La_(0.75)Mg_(0.25)Ni_(3.5-x)M_x(M=Si,Zn;x=0～0.5)储氢合金的相结构与电化学性能

研究Si和Zn元素分别部分替代Ni后合金La0.75Mg0.25Ni3.5-xMx(M=Si,Zn;x=0～0.5)的微观组织及电化学性能.X射线衍射(XRD)结果表明, La0.75Mg0.25Ni3.5-xSix合金由CaCu5型相、Ce2Ni7型相和LaMgNi4型相组成,随着Si含量增加,CaCu5型相明显增加.La0.75Mg0.25Ni3.5-xZnx合金由CaCu5型相、Ce2Ni7型相和LaNi3型相组成.随着Zn的增加,合金中Ce2Ni7型相逐渐减少,CaCu5型相和LaNi3型相则相应增加.电化学实验表明,2种元素的加入均使得合金的高倍率放电性能下降;Si的加入降低了合金最大放电容量和交换电流密度,但活化次数也随之减少,电化学循环稳定性提高.Zn元素的加入,对合金最大放电容量影响较小.     

快淬AB5型稀土储氢合金的微结构与电化学性能

采用磁悬浮感应熔炼法和快淬法制备了Mm0.3Ml0.7Ni3.55Co0.75Mn0.4Al0.3稀土储氢合金,系统研究了快淬速度对合金微结构和电化学性能的影响.X射线衍射(XRD)及扫描电镜(SEM)分析表明,快淬态合金中出现了新相LaNi3和La2Ni3,且LaNi3和La2Ni3相含量随快淬速度的增大而增大.电化学性能测试表明,合金的放电特性和最大放电容量随快淬速度的增大呈现出先变好后变坏的变化规律,15m/s快淬态合金的放电特性和最大放电容量达到最佳.此外,恰当的快淬速度能明显改善合金的循环稳定性.     

La0.7Mg0.3Ni3.4-x(Al0.3Co0.4)0.2+x(x=0~0.3)合金电极电化学性能研究

在氩气保护下,采用悬浮熔炼法制备La0.7Mg0.3Ni3.4（Al0.3Co0.7）x（x=0,0.2,0.4,0.6）储氢合金,用X射线衍射仪测试相组成,并用MDI Jade 5.0软件分析相组成和晶胞参数,用开口三电极法测试电极电化学性能。结果表明,合金相主要由LaNi5、LaMg2Ni9、La2Ni7和LaNi2.28相组成,随着合金中Al和Co含量的增加,合金放氢平台压下降,最大吸氢量为1.43%（x=0）,合金电极最大放电容量Cmax为381mA.h.g-1（x=0）,合金电极100个充放循环后的容量保持率S100从53.0%（x=0）增加到57.1%（x=0.3）,循环稳定性增强。当x=0.1时,合金电极的电化学动力学性能较好。     

La-Mg-Ni基合金储氢性能的研究

采用高频感应熔炼制备La0.7Ca0.3Ni2.8-xMgx(x=0.1、0.2、0.3、0.4)合金,进行X射线衍射(XRD)实验,气相储氢性能测试和电化学性能测试,分析Mg部分替代Ni对合金的储氢和电化学性能的影响。分析结果表明,合金具有多相结构,当x=0.1、0.3时,合金的主相是CaCu5-型结构的LaNi5相,当x=0.2、0.4时,合金的主相是AB2-型Laves相LaNi2相。随x=0.1、0.2、0.3、0.4合金电极的放电容量(mAh/g)依次为244.7、140.8、257.6、164。当x=0.1时,在2MPa氢压、25℃时,合金La0.7Ca0.3Ni2.7Mg0.1的储氢量达到1.1wt%。     

