纳米BiOBr/I复合材料的合成及其对有机物的光催化降解性能

采用沉淀——离子交换法合成了BiOBr/I复合材料,通过降解有机物染料罗丹明B考察了其光催化性能.研究表明:BiOBrI-1复合材料是由BiOBr纳米片直接插入BiOI纳米微球所得,其具有更强的光催化性能的原因在于复合材料独特的微观形貌特性以及有效复合后的连续共溶体具有的合适能带值和BiOBr含量比率.     

Synthesis of magnetically recoverable visible-light-induced photocatalysts by combination of Fe_3O_4/ZnO with BiOI and polyaniline

Magnetically recyclable photocatalysts with efficient performances under visible light were synthesized by combining Fe_3O_4/ZnO with BiOI and polyaniline(PANI). The FT-IR, XRD, HRTEM, SEM, EDX, XPS, UV–vis DRS,VSM, BET, and PL instruments were utilized for characterization of the as-prepared products. The activity tests exhibited that the superior rate constant in photocatalytic performance was achieved over the Fe_3O_4/ZnO/BiOI/PANI(20%) nanocomposite, which enhanced for more than 59.9, 10.0, and 6.57 times, as compared to those of the Fe_3O_4/ZnO, Fe_3O_4/ZnO/PANI, and Fe_3O_4/ZnO/BiOI photocatalysts in degradation of RhB, respectively.Successful photocatalytic degradations of MO/MB and photo reduction of Cr(VI) were also investigated to confirm the potential application of the photocatalyst in removal of various pollutants. The considerably enhanced activity pointed to a promoting effect of p-n-p heterojunctions formed between PANI, ZnO, and BiOI, and improved textural characteristics, which are benefit for improvement of the photocatalytic performances.     

叶片状CuO/BiVO4的合成及可见光催化性能研究

以Bi(NO3)3.5H2O和NH4VO3为原料,P123为表面活性剂,辅助水热法在反应液pH值为6,7,9和10时合成了4种CuO/BiVO4复合光催化剂。并采用X-射线衍射(XRD)和扫描电子显微镜(SEM)对样品的晶相和形貌进行了表征。以亚甲基蓝作为降解物,研究了所制备样品的可见光催化活性。结果表明,pH=6时所制备的样品为单斜相BiVO4复合材料,具有叶片状形貌,其光催化活性最强;样品的降解率随着亚甲基蓝溶液的pH值增大而增大,当pH=10时,可见光照射120 min后,样品对初始溶度为20 mg/L的亚甲基蓝溶液的降解率可达95%。     

Au/Cu_(1.94)S/ZnS纳米复合物的制备及其光催化性能研究

在油胺中合成Cu1.94S/ZnS,并将其分散到乙醇溶液中在磁力搅拌下与金纳米粒子复合,制备了Au/Cu1.94S/ZnS三元纳米复合物,利用X射线衍射仪(XRD)、透射电子显微镜(TEM)、紫外可见分光光度计(UV-Vis)等分析测试手段对所得产物进行表征,考察了在可见光下Au/Cu1.94S/ZnS纳米复合物对染料RhB的光催化降解性质.结果显示:Au/Cu1.94S/ZnS纳米复合物具有优异的光降解性能.     

BiOI-TiO2复合材料光催化降解双酚A的研究

采用 Triton X-100/正己醇/环己烷/水的微乳体系合成了一系列BiOITiO2的纳米材料，分析了其晶体结构、表面结构和光谱特征，探讨了可见光光催化降解双酚A废水的可行性.结果表明: BiOI-TiO2的分散性能好、比表面积大.光催化结果表明，复合材料中BiOI与TiO2的摩尔比对光催化性能影响很大且比值达到75%时效果最好，光催化降解机理符合一级动力学方程，反应速率常数（kobs）与催化剂投加量及初始pH值有关.催化剂重复多次使用的降解效果稳定.     

