉淀法和溶胶凝胶法制备了以CuMn2O4尖晶石为主相的Cu-Mn复合氧化物粉体,并制成负载型CuMn2O4/(Ce(Zr)O2)/cord催化剂,同时测定了CO-O2和CO-NOx的反应活性即λ特性和温度特性,发现空速≤3000 h-1情况下,富氧条件下(λ>1.02)溶胶凝胶法制备的CuMn2O4/(Ce(Zr)O2)/cord催化剂的NOx转化率高于Pd/Ce(Zr)O2/cord.     

K2CO3-KCl-K2B4O7-H2O四元体系298 K介稳相平衡的实验研究

采用等温蒸发法研究了K2CO3-KCl-K2B4O7-H2O四元体系298 K介稳平衡相关系,并测定了该体系达介稳平衡时液相的密度、折光率和pH值等物化性质.根据实验数据,绘制了该体系298 K的介稳相图及物化性质-组成图.结果表明:该四元体系属简单共饱型,无复盐或固溶体形成;其溶解度等温图含有一个共饱点、三条单变量曲线和3个结晶相区.3个结晶相区分别对应于K2B4O7·4H2O,K2CO3·3/2 H2O和KCl.共饱点的平衡液相组成为w(K2CO3)=51.57%,w(KCl)=1.09%,w(K2B4O7)=1.29%,所对应的平衡固相为K2CO3·3/2 H2O KCl K2B4O7·4H2O.     

CaO-SiO_2-MgO-10%Al_2O_3-5%TiO_2体系液相线的实验测定

针对CaO-SiO_2-MgO-Al2O3-TiO_2体系等温线等热力学数据的缺失等问题,采用热丝法(SHTT)熔化析晶性能测定仪对CaO-SiO_2-MgO-10%Al2O3-5%TiO_2五元渣系相图中MgO质量分数分别为5%,10%和15%特定成分下渣系的熔化温度进行测定,得到不同MgO质量分数下温度随碱度的变化规律,并依据同一初晶区内组分与熔化温度的热力学函数关系拟合得到该渣系1 250,1 300和1 350℃下的液相线。将本实验测定的渣系相图信息与文献中相同相图区域进行对比。研究结果表明:采用热丝法熔化析晶性能测定仪测定渣系温度并绘制等温线的方法是可行的。     

Cu_y/Ce_(1-λ)Zr_λNi_xO_2/La-Al_2O_3催化剂的制备及性能研究

采用共沉淀法制得Ce1-λZrλNixO2载体,将其与La-Al2O3机械混合,然后用等体积浸渍法负载Cu,制得Cuy/Ce1-λZrλNixO2/La-Al2O3催化剂.结果表明:Cu0.03/Ce0.6Zr0.4Ni0.1O2/La-Al2O3显示出更好的催化性能,在其催化下,CO、NO和C3H6的起燃温度都较低,CO的起燃温度低于100℃,NO和C3H6的起燃温度分别为240℃和250℃,并且300℃时,CO和NO能完全转化,450℃时,C3H6能完全转化.表征分析结果表明:由于Ce-Zr-Ni形成稳定的立方晶相固溶体,不出现NiO单斜晶相以及CuO在载体表面富集等现象,La-Al2O3能促使催化剂颗粒更加细化,所以Cu0.03/Ce0.6Zr0.4Ni0.1O2/La-Al2O3的催化性能更好.     

反相胶束微反应器制备α-Fe2O3超细粒子的研究

测定了水 -TritonX - 10 0 -环己烷微乳液体系相图 (2 94K) ,用该反相胶束微反应器制备了α -Fe2 O3超细粒子 ,并研究了制备介质的循环使用 .由Scherrer公式估算得这些晶粒粒径分别为 11.7、2 1.3、2 2 3nm .     

