Inhibitive effect of <Emphasis Type="Italic">Xylopia ferruginea</Emphasis> extract on the corrosion of mild steel in 1M HCl medium

The alkaloid content of the leaves and stem bark of Xylopia ferruginea plant was isolated and tested for its anticorrosion potential on mild steel corrosion in a hydrochloric acid medium by using electrochemical impedance spectroscopy, potentiodynamic polarization measurement, scanning electron microscopy (SEM), and Fourier transform infra red (FTIR) analysis. The experimental results reveal the effective anticorrosion potential of the plant extract. The mixed mode of action exhibited by the plant extract is evidenced from the polarization study. SEM images proof the formation of a protective layer over the mild steel surface, and this is supported by the FTIR study. The possible mode of the corrosion inhibition mechanism has also been discussed.     

Q235钢在含硫酸盐还原菌海水中的腐蚀行为

为了更好地揭示微生物腐蚀的机理,文中采用腐蚀电位法、极化曲线法、电化学阻抗法、环境扫描电镜法对低碳钢Q235在灭菌海水、接种硫酸盐还原菌(SRB)的海水中的不同腐蚀行为进行了研究.结果表明:在含有SRB的海水中,低碳钢的自腐蚀电位向负相有较大的偏移,最终在-740 mV左右逐渐稳定;与在灭菌海水中的腐蚀相比,低碳钢在含SRB海水中的腐蚀电流密度变大,极化电阻减小,腐蚀速度加快;经微生物腐蚀后,低碳钢表面出现了大量的腐蚀孔,发生了严重的孔蚀行为.     

对苯二酚对亚硫酸盐防腐蚀效果的影响

通过除氧试验、腐蚀试验和电化学试验，研究了对苯二酚对亚硫酸盐防腐蚀效果的影响。结果表明，对苯二酚使亚硫酸盐几乎失去了除氧作用，但却提高了亚硫酸盐在含氧水中对２０ｇ钢的防腐蚀性能，使钢的自腐蚀电位更剧烈负移并使阴极极化增加。     

铸铝-碳钢电偶腐蚀及PBTCA的缓蚀研究

铸铝 -碳钢电偶腐蚀是工业水系统常见的腐蚀类型 .通过电偶腐蚀、腐蚀失重、扫描电镜 (SEM)、俄歇电子能谱 (AES)等表面分析技术 ,结合自腐蚀电位和极化曲线测量 ,研究铸铝 -碳钢电偶在水中的腐蚀及有机膦羧酸PBTCA对它们的缓蚀作用 .PBTCA对铸铝是一种阴极型缓蚀剂 ,能有效防止铸铝的点蚀 ,与硼酸盐结合使用能较好地抑制铸铝 -碳钢的电偶腐蚀 .     

20#碳钢管道内沉积物对腐蚀行为的影响

 塔河油田地面原油集输金属管道主要材质为20^#碳钢。地面原油集输金属管道腐蚀主要为内壁点蚀,点蚀区域存在有沉积物。为研究沉积物对地面原油金属集输管道的腐蚀行为的影响,在对管道内壁沉积物类型分析的基础上,通过将无、有沉积物覆盖的20^#碳钢试片挂入高压釜来模拟现场腐蚀实验,应用失重法分析、电位极化曲线测试、丝束电极测试及扫描电镜技术对无沉积物覆盖的20^#碳钢试片及有沉积物覆盖下的20^#碳钢试片的腐蚀失重速度、腐蚀过程、腐蚀电位分布及扫描电镜特征进行测试。分析表明：无沉积物覆盖区20^#碳钢相比有沉积物覆盖腐蚀失重速度小;两者腐蚀过程均受阴极扩散控制,后者阳极过程受到促进,腐蚀电位降低、耐蚀性变差;前者腐蚀电位分布随时间变化不大,以全面腐蚀为主,后者腐蚀电位分布随时间变化大,点蚀特征明显,建立了无、有沉积物覆盖的20^#碳钢腐蚀行为影响过程模型。     

