Growth, structure and upconversion mechanisms of Ba2ErCl7 crystal

The methods to grow a novel upconversion crystal Ba₂ErCl₇ are reported in this note. Ba₂ErCl₇ material was synthesized with Er₂O₃, BaCl₂·2H₂O and NH₄Cl by using a so-called “direct synthesis method”. High quality Ba₂ErCl₇ single crystals with size up to 4 mm×8 mm×15 mm were grown by using the Czochralski and the Bridgman methods. Intense yellow-green luminescence was detected when the crystal was pumped by an 803 laser diode (LD). Transmittance spectrum was measured by using HITACH U-3500 spectrophotometer at room temperature for the first time, in which one can see that the transmittance is high in the range from 350 to 1 600 nm and the cut-off wavelength of the crystal was 230 nm. The upconversion mechanisms were discussed.     

Nd^3＋：Li3Ba2Re3（MoO4）8（Re=Y，Gd，La）晶体的生长、结构和光谱性能研究

采用顶部籽晶法生长了Nd^3＋：Li3Ba2Re3（MoO4）8（Re=Y,Gd,La）晶体。利用X射线单晶衍射仪证实了其结构,并得到了其晶胞参数。测量了这三种晶体的室温吸收谱和荧光光谱,并计算了吸收光谱和荧光光谱中的相关参数。吸收光谱表明,这三种晶体在805nm处均有较强的吸收,其吸收半峰宽分别为6nm、6nm、7nm,非常适合于LD泵浦。同时根据这三种晶体的荧光光谱计算了其在1．06μm处的发射截面,其峰值分别为：11．6×10-20cm2（Nd3＋：Li3Ba2Y3（MoO4）8）,8．7×10-20cm2（Nd3＋：Li3Ba2Y3（MoO4）8）,6．2×10-20cm2（Nd3＋：Li3Ba2Y3（MoO4）8）。最后,本文将这三种晶体的相关光谱参数与其它一些掺Nd离子的激光晶体进行了对比。结果显示,Nd^3＋：Li3Ba2Re3（MoO4）8（Re=Y,Gd,La）晶体是一种有潜力的固体激光材料。     

掺杂方式对Mg：Ba0．3Sr0．7Zr0．18Ti0．82O3陶瓷微结构及性能的影响

采用溶-凝胶法制备Mg：Ba0．3Sr0．7Zr0．18Ti0．82O3陶瓷粉末,以传统陶瓷制备工艺制备Mg元素掺杂的Mg：Ba0．3Sr0．7Zr0．18Ti0．82O3陶瓷．研究MgO掺杂量为1．6％（质量分数）时,MgO固相掺杂和Mg计湿化学法掺杂两种不同的掺杂方式对Mg掺杂的Mg：Ba0．3Sr0．7Zr0．18Ti0．82O3陶瓷显微结构及电学性能的影响．研究结果表明,当Mg掺杂量相同时,掺杂方式对Mg掺杂的Mg：Ba0．3Sr0．7Zr0．18Ti0．82O3。陶瓷的显微结构和电学特性有显著的影响,相比纯的Mg：Ba0．3Sr0．7Zr0．18Ti0．82O3陶瓷,两种掺杂方式中,Mg2＋湿化学法掺杂相对于MgO固相掺杂,在BSZT陶瓷中的分布更均匀,替位程度更高,所以其对介电常数的影响也相对更大．而MgO固相掺杂相对于Mg2＋湿化学法掺杂明显地促进了陶瓷晶粒的生长,提高了陶瓷的致密性,同时其击穿电场和电阻率也有较大提高．1350℃下烧结的固相MgO掺杂的Mg：Ba0．3Sr0．7Zr0．18Ti0．82O3陶瓷性能较优,介电常数约为590,介电损耗低于0．0005,电阻率为7．78×10^13Ω·mm,击穿场强为6．56kV／mm．     

Nd:KY(WO4)2晶体的光谱及上转换发光

在室温下,测试分析了Nd:KYW晶体的吸收光谱,确定Nd3 离子的能级结构.使用波长为808nm激光二极管作为激发光源,观察912、1 069、1 351 nm荧光光谱.采用不同波长(594、812 nm)的氙灯光泵浦晶体,获得了紫、蓝、绿和红色上转换荧光,并分析了上转换发光的过程和比较它们的发光特点.     