热处理对贮氢电极合金La0.7Mg0.3Ni2.45Co0.75Mn0.1Al0.2的微结构与电化学性能的影响

研究了热处理时间对贮氢电极合金La0.7Mg0.3Ni2.45Co0.75Mn0.1Al0.2的微结构与电化学性能的影响。XRD分析结果表明,所有合金均由(La,Mg)Ni3与LaNi5两相构成,热处理并没有使该贮氢合金发生相变。电化学研究结果表明,随着热处理时间的延长,合金电极的最大放电容量与循环稳定性能均得到明显改善,而高倍率放电性能却逐渐恶化。     

La-Ni-Al合金电极电化学性能研究

研究了两种不同配比La-Ni-Al的储氢合金电极的电化学性能。测试结果表明,LaNi4.061Al0.222储氢合金的最大放电容量为292mAh·g1(303 K),且具有较好的倍率性能。同时研究了Zr的添加对LaNi4.061Al0.222Zr(=0-0.2)储氢合金电极电化学性能的影响。结果表明,=0.2时,储氢合金电极具有最大的放电容量309.9mAH·g-1和高倍率放电性能。     

(La1-xNdx)2Mg(Ni0.8Co0.15Mn0.05)9(x=0～0.3)合金的储氢与电化学性能研究

采用高频悬浮感应熔炼方法制备(La1-xNdx)2Mg(Ni0.8Co0.15Mn0.05)9(x=0～0.3)系列合金,分析Nd部分取代La对合金的相结构、吸放氢性能和电化学性能的影响.结果表明,铸态合金的主相为具有六方CaCu5结构的LaNi5相,并存在具有立方MgCu2结构的LaNi2相以及LaMg3相.合金主相...     

Ti对La_(0.7-x)Ti_xMg_(0.3)Ni_(3.5)(x=0.00,0.05,0.10)合金电极电化学性能的影响

在氩气保护下用悬浮熔炼制备La0.7-xTixMg0.3Ni3.5(x=0.00,0.05,0.10)储氢合金,研究Ti含量对合金电极电化学性能的影响。X射线衍射(XRD)分析表明,合金相主要由LaNi5、LaMg2Ni9和La2Ni3相组成。当x=0.10时,合金中有TiNi3相产生,随着Ti含量的增加,LaNi5、LaMg2Ni9和La2Ni3相的晶胞体积减小。电化学性能测试表明,合金电极最大放电容量分别为370 mAh/g(x=0.00)、331 mAh/g(x=0.05)和252 mAh/g(x=0.10);合金电极循环伏安特性曲线氧化峰电位随着Ti含量的增加而降低,表明Ti的加入使合金电极易于发生氧化反应。     

湿法球磨结合表面改性制备贮氢合金粉

研究湿法球磨结合KBH4表面改性一步处理法对AB5型贮氢合金晶体结构和电化学性能的影响，并比较此新方法和先湿法球磨制粉后表面处理两步法制备的贮氢合金粉的电化学性能。研究结果表明：采用此新方法能显著提高贮氢合金的综合性能；当KBHt的浓度为0．08mol／L时，利用此法制得合金粉的晶体主相仍为LaNi5相，出现Al2Os杂相；其电化学容量变化不大；达到最大容量的活化次数从12降低到5；放电中值电压从1．22V升高到1．28V；倍率为2C的放电效率从79．0%提高到86．1％，容量保持率S200从74％提高到86％。     

热处理对贮氢电极合金La0. 7 Mg0. 3 Ni2. 45 Co0. 75 Mn0. 1 Al0. 2的微结构与电化学性能的影响

研究了热处理时间对贮氢电极合金La0. 7 Mg0. 3 Ni2. 45 Co0. 75 Mn0. 1 Al0. 2的微结构与电化学性能的影响。XRD分析结果表明，所有合金均由（La，Mg）Ni3与LaNi5两相构成，热处理并没有使该贮氢合金发生相变。电化学研究结果表明，随着热处理时间的延长，合金电极的最大放电容量与循环稳定性能均得到明显改善，而高倍率放电性能却逐渐恶化。     

