热轧和退火温度对SP-700合金组织和力学性能的影响

The effect of rolling temperature on both two- and single-phase regions and annealing in a temperature range of 700–950°C on the microstructure and mechanical properties of Ti?5Al?4V?2Fe?1Mo alloy was investigated. The results indicated that the best balance of strength and ductility is obtained by rolling in the two-phase region due to the globularization of the alpha phase and increase in its volume fraction. After rolling in the two-phase region, the ductility of the specimens annealed at 700 to 800°C increased because of the finer size and globularized alpha phase, while the reduction in strength was attributed to a decrease in the alpha phase volume fraction. However, at 950°C, the strength increased and ductility dropped by the formation of acicular alpha phase due to an increase in the phase boundary area. Annealing and aging after rolling in the beta-phase region increased the strength and decreased the ductility, which is attributed to the formation of a secondary alpha phase. A combination of favorable yield strength (1113 MPa) and elongation (13.3%) was obtained through rolling at 850°C followed by annealing at 750°C and aging at 570°C.     

热轧温度对铝合金电工圆杆组织和性能的影响

本文采用抗拉强度、导电率性能测试和扫描电镜(SEM)等分析方法研究了不同梯度的热轧温度对La-Ce-Y-Cu铝合金电工圆杆显微组织及性能的影响。结果表明:随着热轧温度的升高,晶粒内部的析出相逐渐偏聚于晶界,其导电率呈明显增加趋势,热轧温度为150℃时,其导电率达到58.6%IACS,而抗拉强度在低温(23～100℃)轧制过程中变化不大,基本维持在158 Mpa左右。热轧温度持续升高,热轧后的析出相尺寸显著细化,弥散分布于晶界与晶内,其导电率呈先减后增的趋势,而抗拉强度不断下降。经400℃热轧处理合金导电率基本维持稳定,约为59. 2%IACS,抗拉强度值约为131 Mpa,相比于峰值强度降低了37 Mpa。     

铝含量和退火温度对锆铝合金组织性能的影响

为丰富空间结构材料种类,扩大Zr合金的应用范围,利用非自耗电弧炉熔炼了Al含量分别为2%,3%和4%（质量分数）的Zr-Al二元合金,在真空管式炉内分别进行750 ℃和800 ℃保温4 h的退火处理,借助光学显微镜、X射线衍射仪、扫描电子显微镜分析合金的微观组织和断口形貌,并进行硬度测定和拉伸试验。结果表明：经750 ℃保温4 h退火处理后,Zr-4Al合金的铸态组织由α-Zr和Zr₂Al转变为α-Zr和塑性更好的Zr₃Al相;在相同热处理条件下,随着Al含量的增加,合金的硬度及抗拉强度升高,延伸率下降;当Al含量相同时,随着热处理温度的升高,合金硬度、抗拉强度及延伸率下降。因此,采用向Zr中添加适量Al元素并辅之热处理的方法,可制备一种新型的Zr-Al合金,为开发新型空间结构材料提供了一种新思路。     

热轧工艺中加热温度对IF钢组织性能的影响

选取Ti-Nb-IF钢热轧工艺中的加热温度为影响因素,采用显微观察、TEM二相粒子分析、织构分析等实验分析手段,研究了1 140℃和1 214℃两种热轧加热温度制备的Ti-Nb-IF钢样品在随后的冷轧、退火和平整过程中显微组织演变和织构演变特征的影响及最终产品的力学性能.结果表明,低温加热有利于IF钢屈强比的降低及深冲性能的提高,加热温度为1 140℃比1 214℃,其屈服强度可降低30 MPa,塑性应变比可提高0.16.其主要原因为低温加热工艺保障IF钢热轧后产生粗大的二相粒子和细小铁素体晶粒,在随后的冷轧和退火处理过程中产生分布均匀和强的γ再结晶织构.     

