大厚度紫铜搅拌摩擦焊接

采用搅拌摩擦焊接方法对厚度为30mm和50mm的T2紫铜板分别进行单面和双面焊接实验,并对焊缝的微观组织与力学性能进行了分析.结果表明:在一定的参数范围内,可获得表面成形美观、内部无缺陷且变形小的对接接头.30mm T2紫铜板单道焊焊后平均抗拉强度为177.2 MPa,达到母材的81.7%,断后平均伸长率为25.4%;焊缝横切面显微硬度分布波动较大,最低值位于前进侧热影响区底部,说明了此处位置是焊缝薄弱环节.     

焊接速度对铝合金搅拌摩擦焊接头性能的影响

以厚度3 mm的6061-T6铝合金板材搅拌摩擦焊对接接头为研究对象,建立热力耦合有限元模型,准确模拟了焊接过程的温度场分布及演变规律,采用光学显微观察、电子背散射衍射、显微硬度测量以及拉伸试验等表征方法,研究了焊接速度对焊接接头成形特性、显微组织和力学性能的影响机理.结果表明:接头焊核区在焊接过程中经历了完全动态再结晶,形成细小等轴晶;后退侧热影响区经历了动态回复,晶粒显著长大,晶界强化作用弱于焊核区晶粒;当焊接速度为300～800 mm/min时,接头焊缝成形良好,拉伸断裂均在焊缝后退侧热影响区,在焊接过程中受温度(400～480℃)影响显著,析出强化相溶解导致力学性能明显降低,在此焊接速度范围内,随速度的提高,接头强度增加,最高强度系数为80.86％(800 mm/min);当焊接速度进一步增加至1200 mm/min时,接头的焊接成形性变差,焊核区出现未焊合和隧道缺陷,接头拉伸试验时在焊核区发生断裂.     

2219-T6静轴肩辅助搅拌摩擦焊组织与性能分析

为探究安装外部静止轴肩对搅拌摩擦焊接头成形和力学性能的影响,采用自主研制的外部静止轴肩辅助搅拌摩擦焊(Non-Rotational Shoulder Assisted Friction Stir Welding,NR-SA-FSW)焊具对2219-T6铝合金4 mm厚板材进行对接焊试验,观察焊后接头表面成形情况.采用拉伸和显微硬度试验对焊缝的力学性能进行测试,并与相同焊接参数下的搅拌摩擦焊(Friction Stir Welding,FSW)进行对比分析.使用金相显微镜和场发射扫描电镜对接头焊缝组织进行分析.结果表明,由于静止轴肩的平动刮擦作用,NRSA-FSW相比FSW,接头表面更加光滑,无鱼鳞纹、飞边以及接头减薄现象.NRSA-FSW接头相比于FSW接头软化区有所增加,接头显微硬度分布更加均匀.NRSA-FSW接头平均抗拉强度323 MPa,达到母材的72％,抗拉强度同FSW相近.NRSA-FSW焊核呈"U"状,焊缝组织无缺陷.接头拉伸试验在焊核区(Nuggest-Zone,NZ)处断裂,为韧性断裂.     

35#钢摩擦焊多级加压对轴向缩短量及焊后组织的影响

以35#钢为焊接母材,应用连续驱动摩擦焊接方式,采用正交试验的方法并经过极差分析后,探究了中等直径焊件多级加压方式下各工艺参数对轴向缩短量的影响规律,并对焊接接头显微组织及显微硬度进行了分析.实验结果表明,对焊件轴向缩短量影响程度依次为:二级摩擦位移、二级摩擦压力、一级摩擦压力、一级摩擦位移;观察焊接接头显微组织发现焊缝处得到了细小的铁素体与珠光体相互融合的优良组织,焊缝组织达到正火态;通过对焊件焊缝及热影响区显微硬度测试后可以得出,各焊件焊缝的显微硬度值明显高于母材,不同焊接工艺参数组合方式对焊件接头晶粒存在一定影响并直接影响焊件接头硬度.     

