Microstructural evolution and mechanical behavior of metastable β-type Ti–30Nb–1Mo–4Sn alloy with low modulus and high strength

A metastable P-type Ti-30Nb-lMo-4Sn alloy with ultralow elastic modulus and high strength was fabricated.Under the solution treatment state,the Ti-30Nb-1Mo-4Sn alloy possesses low yield strength of about 130 MPa owing to the presence of the coarse α " martensitic laths.Upon a cold rolling and annealing process,the martensitic transformation from β to α" is significantly retarded due to the inhibitory effect of grain boundaries and dislocations.As a result,the metastable β phase with low total amount of β-stabilizers is retained to room temperature,giving rise to a low modulus of 45 GPa.Meanwhile,nano-sized a precipitates and dislocation tangles play a key role in strengthening the Ti-30Nb-1Mo-4Sn alloy,resulting in a high tensile strength of ~ 1000 MPa.With low elastic modulus and high strength,the metastable P-type Ti-30Nb-1Mo-4Sn alloy could be a potential candidate for biomedical materials.     

Effect of pre-annealing treatment on the microstructure and mechanical properties of extruded Al-Zn-Mg-Cu alloy bars

Taking extruded Al-Zn-Mg-Cu alloy (7A04 alloy) bars as the research object, the effect and mechanism of pre-annealing treatments on the microstructure and mechanical properties of the aged alloy bars were investigated. The results show that a pre-annealing treatment at 350℃ for 15 h before a T6 treatment substantially reduced the sensitivity of the microstructure and mechanical properties of the extruded 7A04 aluminum alloy specimens toward the extrusion temperature. The average grain sizes of the specimens extruded at 390 and 430℃ after T6 treatment were 3.4 and 8.1 μm, respectively, and their elongations to failure were 7.0% and 9.2%, respectively. However, after pre-annealing + T6 treatment, the differences in both the grain sizes and the elongations of the specimens became small, i.e., their average grain sizes were 3.2 and 3.8 μm and their elongations were 12.0% and 13.3%, respectively. For the specimens extruded at the same temperature, pre-annealing treatment obviously improved the plasticity of the alloy, which is attributed to an increase in soft texture or to grain refinement in the specimens as a result of the pre-annealing + T6 treatment.     

Improved strength and ductility of high alloy containing Al-12Zn-3Mg-2.5Cu alloy by combining non-isothermal step rolling and cold rolling

Al-12Zn-3Mg-2.5Cu alloy was prepared using a liquid metallurgy route under the optimized conditions. A sample cut from the ingot was rolled non-isothermally from 400℃ to 100℃ in 100℃ steps, with 15% reduction in thickness; it was then cold rolled isothermally at room temperature for 85% reduction. The cold-rolled alloys were characterized by electron microscopy, hardness test, and tensile test to elucidate their structural evolution and evaluate their mechanical behavior. In the results, the cast alloy consists of α-aluminum and various intermetallic compounds. These compounds are segregated along the grain boundaries, which makes the alloy difficult to roll at room temperature. The combined effect of non-isothermal step rolling and cold rolling results in the nano/microsized compounds distributed uniformly in the matrix. The hardness is substantially increased after rolling. This increase in hardness is attributed to the ultra-fine grain size, fine-scale intermetallic compounds, and structural defects (e.g., dislocations, stacking faults, and sub-grains). The ultimate tensile strength of the rolled alloy is approximately 628 MPa with 7% ductility.     

Microstruct ural evolution and mechanical behavior of metastable β -type Ti – 25Nb–2Mo – 4Sn alloy with high strength and low modulus

This paper presents a systematic study of newly developed metastable β-type Ti-25Nb-2Mo-4Sn (wt%) alloy with high strength and low elastic modulus, with focus on the microstructural evolution and mechanical behavior associated with aging. The pre-treatment (solution treatment or cold rolling) prior to aging exerts substantial influence on the subsequent aging response including microstructural evolution and mechanical behavior. Even under the same aging treatment, the aging products could be (β+ω), or alternatively (β+α), depending on the pre-treatments. This interesting aging response was discussed on the basis of the mechanism for ω formation. High-density dislocation tangles and grain boundaries induced by severe cold rolling play a key role in hindering the transition from β to isothermal ω, favoring the precipitation of α phase on aging. By aging cold-rolled specimen for short time, superior mechanical properties, i.e. high ultimate strength of ～1113 MPa and low elastic modulus of ～65 GPa, achieved in Ti-25Nb-2Mo-4Sn alloy. The characterization of microstructural evolution and compositional change indicated that the precipitation of fine α does not cause the enrichment of β-stabilizers in β matrix upon a short-time aging, guaranteeing low elastic modulus of the short-time aged specimen. Meanwhile, fine α precipitates as well as dislocations play a crucial part in strengthening, giving rise to its high yield strength and high ultimate tensile strength.     

