为研究高铌高磷GH4169C高温合金在高温长期时效过程中的组织稳定性,通过场发射扫描电镜和数显布氏硬度计对GH4169和GH4169C两合金分别经600、650、704及720℃时效30~10000 h的显微组织和硬度变化进行对比分析。结果表明：在服役温度(650℃)范围内长期时效,GH4169合金和GH4169C合金均表现优异的稳定性;在服役温度以上长期时效, GH4169合金和GH4169C合金稳定性较差,短时间内,合金组织就出现失稳。对比而言,704℃时GH4169C合金组织稳定性较GH4169合金高,而720℃时GH4169C合金组织稳定性劣于GH4169合金。分析认为,GH4169C合金由于提高Nb含量和P含量使的γ＇相稳定性增加,得以在服役温度以上(704℃)表现比GH4169合金更为优异的组织稳定性,但Nb含量的提高也引起啄相含量的增加,导致组织稳定性下降。在超高温(720℃)下,GH4169C 合金稳定性劣于 GH4169合金。由此推知,相比GH4169合金,改型GH4169C合金在使用温度上有所提高,但提高有限,在超高温下,其稳定性反而降低。     

Influence of process parameters on the microstructural evolution of a rear axle tube during cross wedge rolling

In the shaping process of cross wedge rolling (CWR), metal undergoes a complex microstructural evolution, which affects the quality and mechanical properties of the product. Through secondary development of the DEFORM-3D software, we developed a rigid plastic finite element model for a CWR-processed rear axle tube, coupled with thermomechanical and microstructural aspects of workpieces. Using the developed model, we investigated the microstructural evolution of the CWR process. Also, the influence of numerous parameters, including the initial temperature of workpieces, the roll speed, the forming angle, and the spreading angle, on the grain size and the grain-size uniformity of the rolled workpieces was analyzed. The numerical simulation was verified through rolling and metallographic experiments. Good agreement was obtained between the calculated and experimental results, which demonstrated the reliability of the model constructed in this work.     

Reductive recovery of manganese from low-grade manganese dioxide ore using toxic nitrocellulose acid wastewater as reductant

The hydrometallurgical strategy of extracting Mn from low-grade Mn ores has attracted attention for the production of electrolytic manganese metal (EMM). In this work, the reductive dissolution of low-grade MnO₂ ores using toxic nitrocellulose acidic wastewater (NAW) as a reductant was investigated for the first time. Under the optimized conditions of an MnO₂ ore dosage of 100 g·L-1, an ore particle size of -200 mesh, concentrated H₂SO₄-to-NAW volume ratio of 0.12, reaction temperature of 90℃, stirring speed at 160 r·min-1, and a contact time of 120 min, the reductive leaching efficiency of Mn and the total organic carbon (TOC) removal efficiency of NAW reached 97.4% and 98.5%, respectively. The residual TOC of 31.6 mg·L-1 did not adversely affect the preparation of EMM. The current process offers a feasible route for the concurrent realization of the reductive leaching of Mn and the treatment of toxic wastewater via a simple one-step process.     

Hot deformation map and its application of GH4706 alloy

The hot deformation behaviors of GH4706 alloy were investigated using compression tests in a deformation temperature range from 900℃ to 1200℃ with a strain rate range of 0.001–1 s?1. Hot processing maps were developed on the basis of the dynamic material model and compression data. A three-dimensional distribution of power dissipation parameter (η) with strain rate and temperature reveals that η decreases in sensitivity with an increase in strain rate and a decrease in temperature. Microstructure studies show that the grain size of GH4706 alloy increases when η is larger than 0.32, and the microstructure exhibits local deformation when η is smaller than 0.23. The hot processing map at the strain of 0.7 exposes a domain peak at η=0.32 for the temperature between 940℃ and 970℃ with the strain rate from 0.015 s?1 to 0.003 s?1, and these are the optimum parameters for hot working.     

Improved strength and ductility of high alloy containing Al-12Zn-3Mg-2.5Cu alloy by combining non-isothermal step rolling and cold rolling

Al-12Zn-3Mg-2.5Cu alloy was prepared using a liquid metallurgy route under the optimized conditions. A sample cut from the ingot was rolled non-isothermally from 400℃ to 100℃ in 100℃ steps, with 15% reduction in thickness; it was then cold rolled isothermally at room temperature for 85% reduction. The cold-rolled alloys were characterized by electron microscopy, hardness test, and tensile test to elucidate their structural evolution and evaluate their mechanical behavior. In the results, the cast alloy consists of α-aluminum and various intermetallic compounds. These compounds are segregated along the grain boundaries, which makes the alloy difficult to roll at room temperature. The combined effect of non-isothermal step rolling and cold rolling results in the nano/microsized compounds distributed uniformly in the matrix. The hardness is substantially increased after rolling. This increase in hardness is attributed to the ultra-fine grain size, fine-scale intermetallic compounds, and structural defects (e.g., dislocations, stacking faults, and sub-grains). The ultimate tensile strength of the rolled alloy is approximately 628 MPa with 7% ductility.     