BiOI/H2O2协同光催化降解四环素性能研究

碘氧铋（BiOI）是一种新型光催化剂,以硝酸铋（ Bi (NO₃)₃）、碘化钾（KI）为原料,分别采用水热法以及溶剂热法制备两种形貌的BiOI材料,通过X射线粉末衍射仪（ XRD）、扫描电子显微镜（SEM）、红外光谱（ FTIR）、紫外可见漫反射（ UV-Vis DRS）和N₂吸脱附测试仪对其进行形貌、结构、性能表征。以四环素（TC）水溶液为例,测试制得的BiOI光催化降解性能,重点考察材料结构、光照条件、双氧水（H₂O₂）协同作用等对降解性能的影响。实验结果表明,溶剂热法制备的BiOI和H₂O₂协同作用时,在模拟太阳光下对四环素降解效果最好,4 h降解率可达99.11%。     

CeO2/CNTs复合光催化剂的制备及其对抗生素废水光催化降解研究

以多壁碳纳米管(MWCNTs)为载体,硝酸锶铵为锶源,采用水热法制备CeO2/CNTs复合管光催化剂．采用场发射扫描电子显微镜(FE．SEM)对碳纳米管负载CeO2前后的形貌进行了的表征;以阿莫西林溶液的降解为目标反应,考察了催化剂的紫外光、可见光(A>420 nm)催化活性．结果表明：所制备的催化剂基本保持了原始MWCNTs的纤维状形貌,二氧化锶在MWCNTs表面分布均匀,MWCNTs增强了污染物在催化剂表面的吸附,提高了对光的吸收和利用,因此所制备的CeO2／MWCNTs复合光催化剂表现出较高的光催化活性．     

金红石与针铁矿光催化材料结构与性能的关联

以TiCl4为钛源,针铁矿（α-FeOOH）为载体,采用水解沉淀法制备了金红石（TiO2）与α—FeOOH光催化材料．应用x射线衍射分析、扫描电子显微镜和透射电子显微镜对样品的晶相组成、形貌、微结构进行了表征．结果表明,制备温度对样品的晶相组成、形貌、颗粒大小和结构有明显的影响．随着制备温度升高．样品中α-FeOOH相的含量逐渐减少并最终消失,而金红石相TiO2的含量逐渐增加并最终全部金红石相TiO2;样品的形貌由棒状变为管状;复合材料的结构实现负载型→复合型→溶蚀复合型转变．应用紫外和模拟可见光谱对样品光性能进行了测试．样品对可见光的吸收得到了增强．在室温下以甲基橙为降解对象,分别在紫外光和模拟可见光照射下对样品光催化活性进行了评估．复合型和溶蚀复合型结构样品的活性均得到了不同程度的提高,而负载型结构样品的活性没有明显变化：在紫外及可见光照射下,样品对甲基橙的光催化降解效果较好,溶蚀复合型结构样品的活性最高．这说明样品的性能与结构有良好的关联性．     

水解沉淀法制备氮掺杂TiO_2可见光光催化剂

为拓展TiO2可见光的响应范围,以氨水为氮源,在常温条件下采用水解沉淀法制备了氮掺杂TiO2粉末。以X射线衍射、紫外-可见漫反射吸收光谱和X射线光电子能谱等对TiO2进行了表征。对可见光照射下的光催化活性进行了测试,并考察了煅烧温度及掺杂量等对光催化活性的影响。结果表明:氮掺杂致使TiO2吸收边带向可见光区偏移,在降解亚甲基蓝的实验中表现出良好的可见光催化活性;随煅烧温度的增加,氮摩尔分数增加,晶粒增大,可见光催化活性减弱;煅烧温度为400℃,氮的摩尔分数为2%时制备样品的光催化活性最高。     

Synthesis of Porous Hollow Micro spheres of BiVO_4 Based on EDTA and SDBS via Hydro thermal Method

Porous hollow microspheres of bismuth vanadate(BiVO_4) were successfully synthesized with the assistances of ethylenediamine tetraacetic(EDTA) and sodium dodecylbenzene sulfonate(SDBS) via hydrothermal method.The as-prepared BiVO_4 samples were characterized by X-ray diffraction(XRD),field-emission scanning electron microscopy(FE-SEM) and UV-vis diffuse reflectance spectra(DRS).It was found that the ratio of EDTA and SDBS had a significant impact on the crystalline structure,size and morphology of BiVO_4 photocatalyst.The crystal phase could be adjusted by changing the mass ratio of EDTA and SDBS.The photocatalytic activities of different BiVO_4 samples were investigated through the degradation of RhB in the presence of H_2O_2 under visible light irradiation.The results indicated that the photocatalytic performance of the BiVO_4 microstructures was greatly influenced by the porous structure,morphology and band gap.The BiVO_4 sample prepared with the EDTA and SDBS ratio of 2:1 and total amount of 1.5 g have shown superior photocatalytic performance for its unique morphology,good porous structure and low band gap energy.     