Effect of Zn addition on microstructure and mechanical properties of an Al–Mg–Si alloy

In the present work, an Al–0.66Mg–0.85Si–0.2Cu alloy with Zn addition was investigated by electron back scattering diffraction(EBSD), high resolution electron microscopy(HREM), tensile and Erichsen tests. The mechanical properties of the alloy after pre-aging met the standards of sheet forming. After paint baking, the yield strength of the alloy was improved apparently. GP(Ⅱ) zones and η’phases were formed during aging process due to Zn addition. With the precipitation of GP zones, β″ phases, GP(Ⅱ) zones and η’phases, the alloys displayed excellent mechanical properties.     

Peculiar aging response of near b Ti–25 Nb–2Mo–4Sn alloy for biomedical applications

In this paper,aging response of a recently developed near β Ti-25Nb-2Mo-4Sn(wt%) alloy with high strength and low modulus was investigated intensively.The experimental results from X-ray diffraction and transmission electron microscopy showed that the aging production of the Ti-2524 alloy was(β+ω) or(β+α) even under the same aging treatment condition,depending on the pre-treatments prior to the aging.Solid evidence confirmed the competition between stable α phase and metastable ω phase during the decomposition of β phase on aging.Different aging response of Ti-2524 alloy can be attributed to high-density dislocations and grain boundaries which suppress the formation of ω,and alternatively promote a phase formation.This provides a thermo-mechanical approach to inhibit deleterious ω phase formation and assist fine α phase precipitation.Upon an appropriate aging treatment,superior mechanical properties of high ultimate tensile strength(1233 MPa) and low elastic modulus(77 GPa) were achieved in Ti-2524 alloy.     

Effects of gadolinium addition on the microstructure and mechanical properties of Mg-9Al alloy

This research aims to study the significance of Gd addition (0wt%-2wt%) on the microstructure and mechanical properties of Mg-9Al alloy. The effect of Gd addition on the microstructure was investigated via X-ray diffraction (XRD), optical microscopy, scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The Mg-9Al alloy contained two phases, α-Mg and β-Mg17Al12. Alloying with Gd led to the emergence of a new rectangular-shaped phase, Al₂Gd. The grain size also decreased marginally upon Gd addition. The ultimate tensile strength and microhardness of Mg-9Al alloy increased by 23% and 19%, respectively, upon 1.5wt% Gd addition. We observed that, although Mg-9Al-2.0Gd alloy exhibited the smallest grain size (181 μm) and the highest dislocation density (5.1×1010 m-2) among the investigated compositions, the Mg-9Al-1.5Gd alloy displayed the best mechanical properties. This anomalous behavior was observed because the Al₂Gd phase was uniformly distributed and present in abundance in Mg-9Al-1.5Gd alloy, whereas it was coarsened and asymmetrically conglomerated in Mg-9Al-2.0Gd.     

Effect of cold rolling and first precipitates on the coarsening behavior of γ″-phases in Inconel 718 alloy

The coarsening behaviors of γ″-phase particles in Inconel 718 alloy aged at 750, 800, and 850°C were investigated by scanning electron microscopy (SEM). Detailed observations and quantitative measurements were conducted to characterize the coarsening behavior of the γ″-phase under various aging conditions. The experimental results indicate that the existence of the δ-phase retards the formation and coarsening of the γ″-phase, without influencing its final particle size or amount. Moreover, when cold rolled with a reduction of 50%, the dimensions of the γ″ particles in Inconel 718 alloy decrease with increasing aging time. Furthermore, the coarsening behavior of the γ″-phase in the Inconel 718 alloy after a normal aging treatment (sample A) and that of the primary δ-phase (sample B) follow the Lifshitz–Slyozov–Wagner (LSW) diffusion-controlled growth theory; the thus-obtained activation energies for the γ″-phase are 292 kJ·mol-1 and 302 kJ·mol-1, respectively.     

Effect of pickling processes on the microstructure and properties of electroless Ni–P coating on Mg–7.5Li–2Zn–1Y alloy

The electroless plating Ni–P is prepared on the surface of Mg–7.5Li–2Zn–1Y alloys with different pickling processes.The microstructure and properties of Ni–P coating are investigated.The results show that the Ni–P coatings deposited using the different pickling processes have a different high phosphorus content amorphous Ni–P solid solution structure,and the Ni–P coatings exhibit higher hardness.There is higher phosphorus content of Ni–P amorphous coating using 125 g/L Cr O3and 110 ml/L HNO3(w68%)than using 180 g/L Cr O3and 1 g/L KF during pre-treatment,and the coating structure is more compact,and the Ni–P coatings exhibit more excellent adhesion with substrate(Fcup to22 N).The corrosion potential of Ni–P coating is improved and exhibits good corrosion resistance.As a result,Mg-7.5Li-2Zn-1Y alloy is remarkably protected by the Ni–P coating.     