Hot deformation behavior of uniform fine-grained GH4720Li alloy based on its processing map

The hot deformation behavior of uniform fine-grained GH4720Li alloy was studied in the temperature range from 1040 to 1130℃ and the strain-rate range from 0.005 to 0.5 s?1 using hot compression testing. Processing maps were constructed on the basis of compression data and a dynamic materials model. Considerable flow softening associated with superplasticity was observed at strain rates of 0.01 s?1 or lower. According to the processing map and observations of the microstructure, the uniform fine-grained microstructure remains intact at 1100℃ or lower because of easily activated dynamic recrystallization (DRX), whereas obvious grain growth is observed at 1130℃. Metallurgical instabilities in the form of non-uniform microstructures under higher and lower Zener–Hollomon parameters are induced by local plastic flow and primary γ′ local faster dissolution, respectively. The optimum processing conditions at all of the investigated strains are proposed as 1090–1130℃ with 0.08–0.5 s?1 and 0.005–0.008 s?1 and 1040–1085℃ with 0.005–0.06 s?1.     

GH4169合金管材正挤压工艺优化的数值模拟

结合GH4169在不同温度、应变速率下的真应力-应变曲线,应用Msc.Superform有限元软件对GH4169合金管材正挤压进行了数值模拟,系统分析讨论不同挤压参数对挤压过程的影响.结果表明:GH4169合金管材可以通过热正挤压成形,当挤压速度为100 mm.s-1和300 mm.s-1,模角为20～30°,坯料预热温度为1040～1 050℃时,以及在良好的润滑条件下可以获得优化可控的挤压工艺.     

Influence of hot-rolling on the microstructure and mechanical properties of a near β-type Ti-5.2Mo-4.8Al-2.5Zr-1.7Cr alloy

In this work, the 90° clock rolling and the uni-directionally rolling processes at high temperature were carried out on the near β-type Ti-5.2Mo-4.8Al-2.5Zr-1.7Cr titanium alloy cutting from an ingot, respectively. The corresponding microstructures were quantitatively characterized, and its effect on the dynamic mechanical properties and fracture mechanism were emphatically investigated. It was found that after 90° clock rolling, the microstructure composed of equiaxed primary α phase(α_p) with an average size of about 2 ?μm and the β transformed regions containing the acicular secondary α phase(α_s) with an average thickness of about 50 ?nm and the separated β phase was obtained. However, in the uni-directionally rolled titanium alloy, no acicular α_s was observed, and the corresponding microstructure consisted elongated lamellar α phase (average thickness: about 1.3 ?μm), few equiaxed α phase (average grain size: about 300 ?nm) and the inlaid β phase. The microstructural difference of the hot-rolled titanium alloys was closely related to the deformation process. Moreover, a great number of α_p and α_s in the 90° clock rolled titanium alloy effectively enhanced the strength, and the dynamic compressive strength reached to 1730 ?MPa. Furthermore, equiaxed α_p was conducive to the homogeneous deformation, which counteracted the localized deformation caused by acicular α_s to a certain extent and made the 90° clock rolled titanium alloy exhibit an acceptable critical fracture strain of about 10.5%. Moreover, the fracture microstructures showed that the main failure mode of the 90° clock rolled and the uni-directionally rolled titanium alloy were ductile fracture and brittle fracture, respectively.     

A fractal-based model for the microstructure evolution of silicon bronze wires fabricated by dieless drawing

The back-propagation neural (BPN) network was proposed to model the relationship between the parameters of the dieless drawing process and the microstructures of the QSi3-1 silicon bronze alloy. Combined with image processing techniques, grain sizes and grain-boundary morphologies were respectively determined by the quantitative metallographic method and the fractal theory. The outcomes obtained show that the deformed microstructures exhibit typical fractal features, and the boundaries can be characterized quantitatively by fractal dimensions. With the temperature of 600–800℃ and the drawing speed of 0.67–1.00 mm·s-1, either a lower temperature or a higher speed will cause a smaller grain size together with an elevated fractal dimension. The developed model can be capable for forecasting the microstructure evolution with a minimum error. The average relative errors between the predicted results and the experimental values of grain size and fractal dimension are 3.9% and 0.9%, respectively.     

