Effect of Al2O3 on the viscosity of CaO-SiO2-Al2O3-MgO-Cr2O3 slags

We investigated the effect of Al2O3 content on the viscosity of CaO-SiO2-Al2O3-8wt%MgO-1wt%Cr2O3(mass ratio of CaO/SiO2 is 1.0,and Al2O3 content is 17wt%-29wt%)slags.The results show that the viscosity of the slag increases gradually with increases in the Al2O3 content in the range of 17wt%to 29wt%due to the role of Al2O3 as a network former in the polymerization of the aluminosilicate structure of the slag.With increases in the Al2O3 content from 17wt%to 29wt%,the apparent activation energy of the slags also increases from 180.85 to 210.23 kJ/mol,which is consistent with the variation in the critical temperature.The Fourier-transform infrared spectra indicate that the degree of polymerization of this slag is increased by the addition of Al2O3.The application of Iida’s model for predicting the slag viscosity in the presence of Cr2O3 indicates that the calculated viscosity values fit well with the measured values when both the temperature and Al2O3 content are at relatively low levels,i.e.,the temperature range of 1673 to 1803 K and the Al2O3 content range of 17wt%-29wt%in CaO-SiO2-Al2O3-8wt%MgO-1wt%Cr2O3 slag.     

Al2 O3和二元碱度对炼钢炉渣中磷酸盐富集机理的综合影响

以六元CaO-SiO2-FeO-P2 O5-Fe2 O3-Al2 O3炼钢渣系为研究对象,结合热力学计算和实验检测,分析( Al2 O3)和二元碱度B综合变化对该六元渣系中磷酸盐富集行为的影响.结果表明：炼钢炉渣中生成游离C2 S含量对磷酸盐富集相nC2 S-C3 P内的( P2 O5)至关重要.该渣系中增加SiO2会降低总的C2 S生成量,增加Al2 O3可促进钙铝黄长石C2 AS相生成,降低游离C2 S ( f-C2 S)的量,进而影响磷酸盐的富集.六元CaO-SiO2-FeO-P2 O5-Fe2 O3-Al2 O3炼钢炉渣获得较好磷酸盐富集程度,渣中二元碱度B和Al2O3含量需满足的耦合关系为：(%Al2O3)=-27.70+21.62B,(Al2O3)<20.0%,B>1.3.     

CaO-Al2O3-CaF2-SiO2渣系的黏度

采用内旋转圆柱法测量了不同组成的CaO-Al2O3-CaF2-SiO2渣系的黏度,采用XRD分析技术对高温熔炼渣的物相进行分析,并计算了各渣样的黏流活化能.结果表明:当w(CaO)/w(Al2O3)一定,配渣中SiO2质量分数低于8%时,对渣样的高温黏度并没有明显的影响,在1 490℃以上时,熔渣黏度都低于0.5Pa.s;当SiO2质量分数增加到10%,渣样的高温黏度开始显著降低,温度高于1 440℃时,黏度值低于0.2Pa.s.随着SiO2含量的增加,熔渣的碱度逐渐降低,破坏了原来熔渣的大网状结构,熔渣的黏度明显降低.渣系的黏流活化能变化趋势与渣样的黏度值变化趋势一致.     

MgO含量对CaO-Al2O3-MgO-FexO-SiO2-K2O系熔体性质的影响

研究了MgO含量变化对CaO-Al2O3-MgO-FexO-SiO2-K2O系熔体黏度和熔化特性的影响,结合X射线衍射和扫描电镜分析熔渣冷却过程中的物相析出,并通过FactSage软件计算了该体系的黏度、熔点和冷却过程中析出相的含量与温度的关系,并与实验结果进行了对比和分析.结果表明,MgO含量的增多会造成熔渣熔化温度的升高,黏度随温度变化时会出现黏度骤增的转折点,高于转折点温度时,熔渣黏度随MgO含量变化不大,同时该转折点温度随MgO含量的增加而升高.在熔渣冷却过程中析出相主要为固溶的橄榄石相和Fe3O4尖晶石相,MgO含量的增大可以促进橄榄石相的析出,熔体黏度骤增主要由于橄榄石相的析出造成的.     