由FeO—V2O3和V2O3-SiO2二元相图提取活度

本文研究了在正规溶液的假设下,运用由二元相图提取活度的方法,分别计算了FeO—V2O3和V2O3-SiO2渣系相图在2500K温度下的活度。经加权平均计算,计算值和实验值的相对误差分别为13．34％和6．5％．这个精度处于Turkdogan提出的10％-30％的实验误差范围以内,可以作为进一步研究复杂含钒渣系时的热力学参考数据。     

符号函数矩阵判别法在水盐相图计算机成图中的应用Ⅱ.复杂三元水盐体系的W1-W2和m1-m2及X1-X2相图

作者以复杂的三元体系Li+ ,K+ ∥SO2 - 4 H2 O在 2 98.15K和 10 1kPa时的W1 W2 ,m1 m2 和X1 X2 相图为例 ,用符号函数矩阵判别法 (SFM法 ) ,对相图中各曲线的稳定区间及无变度点的稳定性进行了判别 ,所得结果均与实验事实相吻合 ,从而解决了此类相图的预测和计算机成图过程中的相关问题 .     

ZrO_2 CeO_2涂层显微组织和抗热震性能

为了改善等离子喷涂ZrO2 涂层的抗热震性能 ,利用热震试验、SEM和EPMA等技术 ,研究了CeO2 添加剂对其显微组织和抗热震性能的影响 .研究结果表明 :当CeO2 添加剂的质量分数小于 9.0 %时 ,涂层的抗热震性能随CeO2添加剂质量分数的增加而提高 ,当CeO2 质量分数大于 9.0 %时 ,涂层的抗热震性能随其质量分数的增加而降低 ;ZrO2 涂层的抗热震次数为 46次 ,而ZrO2 9.0 ?O2 涂层的抗热震次数为 10 5次 ;ZrO2 9.0 ?O2 涂层在热循环中形成网状微裂纹 ,不仅可以降低涂层中的应力 ,而且可以提高涂层开裂的临界温差 ,从而改善其抗热震性能 .     

γNaF·AlF_3-Al_2O_3-Ceo_2系熔体中CeO_2的活度

利用ZrO_2(+MgO)固体电解质组成氧桥式浓差电池并测得了在不同温度与熔体组成的电池的电动势。由电动势数据进一步求出了熔体中CeO_2活度与各种因素关系的回归方程。讨论了各因素对CeO_2活度的影响。指出CeO_2活度随熔体中CeO_2和Al_2O_3含量的增加而加大,随温度升高略有减小,冰晶石比对它的影响不大。为考查各因素的交互作用,绘制了CeO_2活度的等值图。     

Influence of CeO<Subscript>2</Subscript> addition on the preparation of foamed glass-ceramics from high-titanium blast furnace slag

Foamed glass-ceramics doped with cerium oxide (CeO₂) were successfully prepared from high-titanium blast furnace slag by one-step sintering. The influence of CeO₂ addition (1.5wt%–3.5wt%) on the crystalline phases, microstructure, and properties of foamed glass-ceramics was studied. Results show that CeO₂ improves the stability of the glass phase and changes the two-dimensional crystallization mechanism into three-dimensional one. XRD analysis indicates the presence of Ca(Mg, Fe)Si₂O₆ and Ca(Ti, Mg, Al)(Si, Al)₂O₆ in all sintered samples. Added with CeO₂, TiCeO₄ precipitates, and crystallinity increases, leading to increased thickness of pore walls and uniform pores. The comprehensive properties of foamed glass-ceramics are better than that of samples without CeO₂. In particular, the sample added with a suitable amount of CeO₂ (2.5wt%) exhibits bulk density that is similar to and compressive strength (14.9 MPa) that is more than twice of foamed glass-ceramics without CeO₂.     

CeO2在Al2O3及TiO2载体上的分散

采用等体积浸渍法制备了CeO2/Al2O3、CeO2/TiO2复合氧化物载体。应用X-射线粉末衍射（XRD）、比表面积测定、激光Raman光谱、扫描电子显微镜（SEM）等技术研究了CeO2在Al2O3及TiO2载体上的分散状态。结果显示：对CeO2/Al2O3，CeO2主要存在于Al2O3表面，晶粒小、分散性好；而对CeO2/TiO2，大部分CeO2以体相形式与TiO2共存，晶粒大、分散性也差。此外，也没有发现TiO2由锐钛矿向金红石的晶相变化。CeO2/Al2O3具有比Ce/TiO2更大的比表面积，更适合用于催化剂的载体。     

Phase transformation and crystal growth behavior of 8mol% (SmO1.5, GdO1.5, and YO1.5) stabilized ZrO2 powders