LaNi_(2.5)Co_(0.5)储氢合金在充放电循环过程中的电化学性能研究

以感应熔炼法制备的LaNi_(2.5)Co_(0.5)合金为研究对象,对该合金及其氢化物的相结构进行了分析,并对合金电极的放电容量保持率、高倍率放电性能、氢扩散系数及极化电流密度等电化学性能进行了研究.结果表明:吸氢后的合金会产生明显的非晶化现象,造成合金吸放氢能力和氢化物稳定性下降.随着循环次数的增加,合金的放电容量和高倍率放电性能均表现出先快速下降到逐渐缓慢降低的趋势,而合金的氢扩散系数和极化电流密度却呈现出不同的变化趋势.高倍率放电性能的下降主要与合金表面反应活性相关,说明表面劣化现象是造成合金电化学性能衰退的主要因素.     

一种改善La-Mg-Ni贮氢电极合金性能的方法

提出用放电等离子烧结技术(SPS)改善La-Mg-Ni贮氢电极合金的综合电化学性能.所选La-Mg-Ni贮氢电极合金为La0.7Mg0.3Ni2.5Co0.5.实验结果表明,用SPS和真空中频感应熔炼制备得到的合金具有近似的最大放电容量.SPS技术增强了合金电极的循环寿命:在经过150次的充放电循环后,用SPS法制备的La0.7Mg0.3Ni2.5Co0.5合金的容量保持率为61.8%;而感应熔炼法得到的合金电极的容量保持率仅为39.6%.同时用SPS技术使合金的放电中值电压增加,放氢平台变宽,平台倾斜度减小.     

Hydrogen storage and low-temperature electrochemical performances of A2B7 type La-Mg-Ni-Co-Al-Mo alloys

The effect of Mo-addition on hydrogen storage and low-temperature electrochemical performances of La-Mg-Ni-Co-Al alloys is investigated. The alloys were synthetized via vacuum induction melting followed by annealing treatment at 1123 K for 8 h. The major phases in the annealed alloys are consisted of (La, Mg)2Ni7, (La, Mg)5Ni19 and LaNi5 phases. Mo-addition facilitates phase transformation of LaNi5 into (La, Mg)2Ni7 and (La, Mg)5Ni19 phases. Hydrogen absorption/desorption PCI curves indicates that the hydrogen storage capacity of the alloy increases remarkably with the addition of Mo. Furthermore, the La0.75Mg0.25Ni3.05Co0.2Al0.05Mo0.2 alloy shows excellent hydriding/dehydriding kinetics with a higher capacity, requiring only 100 s to reach its saturated hydrogen capacity of 1.58 wt% at low temperature of 303 K, and releasing 1.57 wt% hydrogen within 400 s at 338 K. Electrochemical experiments manifest that the Mo-added alloy electrode has perfect activation properties and the maximum discharge capacity. The low-temperature dischargeability shows that the La0.75Mg0.25Ni3.05Co0.2Al0.05Mo0.2 alloy exhibits the excellent low-temperature discharge performance, and the maximum discharge capacity is improved from 231.0 to 334.6 mAh/g at 253 K. The HRD property of the alloy electrode is enhanced, suggesting that Mo enhances the kinetic ability at low-temperature.     

稀土Ce掺杂铝合金阳极的结构和电化学性能

通过向Al-5Zn-0．05In-0．1Sn铝舍金基体中添加不同量的稀土元素Ce，制得一系列含稀土Ce的合金。采用扫描电镜和能谱分析，研究稀土对铝合金阳极微观组织的影响，并进行将稀土铝舍金用作铝空气电池阳极的电化学性能测试。研究结果表明：当Ce的含量不大于0．5％时，细化枝晶的效果较好；添加稀土元素Ce，铝舍金阳极的自腐蚀电位负移，放电稳定性和放电电压提高；当以50mA／cm^2的电流密度恒流放电时，Ce含量为0．3％的舍金放电性能最好，放电电压为1．118V，放电时间达到13h；添加稀土元素Ce能改善铝舍金阳极的耐腐蚀性能。     

Microstructural evolution and performance of hydrogen storage and electrochemistry of Co-added La0.75Mg0.25Ni3.5−xCox (x = 0, 0.2, 0.5 at%) alloys

