ZnO:Al(ZAO)薄膜的特性研究

用直流磁控反应溅射技术制备了综合性能优良的ZnO:Al(ZAO)薄膜.X光衍射(XRD)、光电子能谱(XPS)和Auger电子能谱(AES)等分析结果表明,适量的铝掺杂和氧流量可有效地控制Al2O3相的生成.铝在薄膜表面的存在形式单一,并且Zn,O,Al各元素纵向分布均匀.理论与实验研究表明,对于高度简并的ZAO半导体薄膜,在温度较低时,离化杂质散射占主导地位;温度较高时,晶格振动散射将成为主要的散射机制;晶界散射仅当晶粒尺寸较小(与电子的平均自由程相当)时才起作用.此外,优化工艺参数可获得低电阻率(～5×10-4Ωcm)的ZAO薄膜.在可见光区,其透射率＞80%;在近中红外光区,其反射率＞60%.     

常压固相烧结法制备ZAO靶材及其性能的研究

采用常压固相烧结法,通过优化烧结工艺,制备出平整、组织均匀、致密的ZAO靶材.研究了掺杂含量、烧结温度对陶瓷靶材微观结构和性能的影响,并使用自制靶材,采用射频磁控溅射法镀膜.结果表明:Al2O3的掺杂没有破坏ZnO晶体结构,Al原子对Zn原子进行有效替位;晶粒尺寸随着掺杂量的增多而减小;靶材的电阻率随掺杂量的增加呈U型变化,在3wt%时取得最小值4.2×10-2Ω.cm;靶材致密度超过96%.使用该靶材生长的多晶ZAO薄膜具有(002)择优取向,结晶均匀,呈柱状生长,薄膜电阻率和可见光平均透射率可分别达到8×10-4Ω.cm～9×10-4Ω.cm和85%.图9,表1,参14.     

ZnO:Al透明导电薄膜的制备及其光电性能的研究

利用溶胶-凝胶法在石英衬底上制备Al3+掺杂ZnO薄膜,研究了Al3+掺杂对ZnO薄膜微结构和光学性能的影响.XRD测量结果表明,Zn1-xAlxO薄膜具有六角纤锌矿结构,晶格常数随着Al掺杂浓度的增加而减小;紫外-可见透射光谱(UV)表明,所有薄膜在可见光区的透过率均超过80%;光致发光谱研究发现,随着Al掺杂浓度的增加ZnO的吸收带边发生蓝移,XRD和光学性能研究都证实了ZnO薄膜中的Al3+是以替位式形式存在于晶格中.     

氧化锌透明导电膜的光电性能研究

采用磁控溅射法在载玻片上制备出Al3 掺杂型ZnO透明导电薄膜.对不同厚度薄膜的光电性能进行了研究.结果表明,所制备的薄膜随着厚度的增加,透过率略有下降;ZnO薄膜在可见光区的吸光度很小,对可见光几乎不吸收.     

Al-Y共掺杂ZnO透明导电薄膜制备及光电性能研究

 采用溶胶 凝胶法,在玻璃衬底上制备出Al-Y共掺杂的ZnO透明导电薄膜。X射线衍射(XRD)表明,Al-Y共掺杂ZnO透明导电薄膜为六角纤锌矿结构的多晶薄膜,且具有C轴择优取向。制备的Al-Y共掺杂ZnO薄膜电阻率最小值为1.63×10² Ω·cm,在可见光区(400-800 nm)平均透过率超过85 %。     

薄膜厚度对ZAO透明导电膜性能的影响

采用直流反应磁控溅射法,用Al含量为2%的Zn/Al合金靶材,室温下在玻璃衬底上制备了ZAO透明导电薄膜样品.在其他参数不变的情况下,由不同溅射时间得到不同的薄膜厚度,研究了薄膜的结构性质、光学和电学性质随薄膜厚度的变化关系.制备的ZnO:Al薄膜具有(002)面的单一择优取向的多晶六角纤锌矿结构,电阻率为5.1×10-4Ω.cm,平均透射率达到88%.     

溶胶-凝胶旋涂法制备Al掺杂ZnO薄膜及其光电性能的研究

利用溶胶-凝胶(sol-gel)旋涂法制备不同Al掺杂量的ZnO薄膜.采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、紫外可见分光光度计(UV-Vis)和光致发光谱(PL)等测试手段对Al掺杂ZnO薄膜的晶体结构、表面形貌及光电性能进行表征.结果表明:所制备的样品均沿(002)方向择优生长,无其他杂相的出现.随着Al掺杂量的增加,薄膜的晶粒尺寸先减小后增大,当Al掺杂量为0.020时晶粒尺寸最小,其表面晶粒最为均匀、致密;近紫外发光峰的强度先增强后减弱,并且出现了轻微蓝移的现象;薄膜的电阻值先减小后轻微增大.当Al元素的掺杂量为0.015时,薄膜表面相对均匀致密,禁带宽度有所增加,可见光范围内平均透过率最高达到90%,并且具有较好的导电性能.     

