楔横轧空心件压扁变形对成形的影响

楔横轧空心零件过程中轧件会发生压扁变形,增加了成形的困难. 文中首先采用有限元数值模拟的方法,对平板压缩实心零件和空心零件进行对比,研究了空心零件压扁变形的特征,并得到了压下量和相对壁厚是影响压扁变形程度的主要因素. 通过模拟两辊楔横轧成形实心和空心零件的轧制过程,分析了压扁变形使空心零件旋转条件变差的原因及其对轧制过程和成形结果产生的影响,进而提出了改善成形条件的方法.      

金属橡胶辊压成形工艺及力学性能关联分析

针对新型辊压和传统冲压两种成形工艺制备薄壁平板状金属橡胶的微观结构和力学性能差异性,利用ABAQUS软件对成形过程进行有限元仿真,预测了两种金属橡胶内部细观结构的变形特征,验证了金属橡胶力学性能与结构的关联性,并确定了辊压优选参数。试验结果表明,不同成形工艺过程影响金属橡胶内部螺旋丝的钩连和接触形式,辊压比冲压得到的试样的刚度明显更低,但对金属橡胶的宏观损耗因子影响并不大;辊压时采用多道次、小压下量可以提高金属橡胶的阻尼性能,辊压速度和进料方向对金属橡胶的力学性能影响不明显。本研究工作为辊压成形制备金属橡胶的工艺设计及工程化应用提供了参考价值。     

Influence of a multi-step process on the thickness reduction error of sheet metal in a flexible rolling process

Flexible rolling is a forming process based on thickness reduction, and the precision of thickness reduction is the key factor affecting bending deformation. The major purpose of the present work is to solve the problem of bending deformation error caused by insufficient thickness reduction. Under the condition of different rolling reductions with the same sheet thickness and the same thickness reduction with different sheet thicknesses, the thickness reduction error of sheet metal is analyzed. In addition, the bending deformation of sheet metal under the same conditions is discussed and the influence of the multi-step forming process on the thickness reduction error is studied. The results show that, under the condition of the same sheet thickness, the thickness reduction error increases with increasing rolling reduction because of an increase in work hardening. As rolling reduction increases, the longitudinal bending deformation decreases because of the decrease of the maximum thickness difference. Under the condition with the same thickness reduction, the thickness reduction error increases because of the decrease of the rolling force with increasing sheet thickness. As the sheet thickness increases, the longitudinal bending deformation increases because of the increase in the maximum thickness difference. A larger bending deformation is divided into a number of small bending deformations in a multi-step forming process, avoiding a sharp increase in the degree of work hardening; the thickness reduction error is effectively reduced in the multi-step forming process. Numerical simulation results agree with the results of the forming experiments.     

高强度钢冷弯成型过程应力状态模拟分析

运用有限元分析软件对不同工艺下的高强度钢冷弯成型过程应力、应变状态进行模拟分析。结果表明,所作的有限元应力、应变状态模拟符合实际成型情况;3种不同成型道次中,4道次成型为最佳成型道次;上轧辊角大于成型角4°可最大限度地减小残余轧制应力。     

冷连轧过程控制轧制力模型综合参数自适应

轧制力模型是冷连轧过程控制系统的基本模型,影响其预报精度的主要因素是材料的变形抗力和摩擦因数. 本文采用参数自适应方法来提高轧制力的预报精度. 在对轧制力模型进行自适应过程中,将材料的变形抗力作为轧制过程模型的整体属性,各机架根据累计变形程度确定各自的变形抗力. 在此基础上,将摩擦因数看成是各机架的单体属性,各机架取不同的模型参数. 实践证明,这种综合考虑变形抗力和摩擦因数的参数自适应方法可以对二个参数同时进行修正,能有效提高轧制力模型的预报精度.     

连铸坯液芯轧制的模拟实验与计算

对连铸方坯带液芯轧制的工艺进行了计算机模拟实验的分析，指出了方坯带液芯轧制时的变形特点、应力、应变的变化趋势，以及液芯率的大小对轧制能耗和应力、应变及变形规律的影响．在有液芯存在时，轧件的上下表面向内凹陷，侧面易于形成单鼓变形，并且随液芯率的增大而增大；同时由于静不定的作用引起轧件角部的旋转．加上变形的作用，将导致边部应力大大增加，其表现出来的变化是先减小而后增大的趋势．     

工艺参数对楔横轧4Cr9Si2表面螺旋痕的影响

借助DEFORM软件对4Cr9Si2楔横轧成形过程进行了数值模拟,分析了工艺参数对楔横轧4Cr9Si2轧件表面螺旋痕影响规律.结果表明:轧件表面螺旋痕是轧件在成形过程中产生应力状态改变而产生的缺陷.随着成形角增大,表面螺旋痕深度将增加;随着楔尖圆角增大,表面螺旋痕将迅速降低;展宽角对表面螺旋痕影响较小;断面收缩率减小,塑性变形量小,表面螺旋痕将减轻.通过实验验证了有限元模拟的正确性.最后对某型气门进行了模拟和实验,当Ψ=70.84%时,在α=32°,β=7.5°,R=12mm下得到了表面无螺旋痕气门.     