热处理对30CrMnSiA高强钢焊接接头力学性能的影响

针对某型飞机的焊接模拟件展开了力学特性研究,模拟件为30CrMnSiA高强钢板件的一次焊接试验件,分为焊后热处理与焊后不进行热处理两种加工状态。通过拉伸试验、疲劳试验,对疲劳断口显微组织进行了分析,研究了热处理对30CrMnSiA高强钢焊接接头力学性能的影响。结果表明:焊后热处理可以改善焊接接头的力学性能,其中拉伸强度与中值疲劳强度明显提高。通过断口的显微组织观察,可以发现热处理减小了焊缝区的气孔缺陷,改善了焊接接头的疲劳性能。     

HRB500E高强度抗震钢筋焊接性能

国内某厂通过铌微合金化和控冷工艺开发试制HRB500E高强度抗震钢筋,采用金相显微镜、维氏硬度计、闪光焊接、疲劳试验机及力学性能测试,对HRB500E钢筋焊接样力学性能、HV5硬度、金相显微组织、焊接接头强度及疲劳强度进行了试验研究。结果表明:焊接前后焊件和母材强度变化小于5 MPa,强度变化不大,焊件拉伸断口远离焊缝,为延性断口,焊接性能良好;在焊接热循环作用下,焊接接头焊缝、热影响粗晶区、热影响细晶区的表层和芯部经历奥氏体化后再结晶,其组织和硬度变化不大;混晶区至母材表层和芯部则经历不完全奥氏体化后的再结晶,母材芯部组织为F+P+B、表层组织为S,表层硬度HV5高于芯部硬度30 HV5,其组织和硬度变化较大;焊接接头的抗拉断负荷从焊缝到混晶区逐渐减小,焊缝和热影响粗晶区的抗拉断负荷比母材的高;采用国际焊接学会推荐的FAT75疲劳设计曲线对钢筋焊接接头疲劳强度设计是安全的。     

YAG激光焊接不锈钢薄板焊接工艺参数优化

激光焊接是目前应用较广的激光焊接技术,对于薄板焊接时激光深熔焊接的焊接深熔比可以达到2:1,其焊接强度和稳定都优于传统焊接。本文采用YAG激光器对2mm厚的0Gr18Ni9进行焊接试验,测量焊接的熔深和熔宽,并采用正交试验法进行参数优化,分析激光参数对焊缝的影响,通过显微硬度测试分析焊接接头的硬度,为激光焊接工艺参数...     

不锈钢水下激光焊接焊缝成形与力学性能

摘要： 采用水下局部干法激光焊接技术对1 mm厚SUS304不锈钢进行了焊接试验,重点分析了水深及保护气体流量对焊缝成形与力学性能的影响.实验结果表明：通过适当的水深与保护气体流量匹配,可以获得成形良好、剪切拉伸强度与母材相当的焊缝.在水深一定时,随着气体流量的增加,焊缝熔宽变宽,熔深变浅,深宽比减小.在气体流量一定时,随着水深的增加,焊缝熔深和熔宽也表现出类似的变化规律.与普通激光焊接相比,水下激光焊接改变了焊缝的散热方向以及散热速度,因此同一焊接工艺参数下,水下激光焊接的熔深变浅,熔宽变宽.
关键词： 水下焊接; 激光焊; 奥氏体不锈钢; 焊缝成形; 力学性能
中图分类号： TG 456.7文献标志码： A     

H62 黄铜激光焊接性的研究

研究了激光焊接Ｈ６２黄铜时工艺参数对焊缝成形、内部缺陷及合金成分变化的影响规律。结果表明：激光焊接黄铜时线能量不宜过大，过大的线能量将导致飞溅严重，焊缝凹陷加剧、焊缝α相增多、晶粒粗大和焊缝硬度（强度）显著下降。采用大功率激光和大焊速焊接黄铜时焊缝热裂纹倾向增大。激光焊接线能量为１．３５～１．６５ｋＪ／ｃｍ、焦点位置为０．５～１．５ｍｍ时，可获得３ｍｍ厚黄铜板全熔透、无内部缺陷及锌损失小的焊缝。用夹片和盖片方法进行激光焊接可解决焊缝凹陷的问题。     

