复合法制备的(K0.48Na0.52)1-x（LiSb）xNb1-xO3无铅压电陶瓷性能研究

采用传统的固相反应法和普通的烧结工艺,分别制备了(K0.48Na0.52)1-x(LiSb)xNb1-xO3(x=0.055,0.060,0.065)和x=0.055,x=0.065按摩尔比1:1复合的无铅压电陶瓷样品(55-65),并对样品的压电、介电等性能进行了测试研究.实验结果表明:55-65不等同于x=0.060的组分,其压电性能远低于x=0.060的样品,进一步研究表明,相同烧结温度下,55-65样品的损耗较高,晶粒难以生长,相对较小,较小的晶粒可能在样品形变时产生的应力较大,这可能是55-65样品压电性能较低的原因.     

La2/3Sr1/3MnO3/NiFe2O4复合多晶材料的磁电阻效应

用化学共沉淀法制备了NiFe2O4粉体样品,采用溶胶-凝胶(sol-gel)法制备了La2/3Sr1/3MnO3的多晶样品.用无压烧结制备了名义组分为(La2/3 Sr1/3MnO3)1-x(NiFe2O4)x(x=0,0.05,0.10,0.20)的多晶样品.在1.8×107A/m磁场作用下,当x=0时,样品的磁电阻随温度几乎成线性变化;当x=0.10时,样品在335 K时出现峰值,磁电阻值达35%.     

Ca、Zn掺杂对高温超导体YBa2Cu3O7-δ晶体结构的影响

采用固相反应法成功的制备出了Y1-yCayBa2Cu3-xZnxO7-δ(y=0,x=0;y=0.1,x=0,0.05,0.1,0.2)的系列样品.利用X射线衍射(XRD)和扫描电镜(SEM)对所制备系列样品结构进行了研究.结果表明,在整个掺杂范围内样品的单相性很好.随着锌离子掺杂量的增加,样品的晶格常数和表面形貌都发生了较大的变化,这是因为掺杂使样品的电子局域化增加,从而使样品的结构发生变化.     

Bi含量对SrBi4Ti4O15铁电材料性能的影响

按n(Sr)n(Bi)n(Ti)为14(1+x)4(x=-0.05,0,0.05,0.10,0.15,0.20)配料,采用固相烧结工艺,制备了不同Bi含量SrBi4Ti4O15的陶瓷样品.用X射线衍射对样品的微结构进行了分析,并测量了其铁电、介电性能.结果发现x=0.05,0.10的样品形成单一的SrBi4Ti4O15相.x=0.05时,材料具有较好的铁电与介电性能剩余极化强度2Pr=2.86×10-9C@m-2,矫顽电场强度Ec=8.65×106V@m-1,介电性能在频率f=1 kHz～4 MHz范围内变化不大,f=1 MHz时,介电常数εr=425.     

溶胶-凝胶法制备Ni_(1-x)Zn_xFe_2O_4及其Zn~(2+)掺杂对磁性质的影响

采用溶胶-凝胶法制备了系列Ni_(1-x)Zn_xFe_2O_4(x=0,0.2,0.4,0.6,0.8,1.0)粉末样品,利用X射线衍射(XRD)、场发射扫描电镜(FESEM)和振动样品磁强计(VSM)对样品的晶体结构、形貌及磁性进行了研究.结果表明,750℃是制备样品的最佳煅烧温度,在此温度下制备的Ni_(1-x)Zn_xFe_2O_4均为单一尖晶石相.NiFe2O4纳米颗粒类似球形,大小均匀且分散性好;掺杂Zn~(2+)后,颗粒尺寸增大,有少量团聚.随着Zn~(2+)含量的增加,饱和磁化强度(Ms)先增大后减小,在x=0.4时达最大值,Ms=65.63emu·g~(-1);矫顽力Hc呈现持续降低趋势,x=0时有较高的矫顽力,Hc=196.09Oe.     

Rietveld方法研究Bi_(1-x)Sm_xFeO_3晶体结构

采用溶胶-凝胶法成功制备B i1-xSmxFeO3(BSFOx,x=0.000~0.175)粉体.测得BSFOx(x=0.000~0.175)样品的X射线衍射谱(XRD).XRD结果显示Sm掺杂引起了晶格常数变化并最终导致结构相变.XRD的R ietveld全谱拟合结果表明x=0.000~0.125的BSFOx样品为三角相结构,且随着掺杂含量Sm的增加,晶格常数a、c线性减小;Sm掺杂量增加到x=0.150时,样品转变为正交相结构.     

