分散剂对铁氧体烧结粉体的影响

采用加入分散剂的方法对传统氧化物法制备Mn-Zn铁氧体进行改进.利用X射线衍射(XRD)仪、扫描电子显微镜(SEM)及激光粒度分析仪观察烧结体显微结构及粒度情况.并分析了原料配比与材料磁性能的关系.结果表明:加入分散剂后欲烧粉末的粒度有了明显减小、粒度分布也更为均匀、粉体颗粒的基本形状为球形,有利于使用低温烧结技术.同时分散剂的加入使烧结体的软磁特性更加突出.     

TiO2和SiO2-Ag混合纳米粉体在水溶液中的分散

研究不同分散介质和分散剂对TiO2和SiO2-Ag混合纳米粉体在水溶液中分散的影响,采用分散相的沉降高度和分散后颗粒的粒度分布评价分散效果,得出（NaPO3）6是TiO2和SiO2-Ag粉体的良好分散剂.通过测定分散相在分散介质中ζ电位,分析分散剂的分散机制,（NaPO3）6可分别显著提高水溶液分散中TiO2和SiO2-Ag粉体表面ζ电位的绝对值,使超细混合粉体在水溶液中获得良好稳定的分散.     

粉体粒度及成型压力对YBa2Cu3O7-δ超导体烧结前后致密度的影响

应用固态反应法,制备了YBaCuO超导粉体.研究了粉体粒度及成型压力对YBaCuO超导体烧结前后致密度的影响.结果表明,不同粒度YBaCuO超导粉体的压坯密度、烧结密度(即烧结前后的致密度)随压力的变化规律不同.在粉体干压成型过程中,同一粒度粉体的压坯密度随压力增大而增大;不同粒度粉体相比,粒度大的粉体压坯密度较大.在压坯烧结过程中,粒度小的粉体表面活性大,其压坯烧结密度也较大;同一粒度不同坯体的烧结密度随压坯密度的增大而增大.     

不同分散剂对制备NiO/SDC粉体粒度和团聚的影响研究

采用柠檬酸法制备NiO/SDC粉体,研究了不同分散剂对制备NiO/SDC粉体粒度和团聚的影响。借助X-射线衍射仪,透射电子显微镜对粉体形貌进行分析,激光粒度仪对NiO/SDC粉体粒径分布和比表面积进行测定。结果表明:添加非离子型分散剂聚乙二醇6000的NiO/SDC粉体具有最小的体积平均粒径1.758μm,最大的比表面积6.44m2/g和最小的表面积平均粒径0.932μm,具有最好的分散效果。     

氧化铝多孔陶瓷凝胶注模成型研究

以TH-903为分散剂,刚玉粉体为基体材料,以碳粉为造孔剂,采用凝胶注模成型方法制备了多孔氧化铝陶瓷.研究了分散剂、球磨时间和固相含量对浆料粘度的影响以及造孔剂含量对多孔陶瓷性能的影响.结果表明:加入质量分数为2.5%的分散剂可制得低粘度、高固相含量的陶瓷浆料.成型后的坯体经1360℃烧结1h,可获得孔径分布均匀、高显气孔率及强度较高的产品.     

有机分散剂对球形氧化铝前驱体形貌的影响

采用均匀沉淀法在较低浓度下制备的氧化铝前驱体呈单分散球形,在提高浓度后发生团聚并偏离球形.在反应物中加入聚乙烯吡咯烷酮(PVP)及聚乙烯醇(PVA)作为有机分散剂,可以改善粉体形貌和团聚状态.结果表明:1%的PVP可以有效改善粉体的团聚状态,但粉体粒度分布不均匀,继续增加PVP的用量使团聚现象加剧.PVA则能改善前驱粉体的形貌和粒度分布.当同时加入1%PVP和1%PVA其作用效果优于单独加入时,所制得的氧化铝前驱体呈球形无定型态,粒度约850nm.     

低温固相反应合成NiFe2O4尖晶石纳米粉

以FeSO4.7H2O,NiSO4.6H2O和NaOH为原料,NaCl为分散剂,在室温下充分研磨反应制备前驱体,然后将前驱体进行煅烧得到NiFe2O4尖晶石纳米粉.重点研究了分散剂含量、煅烧温度和保温时间对粉体粒度和形貌的影响.利用X射线衍射仪(XRD)和扫描电子显微镜(SEM)对所得产物进行表征.结果表明:添加20%(质量分数)NaCl制得的前驱体在800℃下煅烧1.5h得到的纳米粉分布均匀,颗粒呈球形并且晶型完整单一,平均粒径约为75nm.     