2219铝合金焊缝组织及其对力学性能的影响

针对厚度为4 mm的2219-T87铝合金进行惰性气体钨极保护焊(Tungsten inert gas arcwelding,TIGAW)试验研究,分析焊缝的组织结构及力学性能。拉伸试验结果显示,接头试样平均屈服强度为母材的49.3%,平均抗拉强度为母材的67.8%,断后伸长率为母材的18.5%。测试了焊接试样各区域的显微硬度,测试结果表明焊缝区域硬度高于其他部位,其中熔合线和热影响区之间的显微硬度最低,同时焊接试样的整体区域硬度均比母材低。对焊接试样进行腐蚀试验,发现接头焊缝区抗腐蚀能力明显强于母材。要提高2219铝合金焊接性能,需改进焊接工艺,减少熔合区以及热影响区的粗大晶粒的形成,解决CuAl2相的偏析等问题。     

2024-T42铝合金点焊接头性能研究

为改善高强铝合金接头连接性能,提高焊接质量,研究了2024-T42铝合金回填式搅拌摩擦点焊(RFSSW)、电阻点焊和铆接3种不同接头的连接性能,采用显微组织观察试验、拉伸试验、拉剪试验和显微硬度试验等方法,对接头组织和性能进行表征与分析.结果 表明:RFSSW接头的力学性能最优,拉剪性能达到7.23 kN,较铆接和电阻...     

激光功率对6061-T6铝合金激光填丝焊接头组织及性能的影响

采用激光填丝焊将厚度为2 mm和3 mm的6061-T6铝合金板材进行搭接叠焊,研究激光功率对接头成形质量的影响,分析了接头的显微组织和力学性能。结果表明,增大激光功率可以有效增加热输入量,焊道逐渐宽化,焊缝熔深增加。进一步分析发现,焊缝中心区和热影响区的析出相均为Mg₂Si。硬度试验结果表明,焊缝中心区由于细小等轴晶和析出相的双重作用,硬度远高于母材区与热影响区的。拉伸试验结果表明,接头的抗拉强度随激光功率的增大而升高,激光功率由2.0 kW升高至2.8 kW,抗拉强度升高约39%。     

TIG焊工艺对5083铝合金焊接接头力学性能的影响

5083铝合金焊接接头的力学性能是影响产品质量的关键因素之一.设定不同TIG焊工艺,用6012铝合金焊丝对10 mm厚的5083铝合金板进行焊接.焊接试样分为四组,在氩气流量、层间温度相同的情况下,四组试样分别采用五层不同焊接电流、焊速、不填丝自熔或加硼方式的焊接工艺.通过对四组试样进行拉伸实验、断口形貌观察,结合金相组织分析,探究TIG焊工艺对5083铝合金焊接接头力学性能的影响.结果表明：中厚板5083铝合金TIG焊接,采用6012铝合金焊丝,层间温度控制在80 ℃,第五道焊道采用不填丝自熔时,焊接接头的综合力学性能最好.     

LD10CS铝合金点焊的神经网络质量估测

针对铝合金的电阻点焊，研究了人工神经网络在点焊质量估测中的应用。以LD10CS铝合金为例，分析了铝合金焊接时动态电极电压的变化，提出了以每周波动态电极电压为输入参数，以焊点强度和熔核直径为输出参数的误差传播神经网络对点焊质量进行估测的方法。实验结果表明了该估测方法的可行性，为铝合金点焊的在线质量估测奠定了良好的基础。     

Microstructure and mechanical properties of the welding joint filled with microalloying 5183 aluminum welding wires

In this study, 7A52 aluminum alloy sheets of 4 mm in thickness were welded by tungsten inert gas welding using microalloying welding wires containing traces of Zr and Er. The influence of rare earth elements Zr and Er on the microstructure and mechanical properties of the welded joints was analyzed by optical microscopy, energy dispersive X-ray spectroscopy, transmission electron microscopy, hardness testing, and tensile mechanical properties testing. Systematic analyses indicate that the addition of trace amounts of Er and Zr leads to the formation of fine Al₃Er, Al₃Zr, and Al₃(Zr,Er) phases that favor significant grain refinement in the weld zone. Besides, the tensile strength and hardness of the welded joints were obviously improved with the addition of Er and Zr, as evidenced by the increase in tensile strength and elongation by 40 MPa and 1.4%, respectively, and by the welding coefficient of 73%.     