Three Dimension Rigid-plastic Finite Element Simulation for Two-Roll Cross-wedge Rolling Process

Cross-wedge rolling (CWR) is a metal process of ro ta ry forming. To produce a part, one cylindrical billet should be placed between t wo counterrotating and wedge-shape dies, which move tangentially relative each other. The billet suffers plastic deformation (essentially, localized compressio n) during its rotation between the rotating dies. Compared to other numerical si mulation methods, the finite element method (FEM) has advantages in solving gene ral problems with complex shapes of the formed parts. ...     

挤压工艺生产高性能不锈钢管

采用热挤压和冷轧工艺生产HR3C无缝钢管,金属冷成型过程和成品性能均表明热挤压加冷轧工艺生产高合金难变形材料具有明显优势.热挤压加工变形时金属承受三向压应力,可以提高金属的综合性能;通过冷轧加工改善管材表面质量和尺寸精度,可以确保材料在特殊环境中使用安全性更高.     

Deformation Behaviors of Laser Forming of Ring Sheet Metals

Laser forming is a highly flexible sheet metal forming technique. In laser forming along curved irradiation paths, the heated zone is bigger and the effects of the processing parameters on the deformation are complex. The deformation behaviors of laser forming of ring sheet metals have been investigated from the thermal-mechanics analysis by the finite element (FE) simulation based on the proposed finite element method model. The effects of ring central angle and scanning path on deformation of ring sheet metal were investigated. The results are as follows: (1) in comparison with the laser bending along linear path, the marked third point has two peak temperatures during the laser forming process along curved path; (2) the forming process fluctutes continuously and the sheet edge is warped because the rigid-ends effect due to the restriction of sheet; (3) when the ring central angle increases, the displacement difference of the marked three points decreases and then increases, and the warped curvature of sheet edge decreases; (4) when the laser beam diameter increases, the displacement difference of the marked three points decreases and the warped curvature increases.     

FRP布钢与混凝土预应力组合梁受力分析

利用FRP(纤维增强复合材料)耐腐蚀、轻质、高强等优点,在钢与混凝土预应力简支组合梁下表面粘贴FRP布,形成能够有效减小变形和提高承载力的新型FRP布钢与混凝土预应力组合梁.以数值积分方法为基础,考虑材料非线性,提出该组合梁由加载至破坏的全过程非线性分析模式,研制计算程序,得到荷载与变形、荷载与预应力增量关系曲线,对其进行全过程非线性分析,明确组合梁不同受力阶段的工作特性,并通过算例验证该分析模式的正确性.     

FRP-铝合金平面桁架结构极限承载性能试验研究

为了提升脆性FRP拉挤型材应用于桁架体系时的结构延性承载性能,提出了将金属材料构件和不同组合节点应用于FRP桁架体系的组合设计理念。设计和制备了一榀FRP-铝合金平面桁架模型,通过开展结构四点弯曲极限破坏试验,揭示了结构的全过程非线性位移响应、破坏模式及机理,进而对所提设计理念及结构延性提升措施的可行性进行了验证。试验结果表明：组合平面桁架结构在最终失去承载力之前呈现出组合节点滑移、铝合金上弦杆压屈变形、端部GFRP斜腹杆压溃破坏等多种渐进破坏模式,结构全过程荷载-位移曲线表现出明显的非线性变化趋势,特别是铝合金上弦杆的压屈效应使整体结构具备了明显的延性变形特征。建议可通过对FRP桁架在结构和构件层面进行组合设计,使其获得良好的延性承载性能和破坏预警信息,以提升结构的安全性和鲁棒性。     

小断面收缩率楔横轧件的变形规律

对楔横轧轴类零件的成形过程进行有限元数值模拟与轧制实验。从断面收缩率角度研究了轧件的金属变形特点,发现小断面收缩率与常规断面收缩率的分界点在35%左右。对比分析了小断面收缩率与常规断面收缩率轧件的金属变形规律。结果显示：小断面收缩率轧件的主要变形发生在轧件外层附近,而常规断面收缩率轧件的主要变形是在轧件内部;小断面收缩率轧件比常规断面收缩率轧件存在更大的轴向拉伸不均匀变形,易导致轧件在横截面上呈现出椭圆化。     