pH值对Q235钢在模拟酸性土壤中腐蚀行为的影响

通过腐蚀失重计算、扫描电镜、X射线衍射方法、极化曲线分析等手段,研究了pH值对Q235钢在模拟酸性土壤中腐蚀行为的影响.在模拟酸性土壤环境中,Q235钢的腐蚀速率随土壤pH值升高而降低,经360 h腐蚀后,在pH值为4.0、4.5和5.1的土壤中试样的腐蚀速率分别为0.68、0.48和0.42 mm·a-1.随土壤pH值升高,Q235钢锈层更为致密,其表面蚀坑由窄深型发展变为宽浅型发展.腐蚀产物均为SiO2、α-FeOOH、γ-FeOOH、Fe2 O3及 Fe3 O4,随土壤 pH值升高,腐蚀产物中α-FeOOH/γ-FeOOH质量比升高.极化曲线分析表明,随土壤pH值升高,Q235钢腐蚀电位升高,自腐蚀电流密度降低,试样腐蚀速率减小.     

若干无机缓蚀剂对混凝土中钢筋的阻锈作用

通过含NaCl介质溶液的浸泡实验,利用电化学实验检测技术,观测和比较了NaNO2等8种无机缓蚀剂添加于混凝土中对钢筋的阻锈作用,结果表明,在本实验条件下,NaNO2等缓蚀剂对钢筋明显的阻锈作用,在pH=9.50％,含10％NaCl的混凝土模拟液中,外加NaNO2后,混凝土中钢筋的腐蚀电位正移,腐蚀电流可下降至未加缓蚀剂的1／6,缓蚀剂的加入不同程度地提高了钢筋耐点蚀的性能。     

高强耐候钢Q450NQR1腐蚀规律和机制

 通过采用周浸腐蚀试验方法研究了Q450NQR1高强耐侯钢和Q345钢在浓度为0.01mol/L的亚硫酸氢钠溶液中,经过6,24,48,72和96h周浸腐蚀试验后的耐腐蚀性能,并测试了不同周浸腐蚀时间后试样的腐蚀电位和腐蚀电流密度.研究发现,Q450NQR1钢腐蚀速率随试验时间延长而下降,其表面的锈蚀产物膜在周浸腐蚀试验48h后基本达到稳定.Q450NQR1钢在浸泡各个周期内相对Q345钢均有更好的耐腐蚀性.电化学极化实验证实Q450NQR1钢的腐蚀电流48h后趋于稳定,而Q345B 48h后腐蚀电流密度略有增大,这与周浸腐蚀试验结果是一致的.微观腐蚀形貌及EDS分析认为这是由于Q450NQR1钢中添加的Cu和Cr元素参与了腐蚀成膜,并促使腐蚀产物膜整齐致密.XRD分析结果表明,Q450NQR1钢随时间延长,腐蚀产物中的α-FeOOH含量不断增加,在48h后含量基本稳定,大量α-FeOOH促使了锈层更加致密稳定,从而提高了Q450NQR1试样的耐腐蚀能力.     

Effect of temperature on the passivation behavior of steel rebar

Steel rebar normally forms an oxide or rusty skin before it is embedded into concrete and the passivation properties of this skin will be heavily influenced by temperature. To study the effect of temperature on the passivation properties of steel rebar under different surface conditions, we conducted scanning electron microscopy (SEM) observations and electrochemical measurements, such as measurements of the free corrosion potential and polarization curves of HPB235 steel rebar. These measurements identified three kinds of surfaces: polished, oxide skin, and rusty skin. Our results show that the passivation properties of all the surface types decrease with the increase of temperature. Temperature has the greatest effect on the rusty-skin rebar and least effect on the polished steel rebar, because of cracks and crevices on the mill scale on the steel rebar’s surface. The rusty-skin rebar exhibits the highest corrosion rate because crevice corrosion can accelerate the corrosion of the steel rebar, particularly at high temperature. The results also indicate that the threshold temperatures of passivation for the oxide-skin rebar and the rusty-skin rebar are 37℃ and 20℃, respectively.     

300M超高强度钢电化学性能及应力腐蚀开裂

采用动电位扫描技术和慢应变速率拉伸试验研究了超高强度钢300M在3.5%NaCl溶液中的应力腐蚀行为,并利用扫描电镜观察了不同外加电位下的断口形貌.300M钢在3.5%NaCl溶液中开路电位下的应力腐蚀开裂机制为阳极溶解型,Cl-的存在明显地增加了材料的应力腐蚀开裂敏感性.阳极电位-600 mV下300M钢溶解速率加快,表现出较高的应力腐蚀开裂敏感性,断面收缩率损失由开路电路下的52.6%升高至99.5%,裂纹起源于表面点蚀坑处,应力腐蚀开裂为阳极溶解型机制.阴极电位-800 mV下材料处于阴极保护电位范围,表现出较低的应力腐蚀开裂敏感性,强度和韧度与空气中拉伸的数值相近,开裂机制为阳极溶解和氢致开裂协同作用.在更低电位(低于-950 mV)下,300M钢的应力腐蚀开裂机制为氢致开裂,在氢和拉应力的共同作用下表现出很大的应力腐蚀开裂敏感性.     