Microstructure, hydrogen storage and electrochemical performances of Co-added La_(0.75)Mg_(0.25)Ni_(3.5_x)Co_x(x = 0,0.2, 0.5 at%) alloys are studied. XRD and rietveld refinement results suggest that the samples are mainly composed of(LaMg)Ni_3,(LaMg)_2Ni_7 and LaNi_5 phases, Co substitution for Ni changes the phase abundance,but not the phase composition. With the rising of Co content, the amount of(LaMg)_2 Ni_7 phase decreases, but the amount of LaNi_5 phase increases, while the amount of(LaMg)Ni_3 phase firstly increases and then decreases.The alloys reversibly absorb and desorb hydrogen at 298 K smoothly. When Co content is 0.2 at%, the hydrogen absorption capacity reaches the maximum value of 1.14 H/M, and the absorption capacities reach 1.09 H/M and 1.03 H/M in the first minute at 298 K and 323 K, respectively. Electrochemical performance measurement results show that La_(0.75)Mg_(0.25)Ni_(3.5-x)Co_x alloys are completely activated within 2 cycles, and the cyclic stability of La_(0.75)Mg_(0.25)Ni_(3.3)Co_(0.2) alloy approaches 63.7% after 100 charge/discharge cycles, which is higher than that(S_(100) = 60%) of La_(0.75)Mg_(0.25)Ni_(3.0)Co_(0.5) alloy. Thus, the La_(0.75)Mg_(0.25)Ni_(3.3)Co_(0.2) alloy exhibits optimum comprehensive properties of hydrogen storage and electrochemistry.     

La-Mg-Ni系A2B7型贮氢合金表面包覆铜及其电化学性能

以A2B7型贮氢合金La1.5Mg0.5Ni7为研究对象,研究未包覆和表面包覆Cu以及对包覆铜的贮氢合金进行再包覆Ni、Co处理的合金电极电化学性能.实验结果表明,表面包覆Cu和Cu-Ni后的贮氢合金电极循环稳定性有所提高,而包覆Cu-Co的合金电极稳定性较差,但电极容量有所提高.线性极化扫描和电化学阻抗图谱分析结果表明,包覆Cu、Cu-Co及Cu-Ni处理改善合金电极的交换电流密度I0,降低电化学阻抗,说明包覆处理改善合金表面的电催化活性,加快合金表面电荷的迁移速率,从而提高高倍率放电能力.     

导电剂镍粉对La0.7Mg0.3Ni2.6Co0.7合金电极电化学性能的影响

采用放电容量、循环寿命、伏安特性、高倍率放电、交流阻抗等方法研究不同导电剂镍粉含量对La0.7Mg0.3Ni2.6Co0.7合金电极电化学性能的影响。结果表明:La0.7Mg0.3Ni2.6Co0.7+xwt%Ni(x=0.0,5.0,7.5,10.0,12.5)合金电极的放电容量分别为388.0、410.7、409.6、412.2、421.3 mAh/g,高倍率放电性能HRD1200从40.2%(x=0.0)增大到75.7%(x=12.5),同时合金电极的电荷转移阻抗明显降低,添加导电剂镍粉有利于电流在电极中分布趋于均匀化,增大了活性物质的填充量,促使合金电极的放电容量增加。电荷转移阻抗的降低有利于氢原子在合金内部扩散,从而有效地改善合金电极的高倍率放电性能。     

La0.6CexNd0.4-xNi3.0Co0.2Al0.3(x=0~0.4)合金储氢性能研究

采用电弧炉熔炼方法制备La0.6CexNd0.4-xNi3.0Co0.2Al0.3(x=0～0.4)系列合金,并对合金的储氢性能和电化学性能进行测试。测试结果表明,合金在Ce=0时具有最高的电化学容量(284.2mAh/g)和储氢量(0.93wt%)。Ce的添加会降低合金放电容量,但是能够改善合金的循环稳定性能。