La2/3Sr1/3Mn1-xCoxO3(x=0,0.2,0.25)体系的热膨胀和电性能研究

制备了钙钛矿锰氧化物La2/3Sr1/3Mn1-xCoxO3(x=0,0.2,0,25)体系,研究该材料的热膨胀性能和电输运性质.研究发现,所有样品具有相近的热膨胀性能,200-800 ℃温区内的平均线热膨胀系数约为1.2×10-5K-1;x=0和x=0.2掺杂样品在高温下的电输运机制符合小极化子模型;x=0.25掺杂样品具有最高的电导率,在800℃时的电导率为100S/cm.     

中低温固体氧化物燃料电池Sr_(1-x)Na_xSiO_(3-0.5x)(x=0.35,0.45)电解质的性能研究

将具有高离子传导的Sr_(1-x)Na_xSiO_(3-0.5x)(x=0.35,0.45)材料应用于中温固体氧化物燃料电池电解质.利用X射线衍射(XRD)、范德堡法和阻抗测试对电解质样品的结构、电导率和阻抗谱进行了研究.XRD结果表明,利用固相反应法制备样品时,当烧结温度为950℃,烧结时间为15 h后可以获得Sr_(1-x)Na_xSiO_(3-0.5x)电解质材料单相结构.电导率结果表明,x=0.45的电解质样品显示出更高的电导率,其电导率在800℃时,达到0.027 S·cm~(-1).两种样品的阻抗谱结果显示,x=0.45的电解质具有更高的氧离子电导率.     

La_(1-x)Ca_xMnO_3薄膜的制备及结构和磁性研究

采用溶胶-凝胶旋涂法在表面氧化的Si(100)基片上制备了La1-xCaxMnO3(x=0,0.1,0.15)薄膜.利用X射线衍射(XRD)、原子力显微镜(AFM)、扫描电镜(SEM)及振动样品磁强计(VSM)对样品的结构、形貌和磁性进行了研究.结果表明:薄膜为正交钙钛矿结构,具有平整的表面,La0.85Ca0.15MnO3样品的薄膜厚度为334nm.样品在居里温度附近发生铁磁-顺磁转变,随着Ca2+掺杂浓度的增加,样品的居里温度变大,x=0.15时,样品的居里温度为299K.     

BixSr1-1.5xTiO3系列陶瓷的物相、结构与晶粒尺寸的X射线衍射研究

用X射线衍射方法,对采用固相反应法制备的BixSr1-1.5xTiO3系列陶瓷样品(x=0.000,0.013,0.040,0.053,0.100,0.133,0.167)的物相、晶胞参数及晶粒尺寸等,进行了测量与分析.结果表明,上述系列样品都为晶粒尺寸在659～2078(A)范围内的晶相单一的陶瓷结构,具体为:1)当Bi含量x≤0.040时,BixSr1-1.5xTiO3样品的晶体结构都属于空间群P23(195)的立方晶系,晶胞体积随x增加而略有增大(～2％)；2)当x=0.053时,晶体结构变为属于空间群P4(75)的四方晶系,但是晶胞体积变化不大(～1％)；3)对BixSr1-1.5xTiO3(x=0.100,0.133,0.167)的样品,晶体结构变为属于空间群PC(7)的单斜晶系,同时晶胞体积快速减少了～20％.     

微波水热法制备掺稀土铁氧体纳米粒子

用微波水热方法制备组成为Fe2M1-xRExO4(x=0～0．3，M=Co^2 ，Ni^2 ，RE=La^3 ，Ce^3 )的三元铁氧体纳米粒子：所得球形粒子粒度为10～20nm．分析了各产物的晶体结构并对其进行磁性能的测量和表征．结果表明产物为尖晶石结构，饱和磁化强度较块体样品有不同程度地减小，其中镍铁氧体粒子呈超顺磁态．钴铁氧体为亚铁磁性．     

The effect of neodymium substitution on the structural and magnetic properties of nickel ferrite