电迁移加速氯盐传输作用下混凝土中钢筋锈蚀

采用电迁移氯离子法加速了混凝土中钢筋的锈蚀过程.应用腐蚀电位、线性极化法、电化学阻抗谱法和循环极化法对比了C50与C80混凝土试件中钢筋的锈蚀行为.比较了混凝土保护层的开裂情况和钢筋的腐蚀形貌.分析结果表明:掺硅灰的C80试件具有优化的孔结构和较大的电阻率,显著延缓了氯离子到达钢筋表面的时间,因而表现出较好的耐蚀性;而...     

不锈钢表面Ti-O-Y涂层的防腐性能

采用溶胶-凝胶法,经过涂覆、固化、烧结,在不锈钢表面获得不同Ti和Y摩尔比的Ti-O-Y复合涂层,并通过X衍射(XRD)、扫描电镜(SEM)、电化学腐蚀和高温氧化测试方法,研究其结构和耐蚀性能.结果表明:Ti与Y摩尔比为10∶3的涂层的自腐蚀电位最高,效果最好;不锈钢基材的氧化速率降低,是由于Y离子的掺杂阻碍的氧的向内扩散,起到高温抗氧化的作用.     

Sn对Q125级ERW套管力学性能及腐蚀行为的影响

采用扫描电镜、透射电镜、电子背散射衍射和电化学等分析了Sn对Q125级ERW石油套管用钢力学性能和抗CO2腐蚀性能的影响.结果表明:Sn的加入对钢的显微结构、析出物形态和尺寸均没有影响,因此强度变化不明显;少量Sn的加入改变了钢的活性,引起自腐蚀电位负移,腐蚀电流密度减小,同时实验钢电极反应的极化电阻增大,腐蚀反应变慢,耐腐蚀性能得到提高;Sn的加入使钢中小角度晶界的比例有所增大,提高了实验钢的耐腐蚀性,大角度晶界的比例则减小,使实验钢的延伸率和冲击功显著下降.     

电力输电杆塔用Q235钢聚硅氧烷复合涂层的大气腐蚀行为

采用喷涂法在Q235钢表面涂覆聚硅氧烷复合涂层,在重工业污染区、人口密集区、一般工业区、乡村定居区4个220kV变电站大气环境中自然暴露15个月,采用伏安法、交流阻抗法等研究其腐蚀行为。结果表明,重工业污染区变电站的腐蚀电流密度从3.849 5×10~(-12) A/cm~2增加到15个月的2.257 2×10~(-10) A/cm~2;而人口密集区变电站的腐蚀电流密度值先从1.640 1×10~(-10) A/cm~2降低到6个月的5.736 5×10~(-11) A/cm~2,后增加到15个月的3.929 9×10~(-10) A/cm~2。结合自腐蚀电位和涂层阻抗,聚硅氧烷复合涂层在不同环境中耐蚀性顺序为:人口密集区乡村定居区一般工业区重工业污染区。     

硫化氢质量浓度和温度对碳钢在NACE溶液中腐蚀行为的影响

采用动电位极化曲线和电化学阻抗谱等电化学实验方法以及扫描电镜和能谱等表面分析技术对20#碳钢在不同H2S质量浓度(0,95.61,103.22,224.16 mg.L-1)、不同温度(25,35,45℃)下的NACE溶液(含CO2)中腐蚀行为进行了研究,同时对该环境下腐蚀产物的形成机制进行了探讨.发现在含有CO2的NACE溶液中,加入少量H2S,能加剧碳钢腐蚀,加速阳极铁的溶解和阴极氢气的析出.随着H2S质量浓度的增加,腐蚀电流密度增大,碳钢腐蚀加剧.温度升高,腐蚀极化电阻变小,腐蚀也会加剧.腐蚀试样外层絮状腐蚀产物主要是铁碳化物,接近基体表面的腐蚀产物主要是铁硫化物.     