退火温度对退火马氏体基TRIP钢显微组织和力学性能的影响

将C-Si-Mn系TRIP钢通过完全淬火和两相区退火相结合的工艺,得到一种以退火马氏体为基体的TRIP钢(简称TAM钢),并对比分析了TAM钢在不同温度退火后的显微组织和力学性能.结果表明,TAM钢经退火后的显微组织特征为精细规整的板条退火马氏体基体、片状残余奥氏体和贝氏体/马氏体组成的混合组织.这种组织降低了基体的硬度以及基体和第二相之间的强度比,减少了基体的位错密度.随着退火温度的提高,退火马氏体基体的板条形态逐渐消失,新生马氏体/贝氏体的团状混合组织逐渐增多.当退火温度为780℃时,综合力学性能优异,抗拉强度为1130 MPa,延伸率可达20%,强塑积为22600 MPa·%.当退火温度较低时,残余奥氏体主要以片状存在于退火马氏体板条间,有利于TRIP效应的发生.     

控轧温度区间对含Nb热轧多相钢组织和性能的影响

以含Nb微合金化试验钢为研究对象,通过3个不同精轧温度区间的轧制+层流冷却、空冷、超快冷的TMCP工艺获得了含有铁素体、贝氏体、马氏体以及少量残余奥氏体的显微组织.分析了控轧温度区间对含Nb微合金化试验钢显微组织和力学性能的影响.结果表明,在控冷工艺参数相近的情况下,随着精轧开轧温度和终轧温度的降低,试验钢的抗拉强度减小,屈服强度、延伸率和强塑积增大.其中采用850～800℃的温度区间精轧+层流冷却、空冷、超快冷的TMCP工艺时,试验钢的屈服强度、延伸率和强塑积分别达到了513MPa,35%和25235MPa.%的最大值.     

退火温度对430不锈钢冷轧板组织和力学性能的影响

针对现场生产的430不锈钢冷轧板,通过高温连续退火实验研究了退火温度对材料显微组织、强度、塑性以及各向异性性能的影响.通过实验得到了合理的两段式加热连续退火工艺:选取中间温度为600℃,加热II段的加热速率为2.3℃·s-1,最高加热温度为840℃.随着退火温度的升高,薄板的屈服强度和硬度呈明显的两阶段降低趋势,延伸率呈"S"型趋势增加,平均塑性应变比基本保持不变(1.25左右),而轧制平面各向异性指数有一定的降低.针对430不锈钢冷轧板分别建立了屈服强度与退火软化率和延伸率之间的定量关系.     

卷取温度对热轧F/B双相钢组织性能的影响

采用轧后空冷+超快速冷却工艺,研究卷取温度对热轧铁素体/贝氏体(F/B)双相钢组织性能的影响规律.结果表明:卷取温度由504℃降至250℃时,铁素体体积分数变化很小(857%～878%),铁素体晶粒尺寸变化也很小(36～37μm),组织中的硬相由以贝氏体为主转变为以马氏体为主;实验钢的抗拉强度由510MPa升至597MPa,屈服强度由475MPa降至389MPa,延伸率变化较小(322%～350%).另外,随着卷取温度的降低,铁素体与贝氏体或马氏体间的变形协调能力降低,使扩孔过程中微孔提前形核,同时加快了已有微孔的长大及合并过程,导致试样发生的塑性变形减小,扩孔性能降低,扩孔率由1014%降至524%.     

衬底温度和退火温度对磁控溅射TiNi合金薄膜组织结构的影响

通过扫描电镜(SEM)、X射线衍射仪(XRD)、透射电子显微镜(TEM)等测试方法研究了不同的衬底加热温度和不同晶化退火温度对磁控溅射法制备的TiNi薄膜组织结构的影响。结果表明:加热衬底可以降低薄膜的晶化温度,通过控制加热温度可以控制晶粒的大小,同时可有效抑制析出相的产生;非晶薄膜在晶化的同时伴随Ti3Ni4相的析出,随晶化温度的升高析出相在长大的同时数量也明显增多。     

退火温度对超细晶中锰TRIP钢组织性能的影响

为研究连续退火工艺生产中锰TRIP钢汽车板的可行性,在钢板连续退火模拟机CCT--AY--Ⅱ上研究了590~710℃不同退火温度下保温3 min对低碳中锰钢组织性能的影响.利用扫描电镜、透射电镜、电子背散射衍射和X射线能谱分析等微观分析方法对实验钢进行了组织结构和成分表征,利用X射线衍射法测量了残余奥氏体量,通过拉伸试验机测试了钢的单轴拉伸性能.结果表明:保温3min时,随着保温温度的升高,残奥含量先增加后减少.在650℃退火时断后伸长率(21.3%)和强塑积(28GPa·%)获得最大值,抗拉强度达到1330MPa.马氏体基体通过回复,而残余奥氏体通过孪晶,获得超细晶组织.亚稳奥氏体的TRIP效应和超细晶铁素体(马氏体)共同提供了实验钢高的塑性.实验钢真实应力--应变曲线上呈现锯齿状现象,且稳定阶段加工硬化指数远高于传统TRIP钢.     

