超音速火焰喷涂制备双峰WC-12Co涂层组织性能研究

采用JP-8000型超音速火焰(HVOF)喷涂设备,在低碳钢基体上制备了双峰WC-12Co涂层,测试了涂层的结合强度、显微硬度、气孔率以及抗磨粒磨损性能.并利用XRD对喷涂粉末及涂层进行了相结构分析,用扫描电子显微镜对喷涂粉末、磨粒磨损后的涂层表面形貌进行了观察.结果表明:在喷涂过程中,仅有很少量的WC粒子发生氧化脱碳...     

螺杆泵转子表面HVOF喷涂WC涂层的耐磨抗蚀性能

采用超音速火焰喷涂(HVOF)技术,在螺杆泵转子基材45钢表面分别制备WC-12Co和WC-10 Co-4 Cr涂层,并利用SEM、EDS、XRD及显微硬度计等手段,表征了涂层的微观形貌、孔隙率、相结构和维氏硬度.在摩擦磨损试验和电化学试验基础上,探讨了涂层磨损和腐蚀机理.研究结果表明:WC-12Co涂层和WC-10C...     

添加剂铜在等离子喷涂WC-12Co涂层中的作用研究

以WC-12Co和Cu180粉末为热喷涂材料,采用等离子喷涂系统制备涂层,利用扫描电子显微镜和X射线衍射仪对添加铜的WC-12Co涂层的显微组织和相结构进行观察与分析,并使用MH-6维氏硬度仪测量涂层的显微硬度HV,研究添加铜对WC-12Co涂层微观组织、相组成和硬度的影响规律。结果表明：添加铜后,WC-12Co涂层的显微组织更加致密,但显微硬度降低;涂层主要成分是WC及其脱碳产物W2C以及铜的氧化物Cu2O、CuO,添加铜对WC的脱碳起到了一定的抑制作用;喷涂过程中铜具有很好的流动性,填充到涂层形成过程中颗粒间的孔隙,降低涂层孔隙率。     

超音速火焰喷涂WC-12Co涂层的磨粒磨损行为研究

对超音速火焰WC-12Co涂层进行了磨粒磨损试验,研究了磨粒磨损试验参数对涂层性能的影响,并通过SEM对涂层表面的显微形貌进行了观察分析,探讨了WC-12Co涂层的磨粒磨损失效机制.结果表明:涂层的失重随试验载荷及磨料直径的增加而增加;在载荷或磨料粒度较大时.涂层的磨损失效形式为晶粒剥落及犁沟切削相结合;当载荷或磨料粒度较小时,其失效形式主要为晶粒剥落方式.     

T10钢表面HVOF喷涂WC-10Co-4Cr涂层的耐磨性研究

采用超音速火焰喷涂(HVOF)工艺在T10钢表面制备了WC-10Co-4Cr涂层,用扫描电镜(SEM)、X射线衍射仪(XRD)观察了喷涂粉末和涂层的微观结构,用摩擦磨损试验机测试涂层在无润滑及油润滑条件下的摩擦磨损行为。结果表明:WC-10Co-4Cr涂层的未融颗粒较多,涂层微观结构致密,孔隙率约为0.8%;涂层表面显微硬度呈现常规的单模分布,而涂层-基体截面显微硬度呈现双态分布,涂层表面硬度高于截面硬度,且更为稳定;在干摩擦和油润滑条件下,涂层的摩擦系数随加载力的增大而减小,基体的摩擦系数也随加载力的增大而减小;WC-10Co-4Cr涂层的磨损深度约为T10基体磨损深度的1/3;WC-10Co-4Cr涂层的磨损机制为磨粒磨损,T10基体的磨损机制为黏着磨损。     

粉末的物理性能对热喷涂涂层的影响

在SUS316L不锈钢基体上,采用HVOF和DGS两种不同的工艺方法,分别喷涂WC-12Co和FeAl涂层,观察WC-12Co和FeAl粉末的颗粒形貌、粒度组成以及DTA,研究它们对热喷涂涂层质量的影响.通过表面粗糙度、显微硬度、形貌相以及X射线衍射谱等分析表明,球化程度高,颗粒大小均匀的粉末可使涂层的组织均匀,致密性好,结合强度高.采用HVOF方法喷涂WC-12Co涂层的质量最好,而采用DGS工艺喷涂FeAl涂层的工艺参数还有待于进一步优化.     

HVOF制备的Ni60/WC-10Co4Cr涂层组织和滑动磨损性能研究

为了降低超音速火焰(HVOF)喷涂金属陶瓷涂层的材料和加工成本,使其在更大范围内替代会给环境带来严重污染的电镀硬铬(EHC)涂层,本文将不同比例的Ni60与WC-10Co4Cr相混合,并采用HVOF喷涂工艺分别制备了5种金属陶瓷复合涂层.研究了这些涂层的显微组织、基本性能和滑动磨损性能,并将其与EHC涂层进行对比.结果表明:所有HVOF喷涂工艺制备的Ni60/WC-10Co4Cr涂层都很致密(孔隙率小于1%),随着WC-10Co4Cr比例的增加,Ni60/WC-10Co4Cr涂层的硬度从688.3 HV0.3增加到1 203.4HV0.3,磨损率由2.75×10~(-5) mm~3/N·m降低到7.29×10~(-7) mm~3/N·m.并且,所有HVOF喷涂工艺制备的涂层和与其配对的摩擦副的磨损率以及磨擦系数均低于EHC涂层,表现出良好的抗滑动磨损性能.     

