CoFeMg氧化物纳米晶Fenton-降解亚甲基蓝的反应动力学

采用溶胶-凝胶法制备CoFeMg氧化物纳米晶,并用扫描电子显微镜(SEM)和X射线衍射(XRD)表征样品形貌,考察亚甲基蓝催化剂与H2O2的协同降解作用.采用稳态近似法研究氧化降解亚甲基蓝的动力学过程.结果表明:CoFeMg氧化物纳米晶和H2O2组成的Fenton反应体系可有效降解亚甲基蓝,当催化剂和H2O2的加入量分别为0.8g/L和2mmol/L,初始pH≈7.15时,亚甲基蓝的降解率为95%;与传统的Fenton反应体系相比,溶出铁的质量浓度降低为0.2mg/L;Fenton反应是羟基自由基(·OH)氧化降解有机物的过程,其反应可近似为二级动力学反应.     

Fenton试剂氧化降解亚甲基蓝的动力学研究

采用Fenton试剂氧化降解亚甲基蓝,通过对亚甲基蓝染料处理过程中的紫外、红外光谱分析可知,Fenton对亚甲基蓝的结构造成了严重破坏,探讨了Fenton试剂氧化降解亚甲基蓝的反应动力学．结果表明,Fenton氧化过程中,H2O2初始浓度、FeSO4初始浓度及温度对反应都有影响,且确定反应为一级反应,其动力学方程式为：-dC／dt=0．1842exp（-3．53／RT）·[H2O2]始^0.88561·[Fe^2＋]始^0.88519.     

超声协同作用下亚微米掺铝氧化锌催化降解亚甲基蓝的研究

通过溶液直接沉淀法制备了掺Al3+的亚微米氧化锌Zn(Al)O,利用XRD和SEM确定其晶体结构和形貌大小.采用Fenton/Co2+体系,在掺铝氧化锌存在和超声协同下进行降解亚甲基蓝的实验,研究溶液初始pH、H2O2浓度、反应温度、Zn(Al)O投加量、Co2+浓度、亚甲基蓝(MB)浓度等实验条件对MB降解率的影响,并对4种降解方法的效果进行比较. 结果表明：采用Fenton/Co2++Zn(Al)O+超声体系,在H2O2浓度为100 mmol/L,pH5～9,温度30～50C,Co2+浓度0.1～0.3 mmol/L,Zn(Al)O投加量1.0 g/L的条件下降解初始质量浓度达80 mg/L的MB溶液,自然光下超声1h后降解率高达72%. 对其降解机理进行了初步讨论.对掺铝氧化锌循环使用的研究发现,循环1次后降解率为68%, 2次下降到48%.在自然光下降解,该文合成的Zn(Al)O的降解率是P25（降解率约40%）的1.8倍.     

超声波芬顿法协同降解亚甲基蓝的研究

以亚甲基蓝溶液为模型污染物,在超声波芬顿法协同作用下对亚甲基蓝染料废水的降解作用进行了研究,考察了反应时间、H2O2用量、溶液pH值、Fe2+的浓度等因素对亚甲基蓝溶液降解的影响。结果表明,超声波单独降解亚甲基蓝溶液脱色效果不明显,超声波协同H2O2降解亚甲基蓝,加入30%H2O26mL,脱色率约45.80%;溶液pH2.80,Fe2+浓度为30mmol/L时,超声波芬顿法协同降解甲基蓝180min,脱色率达92.70%。试验证明,超声波芬顿法是一种降解亚甲基蓝的有效方法。     

模拟太阳光条件下草酸钠-Fenton试剂降解苯酚

采用氙灯模拟自然条件下的太阳光, 研究了苯酚在草酸钠 Fenton反应体系作用下 的降解规律. 对光源、 H₂O₂、C₂O^2-₄、Fe^{2+的初始浓度以及pH 值对苯酚的去除率的影响进行了探讨. 结果表明, C₂O2-₄能有效强化Fenton试剂对苯酚的作用, 在初始pH值为4、 过氧化氢浓度为0.735 1 mmol/L、 草酸钠浓度为0.074 63 mmol/L、 亚铁离子浓度为0.053 6 mmol/L时, 溶液中0.595 2 mmol/L苯酚在90 min的降解率可达76.5%, 其降解过程符合一级动力学方程. GC MS分析表明, 苯酚降解的中间产物主要为苯醌和有机酸.}     

模拟太阳光下草酸钠-Fenton试剂处理造纸中段水

光助Fenton技术作为一种高级氧化技术,广泛地应用于废水处理的研究中,草酸盐的加入可以改善对光的利用率,提高对废水中有机物的降解能力,降低成本.采用125W荧光高压汞灯模拟太阳光,研究了造纸中段废水在草酸钠-Fenton反应体系作用下的降解规律.讨论了H2O2 、C2O2-4、Fe2+ 的初始浓度以及pH值对中段水CODcr去除率的影响.结果表明,在初始pH值为5、过氧化氢浓度为4.1 mmol/L、草酸钠浓度为4.0 mmol/L、亚铁离子浓度为0.20 mmol/L时, 中段废水的CODcr值在60 min内的去除率可达91.5%.     