有机缓蚀剂对钢筋的缓蚀作用

应用线性极化法和塔菲尔外推法,研究了乌洛托品、硫脲、8-羟基喹啉三种有机缓蚀剂在0．8mol／LNaCl的模拟混凝土孔隙溶液中对R235钢筋的缓蚀效果．研究结果表明,当溶液的pH值为12．95时,8-羟基喹啉、乌洛托品对钢筋具有较好的缓蚀效果,硫脲几乎没有缓蚀效果;pH值降至10．95时,8-羟基喹啉基本失去缓蚀性;乌洛托品在高浓度时仍具有较好的缓蚀效果;硫脲和乌洛托品有协同作用,可以有效降低乌洛托品的用量．还初步探讨了缓蚀的机理．     

新型耐蚀低合金钢筋腐蚀行为

 应用动电位极化、电化学阻抗谱、周浸腐蚀试验的方法,研究了HRB400 碳钢钢筋和两种Cr 合金化的低合金钢筋在0.01mol/L NaHSO₃溶液中的腐蚀行为。结果表明,相比HRB400 钢筋,Cr 合金化钢筋的开路电位明显正移,Cr 元素提高了钢的热力学稳定性;随着Cr 元素质量分数的增加,钢筋的自腐蚀电流密度减小,极化电阻增大,Cr 合金化的钢筋具有相对较小的电化学腐蚀速率;周浸加速腐蚀72 h 后,HRB400 钢筋和Cr 合金化的钢筋均以均匀腐蚀为主,添加Cr 元素可以显著降低钢筋的均匀腐蚀速率。     

A3钢在碱性NaCl体系中闭塞电池腐蚀的研究

用模拟闭塞电池法研究了A3钢在0.01 (mol·L^-1)NaCl( pH =12.00 )溶液中闭塞区内化学状态的变化。结果表明, 随着阳极极化时间的延长, 闭塞区溶液的pH值下降,开始时下降较快 ,Cl^- 向闭塞区内迁移 ,闭塞溶液的[Cl^- ]与极化时间成直线关系。在不同 pH值下的NaCl溶液中的极化曲线测试结果表明 ,当 pH值大于11时, A3钢极化曲线阳极区出现明显的钝化, 可见, 在pH值大于11的体系中, A3钢发生局部腐蚀的倾向更大。     

Short-term exposure of low-alloyed steels in Qinghai Salt Lake atmosphere

The rusts formed on carbon steel and weathering steel exposed in Qinghai Salt Lake atmosphere for 6 months were characterized by X-ray diffraction （XRD）, infrared transmission spectroscopy （iRS）, scanning electron microscopy （SEM）, electron probe micro analyzer （EPMA） and electrochemical po- larization techniques. The two kinds of steels showed the similar corrosion rate, corrosion product composition and electrochemical polarization behavior. Their rusts were mainly composed of β-FeOOH, Fe8（O,OH）16Cl1.3 and a little γ-FeOOH. Cl^- played an important role during the corrosion process of low-alloyed steels. The alloyed elements Cr, Ni and Cu in weathering steel were detected in the rusts; however, they showed no remarkable protective ability.     

内掺氯离子对钢筋锈蚀的影响及固化性能的研究

参考钢筋锈蚀快速试验法,通过测试试件的半电池电位和阳极极化曲线,考察了拌合时引入的不同种类的氯盐及含氯的原材料对钢筋锈蚀的影响,并对不同矿物组成的水泥及矿渣和粉煤灰对内掺氯离子的固化性能进行了研究。结果表明：CaCl2对钢筋锈蚀的危害比NaCl大,掺CaCl2时较低的氯离子浓度和较小的自由氯离子含量即引起钢筋锈蚀;掺结皮料和垃圾焚烧炉渣作混合材时,结皮料氯离子含量高,掺量≥20%引起锈蚀;炉渣氯离子含量低,对钢筋锈蚀没有危害;有效铝酸盐含量高的水泥及矿渣、粉煤灰的加入均能提高对氯离子的固化能力,有效降低钢筋锈蚀的危害;当体系掺有混合材或其他组分时,阳极极化试验比半电池电位能更有效地反映发生钢筋锈蚀的情况。