CaO-SiO2-Al2O3-MgO-V2O5渣系中钒熔融还原动力学

实验室条件下, 进行了碳饱和铁水还原CaO-SiO2-Al2O3-MgO-V2O5渣中V2O5反应的动力学研究. 在考察了各种因素对还原反应速度和反应程度影响的基础上,进一步探讨了还原反应机理,计算了各种条件下的表观速度常数. 研究表明:高温、合适碱度、大铁渣比以及高初始V2O5含量,使得还原反应进行得较快,效果较好. 反应达到平衡之前,还原反应为表观一级反应. 计算得到还原反应的表观活化能为23.21kJ·mol-1,表明反应的限制性环节为铁液中V的扩散传质.     

Dissolution and diffusion of TiO2 in the CaO-Al2O3-SiO2 slag

The dissolution of TiO2 in the CaO-Al2O3-SiO2 slag under static conditions was studied in the temperature range from 1643 K to 1703 K. After TiO2 dissolved, the microstructure of the interface between TiO2 and the slag was observed by scanning electron microscopy, and the concentration profiles of Ti4＋and other ions across the TiO2/slag interfaces were analyzed by energy-dispersive X-ray spectroscopy. On the basis of these results, the dissolution behavior of TiO2 was evaluated, and the diffusivity of Ti4＋in the bulk slag was estimated. Ac-cording to the Stokes-Einstein relation, the viscosity calculated by a previously reported model gave a diffusivity of Ti4＋ions greater than that estimated by the concentration profiles of Ti4＋ions. The mechanism of TiO2 dissolution in the CaO-Al2O3-SiO2 slag is discussed in de-tail.     

稠油油溶性降黏剂ASAM/C/O的合成与评价

分析了造成稠油高黏的原因及降黏剂的降黏机理,对降黏剂的分子结构进行设计.先以丙烯酸(A)、苯乙烯(S)、丙烯酰胺(AM)为原料合成了中间产物——三元共聚物ASAM,然后以ASAM、多元醇、长链烷基酸为原料通过两步酯化反应合成了一种稠油油溶性降黏剂ASAM/C/O.通过正交实验确定出中间产物ASAM的最佳合成条件:单体质量比m(丙烯酸)∶m(苯乙烯)∶m(丙烯酰胺)为6∶3∶2,引发剂质量分数1.3%,反应时间为6 h.降黏剂ASAM/C/O的最佳合成条件∶m(ASAM)∶m(C)∶m(O)取6∶2∶1.5,长链烷基酸的碳链长度取18,反应温度在110～120℃之间,反应时间为6 h左右.降黏剂ASAM/C/O具有较好的降黏效果;降黏率与温度有关,随温度降低,降黏率升高;加剂处理后稠油体系的活化能大幅度降低,说明体系内的结构强度减弱.     

对甲氧基苯乙酮与人血清白蛋白相互作用的研究

在模拟生理条件下应用荧光光谱、紫外—可见吸收光谱和傅立叶变换红外光谱方法研究了人血清白蛋白(HSA)与对甲氧基苯乙酮的相互作用。通过Stern—Volmer方程求算出在不同温度下(304,307,310 K)的淬灭常数分别为7.64×103,7.68×103和7.73×103L.mol-1,证实了HSA与对甲氧基苯乙酮相互结合作用为动态淬灭过程,并且得到活化能Ea为0.998 kJ.mol-1。与对甲氧基苯乙酮作用后HSA的同步荧光光谱和红外光谱的现象说明HSA的疏水环境降低,并且二级结构发生了由α-螺旋向β-折叠的转化。     

黑木耳、银耳、黑牛肝菌的红外光谱研究

利用傅里叶变换红外光谱仪对三种食用菌(黑木耳、黑牛肝菌、银耳)样品进行了研究。三种菌的光谱各具特征，黑木耳和银耳光谱主要谱峰相似，但与黑牛肝菌的光谱区别较大；根据吸收强度比可以将黑木耳和银耳区分开。光谱结果还显示，三种食用菌多糖，既有α糖苷键，也有β糖苷键。红外光谱具有快速、简便、不需对样品进行分离提取等优点。     