Effect of particle size distribution on the microstructure,texture, and mechanical properties of Al–Mg–Si–Cu alloy

The effect of particle size distribution on the microstructure, texture, and mechanical properties of Al–Mg–Si–Cu alloy was investigated on the basis of the mechanical properties, microstructure, and texture of the alloy. The results show that the particle size distribution influences the microstructure and the final mechanical properties but only slightly influences the recrystallization texture. After the pre-aging treatment and natural aging treatment (T4P treatment), in contrast to the sheet with a uniform particle size distribution, the sheet with a bimodal particle size distribution of large constituent particles and small dispersoids exhibits higher strength and a somewhat lower plastic strain ratio (r) and strain hardening exponent (n). After solution treatment, the sheet with a bimodal particle size distribution of large constituent particles and small dispersoids possesses a finer and slightly elongated grain structure compared with the sheet with a uniform particle size distribution. Additionally, they possess almost identical weak recrystallization textures, and their textures are dominated by CubeND {001}<310> and P {011}<122> orientations.     

Microwave sintering effects on the microstructure and mechanical properties of Ti-51at%Ni shape memory alloys

Ti-51at%Ni shape memory alloys (SMAs) were successfully produced via a powder metallurgy and microwave sintering technique. The influence of sintering parameters on porosity reduction, microstructure, phase transformation temperatures, and mechanical properties were investigated by optical microscopy, field-emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), differential scanning calorimetry (DSC), compression tests, and microhardness tests. Varying the microwave temperature and holding time was found to strongly affect the density of porosity, presence of precipitates, transformation temperatures, and mechanical properties. The lowest density and smallest pore size were observed in the Ti-51at%Ni samples sintered at 900℃ for 5 min or at 900℃ for 30 min. The predominant martensite phases of β2 and β19' were observed in the microstructure of Ti-51at%Ni, and their existence varied in accordance with the sintering temperature and the holding time. In the DSC thermograms, multi-transformation peaks were observed during heating, whereas a single peak was observed during cooling; these peaks correspond to the presence of the β2, R, and β19' phases. The maximum strength and strain among the Ti-51at%Ni SMAs were 1376 MPa and 29%, respectively, for the sample sintered at 900℃ for 30 min because of this sample's minimal porosity.     

Evaluation of the microstructure,secondary dendrite arm spacing,and mechanical properties of Al-Si alloy castings made in sand and Fe-Cr slag molds

The microstructure and mechanical properties of as-cast A356 (Al-Si) alloy castings were investigated. A356 alloy was cast into three different molds composed of sand, ferrochrome (Fe-Cr) slag, and a mixture of sand and Fe-Cr. A sodium silicate-CO₂ process was used to make the necessary molds. Cylindrical-shaped castings were prepared. Cast products with no porosity and a good surface finish were achieved in all of the molds. These castings were evaluated for their metallography, secondary dendrite arm spacing (SDAS), and mechanical properties, including hardness, compression, tensile, and impact properties. Furthermore, the tensile and impact samples were analyzed by fractography. The results show that faster heat transfer in the Fe-Cr slag molds than in either the silica sand or mixed molds led to lower SDAS values with a refined microstructure in the products cast in Fe-Cr slag molds. Consistent and enhanced mechanical properties were observed in the slag mold products than in the castings obtained from either sand or mixed molds. The fracture surface of the slag mold castings shows a dimple fracture morphology with a transgranular fracture nature. However, the fracture surfaces of the sand mold castings display brittle fracture. In conclusion, products cast in Fe-Cr slag molds exhibit an improved surface finish and enhanced mechanical properties compared to those of products cast in sand and mixed molds.     

Effect of Al on microstructure and mechanical properties of as-extruded Mg–1Mn alloy sheet

The effect of Al addition on microstructure and mechanical properties of hot extruded Mg–1 Mn alloy sheet was investigated. The results revealed that the dynamic recrystallization was promoted by increasing Al content. The ultimate tensile strength and yield strength of the alloy increased with the increase of Al content. The Mg–9 Al–1 Mn alloy exhibited the highest strength, with tensile strength of 308 MPa, 307 MPa, 319 MPa, yield strength of 199 MPa, 207 MPa, 220 MPa and the elongation of 20.9%, 20.1%, 19.2% in 0°, 45°, 90°, respectively.The high strength was mainly attributed to the formation of fine dynamically recrystallized grains and large amounts of the second phase. The strengthening mechanism of the alloys was explained.     