Nickel ferrite Ni Fe2O4 is a typical soft magnetic ferrite with high electrical resistivity used as high frequency magnetic material. Neodymium(Nd3+) doped Ni Fe2O4 materials were fabricated using solid state reaction. The properties of the obtained material were investigated by X-Ray Diffraction(XRD), Scanning Electron Microscope(SEM), Fourier-Transform Infrared Spectroscopy(FT-IR), magnetic measurements on SQUID and M?ssbauer spectroscopy. It was found that the material consists of two different phases: Nd3+doped Ni Fet2O4and Nd Fe O3. The Nd3 ions occupy cation sites of the Ni Fe2O4 inverse spinel structure. NdFeO3 phase occurred when the level of Nd3+atoms exceed a percolation limit.The presence of both phases was confirmed by SEM observations. The M?ssbauer spectra analysis showed two sextets, which can be ascribed to iron atoms in tetrahedral and octahedral positions. From their intensities it is concluded that Nd3+occupies octahedral sites in the spinel structure of Ni Fe2O4, which were originally occupied by Ni2+.     

Fabrication of SrFe12-xNixO19 nanoparticles and investigation on their structural,magnetic and dielectric properties

SrFe12?xNixO19 nanoparticles (x = 0–1) were synthesized by a combustion sol–gel method. Their structure, dielectric and magnetic properties were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), an LCR metry, and vibrating sample mag-netometry (VSM).The results reveal that all samples of Ni doped compounds (SrFe12?xNixO19) withx < 0.2 are single phase. It appears that the Fe3+ions are substituted by Ni2+ ions on the crystallographic sites of the SrFe12O19 structure; however, forx≥ 0.2, the secondary Ni phase ferrite (NiFe2O3) appears, which reduces the saturation magnetization and coercivity. In addition, Ni doping reduces the dielectric con-stant, dielectric loss, and alternating current (ac) electrical conductivity of the samples. The variation in ac conductivity (σac) with frequency shows that the electrical conductivity in these ferrites is mainly attributed to the electron hopping mechanism.Therefore; all the single-phase Ni doped samples are suitable for use in magnetic recording media and microwave devices.     

纳米晶Ni_(1-x)Zn_xFe_2O_4铁氧体的水热合成与磁性能

采用水热法在180℃下合成纳米级的尖晶石相NiZn铁氧体,使用Χ射线衍射(XRD)、红外光谱(FTIR)、高分辨透射电镜(HRTEM)和振动样品磁强计(VSM)分别表征NiZn铁氧体纳米粉体的相组成、微结构以及磁性能.XRD衍射谱和红外光谱(FTIR)表明180℃合成的纳米晶NiZn铁氧体为单一尖晶石相;高分辨透射电镜照片分析表明Ni0.6Zn0.4Fe2O4颗粒为立方片状,颗粒均匀,尺寸在20nm左右,晶格结构完整,面间距0.44nm.Ni0.6Zn0.4Fe2O4铁氧体的饱和磁化强度(Ms)和矫顽力(Hc)分别为11.9emu·g-1和93.5Oe,NiZn铁氧体的矫顽力随着Zn2+含量的增加而减小,此为A位和B位磁性离子间超交换作用下降所致.     

氰基桥联铬(Ⅲ)-镍(Ⅱ)和铬(Ⅲ)-铜(Ⅱ)多核配合物的合成、表征和磁性质研究(英文)

合成了配合物［ＭＬ］３［Ｃｒ（ＣＮ）６］２·ｘＨ２Ｏ（Ｍ二Ｎｉ,Ｌ＝三（２－胺基乙基）胺（ｔｒｅｎ）,ｘ＝ Ｏ; Ｍ＝ Ｃｕ, Ｌ＝二丙烯三胺（ ｄｐｔ）, ｘ＝ ８）和［ Ｍ（ ｔｎ）２］２［Ｃｒ（ ＣＮ）６ ］ＣＩＯ４· ＸＨ２ Ｏ（ ｔｎ＝ １, ３－丙二胺,Ｍ＝ Ｎｉ,ｘ＝ Ｏ;Ｍ＝ Ｃｕ,ｘ＝ ２）．用元素分析、ＩＣＰ分析、ＩＲ光谱等对配合物进行了表征,测定了它们的磁性质．变温磁化率研究表明：［Ｃｕ（ｄｐｔ）］３［Ｃｒ（ＣＮ）６］２·８Ｈ２Ｏ中存在弱的铁磁（Ｔ＞ １６．６３Ｋ）和反铁磁（Ｔ＜ １６．６３Ｋ）相互作用;［Ｃｕ（ｔｎ）２］２［Ｃｒ（ＣＮ）６］ＣＩＯ４·２Ｈ２Ｏ中存在反铁磁相互作用（Ｔ＜５．８６Ｋ）．研究发现,这些配合物有两种结构类型：氰基桥联结构和双配合盐结构．     