MgO对高铝高炉渣脱硫的影响及其动力学分析

随着廉价高铝铁矿石的不断使用,高炉炉渣内Al2O3含量也随之升高,这势必会影响高炉炉渣的各项冶金性能。为深入研究高铝高炉渣脱硫性能,明确MgO含量对高铝渣脱硫性能的影响,笔者通过改变高铝渣中MgO的含量,分别设定渣中MgO含量为5%、9%、13%MgO,研究不同MgO含量高炉高铝渣的脱硫性能及其脱硫动力学。结果表明:MgO含量不仅对高铝渣的黏度、脱硫能力有不同的影响,还使炉渣的脱硫速率发生了很大的改变。MgO含量越高对应的黏度越低,脱硫能力越大;但脱硫速率却表现出了不同规律,9%MgO的脱硫速率表现为最大;经过综合比较,当碱度固定为1.1、Al2O3含量固定为17%时,MgO含量为9%的炉渣同时具有较好的粘度和脱硫性能。     

FeO和Al2O3质量分数对高炉初渣粘度的影响

以高铝烧结矿在高炉软熔滴落过程中形成的高炉初渣为主要研究对象,在实验室条件下采用分析纯试剂进行初渣的制备,分别探讨了CaO-SiO_2-MgO-Al_2O_3-FeO五元渣系中,FeO(5%~15%)及Al_2O_3(6%~15%)质量分数对初渣粘度和熔化性温度的影响规律。实验结果表明:在碱度(CaO/SiO_2)为2.0时,炉渣粘度随FeO质量分数的增加而减小,且FeO质量分数越多,炉渣的熔化性温度越低;当FeO质量分数为5%时,随着Al_2O_3质量分数的增大,炉渣粘度和熔化性温度都呈降低的趋势。     

pH值对鲑鱼降钙素溶液构象的影响

采用傅里叶变换红外光谱和圆二色谱,测定鲑鱼降钙素在不同pH值水溶液中的构象,并对各种二级结构的含量进行计算.结果表明pH值对鲑鱼降钙素溶液构象有较大影响,pH值从2.0升高到8.0时鲑鱼降钙素溶液中存在β-折叠、β-转角和无序结构,无α-螺旋结构,且各种二级结构的含量随pH值增加而发生变化.当pH值增加到9.0时鲑鱼降钙素溶液中出现α-螺旋结构,且β-折叠和无序结构含量降低到最小值,β-转角含量增加到最大值.以上研究结果提示较低的pH值有助于鲑鱼降钙素的稳定,为进一步阐明pH值对鲑鱼降钙素稳定性的影响提供了依据.     

TiO2对含铬高钛熔分渣熔化性能和黏度的影响

A study on the melting and viscosity properties of the chromium-containing high-titanium melting slag (CaO–SiO₂–MgO–Al₂O₃–TiO₂–Cr₂O₃) with TiO₂ contents ranging from 38.63wt% to 42.63wt% was conducted. The melting properties were investigated with a melting-point apparatus, and viscosity was measured using the rotating cylinder method. The FactSage 7.1 software and X-ray diffraction, in combination with scanning electron microscopy–energy-dispersive spectroscopy (SEM–EDS), were used to characterize the phase equilibrium and microstructure of chromium-containing high-titanium melting slags. The results indicated that an increase in the TiO₂ content led to a decrease in the viscosity of the chromium-containing high-titanium melting slag. In addition, the softening temperature, hemispheric temperature, and flowing temperature decreased with increasing TiO₂ content. The amount of crystallized anosovite and sphene phases gradually increased with increasing TiO₂ content, whereas the amount of perovskite phase decreased. SEM observations revealed that the distribution of the anosovite phase was dominantly influenced by TiO₂.     

B2O3对高铝钢连铸保护渣理化性能的影响

高铝钢连铸过程中,为了避免或减轻钢液中Al与保护渣中SiO2发生反应,设计了低SiO2、高Al2O3含量的高铝钢连铸保护渣,通过添加适量的酸性氧化物B2O3协调熔渣酸碱性,利用实验分析了B2O3含量对高铝钢保护渣熔融特性、黏度特性及渣膜传热特性的影响。结果表明,B2O3含量在4%～10%时,随着B2O3含量增加,保护渣熔化温度、黏度、黏流活化能均降低,渣膜热流密度增加;保护渣的等温转变曲线(TTT曲线)向孕育时间增加的方向移动,晶体生长速率降低;实验条件下,增加B2O3含量可抑制保护渣中CaF2的析出。     