Preparation of high-strength Al-Mg-Si-Cu-Fe alloy via heat treatment and rolling

An Al-Mg-Si-Cu-Fe alloy was solid-solution treated at 560°C for 3 h and then cooled by water quenching or furnace cooling. The alloy samples which underwent cooling by these two methods were rolled at different temperatures. The microstructure and mechanical properties of the rolled alloys were investigated by optical microscopy, scanning electron microscopy, transmission electron microscopy, X-ray diffraction analysis, and tensile testing. For the water-quenched alloys, the peak tensile strength and elongation occurred at a rolling temperature of 180°C. For the furnace-cooled alloys, the tensile strength decreased initially, until the rolling temperature of 420°C, and then increased; the elongation increased consistently with increasing rolling temperature. The effects of grain boundary hardening and dislocation hardening on the mechanical properties of these rolled alloys decreased with increases in rolling temperature. The mechanical properties of the 180°C rolling water-quenched alloy were also improved by the presence of β″ phase. Above 420°C, the effect of solid-solution hardening on the mechanical properties of the rolled alloys increased with increases in rolling temperature.     

Fe6.5Si合金过喷粉末特性研究

以喷射成形Fe-6.5Si过喷粉末为研究对象,采用OM、XRD、VSM、TEM等手段研究了不同球磨工艺条件下所得合金粉末的组织形貌及微观结构对软磁性能的影响,据此找到较佳的球磨工艺条件.结果表明:Fe-6.5Si合金过喷粉末在366 r·min^-1下球磨24 h后,平均晶粒尺寸为25.9 nm.球磨后粉末的磁性能受残余应力和晶粒尺寸的共同影响,在366 r·min^-1下球磨18 h获得了最佳的磁性能,其饱和磁化强度为205.37 emu·g^-1,矫顽力为30.096 Oe.     

Microstructural evolution during reheating of A356 machining chips at semisolid state

The microstructural evolution of A356 machining chips in the semisolid state was studied at different temperatures and holding times. The results showed that the elongated α-Al grains first recrystallized in the semisolid state and then became globular with a high shape factor (SF). Both the temperature and the holding time clearly affected the grain size and SF. When the heating temperature or holding time was increased, the grain size and SF gradually increased and finally became stable. Moreover, the Vickers hardness of primary α-Al grains gradually decreased with increasing heating temperature. The optimal slurry for semisolid processing, with a good combination of grain size and SF, was obtained when the chips were held at 600℃ for 15 min. The semisolid slurry of A356 chips exhibited a lower coarsening rate of α-Al grains than those produced by most of the conventional semisolid processes. The coarsening coefficient was determined to be 436 μm3·s-1 on the basis of the linear Lifshitz-Slyozov-Wagner (LSW) relationship.     

CSP生产线高速钢轧辊温度场有限元分析

采用有限元软件ANSYS,结合某CSP生产线F4机架工作辊表面温度的实测值,建立轧辊二维温度场模型,对轧辊在轧制过程中的温度和热凸度变化进行研究。结果表明,轧辊在咬入弧区的换热系数为5.8×104 W/(m2·K),在非咬入弧区的水冷等效换热系数为1.1×104 W/(m2·K);在此等效换热边界条件下,使轧辊热凸度达到稳定的烫辊时间约为75min。     

Hot compression deformation behavior of AISI 321 austenitic stainless steel

The hot compression behavior of AISI 321 austenitic stainless steel was studied at the temperatures of 950–1100℃ and the strain rates of 0.01–1 s?1 using a Baehr DIL-805 deformation dilatometer. The hot deformation equations and the relationship between hot deformation parameters were obtained. It is found that strain rate and deformation temperature significantly influence the flow stress behavior of the steel. The work hardening rate and the peak value of flow stress increase with the decrease of deformation temperature and the increase of strain rate. In addition, the activation energy of deformation (Q) is calculated as 433.343 kJ/mol. The microstructural evolution during deformation indicates that, at the temperature of 950℃ and the strain rate of 0.01 s?1, small circle-like precipitates form along grain boundaries; but at the temperatures above 950℃, the dissolution of such precipitates occurs. Energy-dispersive X-ray analyses indicate that the precipitates are complex carbides of Cr, Fe, Mn, Ni, and Ti.     

Improving the sulfidation-flotation of fine cuprite by hydrophobic flocculation pretreatment

Hydrophobic flocculation pretreatment was performed to assess its effect on the recovery of fine cuprite in sulfidation-flotation. The results of the micro-flotation experiment showed that cuprite recovery is related to the particle size, and that an excessive content of fine particles (<18 μm) impacted the recovery of coarse particles. When hydrophobic flocculation pretreatment was used, the recovery of fine cuprite in sulfidation-flotation increased from 60.3% to 86.3% under optimum conditions (pH 9.5; sodium oleate concentration, 2×10-4 mol·L-1; stirring time, 6 min; stirring speed, 1600 r·min-1). The laser particle size analysis and optical microscopy results indicate that hydrophobic flocculation pretreatment effectively reduces the content of fine cuprite, and augments the apparent particle size in the pulp. We performed the Derjaguin-Landau-Verwey-Overbeek (DLVO) theory and extended DLVO theory calculations to further support the interpretation of the results.     