活化过硫酸盐技术处理有机染料废水

为了研究不同因素对活化过硫酸盐体系处理有机染料废水的影响,并获得处理效果较好的优化体系,考察过硫酸盐的初始浓度,亚铁离子的浓度以及反应体系中的温度对脱色亚甲基蓝的影响.实验结果表明:热-Na2 S2 O8体系中,[Na2 S2 O8]=8.0 mmol/L,T=70℃时,20 min内亚甲基蓝脱色率达99％;光-Na2 S2 O8体系中,[Na2 S2 O8]=8.0 mmol/L时,90 min内亚甲基蓝脱色率达99％;Fe2+-Na2 S2 O8体系中,当[Na2 S2 O8]=1.2 mmol/L,[Fe2+]=0.20 mmol/L时,20 min内亚甲基蓝的脱色率达99％,增大或减少均导致效率降低.出于综合经济性考虑,热-Na2 S2 O8体系可作为最佳选择体系.     

纳米磁性Fe_3O_4催化H_2O_2氧化降解亚甲基蓝的研究

通过溶液直接沉淀法制备了纳米磁性Fe3O4催化剂,采用粉末X射线衍射、扫描电镜和拉曼光谱对样品进行了表征.以难生物降解的亚甲基蓝(MB)为分子探针,探究了反应溶液的p H、H2O2用量、催化剂用量及MB的初始浓度等因素对其催化氧化降解效率的影响.结果表明:纳米晶Fe3O4是高效的非均相类Fenton催化剂.当催化剂用量为0.5 g·L-1,H2O2浓度为1 mmol·L-1,p H为3.0,反应温度为25℃,反应时间为5 min,可完全降解100 mg·L-1亚甲基蓝.催化剂再生循环实验表明,催化剂重复使用效果好,回收利用方便.     

α-Fe2O3/SA复合薄膜光催化降解亚甲基蓝的条件及机理研究

在光催化反应器中,紫外灯为光源,以α-Fe2O3/SA薄膜(海藻酸钠简记为SA)为例进行亚甲基蓝溶液的降解研究,考察了催化剂用量、溶液的pH值、亚甲基蓝的初始质量浓度及添加少量的H2O2对亚甲基蓝的降解率的影响,进一步探讨了亚甲基蓝的降解机理.结果表明,单一材料中,电子在光催化作用下由亚甲基蓝的中间态D*转移到激发态D+,从而再转移到α-Fe2O3和TiO2导带上;复合材料α-Fe2O3-TiO2/SA对亚甲基蓝的降解为光电催化氧化机制.     

UV/Fenton试剂处理高浓度含酚废水的实验研究

研究UV/Fenton试剂中各个因素对降解高浓度含酚废水的影响,确定UV/Fenton法处理高浓度含酚废水的最佳工艺条件.保持UV/Fenton体系的基准条件不变,通过改变pH值、H2O2浓度、Fe2+浓度、反应时间等实验条件,考察这些因素对UV/Fenton法处理高浓度含酚废水效果的影响.结果表明,UV/Fenton试剂对高浓度舍酚废水有较好的去除效果和较高的反应速率.当苯酚初始浓度为1 000 mg/L时,紫外光波长为253.7 nm,反应时间为25～40 min,pH值为6～7,H2O2浓度为40～50 mmol/L,Fe2+浓度为28～30 mg/L时,苯酚去除率可迭90%以上,满足后续生物降解要求.     

蜂蜜中铁的价态分析

利用邻菲罗琳分光光度法对峰蜜中Fe（Ⅲ）和Fe（Ⅱ）进行了分析．相对标准偏差为1．1％～2．6％，标准加入回收实验的回收率为96％～100．5％．     

Influence of acid leaching and calcination on iron removal of coal kaolin

Calcination and acid leaching of coal kaolin were studied to determine an effective and economical preparation method of calcined kaolin. Thermogravimetric-differential thermal analysis (TG-DTA) and X-ray diffraction (XRD) demonstrated that 900℃ was the suitable temperature for the calcination. Leaching tests showed that hydrochloric acid was more effective for iron dissolution from raw coal kaolin (RCK), whereas oxalic acid was more effective on iron dissolution from calcined coal kaolin (CCK). The iron dissolution from CCK was 28.78wt%, which is far less effective than the 54.86wt% of RCK under their respective optimal conditions. Through analysis by using M?ssbauer spectroscopy, it is detected that nearly all of the structural ferrous ions in RCK were removed by hydrochloric acid. However, iron sites in CCK changed slightly by oxalic acid leaching because nearly all ferrous ions were transformed into ferric species after firing at 900℃. It can be concluded that it is difficult to remove the structural ferric ions and ferric oxides evolved from the structural ferrous ions. Thus, iron removal by acids should be conducted prior to calcination.     