稀土La^3＋掺杂NiZn铁氧体结构及磁性能的研究

用辅助共沉淀法制备了Ni0.55Zn0.45LaxFe（2-x）O4（x=0．001～0．020）铁氧体粉体,通过粉末x-射线衍射仪（XRD）、振动样品磁强计（VSM）等表征了产物的结构、物相和磁性能。结果表明,不同温度和不同的La掺杂量对样品的物相、晶胞参数、结构和磁性能均产生了明显的影响,因此,通过改变La含量能起到调控样品磁性能的作用,从而为NiZn铁氧体的性能的改善提供了新的线索。     

片式电感用NiCuZn铁氧体材料制备性能研究

采用传统的固相法制备出Ni0.45Cu0.14Zn0.41Fe2O4铁氧体材料,通过掺杂1.2wt V2O5助烧剂对材料进行低温烧结(880℃~920℃)。并通过XRD,SEM,VSM以及磁导率测试对材料进行分析和表征。结果表明:NiCuZn铁氧体实现了良好的低温烧结,成像单一、晶粒均匀,饱和磁化强度达到了67.92 emu/g,磁导率也达到了220。表明稳定的材料性能可以满足片式电感的应用要求。     

Co掺杂对共沉淀法制备Co-Ni铁氧体纳米颗粒结构及磁性能影响研究

利用共沉淀法成功地合成了(x=0、0.2、0.2、0.4和0.8)纳米颗粒并进行了退火处理.对样品进行了XRD、FT-IR、TG-DSC和VSM等表征.结果显示,样品前驱体中存在少量的杂质如吸收水和硝酸盐,退火处理是获得单相和高度结晶Co-Ni尖晶石铁氧体的必备条件.所有退火样品均是单相立方尖晶石结构纳米晶粒,其平均尺寸在40~60 nm的范围.晶格常数随着Co掺杂含量增加而增加.比表面积测试显示Co掺杂量的增加在一定程度上减少了样品的表面体积比,有利于CoNi铁氧体的晶粒生长.样品饱和磁化(Ms)和矫顽力(Hc)与钴掺杂量密切相关.Ms值从37.5 emu/g(x=0)增加到62.0 emu/g(x=0.8),这是由于较高的掺杂Co~(2+)阳离子磁矩的增强导致A和B亚晶格之间的超交换相互作用增强.矫顽力Hc的大小从73.0 Oe(x=0)到558.3 Oe(x=0.8),这主要是由于掺杂Co~(2+)阳离子具有比Ni~(2+)阳离子更大的磁晶各向异性常数.     

纳米晶CoFe2-xCexO4的结构与磁性能研究

采用化学共沉法制备了纳米尺度的CoFe2-xCexO4（x=0～0．3）粉料,分别在不同温度下进行了热处理,利用X射线衍射仪（XRD）、振动样品磁强计（VSM）对样品的结构和磁性进行了测量和分析．实验结果表明：在铈掺杂量x≤0．2时样品形成了单一的具有尖晶石结构的钴铁氧体相,而x〉0．2时钴铁氧体相和CeO2相并存;铈掺杂量对样品的磁性能有较强的影响,在铈含量较低（x≤0．2）时,比饱和磁化强度σs变化不大,矫顽力Hc大幅度增大,而在x〉0．2之后二者都急剧下降,在x=0．1附近样品能同时获得较大的Hc和σs值．     

Al^3＋代换Fe^3＋对钴铁氧体结构与磁性能的影响

采用化学共沉法制备了CoFe2-xAlxO4（x=0．1～0．5）铁氧体纳米粉料,并在不同温度下进行退火处理,利用X射线衍射仪（XRD）、振动样品磁强计（VSM）对样品的结构和磁性进行了测量和分析．结果表明：所有样品均形成了单一的尖晶石相,晶粒尺寸为35～45nm;经1280℃退火后的样品能同时获得较高的比饱和磁化强度如和矫顽力Hc;随铝代换量x的增大,比饱和磁化强度起初变化平缓然后迅速降低,而矫顽力却呈现出了先增后减的趋势,在x=0．3附近出现峰值。