5052/6005A异种铝合金激光填丝焊接头组织与力学性能研究

对铝合金6005A与5052进行异种铝合金激光填丝焊,研究了焊接接头的微观组织及力学性能,并对接头断口微观特征进行了分析。结果表明,焊缝中心为等轴晶与树枝晶,铝合金6005A侧熔合线附近存在清晰柱状晶,铝合金5052侧熔合线较为模糊。拉伸时在铝合金6005A侧热影响区断裂。焊接件焊接接头的平均抗拉强度为197.9 MPa,达到铝合金6005A母材抗拉强度的83%。断裂特征为韧性断裂,接头弯曲性能良好。     

Influence of CO2 laser welding parameters on the microstructure, metallurgy, and mechanical properties of Mg-Al alloys

This study investigated the microstructural characteristics, metallurgy, microhardness, and tensile strength of AZ31 and AZ61 magnesium alloy weldments, fabricated in a CO₂ laser welding process with the adjustment of various parameters. The results show that the AZ31 weldment contains equiaxed grains within the fusion zone (FZ). By contrast, the FZ of the AZ61 weldment contains refined cellular grains and the partially melted zone (PMZ) contains bulk grains. We infer that the difference in aluminum content between the two magnesium alloys results in different supercooling rates and solid grain structures. For both weldments, the ultimate tensile strength (UTS) decreases following the CO₂ laser welding process. However, no significant difference is noted between the UTS of the two weldments, suggesting that tensile strength is insensitive to the Al content of the magnesium alloy. The CO₂ laser welding process is shown to increase the microhardness of both magnesium alloys. Furthermore, grain refinement is responsible for the maximum hardness in the FZ of both weldments. The AZ61 weldment has a higher content of Al, resulting in a greater grain refinement.     

Effects of heat treatment on the intermetallic compounds and mechanical properties of the stainless steel 321-aluminum 1230 explosive-welding interface

The effects of heat treatment on the microstructure and mechanical properties of intermetallic compounds in the interface of stainless steel 321 explosively bonded to aluminum 1230 were investigated in this study. Experimental investigations were performed by optical microscopy, scanning electron microscopy, and microhardness and shear tensile strength testing. Prior to heat treatment, increasing the stand-off distance between samples from 1 to 2.5 mm caused their interface to become wavy and the thickness of intermetallic layers to increase from 3.5 to 102.3 μm. The microhardness increased from HV 766 in the sample prepared at a stand-off distance of 1 mm to HV 927 in the sample prepared at a stand-off distance of 2.5 mm; in addition, the sample strength increased from 103.2 to 214.5 MPa. Heat treatment at 450℃ for 6 h increased the thickness of intermetallic compound layers to 4.4 and 118.5 μm in the samples prepared at stand-off distances of 1 and 2.5 mm, respectively. These results indicated that increasing the duration and temperature of heat treatment decreased the microhardness and strength of the interface of explosively welded stainless steel 321-Al 1230 and increased the thickness of the intermetallic region.     

结晶器铜板上激光熔覆镍基合金

利用5kWCO2激光器在结晶器铜板上熔覆镍基合金,并研究了熔覆层组织性能.选用与结晶器铜板成分相近的镍基自熔合金粉末Nickel-baseHMSP1015-00(Ni1015),利用等离子喷涂技术在铜板上预涂Ni1015合金,然后再采用高能量密度激光进行重熔.借助OM,SEM和显微硬度计分析测定了涂层的显微组织形貌、组织成分和截面显微硬度分布情况.所得到的熔覆层表面平整均匀,与基体为冶金结合;熔覆层平均显微硬度为270HV0.05,是基体的3.2倍(85HV0.05).确定出本实验合适的激光熔覆工艺参数功率密度为1.58×102kW/cm2时,扫描速度为3~4m/min.