H03+:Ba0.8Sr0.2Ti03纳米粉体的光谱性质研究

采用溶胶-凝胶法制备Ho3+:Ba0.8Sr0.2TiO3 (BST)纳米粉体.根据Judd-Ofelt理论对纳米粉体的吸收光谱进行拟合,得到晶体场强度参数Ω2、Ω4和Ω6分别为0.229×10-20、0.515×10-20和0.761×10-20cm2,并系统计算Ho3+各能级跃迁的振子强度、自发辐射跃迁几率、荧光分...     

CaAl_2O_4:Eu~(2+),Nd~(3+)纳米颗粒荧光猝灭法测定水中的Pb~(2+)

基于Pb^2＋对CaAl2O4：Eu^2＋,Nd^3＋纳米颗粒的荧光猝灭作用,建立了用琼脂溶液来固定CaAl2O4：Eu^2＋,Nd^3＋纳米颗粒并用于测定水中微量Pb^2＋的荧光分析新方法．在pH=3．0的条件下,测定的荧光最大激发波长和发射波长分别为328nm和440nm,测定Pb^2＋浓度的线性范围为6．0×10^-6mol·L^-1-8．0×10^-4mol·L^-1,回收率为97．7％-107．0％．该方法用于水中Pb^2＋的测定,结果满意．     

Ba 掺杂和烧结温度对 Sr4V2O9：Eu3＋（5％），Ba2＋（x％）光学性质的影响

采用水热和烧结的方法制备系列Sr4 V2 O9：Eu3＋（5％）,Ba2＋（x％）（x＝0,5）粉末样品。用X射线衍射和荧光分光光度计对样品的结构和光学性质进行了研究。研究结果表明Ba掺杂能提高样品的发光强度,而烧结却降低发光强度。随着烧结温度的增加,Eu离子周围的晶格畸变,导致 Eu离子的磁偶极跳跃减弱并消失。     

上转换材料复合介孔TiO2晶须的可见光催化性能

用溶胶凝胶法制备上转换发光材料Y3Al5O12:Er。反射光谱、发射光谱表明:Y3Al5O12:Er在480 nm光的激发下,产生2个<387 nm的紫外光发射峰。将上转换材料介孔TiO2晶须复合成可见光催化剂,采用X线衍射仪(XRD)、场发射扫描电子显微镜(FESEM)以及低温N2吸附-脱附(BET)等对催化剂进行表征,通过光催化降解亚甲基蓝(MB),对催化剂的活性进行测试。结果表明:复合上转换材料的介孔TiO2晶须在可见光下能够有效降解MB,10%Y3Al5O12:Er的介孔TiO2晶须的MB降解率为73%。     

2-苯基4-硒唑甲酸铜配合物的合成及其与DNA的作用

在水溶液中,由硝酸铜和2一苯基4-硒唑甲酸（HL）合成了配合物NH4[Cu2L5]HL·6H20;用元素分析、红外光谱、摩尔电导率和热重分析方法对配合物进行了表征,用单晶X-射线衍射方法测定了配合物的晶体结构．该配合物C60H53Cu2N70188Se6属于三斜晶系,空间群P-1,a=1．36868（9）nm,b=1．50696（9）nm,c=1．82897（12）nm,a=103．200（4）°,β=100．264（4）°,γ=111．054（4）°,V=3．2839（4）nm^3,Z=2,M,=1760．94,F（000）：1736,De=1．781g·cm^3,p（MoKa）=4．048mm^-1．用溴化乙锭荧光探针法测试了配合物与DNA的作用．     

硼氧酸盐(K2O·CaO·4B2O3·12H2O)的合成与表征

以氯化钙、四硼酸钾为原料,以水为溶媒,采用易于工业化、无污染的水溶液法制备一种新型硼酸钾钙复盐.该方法工艺条件为:去离子水450ml,四硼酸钾和氯化钙的质量比65:7.5,搅拌转速400 r/min,45℃反应3 h.通过化学分析、红外光谱、X射线衍射、扫描电镜等分析测试方法,对所合成的复盐进行了分析和表征.考察了反应...     