Microstructure and texture evolution of TRC A8006 alloy by homogenization

The microstructure and texture evolution of twin-roll cast A8006 alloy by homogenization were characterized using scanning and transmission electron microscopy, and the microhardness was tested as well. According to the relationship between dendritic arm spacing and cooling rate the cooling rate of the as-cast twin-roll cast A8006 sheet of 6 mm in thickness was estimated as 1.48×103 K·s?1. It is found that the grains and the nanostructural precipitates of the twin-roll cast sheet become coarser after homogenization at 580℃ for 4 h in comparison with those after homogenization at 500℃ for 8 h. The textures formed after cold rolling and became weaker during homogenization. The increase in hardness of the as-cast twin-roll cast sheets is related to the supersaturated α-Al solid solution and fine microstructure, but the decrease in hardness after homogenization can be attributed to the coarsening of grains and Al₆Fe(Mn) precipitates.     

Solute atom migration in GH4169 superalloy under electrostatic fields

Electric field treatment (EFT) was applied on GH4169 alloy during aging at 500–800℃ to investigate the microstructure and property variation of the alloy under the action of EFT. The results demonstrate that the short-distance diffusion of Al, Ti, and Nb atoms can be accelerated by EFT, which results in the coarsening of γ′ and γ″ phases. Meanwhile, lattice distortion can be caused by the segregation of Fe and Cr atoms, owing to the vacancy flows migrating toward the charged surfaces of the alloy. Therefore, the alloy is hardened by the application of EFT, even if the strength of the alloy is partly reduced, which is caused by precipitation coarsening.     

Compressive deformation behavior of an indirect-extruded Mg-8Sn-1Al-1Zn alloy

The medium and warm deformation behaviors of an indirect-extruded Mg-8Sn-1Al-1Zn alloy were investigated by compression tests at temperatures between 298 and 523 K and strain rates of 0.001–10 s?1. It was found that the twinning-slip transition temperature was strain rate dependent, and all the true stress-true strain curves could be divided into two groups: concave and convex curves. Associated microstructural investigations indicated that the dynamic recrystallization (DRX) behavior of the alloy varied with deformation conditions. At high strain rate and low temperature, dynamically recrystallized grains preferentially nucleated and developed in the twinned regions, indicating that twinning-induced DRX was dominant. While, at low strain rate, DRX developed extensively at grain boundaries and twins, and the process of twinning contributed to both oriented nucleation and selective growth. For the studied alloy, cracks mainly initiated from the shear band and twinning lamellar over the ranges of temperature and strain rate currently applied.     

Growth and aggregation control of spinel by shear-force-based melting modification of stainless steel slag

To improve the efficiency of melting modification for stainless steel (SS) slag, a shear force was introduced in this work and its effects on the spinel and silicate melt were experimentally investigated. The results indicated that the use of shear force changed the nucleation and growth behaviors of spinel and that the effects of shear force varied with its intensity. The aggregation behavior of spinel under different shear-force conditions was studied, revealing that large spinel clusters could be formed when the stirring speed was controlled. However, no notable change in the melt structure of the silicate was detected in this study. The optimal stirring speed for the melting modification treatment was 50 r·min-1, which substantially promoted spinel growth and aggregation, resulting in modified SS slag with excellent chromium sequestration capability.     

A multi-component nanocrystalline FeCrV alloy with improved mechanical properties and excellent irradiation resistance

An equiatomic low-activated FeCrV ternary alloy was prepared by mechanical alloying and spark plasma sintering. The BCC solid solution alloy exhibited an excellent strength-ductility synergy properties, which was 1.85 ?GPa compressive yield strength, 3.04 ?GPa fracture strength and more than 28% plasticity at room temperature. Even at an elevated temperature of 600 ?°C, its yield strength was still more than 1 ?GPa, revealing a pronounced high temperature resistance. The FeCrV alloy had a homogeneous microstructure with high-density dislocations. A nanocrystalline characteristic was demonstrated and the average grain size was about 322 ?nm, leading to the improved mechanical properties. The strengthening mechanism was discussed in detail and the contributions of strengthening factors were calculated. The FeCrV alloy was irradiated up to 160 dpa with 2 ?MeV Au²⁺ ions at 573 ?K. The nanoindentation test was carried out to simply evaluate the hardening degree under such a high dose irradiation with heavy ions. The semi-quantitative analysis results show that FeCrV alloy has an excellent irradiation tolerance compared with pure Fe.