楔横轧轧制螺旋齿形件力能参数的影响因素

针对楔横轧轧制螺旋齿形轴类件的成形过程复杂、轧制力与轧制力矩等力能参数受轧制条件以及工艺参数的影响规律复杂等问题,采用DEFORM-3D有限元软件模拟楔横轧轧制螺旋齿形件的成形过程,分析不同工艺参数对轧制力和轧制力矩的影响规律。在H630楔横轧机上进行轧制实验,分别采用AD7202压力传感器和TorqueTrak9000扭矩仪测试轧制过程中轧制力和轧制力矩,进而验证各工艺参数对力能参数的影响规律。研究结果表明:轧制力和轧制力矩随轧制温度的升高而减小,随齿高变化率、轧制速度以及轧辊直径的增加而增加,其中,轧制温度对力能参数的影响最明显,齿高变化率和轧制速度的影响次之,轧辊直径的影响最小;进行轧机设计时,为了确保轧机承受足够大载荷,一般选取较低的轧制温度、较大的齿高变化率和较大的轧制速度。     

工艺参数对楔横轧二次楔轧制超大断面收缩率轴类件的影响

为考察楔横轧二次楔轧制在超大断面收缩率情况下的成形规律,在H630轧机上进行了不同工艺条件下的超大断面收缩率轧制实验,得到各工艺参数对轧制质量的影响规律,发现在超大断面收缩率情况下二次楔的工艺参数对内部缺陷和拉断加工界限有决定性影响.结果表明,只要参数得当,二次楔轧制可以获得合格的大断面收缩率轴类件.     

汽车变速器输入轴塑性成形工艺

输入轴是汽车变速器中重要零件,针对其特殊结构提出一火加热和轧锻结合的塑性复合加工工艺,即采用圆柱坯料只进行一次加热,依次采用楔横轧和锻造工艺加工塑性成形输入轴。本文分别设计楔横轧和锻造模具,并进行相关实验。在锻造工艺中轴部圆角采用挤压方案成形,避免其出现折叠缺陷。阶梯轴作为两步工艺的中间产品,其在复合工艺过程中起到承上启下的作用,分别对阶梯轴锥角和轴长进行实验与分析,确定参数的最佳选取范围,并最终通过复合工艺加工成形输入轴。输入轴齿形填充饱满,各部分无缺陷。     

楔横轧小断面收缩率轧件螺旋组织缺陷研究

轧件发生局部变形是楔横轧的主要工艺特征,尤其小断面收缩率轧件轴向流动能力弱,内外变形差异显著导致楔横轧成形困难.除了容易产生心部破坏缺陷,在轧件表层一定范围内出现的螺旋组织缺陷,也会降低产品的机械性能.本文通过轧制实验,展示出轧件螺旋组织缺陷宏观上呈现为车削后在表层一定深度范围内沿展宽螺旋线分布的亮带,微观上由轧件表面折叠向内部延伸呈带状分布的组织形态.结合有限元数值模拟方法研究了缺陷产生的主要原因,发现由于成形区的金属发生沿展宽负向的金属流动,导致轧件形成沿展宽螺旋线分布的表面折叠和小轴向应变带.同时,螺旋带附近较大的径向压缩使轧件由表面向内部沿折叠裂纹方向组织具有方向性.采用对模具楔尖倒圆角局部改善金属沿负展宽方向的轴向流动,可以既消除表层螺旋组织缺陷,又避免轧件心部损伤风险,使成形质量满足使用要求.经实验验证,确定了模具楔尖圆角的最优取值.     

基于条元法的异步轧制金属三维塑性变形分析

采用条元法分析了异步轧制条件下金属在变形区内的变形情况,建立了适用于异步轧制的轧制压力公式及中性点坐标公式,并在计算摩擦力时考虑了粘着区的存在。通过仿真分析,得到了异步轧制条件下变形区内摩擦力的分布规律及应力、应变的分布规律,最后分析了不同速比对等效应力的影响以及不同入口厚度对轧制压力的影响。     

热芯大压下轧制厚板坯缩孔及表面开裂的数值模拟

为了研究连铸坯热芯大压下轧制工艺对铸坯内部缩孔和表面开裂的影响,以EH47船板钢为研究对象,利用数值模拟方法,对比研究了热芯大压下轧制和常规热轧的工艺效果.结果表明,热芯大压下铸坯厚向温度梯度更大,芯部应变水平和厚向变形均匀性提高;当压下量为50 mm时,热芯大压下轧后残余孔隙体积比常规工艺小18.4％;由于热芯大压下...     

微观组织和织构对H65黄铜带材折弯性能的影响

电子产品关键部件小型化对黄铜合金带材折弯性能提出了更高的要求。研究了微观组织和织构对H65黄铜带材折弯性能的影响规律和影响机制。结果表明：带材平行于轧向折弯较垂直于轧向折弯更易于产生表面褶皱和裂纹,且随着折弯半径的减小,折弯性能降低。折弯变形过程中带材外表面易形成剪切带,所产生的剪切变形是造成表面褶皱和开裂的主要原因。微观组织不均匀、较强的Brass织构易导致带材折弯过程中产生剪切变形,造成带材折弯性能下降。通过调控热处理工艺来调整带材织构,减少或抑制剪切带的产生,能够提升带材的折弯性能。