氢氧根辅助氧化亚铜的形貌控制合成及其性质研究

采用简单的室温液相还原法,通过调节OH-的浓度,成功合成了Cu2O纳米颗粒和微米立方块.利用XRD、FT-IR、SEM等手段对产物进行了表征.研究了OH-浓度对Cu2O{100}面生长情况的影响,并探讨了两种形貌Cu2O的形成机理.利用固体紫外可见光谱测得不同形貌Cu2O的带隙能,微米立方块状Cu2O的带隙能小于纳米小颗粒的带隙能.研究了两种不同形貌的Cu2O的光催化降解甲基橙的性能,Cu2O微米立方块和Cu2O纳米颗粒对甲基橙的降解率分别为98.1%和71.4%,前者的光催化效果明显高于后者.光致发光光谱分析表明,Cu2O微米立方块的光致发光光谱强度较低,具有低的电子-空穴对复合率和高的电子-空穴对分离度.此外,还对Cu2O的抑菌性能进行了初步研究.     

纳米TiO_2光催化改性研究

研究了不同类型(非金属、稀土金属、过渡金属)的掺杂元素对TiO2在可见光下的光催化活性的影响。采用XRD对其结构进行表征,以结晶紫为目标降解物,使用紫外-可见分光光度计测试了不同掺杂TiO2在可见光下的光催化性能。     

F掺杂膨润土负载PbSnO_3复合光催化剂的制备及对亚甲基蓝的光催化降解性能

以NH_4F为氟源、膨润土为载体,采用水热合成法制备出了F掺杂膨润土负载PbSnO_3复合光催化剂.采用XRD、IR、SEM等分析手段对样品的形貌和结构进行了表征.并在可见光条件下,以亚甲基蓝溶液作为目标降解物,研究了其光催化性能.结果表明:当光照时间为12 min、F掺杂质量分数为0.04%、光催化剂用量为40mg/L时,其对亚甲基蓝溶液降解效率最高,降解率超过97%.     

钛掺杂BiFeO3光催化剂的制备及其催化性能

用溶胶-凝胶法制备钛(Ti)掺杂BiFeO₃纳米颗粒(Ti-BiFeO₃), 研究不同煅烧温度对Ti掺杂BiFeO₃结构调控及光催化性能的影响, 用X射线衍射（XRD）、 扫描电子显微镜（SEM）、 能谱分析（EDS）、 紫外-可见（UV-Vis)光谱技术对颗粒的相结构、 形貌、 原子比例、 光催化性能等进行测试及分析, 并以罗丹明-B为目标降解物, 对Ti掺杂BiFeO3光催化性能进行研究. 结果表明: Ti掺杂BiFeO₃样品在不同煅烧温度均出现Bi₂Fe₄O₉相; 煅烧温度可对Bi₂Fe₄O₉的含量进行调控, 在650 ℃煅烧样品中含有适量的Bi₂Fe₄O₉相, 能有效提高Ti掺杂BiFeO₃的光催化活性, 且具有较高的降解活性, 60 min内降解效率达85%.     

分层铜锌锡硫纳米结构的合成及其光催化性能研究

采用溶剂热法合成了分层结构的铜锌锡硫（CZTS）纳米结构,用X射线粉末衍射（XRD）、扫描电子显微镜（SEM）、紫外可见分光光度计（UV-Vis）、拉曼光谱等现代表征手段对样品进行表征,并以亚甲基蓝（MB）染色剂的模拟废水为目标污染物,探讨了CZTS纳米结构在可见光照射下的光催化性能.在10h可见光催化反应后,CZTS分层纳米结构对MB的降解率高达93.6％.对比实验研究表明,采用类似方法制备的CZTS无规则纳米粒子对MB的降解率仅为51.6％,表明分层CZTS纳米结构具有优异的光催化性能.我们对分层CZTS纳米结构的光催化性能进行了合理的解释.     