溶胶-凝胶法制备(Ba,Sr)TiO3超细粉体的研究

以硝酸锶、硝酸钡、钛酸四丁酯、氨水、柠檬酸为前驱体原料,采用溶胶-凝胶法制备超细Ba0.7Sr0.3TiO3（BST）陶瓷粉体,详细研究了柠檬酸量、溶液pH值、分散剂、热处理温度对BST粉体粒径的影响。结果表明：通过控制前驱体溶液pH值可以得到均匀的溶胶。当溶液的pH值为7,分散剂含量为2.5 ml,热处理温度为800℃时,得到了性能较好的BST粉体。相比于传统工艺,热处理温度大大降低,粉体粒度分布较窄,平均粒径约为100 nm。     

在水介质中分散剂对微细颗粒分散作用的影响

研究不同颗粒在水介质中的自然分散行为及分散剂对其分散作用的影响，结果表明，分散剂对二氧化硅，重质碳酸钙，滑石和石墨均有不同程度的分散作用，在分散剂浓度较低区域，４种颗粒的分散规律几乎相似；在高浓度区域，对不同颗粒的分散有共各自的特征，分散剂对重质碳酸钙和滑石颗粒的分散作用比对二氧化硅和石墨的分散作用强烈，对同类矿物颗粒来说，亲水性颗粒较疏水性颗粒的分散作用强烈。     

表面活性剂制备ZTM陶瓷的作用机制

用高分子表面活性剂取代无乙醇作分散剂制备ＺＴＭ陶瓷，研究了制备方式对陶瓷烧结性和力学性能的影响。分析了不同粉体的粒度及其分布并采用Ｘ－射线衍射分析计算出各试样的氧化锆含量。研究发现分别以ＰＥＧ、无水乙醇作分散剂制备的试样具有相近的力学性能，为优化工艺、改善性能提供了条件。     

超细无机粉体的水中分散研究综述

叙述表面活性剂对超细无机粉体水中分散的３ 个步骤（润湿、分散、稳定）的影响,重点解释分散稳定机理与分散剂的作用,并介绍表面活性剂的分子结构与分散性的关系。具体列出了用于无机粉体水浆料的３ 种类型分散剂（无机型、有机型、高分子型）,初步讨论了分散剂的使用情况（ 最佳分散剂用量、固含量与最佳分散剂用量关系、粒径与分散剂用量关系） 。     

Effect of Homogenizing Procedures on the Properties of Reaction Sialon Suspension

Homogeneous, high concentrated ceramic suspensions wi th low viscosity are the key controlling factors for the production of ceramic c omponents through colloidal processing. A well-dispersed suspension can be obta ined by choosing suitable dispersant, solvent, particle size distribution etc. B esides these factors, the homogenizing procedure is also a key step. In this paper, reaction sialon suspensions were prepared using 3-wt% KD1 as dis persant in organic media composed of 60-vol% methyletheylketone a...     

Gel Casting of 316L Stainless Steel Powder Through Mold DIS Process

This paper presents the gel casting of metal powder by agar gelation through mold decomposed injection sculpture (DIS) process: verifying the feasibility and improving the processing parameters to prepare stable metal slurry and strong green body. The optimal processing parameters were achieved after investigating the effects of these parameters such as temperature, agar content, dispersant concentration, and solid volume loading. The rheological behavior of metal slurry and the character of formed green body were also investigated. The mixture and dispersion mechanism of metal slurry as well as the consolidation forming and sintering technology of green body were studied based on analysis of experimental results. The results show that the optimal pH range is 8.5–9.5 with the grain size distribution of 2–30 μm and 55% solid suspension, which can be prepared by adding proper dispersant (Polyvinyl Alcohol). The agar and dispersant content has great effect on the properties of slurry. When 1.0 wt.% dispersant and 0.7 wt.% agar content (referred to dry solid) are adopted, stable metal slurry with viscosity less than 1 Pa · s and green body with bending strength of 2.7 MPa are obtained. The sintered bodies with uniform structure, relative density of 90%, and yield strength of 150 MPa are prepared at 1300°C/30min in vacuum. This process can be applied in rapid prototyping of complex shape metal products such as rotor blades.     