Cost-effective integrated strategy for the fabrication of hard-magnet barium hexaferrite powders from low-grade barite ore

Ultrafine barium hexaferrite (BaFe₁₂O₁₉) powders were synthesized from the metallurgical extracts of low-grade Egyptian barite ore via a co-precipitation route. Hydrometallurgical treatment of barite ore was systematically studied to achieve the maximum dissolution efficiency of Fe (~99.7%) under the optimum conditions. The hexaferrite precursors were obtained by the co-precipitation of BaS produced by the reduction of barite ore with carbon at 1273 K and then dissolved in diluted HCl and FeCl₃ solution at pH 10 using NaOH as a base; the product was then annealed at 1273 K in an open atmosphere. The effect of Fe3+/Ba2+ molar ratio and the addition of hydrogen peroxide (H₂O₂) on the phase structure, crystallite size, morphology, and magnetic properties were investigated by X-ray diffraction, scanning electron microscopy, and vibrating sample magnetometry. Single-phase BaFe₁₂O₁₉ powder was obtained at an Fe3+/Ba2+ molar ratio of 8.00. The formed powders exhibited a hexagonal platelet-like structure. Good maximum magnetization (48.3 A·m2·kg–1) was achieved in the material prepared at an Fe3+/Ba2+ molar ratio of 8.0 in the presence of 5% H₂O₂ as an oxidizer and at 1273 K because of the formation of a uniform, hexagonal-shaped structure.     

（Ba0.2Sr0.8）1-1.5xBixZn0.04T i0.98O3陶瓷结构及介电性能的研究

采用传统固相反应方法,制备了（Ba0.2Sr0.8）1-1.5xBixZn0.04Ti0.98O3（x=0.00、0.01、0.02、0.03）陶瓷材料,用X射线衍射、扫描电子显微镜和变温介电谱方法,对它们的晶格结构、微观形貌和复介电常数进行了测量和分析.结果表明：1）Zn2＋和Bi3＋进入到Ba0.2Sr0.8TiO3晶格中并与之形成ABO3钙钛矿型固溶体;2）随Bi2O3掺入,陶瓷的室温晶系结构由立方相转变为四方相,同时出现在约120K的弥散相变转化为弛豫相变;3）Bi2O3掺杂对晶粒生长有明显的抑制作用,但晶粒之间的连接性增强,陶瓷的致密度增加;4）当T=300K,f=1Hz,当Bi3＋的掺杂量为0.01mol时,陶瓷样品室温介电常最大（ε＇=1529.95）,此时室温介电损耗值为最大（tanδ=3.366×10-2）.上述结果为该类陶瓷掺杂改性研究,以及弛豫相变机制探索提供参考.     

1,6,7,12,13,18-六氮杂三萘撑的一种新晶型研究:菱形主体通道与客体溶剂分子包结

采用低温X-射线单晶衍射技术测定了化合物1,6,7,12,13,18-六氮杂三萘撑的一种新晶型.研究结果表明,标题化合物1·2CH3OH·2H2O处于正交晶系,Pccn空间群,晶胞参数为a=2.3797(4)nm,b=0.38404(7)nm,c=2.3242(5)nm,V=2.1241(7)nm3,Z=4.每个主体分子1同时与2个甲醇和2个水溶剂客体分子结晶,主体分子之间存在显著的芳环堆积作用,在晶胞中呈平行排列并形成大的菱形通道,客体分子位于此通道中.此外,客体分子之间存在O-H…O氢键相互作用,进一步稳定了此三维超分子结构.     

新型三环己基锡羧酸酯的合成和晶体结构

以苯做溶剂,以2,5-二羧基-1,4-苯二甲酸二乙酯为配体,与三环己基氢氧化锡进行脱水反应,合成了新型三环己基锡羧酸酯配合物1.采用元素分析、1H NMR、红外光谱及X射线衍射等手段对其进行了结构表征,结果表明:配合物1为三方晶系,空间群为R3,a=b=3.039 4(4) nm,c=1.5637(2) nm,α=β=90°,γ=120°,V=12.510(3) nm3,z=9,D(,)=1.248 g/cm3,μ=9.43 nm-1,F(000)=4 878,R1=0.045 2,ωR2=0.090 7.配合物1是Sn原子化学环境相同的对称结构,Sn原子与3个环己基碳原子和1个羧基氧原子成键,中心Sn原子为畸变四面体构型.分子间的O→ Sn(0.3172 nm)配位作用,形成三维网状堆积结构.     