滴定分析法测定铁矿石中铁含量

SnCl2-TiCl3-K2Cr2O7滴定分析法是试样用盐酸加氟化钠加热分解,让有铁的氧化物及硅酸盐都变成氧化铁进入溶液中。先用氯化亚锡将大部分三价铁离子还原成二价铁,以钨酸钠为指示剂,用三氯化钛将剩余的三价铁还原成二价铁至生成"钨蓝",再用重铬酸钾标准溶液氧化至蓝色消失,加入硫磷混合酸以二苯胺磺酸钠为指示剂,用重铬酸钾标准液滴定。通过调节不同的还原酸度,还原温度,试剂用量和溶样时间,对其最佳实验条件进行了优化。用SnCl2-TiCl3-K2Cr2O7滴定分析法测定铁矿石中铁含量,相对标准偏差在0.68%~2.6%之间,回收率在91.9%~97.9%之间,方法准确可靠。     

几种含铁化合物对煤燃烧特性的影响

利用热重－差热－热重微分仪实验研究了几种含铁化合物,如ＦｅＣｌ３、ＦｅＣｌ２和Ｆｅ２Ｏ３等对煤燃烧特性的影响。结果表明,含铁化合物能够发迹煤的燃烧特性,不同种类的含铁化合物对煤燃烧特性的影响不同。ＦｅＣｌ３和ＦｅＣｌ２能够提高煤燃烧过程低温段的燃烧反应速率,其机理是ＦｅＣｌ３和ＦｅＣｌ２起催化剂的作用,改变了燃烧过程化学反应的动力学参数,从而加快了煤的燃烧速率。ＦｅＣｌ３和ＦｅＣｌ２的催化能力随其     

均相Fenton反应对偶氮染料橙黄G氧化脱色的实验研究

开展了均相Fenton反应对偶氮染料橙黄G（简称为OG）废水溶液氧化脱色的实验研究,考察了废水中OG的初始质量浓度、二价铁离子和过氧化氢的投加量以及反应温度和初始pH值对OG脱色的影响.结果表明,均相Fenton法能够有效对OG废水溶液氧化脱色且该脱色反应遵循二级反应动力学方程.随着反应温度升高和pH的适当降低,OG氧化脱色速率增强.若适当降低OG的初始质量浓度,OG氧化脱色率逐渐增大.在保证足够高脱色率的前提下,适当降低Fe2+离子的初始质量浓度,既实现OG脱色达标排放,又满足铁离子的排放限量规定.     

Degradation kinetics and mechanisms of phenolin photo－Fenton process

Phenol degradation in photochemically enhanced Fenton process was investigated in this work. UV-VIS spectra of phenol degradation showed the difference between photo-Fenton process and UV/H2O2, which is a typical hydroxyl radical process. A possible pathway diagram for phenol degradation in photo-Fenton process was proposed, and a mathematical model for chemical oxygen demand (COD) removal was developed. Operating parameters such as dosage of H2O2 and ferrous ions, pH, suitable carrier gas were found to impact the removal of COD significantly. The results and analysis of kinetic parameters calculated from the kinetic model showed that complex degradation of phenol was the main pathway for removal of COD: while hydroxyl radicals acted weakly in the photo-Fenton degradation of phenol.     

反应条件对SnCl_2-TiCl_3-K_2Cr_2O_7法的影响

为了从理论上对矿物质中全铁含量的测定进行深入研究,利用SnCl2-TiCl3-K2Cr2O7法对其实验条件进行了较详细的分析和研究。SnCl2-TiCl3-K2Cr2O7法即试样用盐酸加氟化钠加热分解,让有铁的氧化物及硅酸盐都变成氧化铁进入溶液中。先用氯化亚锡将大部分三价铁离子还原成二价铁,以钨酸钠为指示剂,用三氯化钛将剩余的三价铁还原成二价铁至生成“钨蓝”,再用重铬酸钾标准溶液氧化至蓝色消失,加入硫磷混合酸以二苯胺磺酸钠为指示剂,用重铬酸钾标准液滴定。通过调节不同的还原酸度,还原温度,试剂用量和溶样时间,对其最佳实验条件进行了优化。结果表明,当还原酸度为4．0mol·L^-1,还原温度范围在60--70℃,浓HCI选取30mL进行溶解,溶样时间25min时,测定全铁含量的准确性最高。为SnCl2-TiCl3-K2Cr2O7法准确测定矿物质中全铁含量提供了最佳的实验条件。     

铁屑内电解法处理EDTA络合铜废水的研究

采用以铁屑为阳极材料,活性炭为阴极催化剂的铁屑内电解法处理EDTA络舍铜废水。通过中试装置间歇流实验研究了铁屑内电解法对EDTA络合铜的去除效果及其影响因素;利用连续流试验确定最佳反应条件：pH=1．39,停留时间为20min。最佳条件下铜和COD的去除率分别为96．75％和27．29％。内电解法处理EDTA络合铜废水...