退火温度对5A06挤压型材组织及性能的影响

通过对型材微观组织的观察及维氏硬度、晶间腐蚀和剥落腐蚀等的测试,研究了退火温度对5A06挤压型材组织及性能的影响。结果表明,随着退火温度的升高,晶粒发生了回复、再结晶和晶粒长大三个阶段。当退火温度达到175 ℃时,型材发生低温回复,硬度变化不大,耐蚀性较差;在225～325 ℃退火,型材发生完全再结晶,硬度变化较明显,耐蚀性得到改善;当退火温度高于325 ℃时,晶粒长大,硬度略降低,耐蚀性变差。结合5A06挤压型材组织及性能研究可知,确定退火温度为225～325 ℃。     

碳对Cu-14Fe合金组织和性能的影响研究

采用真空熔炼制备了不同含碳量的Cu-14Fe-C合金,研究了碳对合金显微组织、力学性能和导电性能的影响规律,发现Cu-14Fe合金中添加C使第二相产生球化趋势,添加量达到0.7%时球化十分显著且尺寸明显增大;扫描电镜分析表明铸态Cu-14Fe-C合金中铁元素和碳元素主要分布在第二相中,基体中含量很少;随着碳含量逐渐增加,合金硬度不断提高,含量增加至0.7%时硬度开始略有下降;合金中碳含量为0.2%时,由于形成碳铁化合物,降低了铁元素在铜基体中的固溶度,使基体对电子的散射作用减弱,导电率提高到21.08IACS%,碳含量继续增加到0.7%,导电率又下降为16.74 IACS%。     

退火温度对TiO2薄膜光学性能的影响

为确定合适的TiO2薄膜退火工艺,研究了退火温度对采用中频交流反应磁控溅射技术制备的TiO2薄膜光学性能的影响.利用分光光度计测得石英玻璃基体TiO2薄膜试样的透射谱和反射谱,用包络线法和经验公式法计算出薄膜的光学常数.结果表明 TiO2薄膜的折射率随退火温度的上升而增加,低温退火时薄膜消光系数略有减小, 500 ℃退火时TiO2薄膜具有最优的光学性能.     

退火温度对MnZn铁氧体薄膜性能的影响

采用射频磁控溅射法在Si(111)基片上沉积了MnZn铁氧体薄膜,用X射线衍射仪(XRD)分析薄膜的物相结构,用振动样品磁强计(VSM)测量薄膜面内饱和磁化强度Ms和矫顽力Hc。结果表明:随着退火温度的升高,MnZn铁氧体薄膜的X射线衍射峰强度逐渐增强,且主峰逐渐由(311)峰变为(222)峰,沿(111)面取向生长明显。薄膜的饱和磁化强度和矫顽力均随着退火温度的升高而升高。     

退火时间对中锰热轧TRIP钢组织演变的影响

为了研究热轧Fe-6Mn-3Al TRIP钢组织演变和力学性能,对实验钢采用淬火+不同时间退火(ART)的热处理工艺.研究发现,随着退火时间的增加,奥氏体晶粒尺寸增大、稳定性降低,冷却过程中部分奥氏体相变为马氏体;其中退火10 min后,实验钢性能最优,其残余奥氏体体积分数能达到50.3%,抗拉强度765 M Pa,总延伸率达到49.1%;拉断后实验钢中的奥氏体含量减少,马氏体含量增加,其中,退火10 min后的实验钢TRIP效应最为明显,奥氏体体积分数由变形前的50.3%降低到变形后的11%,奥氏体转化率为78%.     