蒙脱石中Al2O3的盐酸溶出过程动力学研究

酸溶法是目前对蒙脱石进行活化处理的主要方法之一。文章首先分析了影响酸溶速率的主要因素,并在得出的最佳溶出条件下对Al2O3的溶出速率进行研究;结果表明,蒙脱石结构中Al2O3的盐酸溶出过程适用平板-内扩散控制模型,其浸出率X对反应时间t的关系可表示为(1-X)2=-kt;其表观活化能约为24.3 kJ/mol。     

MgO、PbO对LMAS系微晶玻璃温度系数的影响

研究了不同PbO和MgO质量分数以及不同的热处理温度对SiO2Al2O3MgOLa2O3微晶玻璃系统谐振频率温度系数的影响。结果表明,PbO和MgO质量分数分别为10%和12.3%,温度在850℃下热处理10 h时,样品的谐振频率温度系数为75.9×10-6/℃     

MgO/MgCl2摩尔比与添加剂对菱苦土制品强度的影响

论述通过正交试验法对MgO和氯化镁摩尔比以及硅粉对菱苦土磨具强度的影响规律.在菱苦土结合剂中,活性MgO含量对制品的性能影响极大,同样,合适的卤水密度也很重要,MgCl2浓度过高时,过多的MgCl2与MgO生成复盐,磨具体积收缩产生裂纹.MgCl2浓度过小时,材料硬化不充分,强度不够.当MgO/MgCl2的摩尔比为4～6时,磨具能获得最大的强度,此时主要的微观结构是5MgO.MgCl2.8H2O.硅粉能与氯氧镁水泥中的MgO发生化学反应,形成硅酸盐凝胶,可提高磨具的致密度和强度,改善耐水性.     

氨基二氧化硅固定化纤维素酶及其特性

以氨基化二氧化硅为载体, 戊二醛为交联剂, 采用共价交联法制备固定化纤维素酶, 最佳条件为交联剂浓度4% (体积比), 交联时间60分钟, 给酶量35 U/g载体, 固定化反应时间5小时。所得固定化酶对pH和温度的敏感性降低, 时间稳定性和热稳定性均优于游离酶。热动力学研究表明, 固定酶的失活活化能(Ed)、失活焓(ΔH^*)和失活自由能(ΔG^*)均高于自由酶, 固定化减小酶失活反应速率, 降低酶失活反应趋势。     

Effect of TiO2 on the viscosity and structure of low-fluoride slag used for electroslag remelting of Ti-containing steels

The viscosity of CaF2–CaO–Al2O3–MgO–(TiO2) slag was measured using a rotating crucible viscometer. Raman spectroscopy analysis was performed to correlate the viscosity to slag structure. The viscosity of the slag was found to decrease with increasing TiO2 con-tent in the slag from 0 to 9.73wt%. The activation energy decreased from 95.16 kJ/mol to 79.40 kJ/mol with increasing TiO2 content in the slag. The introduction of TiO2 into the slag played a destructive role in Al–O–Al structural units and Q4 units by forming simpler structural units of Q2 and426TiO- chain. The amount of Al–O–Al significantly decreased with increasing TiO2 content. The relative fraction of4Q units in the [AlO4]5?-tetrahedral units shows a decreasing trend, whereas the relative fraction of2Q units and426TiO- chain increases with increasing TiO2 content accordingly. Consequently, the polymerization degree of the slag decreases with increasing TiO2 content. The varia-tion in slag structure is consistent with the change in measured viscosity.     

TiO_2含量对低镁含锰渣的流动性和热力学性质的影响

为探究钛矿护炉和锰矿洗炉条件下TiO_2对炉渣流动性和热力学性质的影响机理,本文通过黏度实验和FactSage热力学软件计算,分析了不同TiO_2含量低镁含锰渣的黏度和熔化温度、热焓及活度等热力学性质变化。结果表明,随着TiO_2含量的增加,炉渣黏度、熔化性温度和完全熔化温度降低,炉渣的流动性和热稳定性改善。炉渣热焓和液相中的TiO_2活度随TiO_2含量的增加而增大,而热焓的增大将增加高炉的热量消耗和燃料比。在冷却结晶过程中,TiO_2含量的增加有利于增大钙长石、钙钛矿和橄榄石等物相的析出量,而黄长石和硅灰石的析出量则随TiO_2含量的增加而降低。