Effect of ECAP temperature on microstructure and mechanical properties of Al–Zn–Mg–Cu alloy

The effect of equal channel angular pressing(ECAP) at different temperatures(room temperature, 120,150 and 180 °C) on microstructure and mechanical properties of Al-7075 solid solution alloy was investigated. Microstructure of the specimens was examined using orientation imaging microscopy,transmission electron microscopy as well as X-ray diffractometer, and mechanical properties were measured by Vickers microhardness and tensile tests. Microstructural investigations showed that after3 or 4 passes of ECAP, fi ne grains with average grain sizes in range of 300–1000 nm could be obtained at different ECAP temperatures. Increasing ECAP temperature from 120 to 180 °C caused a decrease in mechanical properties as a result of increasing grains and precipitates sizes, decreasing fraction of high angle boundaries and also transformation of η′ into η phase, while increasing ECAP temperature from RT to 120 °C leads to an increase in mechanical properties due to the formation of small η′ precipitates. So it can be concluded that ECAP process at 120 °C is the optimum process for attaining maximum mechanical properties. Quantitative estimates of various strengthening mechanisms revealed that the improvement of mechanical properties was mainly attributed to grain re fi nement strengthening, precipitation strengthening and dislocation strengthening.     

Effects of the deep rolling process on the surface roughness and properties of an Al-3vol%SiC nanoparticle nanocomposite fabricated by mechanical milling and hot extrusion

Deep rolling is one of the most widely used surface mechanical treatments among several methods used to generate compressive residual stress. This process is usually used for axisymmetric components and can lead to improvements of the surface quality, dimensional accuracy, and mechanical properties. In this study, we deduced the appropriate deep rolling parameters for Al-3vol%SiC nanocomposite samples using roughness and microhardness measurements. The nanocomposite samples were fabricated using a combination of mechanical milling, cold pressing, and hot extrusion techniques. Density measurements indicated acceptable densification of the samples, with no porosity. The results of tensile tests showed that the samples are sufficiently strong for the deep rolling process and also indicated near 50% improvement of tensile strength after incorporating SiC nanoparticle reinforcements. The effects of some important rolling parameters, including the penetration depth, rotation speed, feed rate, and the number of passes, on the surface quality and microhardness were also investigated. The results demonstrated that decreasing the feed rate and increasing the number of passes can lead to greater surface hardness and lower surface roughness.     

Effect of rolling geometry on the mechanical properties,microstructure and recrystallization texture of Al–Mg–Si alloys

The effect of rolling geometry on mechanical properties, microstructure, and recrystallization texture of Al–Mg–Si alloys was studied by means of tensile tests, microstructural observations, and electron backscatter diffraction measurements. The results reveal that the elongation and the average plasticity strain ratio(r) values of the T4P(pre-aging plus natural aging)-treated alloy sheet with a rolling geometry value between 1 and 3 are somewhat higher than those of the T4P-treated sheet with a rolling geometry value between 3 and 6. The deformation and recrystallization microstructures of the sheet with a rolling geometry value between 1 and 3 are more uniform than those of the sheet with a rolling geometry value between 3 and 6. The former also possesses somewhat higher surface quality. H {001}110 and Goss {110}001 orientations are the main recrystallization texture components for the former case, whereas the latter case only includes H{001}110 orientation. Texture gradients are present in the two alloy sheets. Shear texture component F on the surface of the sheet with a rolling geometry value between 3 and 6 and its higher texture gradients have revealed that non-uniform deformation occurred during cold rolling. The effects of texture on the yield strength and r value were also discussed.     

Effect of particle size distribution on the microstructure,texture,and mechanical properties of Al–Mg–Si–Cu alloy

The effect of particle size distribution on the microstructure,texture,and mechanical properties of Al–Mg–Si–Cu alloy was investigated on the basis of the mechanical properties,microstructure,and texture of the alloy.The results show that the particle size distribution influences the microstructure and the final mechanical properties but only slightly influences the recrystallization texture.After the pre-aging treatment and natural aging treatment(T4 P treatment),in contrast to the sheet with a uniform particle size distribution,the sheet with a bimodal particle size distribution of large constituent particles and small dispersoids exhibits higher strength and a somewhat lower plastic strain ratio(r) and strain hardening exponent(n).After solution treatment,the sheet with a bimodal particle size distribution of large constituent particles and small dispersoids possesses a finer and slightly elongated grain structure compared with the sheet with a uniform particle size distribution.Additionally,they possess almost identical weak recrystallization textures,and their textures are dominated by CubeND {001}310 and P {011}122 orientations.