Cu2O/Bi2MoO6耦合系统增强光催化活性研究

采用乙二醇为溶剂,成功合成了耦合系统Cu2O/Bi2MoO6,分别采用X射线衍射(XRD)、拉曼光谱(Raman)、X射线光电子能谱分析(XPS)和透射电子显微镜(TEM)进行表征.样品的光催化活性通过在可见光下降解结晶紫来获得.结果表明,当Cu与Mo摩尔比为0.08,Cu2 O/Bi2MoO6展示出最高的光催化性能,仅在100 min结晶紫的降解率达到95.6％.同时,研究了耦合系统中Cu2O的量对其光催化活性的影响,并提出了合理的反应机制.     

铟氮共掺杂氧化锌在可见光下的光催化活性

铟氮共掺杂氧化锌采用两步法合成,首先采用共沉淀方法制备铟离子掺杂的氧化锌,然后采用氨气中退火的方法制备铟氮共掺杂氧化锌.研究表明共掺杂样品比只掺杂氮的样品具有更多的可见光吸收.采用可见光下对异丙醇的降解来评价样品的光催化活性.研究结果表明在氮离子和0.5%铟离子掺杂下具有最好的光催化活性.     

WO3纳米片的制备表征及其可见光下降解罗丹明B的研究

通过水热合成法制备氧化钨（WO₃）纳米片,采用扫描电子显微镜（SEM）、固体紫外漫反射（UV-vis）和X 射线光电子能谱（SEM-EDX）对WO₃纳米片进行表征,并通过实验研究了可见光下WO₃对溶液中罗丹明B（RhB）染料废水的光催化降解性能。实验结果表明：WO₃投加量为0.10g时,在150W氙灯模拟可见光照射4h条件下,对质量浓度为10mg/L,体积为100mL罗丹明B染料废水的光催化降解率达到88.3%。此结果说明制备的WO₃催化剂对罗丹明B染料废水具有良好的光催化活性。     

SDS对所制备的TiO2可见光催化活性的影响

十二烷基磺酸钠(SDS)辅助TiCl4水解,成功地制备了纯二氧化钛光催化剂(TPC),利用透射电子显微镜、X射线衍射、紫外-可见光谱及氮气吸附/脱附对所有的TPC进行了表征.光催化活性测试结果表明:所制备的样品可见光催化降解甲基橙的活性均好于P25,且随着TiCl4与SDS物质的量比增大,催化降解效率提高.SDS的存在有助于通过调控颗粒间的作用强度来调控高能氧桥键的分布,从而调控可见光催化活性;活性晶面的暴露也利于光催化活性的提高.使用TiCl4与SDS物质的量比为51.2的TPC4,在可见光(35 W普通民用光源)下照射3h,甲基橙降解率高达74.4%,预示其在光催化自清洁内墙涂料方面具有潜在的应用前景.     

碳纳米管-二氧化钛纳米复合材料的制备、表征及其光催化性能

为了提高二氧化钛在可见光下的光催化活性,本文采用溶胶—凝胶溶剂热法制备不同负载量的碳纳米管—二氧化钛(CNTs-Ti O)纳米复合材料,采用扫描电子显微镜(SEM)2、透射电子显微镜(TEM)、X-射线衍射(XRD)等对该复合材料形貌和晶型的结构进行表征;对比CNTs-Ti O2和市售Ti O(P25)UV-vis2图谱,结果显示P25只能吸收单一的紫外光,而CNTs-Ti O2则在紫外和可见光下均有良好的光吸收性,并且随着CNTs含量的增加,CNTs-Ti O2对光的吸收性能越好;采用降解亚甲基蓝(MB)溶液研究CNTs-Ti O2的光催化活性,实验结果表明CNTs-Ti O2在可见光下具有良好的光催化性能。上述结果表明可以将CNTs-Ti O2纳米复合材料应用于降解工业废水污染物。