Characteristic parameters and operational curves of γ-Al2O3 nanofiltration membranes

The γ-Al2O3 nanofiltration membranes were manufactured by the sol-gel technique. The result of N2 adsorption and desorption test indicates that the characteristic parameters of the membranes: BJH desorption average pore diameter, BJH desorption cumulative volume of pores and BET surface area are about 3.9 nm, 0.33 cm^3/g and 245 m^3/g respectively, and the pore size distribution is very narrow.The operational curves of γ-Al2O3 nanofiltration membranes of the Ca^2 retention rate vs the trans-membrane pressure,feed concentration of solution treated and pH of solution treated were studied for the first time. It is found that the retention rate for Ca2~ increases with the transmembrane pressure increasing and decreases with the feed concentration of CaCl2 solution increasing. The retention of Ca^2 is very rmuch dependent on the pH of the solution. Minima Ca^2 retention rate is found at the isoelectric point (pH=7.5).     

红色荧光粉Ca_3B_2O_6:Eu~(3+)的制备及发光性能

采用高温固相法合成了Ca3B2O6:Eu3+红色荧光粉,并对其发光性质进行了研究.样品的激发光谱由位于220~350 nm的带状谱和350~500 nm的一系列窄带组成,这些窄带是由Eu3+的f-f跃迁引起的,光谱峰值分别为280,396和469 nm.它可以被近紫外光辐射二极管管芯产生的350~410 nm辐射有效激发.用396 nm激发得到样品的发射光谱,峰值位于578,590,610,618和650 nm,分别由Eu3+离子的5D4→7FJ(J=0,1,2,3)跃迁引起的.研究了Eu3+离子浓度和电荷补偿剂对发射光谱的影响.结果显示随着Eu3+浓度增加,发光强度逐渐增强,未发现浓度猝灭现象.掺入Li+,Na+,K+3种离子作为电荷补偿剂,均提高了样品的发光强度,其强度从大到小依次为I(Li+)I(Na+)I(K+),说明Li+是最佳的电荷补偿剂.     

Ga2O3/ITO/Ga2O3深紫外透明导电膜的研究

采用常压烧结方法制备了Ga2O3陶瓷靶,用X射线衍射仪、金相显微镜对Ga2O3陶瓷靶的结构和形貌进行了研究.用射频磁控溅射Ga2O3陶瓷靶材和直流磁控溅射ITO（锡铟氧化物）靶材分别制备了Ga2O3薄膜、Ga2O3/ITO/Ga2O3膜,用紫外-可见分光光度计、四探针测试仪对Ga2O3薄膜、Ga2O3/ITO/Ga2O3膜的光学透过率和电阻率进行了表征.Ga2O3薄膜不导电,光学带隙5.1 eV;Ga2O3（45 nm）/ITO（14 nm）/Ga2O3（45nm）膜在300 nm处的光学透过率71.5%,280 nm处60.6%,电阻率1.48×10-2Ω.cm.ITO层的厚度影响Ga2O3/ITO/Ga2O3膜的光电性质.     

Al_2O_3-SiO_2∶Ln~(3+)发光陶瓷的合成及发光行为

采用溶胶－ 凝胶法合成出了Ａｌ２Ｏ３－ＳｉＯ２∶Ｌｎ３＋ （Ｌｎ＝ Ｅｕ,Ｔｂ）发光陶瓷粉末．利用ＸＲＤ、ＴＧ－ＤＴＡ和ＩＲ等实验技术,研究了发光陶瓷的形成过程,并对其发光行为进行了研究．     

用于白光LED的荧光粉Sr3MgSi2O8:Eu2+的发光特性

使用高温固相法制备不同NH4Cl(作为助熔剂)加入量和不同Eu2+浓度的Sr3MgSi2O8:Eu2+,并研究其成相和发光性质.研究结果表明:NH4Cl加入量为24%时,样品为纯相,发光最强.Sr3MgSi2O8:Eu2+样品在近紫外区存在强激发带(250～400 nm),谱峰位于366 nm相应的发射谱带位于蓝光区(...     

用于复合纳滤膜的PAN基底膜的改性及性能表征

采用湿法相转换法制备PAN基膜,并对基膜进行改性,使其腈基水解生成羧基.通过环境扫描电镜观察了改性前后的膜孔形态,利用测接触角对改性前后膜的亲水性进行比较,用红外光谱对改性前后的膜组成进行比较.结果表明,改性后的膜的亲水性增强,改性膜上有羧基生成且性能得到了提高.     