掺铝氧化锌ZAO(ZnO:Al)薄膜研究

描述ZAO(ZnO:Al)薄膜的晶体结构,论述ZAO薄膜的光学、电学性质与其结构的关系,介绍了掺铝氧化锌ZAO薄膜的各种制备方法,并总结了ZAO薄膜在各种领域中的应用.提出了薄膜材料研究的关键问题以及今后的发展方向.     

纳米铈-铝共掺杂氧化锌透明薄膜的光学性能研究

用溶胶-凝胶浸渍提拉法在普通玻璃片上制备了纳米Ce-Al共掺杂ZnO(Ce-AZO)透明薄膜,并研究了Ce-AZO薄膜的光学性能.结果表明:Ce-AZO薄膜在可见光区的平均透过率均在85%以上;Al和Ce掺杂摩尔分数分别为4%和2%、pH 7.1、退火温度450℃时,Ce-AZO薄膜在可见光区500～700 nm的透过率达到92%,在紫外区300～350 nm平均透过率只有2%.     

溶胶-凝胶法制备掺铝氧化锌透明导电膜的正交实验研究

采用溶胶-凝胶法制备了掺铝氧化锌(ZnO：Al,ZAO)透明导电膜。对薄膜用X射线衍射(XRD)、扫描电镜(SEM)、四探针仪及紫外 可见分光光度计等分析测试手段进行了表征;通过正交实验探讨了溶胶浓度、铝离子的摩尔掺杂量以及退火温度等因素对其电阻率的影响。结果表明,薄膜电阻率随溶胶浓度、铝离子掺杂量的增加,呈现先减小后增大的趋势,并随退火温度的升高而减小,从而确定了制备ZAO透明导电膜的优化工艺条件为：溶胶浓度0.8mol/L,铝离子的掺杂量1.0%(摩尔分数),退火温度550℃。在优化工艺条件下制得的ZAO透明导电薄膜具有标准的ZnO纤锌矿结构,其电阻率为1.275×10^-3Ω·cm,平均透光率达84%。     

一种三明治结构透明导电薄膜的制备及光电性能

采用直流磁控溅射法制备了ZAO/Cu/ZAO多层透明导电薄膜,研究了参铝氧化锌(ZAO)薄膜厚度对多层膜晶体结构和光电特性的影响.用X射线衍射仪、原子力显微镜、紫外可见光分光光度计及四探针对样品的晶体结构与光电性能等进行了表征.结果表明,多层膜的平均透过率最高达86%,方块电阻达9/sq;ZAO膜层厚度对多层膜的导电性能影响很小,但严重影响可见光透过率;多层膜中的ZAO层仍呈ZnO晶态结构,且具有明显的c轴取向特征.这种三明治结构是一种性能优良的太阳能透明导电层候选材料.     

磁控溅射制备参数对 ZnO:Al电学性能的影响

ZnO:Al(ZAO)透明导电薄膜是一种n型半导体,有高的载离子浓度和大的光学禁带宽度,具有优异的电学和光学性能,有极广的应用前景.本文介绍了ZAO薄膜的广泛用途和今后研究的趋势,并着重分析了磁控溅射制备参数对电学性能的影响.     

Study on ZnO:Al (ZAO) films by DC reaction magnetron sputtering

The high quality ZnO: A1 films were successfully produced by DC reaction magnetron sputtering technology. The Al-doping effect on electrical and optical properties and its scattering mechanism are discussed in detail. The analyses of X-ray diffractometer (XRD), X-ray photoelectron spectroscopy(XPS) and high resolution Auger electron spectroscopy (AES) show that Al2O3 could be effectively removed by controlling oxygen flow and Al-doping concentration during deposition of ZnO: Al films. Zn, Al and oxygen elements are well distributed through the films. For highly degenerated ZnO:A1 semi-conductive thin films, the theoretical and experimental results reveal that the ionized impurity. scattering dominates the Hall mobility in the films in the low-temperature range, while the lattice vibration scattering becomes a major scattering mechanism in the high-temperature range. The grain boundary scattering only plays a major role in the ZAO films with small grain size (as compared to the electron mean free path). The photoelectric properties of ZAO films show that it has low resistivity ( ～ 5 × 10-4 Ωcm), and the transmittance in visible range and the reflectance in IR region are above 80% and 60%, respectively.     