热处理对Cu-0.23Be-0.84Co合金性能和组织的影响

利用硬度计、导电仪和金相电子显微镜,分析了固溶和时效对Cu-0.23Be-0.84Co合金性能和组织的影响。研究结果表明:Cu-0.23Be-0.84Co合金经950℃×1 h固溶、480℃×4 h时效处理后,综合性能指标较好,其中,硬度可达117.0HB,导电率达71.6%IACS;在试验范围内,随着固溶温度的升高,晶粒结构形貌相似,未溶物逐渐减少,晶粒尺寸逐渐增大;950℃时,晶粒呈等轴状,大小均匀,固溶较完全;时效后,试验合金内部保留着较清晰的应变孪晶,强化相在晶界处不连续析出、集聚而产生黑色组织,且黑色组织数量随着时效时间的延长不断增多。     

Ce对Cu-0.4Mg-xCe合金组织和性能的影响

通过在Cu-Mg合金中添加Ce制备Cu-0.4Mg-xCe (x=0, 0.1, 0.2, 0.3)合金。采用扫描电子显微镜（scanning electron microscope,SEM）、透射电子显微镜（transmission electron microscope,TEM）、拉伸试验机和电导率测试仪等设备对Cu-0.4Mg-xCe 进行表征。结果表明,Ce能明显降低Cu-0.4Mg-xCe合金的晶粒尺寸,净化Cu基体。Ce的质量分数超过0.2%后,会出现Ce的化合物,Cu-0.4Mg-xCe合金的塑性和导电率降低。Cu-0.4Mg-0.2Ce合金的综合性能最优,退火处理后,其维氏硬度、抗拉强度、导电率、软化温度分别为 213,548 MPa, 75.6 %IACS,430 ℃。     

MoCrFeMnNi高熵合金退火后的组织和性能

高熵合金因具有高强度、耐腐蚀、耐高温氧化等优异的性能而备受关注.采用铝热反应法制备MoCrFeMnNi高熵合金,用XRD、SEM、EDS、显微硬度和压缩实验研究了铸态及700 ℃/12 h、800 ℃/6 h、1 000 ℃/3 h退火后合金的组织和性能变化.结果表明:铝热法制备的MoCrFeMnNi高熵合金为典型的枝晶形貌,晶体结构主要由BCC相、FCC相以及少量的σ相构成,其中枝晶区域为BCC结构,富含Mo和Cr元素;枝晶间区域为FCC结构,富含Ni元素.随着退火温度的上升,枝晶间逐渐析出纳米级σ相,使得合金硬度上升,在800 ℃/6 h退火处理后达到667 HV,抗压强度达到1 050 MPa;1 000 ℃/3 h退火后,σ相团聚成球状和针状并在高温下部分溶解,σ相的减少使得合金硬度下降,抗压强度与铸态时相当,塑性显著提升.     

退火温度对淬火后冷轧5083铝合金组织及腐蚀性能的影响

采用金相显微镜、电镜、慢应变拉伸、阳极极化及交流阻抗测试研究退火温度对淬火后冷轧5083铝合金耐蚀性的影响。研究结果表明:冷轧后在100℃和150℃退火40 min的5083铝合金仍呈变形组织特征,在局部变形区呈现连续分布的β相(Mg5Al8),合金具有较强应力腐蚀敏感性和较弱的耐点蚀能力;在200℃和250℃退火40 min后的合金,局部开始发生再结晶,但组织中仍包含由位错缠结而成的胞状亚组织,球状β相在晶内和晶界不连续分布,合金具有高的抗应力腐蚀和耐点蚀能力;在300℃和350℃退火40 min的5083铝合金,为完全再结晶组织,β相又趋于连续分布,合金抗应力腐蚀和耐点蚀能力变弱。     

退火温度对Ti-IF钢性能及织构的影响

对冷轧压下率为80%、厚1mm的Ti-IF钢经不同温度退火处理后进行拉伸试验,测量其塑性应变比r值.观察退火试样的显微组织,并利用电子背散射衍射技术(EBSD)对其性能和再结晶织构进行分析.结果表明,冷轧试验钢分别在780、810、840℃退火3min后,均发生了再结晶;随着退火温度的升高,大多数晶粒尺寸由5～6μm增大到9～10μm;试验钢的r值随退火温度升高而增大;退火钢再结晶织构表现为强烈的{111}织构,主要由{111}〈110〉和{111}〈112〉两类取向晶粒组成.