烧成温度对Al_2O_3-Fe_2O_3复合材料性能的影响

以煅烧α-Al2O3粉、氧化铁为原料,采用MgO为添加剂,控制配料的Al2O3/Fe2O3的摩尔比为1、3、5,MgO引入量质量百分数分别为2%、4%、6%,成型压强为100 MPa,烧结温度为1500℃、1550℃、1600℃,保温3小时可获得Al2O3-Fe2O3复合材料,对烧后试样了烧结与抗热震性能研究。结果表明：控制Al2O3-Fe2O3复合材料试样AF34-2的Al2O3/Fe2O3摩尔比为3,MgO引入量为4%,烧成温度为1550℃保温3小时的工艺条件,可以制备出较高致密度、常温抗折强度及抗热震性能的Al2O3-Fe2O3复合材料。该复合材料试样AF34-2的SEM显微结构照片显示出材料晶粒间结合紧密,形成具有直接结合的镶嵌结构。     

Bi掺杂及制备工艺条件对Y_2O_3:Eu~(3+)发光性质的影响

通过水热反应成功制备了系列纳米发光材料Y1.95-xB ixEu0.05O3(0≤x≤0.15).B i3+掺杂后,Y2O3:Eu3+在342 nm处产生了一个由B i-O带引起的激发带;此外,Y2O3:Eu3+掺杂2 mol%B i3+后与未掺杂B i3+的Y2O3:Eu3+相比,发光强度增加了约1.33倍,这是由于B i3+充当了敏化剂离子,传输能量给激活剂Eu3+.基于在218、342、469 nm激发波段的Y1.93B i0.02Eu0.05O3发射光谱,发现与敏化剂B i3+相比,Y2O3主晶格更能有效地传输能量给激活剂Eu3+.此外,工艺条件(pH和退火温度)对Y1.93B i0.02Eu0.05O3荧光性质的影响也进行了研究.     

WO_3-Fe_2O_3异质结的制备及光催化活性

利用新型燃烧法和水热法分别制得α-Fe2O3及六方晶系无水WO3,再用溶剂分散法制得WO3-Fe2O3异质结.采用XRD,TEM,BET比表面积、紫外-可见漫反射谱 (DRS) 等技术对WO3-Fe2O3进行了表征,并以罗丹明B的光催化降解为探针反应, 评价了其光催化活性.结果表明,复合氧化物WO3-Fe2O3的粒子形态均为棒状,粒径约为80 nm,比表面积为46.91 m2/g;在可见光区有强吸收, 带隙估算为2.4 eV;对多种染料具有光催化降解活性,其中0.1 g WO3-Fe2O3(ω(Fe2O3 )=5%)在可见光作用下,100 mL 10 mg/L的罗丹明B降解率可达到97.73%, 表现出明显的可见光降解活性.通过计算半导体能带位置,讨论了光催化反应活性提高的机理.     

CaO-Al_2O_3-P_2O_5玻璃的结构与相变

FT -IP分析表明 ,5 0CaO·(5 0 -x)P2 O5·xAl2 O3 (x=0～ 7 5 )玻璃中同时存在偏磷酸盐和焦磷酸盐结构基团 ,随着摩尔比增大 ,P原子聚合度下降 ,析晶种类受此影响。Al3 存在于网络外 ,随着Al2 O3 含量增加 ,玻璃熔体粘度增大 ,玻璃分相受到抑制     

Ni/Al2O3、Co /Al2O3和Ni-Co /Al2O3催化剂催化乙醇水蒸气重整制氢的性能

利用浸渍法制备Ni/Al2O3、Co/Al2O3、Ni-Co/Al2O3催化剂,考察催化剂对乙醇水蒸气重整反应的催化性能,对催化剂进行x射线衍射(XRD)表征.实验结果表明,Ni/Al2O3催化剂具有较好的低温活性,Co/Al2O3催化剂具有较高的氢气选择性和较低的甲烷选择性,而Ni-Co/Al2O3催化剂表现出良好的催化性能,有较高的低温活性,较高的氢气、二氧化碳选择性,较低的一氧化碳、甲烷选择性,450 ℃时乙醇转化率达到100%, 氢气选择性为79.8%,二氧化碳选择性为91.9%.     

Al2O3对B4C-Al2O3-Al显微组织与力学性能的影响

在B4C-Al2O3预烧体中真空熔渗铝制备了B4C-Al2O3-Al复合材料,分析了w(Al2O3)对复合材料显微组织和力学性能的影响.结果表明:B4C-Al2O3-Al复合材料主要由B4C,Al2O3,Al,Al3BC和AlB2等相组成;随着w(Al2O3)的增加,复合材料的HRA硬度先增大后减小,材料的抗弯强度和断裂韧性均先减小后增大,当w(Al2O3)为25%时,复合材料具有较好的综合性能,它的气孔率、硬度、抗弯强度和断裂韧性分别为2.06%,84.4HRA,440.36 MPa和6.53 MPa.m1/2;延性铝的加入、裂纹的偏转和分叉、晶粒的细化、增韧相AlB2的生成及热膨胀的不匹配...     