Preparation of Cu（In,Ga）Se2 thin film by sputtering from Cu（In,Ga）Se2 quaternary target

Cu(In,Ga)Se2 (CIGS) thin films were prepared by directly sputtering Cu(In,Ga)Se2 quaternary target consisting of Cu:In:Ga:Se 25:17.5:7.5:50 at%. The composition and structure of CIGS layers have been investigated after annealing at 550 ℃ under vacuum and a Se-containing atmosphere. The results show that recrystallization of the CIGS thin film occurs and a chalcopyrite structure with a preferred orientation in the (112) direction was obtained. The CIGS thin film annealed under vacuum exhibits a loss of a portion of Se, while the film annealed under Se-containing atmosphere reveals compensation of Se. Several solar cells with three different absorber thicknesses were fabricated using a soda lime glass/Mo/CIGS/CdS/i-ZnO/ZnO:Al/Al grid stack structure. The highest conversion efficiency of 9.65% with an open circuit voltage of 452.42 mV, short circuit current density of 32.16 mA cm2 and fill factor of 66.32% was obtained on a 0.755 cm2 cell area.     

直流磁控溅射制备透明导电ZAO薄膜退火处理时间的研究

为改进太阳能薄膜材料制备工艺,利用直流磁控溅射方法,在较高氩气压强——12.7 Pa下制备出透明导电掺铝ZnO(ZAO)薄膜,并对其进行退火处理时间的研究。与其他研究者不同,利用较高压强也制备出高性能ZAO薄膜,并且可以利用退火处理改善薄膜的晶体结构、内应力、表面形貌以及光电性能。薄膜的电阻率随着退火时间的增加而降低,从原位沉积时的3.5×10-3Ω.cm,下降到1.9×10-3Ω.cm;薄膜的平均透光率增加到80%以上,光谱吸收边发生蓝移。结果表明,退火2 h,ZAO性能改善最优。     

Photore sponse and H2 gas sensing properti es of highly oriented Al and Al/Sb doped ZnO thin films

ZnO:Al and ZnO:Al/Sb thin films have been prepared and investigated.The thin films were deposited on Si substrates by the sol-gel method.The structural,optical and electrical properties of ZnO films have been investigated by spectrophotometry,ellipsometry,X-ray diffraction and current-voltage characterizations.It is found that the films exhibit wurtzite structure with a highly c-axis orientation perpendicular to the surface of the substrate,a high reflectivity in the infrared region and a response to illumination.Furthermore,it has been found that Si/（ZnO:Al/Sb）/Al photodiode is promising in photoconduction device while Si/（ZnO:Al）/Al can be used as gas sensor responding to the low H₂concentrations.     

磁控溅射表面镀膜对Nd2Fe14B稀土永磁体抗腐蚀性能的影响

在Nd₂Fe₁₄B稀土永磁体基体表面,采用磁控溅射（直流+射频）技术制备了Ti/Ni,Ti/Al和Al/Ni等二元合金薄膜和Ti/Al/Ni三元合金薄膜。并通过中性盐雾试验、腐蚀失重计算、电化学腐蚀试验、金相观察等方式,对比研究了不同表面处理对Nd₂Fe₁₄B稀土永磁体基体抗腐蚀性能的影响,并构建了腐蚀模型。研究发现：Ti/Ni,Ti/Al和Al/Ni等二元合金薄膜和Ti/Al/Ni三元合金薄膜均有效地提高了Nd₂Fe₁₄B稀土永磁体基体耐中性盐雾腐蚀和电化学腐蚀的能力;Ti/Al/Ni三元合金薄膜较Ti/Ni,Ti/Al和Al/Ni等二元合金薄膜有更优良的综合耐腐蚀性能,其磁控溅射工艺参数为：Ar流量60 sccm,基片温度常温,Ni,Al,Ti的溅射功率都为250 W,基片转速20 r·min^-1,镀膜均速0.3 nm·s^-1,总计溅射时间1 h。     

A1掺杂ZnO薄膜的结构研究

采用直流反应磁控溅射方法,在玻璃衬底上制备了Al掺杂ZnO薄膜.系统研究了不同氩氧体积比、不同退火温度和氛围、不同Al掺杂浓度对薄膜结构的影响.结果显示,Al掺杂ZnO薄膜为多晶薄膜,呈六角纤锌矿结构,制备条件和后期处理以及掺杂浓度对薄膜的微结构有着很大的影响.在氩氧体积比6:1条件下制备的薄膜,经真空500℃退火后具...