Nanocrystalline powders of ZrO2–8mol%SmO1.5(8SmSZ), ZrO2–8mol%GdO1.5 (8GdSZ), and ZrO2–8mol%YO1.5 (8YSZ) were prepared by a simple reverse-coprecipitation technique. Differential thermal analysis/thermogravimetry (DTA/TG), Fourier transform infra-red spectroscopy (FTIR), X-ray diffraction (XRD), Raman spectroscopy, and high-resolution transmission electron microscopy (HRTEM) were used to study the phase transformation and crystal growth behavior. The DTA results showed that the ZrO2 freeze-dried precipitates crystallized at 529, 465, and 467°C in the case of 8SmSZ, 8GdSZ, and 8YSZ, respectively. The XRD and Raman results confirmed the presence of tetragonal ZrO2 when the dried precipitates were calcined in the temperature range from 600 to 1000°C for 2 h. The crystallite size increased with increasing calcination temperature. The activation energies were calculated as 12.39, 12.45, and 16.59 kJ/mol for 8SmSZ, 8GdSZ, and 8YSZ respectively.     

CeO2对自保护药芯焊丝性能的影响

通过向BaF2-Al-Mg渣系自保护药芯焊丝药芯中加入稀土氧化物CeO2，研究了CeO2对该渣系自保护药芯焊丝焊接工艺及熔敷金属低温冲击韧性的影响．研究表明，用适量CeO2代替传统使用的MgO、Al2O3加入到药芯中，经冶金反应生成铈铝复合氧化物CeAlO3，能够有效调整熔渣的物化性能，减小焊接飞溅，改善熔渣覆盖和脱渣性；更为重要的是，以CeO2代替MgO、Al2O3造渣，降低了熔敷金属中大尺寸AIN、MgO·Al2O3等脆性夹杂物的含量，从而提高并稳定了自保护药芯焊丝熔敷金属的低温冲击韧性．     

CeO2对原位自生Al2O3-TiCP/Al基复合材料组织结构的影响

利用Al-TiO2-C体系熔铸法制备含稀土CeO2原位自生Al2O3-TiCP/Al基复合材料.借助差示扫描量热仪(DSC)、扫描电子显微镜(SEM)、能谱分析仪(EDS)、X射线衍射仪(XRD)等测试技术,对Al-TiO2-C体系的组织结构进行了详尽的分析,讨论了对稀土CeO2铝对Al2O3-TiCP/Al基复合材料的影响规律.实验结果表明,稀土CeO2的加入可改善陶瓷颗粒Al2O3和TiC与熔体的润湿性,而且有效的细化和净化了组织,降低了反应温度.稀土CeO2添加剂含量为0.5%时利用熔铸法制备的复合材料中原位形成的Al2O3,TiC颗粒尺寸较小,分布均匀.     

Sr_2CeO_4物相形成过程的XRD分析

采用X射线衍射技术分析了SrCO3和CeO2 (摩尔比 2∶1 )混合粉料经不同灼烧时间反应后的物相组成 .结果表明在Sr2 CeO4的形成过程中将出现不稳定的中间相SrCeO3,原始粉料CeO2 相会提前消失 ,SrCeO3与SrCO3反应生成最终稳定的目标相Sr2 CeO4.X射线衍射数据显示Sr2 CeO4属正交晶系     

H4SiW12O40/ZrO2-Al2O3催化合成环己酮乙二醇缩酮

采用浸渍法制备了H4SiW12O40/ZrO2-Al2O3催化剂,并通过FT-IR、XRD对其进行了表征。探讨了该催化剂对合成环己酮乙二醇缩酮的催化活性,研究了不同因素对产品收率的影响。在n（乙二醇）∶n（环己酮）=1.4∶1,催化剂用量为反应物总质量的1.5%,反应时间75 min的条件下,环己酮乙二醇缩酮的收率为87.5%.     

苯催化燃烧反应Cu-Mn-Ce-Zr-O催化剂催化活性的研究

用共沉淀法合成了铜-锰-铈-锆复合氧化物系列催化剂,用常压气体流动评价装置考查了其对苯蒸气的催化活性,并根据穿透曲线、XRD衍射对催化剂表面性质进行了分析。结果表明:CeO₂和ZrO₂对以铜、锰氧化物催化剂的催化活性有促进作用。