Ni-P-Al_2O_3化学复合镀的机理

为了改善化学镀Ni-P合金镀膜的耐磨性,研究了Ni-P-Al_2O_3化学复合镀膜的工艺条件及其影响因素。得出了适当的化学镀液组成和最佳工艺条件;并测定了热处理对镀膜硬度和耐磨性的影响。     

Gd_2Mo_4O_(15):Eu~(3+)荧光材料的制备与发光性能研究

采用了高温固相法制备了稀土离子Eu3+掺杂的Gd2M04O15:Eu3+荧光粉,通过X-射线衍射(XRD)和荧光光谱的测定,分别讨论了烧结温度、烧结时间以及稀土离子Eu3+掺杂量对发光性能的影响.测试结果表明Gd2Mo4O15:Eu3+荧光粉在近紫外区(uv)(393 nm)和蓝光区(464 nm)可以被有效的激发,Gd2Mo4O15:Eu3+荧光粉发出明亮的红光,对应于Eu3+的4f-4f跃迁,当Eu3+的掺杂浓度约为40 mol%时,在616nm处的发光强度最大.在393,464 nm的吸收分别与目前应用的紫外光和蓝光LED芯片相匹配.因此,Gd2Mo4015:Eu3+是一种可能应用在白光LED上的红色荧光材料.     

B_2O_3-MgO-SiO_2系富硼渣活性的研究

研究了B_2O_3-MgO-SiO_2系富硼渣的活性与组成和结构的关系。在限定10％≤B_2O_3≤30％,10％≤SiO_2≤30％,MgO≤60％范围内,MgO的含量和熔体固化过程玻璃体的形成是影响富硼渣活性的关键因素。     

一维La2O3:Eu纳米纤维的制备及荧光性质

采用高压静电纺丝技术, 经高温焙烧制得掺杂Eu3+的一维六方晶相La2O3纳米纤维。采用扫描电镜(SEM)、X 射线衍射(XRD)、差热-热重分 析(TG DTA)及荧光光谱(PL)等测试手段对纤维的表面形貌、纯度、晶型及荧光性质进行了表征。由扫描电镜照片可以看出所制得的纤维较为均匀,纤维直径分布在370～430?nm之间,经过1?100?℃焙烧后 直径减小至245?nm左右。荧光光谱测试显示出样品具有较好的荧光性质,尤其是Eu3+的f f跃迁激发及电荷转移跃迁引起较强发光。     

CaO-SiO_2-B_2O_3:Gd_2O_3玻璃的合成及发光性质研究

用常规的高温合成法合成了CaO-SiO2-B2O3:Gd2O3玻璃,探讨了玻璃的最佳合成温度、玻璃的网络结构并研究了其发光性质.在CaO-SiO2-B2O3:Gd2O3玻璃体系中观察到了Gd3+的发射光谱.样品的激发光谱主激发峰在315 hill,对应于Gd3+的8S7/2→6P7/2,主发射峰在366 nm,对应于Gd8+的6P7/2→8S7/2研究了Gd3+的能级图.     

复合纳米材料Bi_2O_3-TiO_2的制备与表征

采用均匀沉淀法,以硫酸钛为前驱体,制备了Bi2O3-TiO2复合纳米粉体材料,利用XPS、XRD、UV-Vis等现代化技术手段对复合纳米材料的结构和性质进行了表征。研究结果表明,TiO2的加入阻碍了Bi2O3晶粒的生长,导致复合纳米材料粒径的减小;而光生电子产生于Bi2O3并迁移到TiO2表面,所需的激发光频率变低,从而使复合纳米材料的吸光波长向可见光区域扩展。     

Y2O3：Er纳米透明陶瓷的制备及其显微结构研究

以甘氨酸为燃烧剂,采用低温燃烧法制备了Y2O3：Er纳米前驱体粉末,采用XRD和TEM对纳米粉末的物相结构及其形貌进行了表征,结果表明前驱纳米粉末为分散均匀、轻微硬团聚、粒径均一、Y2O3立方晶相。前驱纳米粉末经研磨、高压钢模成型和1570℃真空烧结6h得到Y2O3：Er透明陶瓷。通过光学显微镜对陶瓷表面及断裂面观察和分析,定性讨论了低温燃烧法制备的纳米粉体的特性对陶瓷透光性的影响。     

内氧化工艺对Al_2O_3/Cu复合材料中Al_2O_3颗粒分布的影响

采用压块加入法和分别加入法两种内氧化工艺 ,将 Cu O和 Al粉末加入到 Ar气保护的铜液中制备 Al2 O3/ Cu复合材料 ,在光学显微镜、扫描电镜及 X射线衍射仪上观察分析了Al2 O3颗粒的数量、分布及材料的相组成。结果表明 ,压块加入法生成的 Al2 O3颗粒呈枝晶状分布 ,最佳保温时间为 30～ 45 min;分别加入法生成的 Al2 O3颗粒呈弥散状分布 ,最佳保温时间为 45～ 6 0 mi