用NaCl解决胶体絮凝问题的研究

为了防止胶体迁移实验中产生胶体絮凝,以高岭土溶液胶体为例,利用NaCl对胶体溶液进行了处理,在对激光粒度分析仪测量稳定性进行验证后,通过一系列比对实验研究表明,利用NaCl处理胶体溶液可以有效地防止溶于水后的胶体产生絮凝,且NaCl处理后悬浊液粒径分布并不会因为时间延续和胶体溶液中NaCl的浓度变化而发生较大改变,具有很好的稳定性.进一步分析表明胶体溶液的振荡、NaCl的漂洗等物理过程对悬浊液粒径分布的影响很小,利用NaCl处理胶体溶液是解决胶体絮凝问题的一种有效方法.     

ZrO2基陶瓷注凝成型料浆流变性的研究

陶瓷料浆流变性能是注凝成型工艺的关键,料浆流变性要求高固含量,低粘度.实验通过在ZrO2表面包覆Al2O3,形成ZrO2-Al2O3复相陶瓷料浆.根据静电位阻稳定理论,通过调节pH值和分散剂的加入量,可得到满足成型要求的高固含量,低粘度的料浆.结果表明,在pH值为10左右,分散剂加入量为粉料质量的3%时,料浆固相体积分数可以达到40%.同时表明了Al2O3对ZrO2颗粒表面有改性作用,提高了悬浮体的稳定性.     

SN5040对纳米碳酸钙粒子分散作用的实验研究

为研究纳米碳酸钙注浆技术,必须解决纳米材料在水性介质中的分散问题。本文分别从粒度分布、微观形貌、粘度指标研究了SN5040分散剂对粒径15-40nm的碳酸钙粉体在水溶液中的分散行为。重点研究了SN5040分散剂用量、超声作用时间对分散性影响及此分散剂作用下纳米浆液的流变特性。研究表明,通过合理控制影响纳米碳酸钙分散效果的因素,能够使得纳米材料在水中得到较好的分散;SN5040对纳米碳酸钙具有良好的分散性能,分散后的颗粒粒径90%以上处于255nm以下。     

微硅粉固相反应制备莫来石粉体工艺

 以微硅粉和工业氧化铝为原料,在空气气氛下固相反应合成莫来石粉体。研究了煅烧温度和Al₂O₃/SiO₂的物质的量比对反应产物物相组成的影响,结果表明,当Al₂O₃ /SiO₂的物质的量比为3：2.5、煅烧温度为1450℃时,制备莫来石粉体质量分数达到最高,根据K值法计算其质量分数为95%。莫来石粉体平均粒径随球磨时间延长而逐渐减小,最终粉体平均粒径为0.58μm,比表面积为9.26m²/g,粒径分布由单峰分布演变为双峰分布,莫来石粉体颗粒形状不规则,以多边体状存在。     

镍微粉的颗粒度测定条件研究

镍微粉的粒度对其最终产品的性能有显著的影响．本文采用激光粒度法测定了镍微粉的颗粒度,研究了分散剂种类、分散剂用量、超声时间、搅拌速度和循环分数对镍微粉粒度测定的影响,得出最佳测定条件为：添加的分散剂为正丁醇;分散剂用量为5．0％;超声时间为1．5min;搅拌速度为30％：泵循环分数为25％．     

Preparation of Waterborne Nanoscale Carbon Black Dispersion with Sodium Carboxymethyl Cellulose

Waterborne nanoscale carbon black dispersion （NCBD） was widely used in inkjet printing, spun.dyeing fibers and coloration fabrics. In this paper, NCBD was prepared using sodium carboxymethyl cellulose （CMC） as dispersant. Effects of CMC viscosity, ultrasonic time and oxidation with hydrogen peroxide on carbon black （CB） particle size were discussed. The results showed that CB particle size decreased by mechanical agitation while it Increased by ultrasonic with the increase of CMC viscosity. Uitrasonk is a more effective method to disperse CB particles than that of mechanical agitation. CB particle size lbviously decreased with itcreasing ultrasonic time and arrived at about 160 nm for 60min.In addition,oxidation with 2 mol/L of H2O2 and 0.2wt% of CMC300 reduced CB particle size to 160nm at 90℃ for 2.5h.     

水热法合成超细T型分子筛

在较低温度和添加四甲基氢氧化锰溶液(TMAOH)模板剂条件下,采用水热法合成了平均粒径为150nm的超细T型分子筛.采用XRD、IR、SEM和N2吸附脱附法表征了合成的样品.结果表明,合成的超细T型分子筛晶粒具有均匀的颗粒粒径分布和大的比表面积,而且极少量的超细晶种就能有效地促进T型分子筛的结晶.添加晶种或模板剂均可以有效地控制生成晶粒的大小和分布.