籽晶保护条件下铈掺杂溴化镧晶体生长及其性能

为定向生长出铈掺杂溴化镧（LaBr3:Ce）晶体,改进了坩埚下降法,并在籽晶接种过程引进冷却气体的保护装置。生长出的LaBr3:Ce晶体在137Cs放射源辐照下,其能量分辨率为3.08%,衰减时间为20.1 ns。采用多通道DRS4采集系统,以XP20D0型光电倍增管耦合 Ф 20 mm×5 mm 溴化镧器件作为开始道探测器,H8500型光电倍增管耦合LaBr3:Ce阵列作为被测停止道探测器,放射源为22Na（511 keV）。制备了6×6的LaBr3:Ce阵列,单根晶体条的尺寸为2 mm×2 mm×15 mm。利用数字化波形分析法,获得阵列的清晰二维散点图和一维位置谱,阵列x和y方向的位置分辨率分别为1.01 mm和0.89 mm。制备出的LaBr3:Ce晶体具有优异的能量分辨率和位置分辨率,可以应用于PET等医学成像技术领域。     

毛细管电泳法测定复方乳酸环丙沙星注射液

基于环丙沙星和利巴韦林药物的配伍使用,建立了一种快速分离并同时测定复方乳酸环丙沙星注射液中环丙沙星和利巴韦林配伍药的毛细管区带电泳新方法.选用6×10-2mol/L硼砂作缓冲液,在18 kV电压,20℃条件下5 kPa进样8 s,紫外检测器于275 nm波长下检测乳酸环丙沙星,207 nm波长下检测利巴韦林.结果环丙沙星和利巴韦林的校准曲线在5～100 mg/L内呈良好的线性关系(r0.999 9),复方乳酸环丙沙星注射液回收率为97.2%～110%,相对标准偏差小于2%,日内精密度小于3%,日间精密度小于4%.     

反相高效液相色谱法测定盐酸阿朴吗啡

建立了用反相高效液相色谱测定盐酸阿朴吗啡片剂中盐酸阿朴吗啡含量的方法.用C18(4.6mm×250mm,5μm)柱,甲醇∶0.02mol/LKH     

上转换材料LiLa(MoO4)2:Yb3+,Er3+(Tm3+)的制备及其光谱性质测定

采用溶胶-凝胶法制备了上转换材料LiLa(MoO4)2:Yb3+,Er3+(Tm3+),并对其进行了X射线衍射分析以及荧光光谱测定.在980 nm红外激光器激发下,LiLa(MoO4)2:Yb3+,Er3+发出波长为530 nm和550 nm的绿色可见光,而LiLa(MoO4)2:Yb3+,Tm3+发出波长为475 nm的蓝色可见光.对Yb3+/Er3+和Yb3+/Tm3+双掺体系的上转换发光机理进行了探讨,其中Er3+发出绿色上转换光的过程为双光子过程,而Tm3+发出蓝色上转换光的过程为三光子过程.     

新型红色长余辉发光材料Gd2O2S:EU3+,Si4+,Ti4+的合成及性能表征

采用高温固相反应法首次合成了新型红色长余辉发光材料Gd2O2S:Eu3+,Si4+,Ti4+.用X射线粉末衍射(XRD)、扫描电镜(SEM)、分光光度计等对合成产物进行了分析与表征.结果表明:Gd2O2S:Eu3+,Si4+,Ti4+的晶体结构与Gd2O2S相同,为六方晶系.颗粒的形貌为类球形.Gd2O2S:Eu3+,Si4+,Ti4+的激发光谱呈250～400 nm宽带状,激发光谱主峰位于365 nm;发射光谱为线状光谱,归属于Eu3+的5DJ(J=0,1)→7FJ(K=0,1,2,4)跃迁.最强的发射峰为627 nm和617 nm,均属于5D0→7F2跃迁,且627 nm的发射峰明显远强于617nm,显示出纯正的红色发光;并且Si4+和Ti4+离子的共掺杂可显著延长样品Cd2O2S:Eu3+的余辉时间.     

用光折变扇形效应实现非相干图像的相干转换

利用Ｂａ１－ｘＳｒｘＴｉＯ３光折变晶体的扇形散射效应实现非相干图像的相干转换，得到非相干图像的相干正转换图像，且相干输出图像有很高的保真度，分辩率可达到２８ｌｉｎｋ ｐａｉｒｓ／ｍｍ。