Cr12钢电火花沉积超细涂层的摩擦磨损性能

采用电火花沉积技术,在Cr12模具钢表面沉积了WC-12Co超细硬质合金涂层;并考察了涂层的显微组织及摩擦磨损性能.结果表明:沉积层组织均匀,与基体呈冶金结合,超细的硬质相弥散分布于沉积层中,其中部分区域硬质相达到了纳米颗粒尺寸.沉积层的平均显微硬度为1 474.8 HV0.1,约是基体硬度的3倍,沉积层的耐磨性能是基体的3.3倍.沉积层的磨损机制主要是磨粒磨损和疲劳磨损.弥散分布的细小硬质相是沉积层硬度及耐磨性能提高的主要因素.     

喷距对低温超音速火焰喷涂WC-10Co4Cr涂层性能的影响

以粒度为5~15μm的WC-10Co4Cr为热喷涂粉末,采用低温超音速火焰喷涂(LT-HVOF)技术制备WC-10Co4Cr涂层,并利用粒子收集技术研究喷距对涂层显微结构和性能的影响。采用扫描电子显微镜(SEM)、粗糙度测试仪和显微硬度仪分别对涂层的显微结构、粗糙度、硬度和韧性进行测试分析。实验结果表明:WC-10Co4Cr涂层的显微硬度(HV0.3)和致密度随着喷距的增大而降低,分别由喷距100 mm时的1 484.19和0.5%降低至喷距310 mm时的930.50和2.2%;涂层的结构和性能与粉末在焰流中的熔融状态和飞行速度相关,喷距在100~190 mm范围内粉末呈未熔化状态,220~310 mm范围内呈微熔化状态,粉末的飞行速度随喷距的增加呈下降趋势;粉末呈微熔化状态时断裂韧性与HVOF涂层相当且明显高于粉末呈未熔化状态的断裂韧性;优化的喷涂距离为220~280 mm,该段距离内可以获得涂层粗糙度约为2μm、孔隙率小于1%、显微硬度大于1 018(HV0.3)、断裂韧性大于3.323 1 MPa·m1/2的涂层。     

工艺参数对低功率等离子喷涂10%Cu-WC-12Co涂层性能的影响研究

以WC-12Co和Cu180粉末为热喷涂材料,采用低功率等离子喷涂系统制备涂层,用OLYMPUS GX51型金相显微镜观察涂层剖面的显微组织形貌,用OLYCIA专业金相分析系统结合栅格法计算出该断面不同部位的孔隙率,用MH-6维氏硬度仪测量涂层截面的显微硬度,研究工艺参数对10%Cu-WC-12Co涂层气孔率和显微硬度的影响规律,确定最佳工艺参数。     

Cr3C2-NiCr涂层磨料磨损行为

采用橡胶轮磨损实验机 ,对三种类型粉末制备的 HVOF Cr3 C2 - 2 5 % Ni Cr涂层进行了磨料磨损实验 ,研究了涂层的磨损特性和喷涂工艺条件、粉末制备工艺对涂层磨损速率的影响。在运用扫描电镜对涂层结构和磨损表面观察分析的基础上 ,结合涂层结构和橡胶轮磨料磨损的特征 ,探讨了该涂层的磨料磨损失效行为。     

Microstructure and mechanical properties of twin-wire arc sprayed Ni-Al composite coatings on 6061-T6 aluminum alloy sheet

We have systematically studied the microstructure and mechanical properties of Ni-5wt%Al and Ni-20wt%Al composite coatings fabricated on 6061-T6 aluminum alloy sheet by twin-wire arc spraying under different experimental conditions. The abrasive wear behavior and interface diffusion behavior of the composite coatings were evaluated by dry/wet rubber wheel abrasive wear tests and heat treatment, respectively. Experimental results indicate that the composite coatings exhibit features of adhesive wear. Besides, the Vickers microhardness of NiAl and Ni₃Al intermetallic compounds is relatively larger than that of the substrate, which is beneficial for enhancing the wear resistance. With the increase of annealing temperature and time, the interface diffusion area between the Ni-Al coating and the substrate gradually expands with the formation of NiAl₃ and Ni₂Al₃ phases, and is controlled by diffusion of aluminum atoms. The grain growth exponent n of diffusion kinetics of the Ni-Al coating, calculated via a high-temperature diffusion model at 400, 480, and 550℃, is between 0.28 and 0.38. This satisfies the cubic law, which is consistent with the general theoretical relationship of high-temperature diffusion.     

反应火焰喷涂TiC-Fe涂层的耐磨性能

研究以钛铁,石墨和纯铁粉为原料,用反应火焰喷涂技术制备TiC-Fe金属陶瓷涂层的耐磨性能,结果表明,涂层中富ＴiC和贫TiC片层的显微硬度分别达11．9－13．7GPa和3．3－6．0GPa,在SRV磨损试验机上经20min的干磨擦试验表明,反应火焰喷涂TiC-Fe涂层具有良好的耐磨性能,大约是常规火焰喷涂WC－Ni45金属陶瓷涂层的5倍,综合磨痕的轮廓曲线及其SEM形貌发现,其磨损机理主要是粘着磨损,但也有少量细小的硬质相相剥落。     

氩弧熔敷原位自生WC复合涂层组织及耐磨性

为提高采煤机中截齿的耐磨性能,利用氩弧熔敷技术,在35CrMnSi钢表面制备WC增强Ni基复合涂层。利用OM、SEM、XRD和EDS分析复合涂层的显微组织,采用显微维氏硬度仪测试复合涂层的显微硬度,并测试涂层在室温磨损条件下的耐磨性能。结果表明：氩弧熔敷涂层组织均匀致密,熔敷涂层与基体呈冶金结合,主要由WC、W：C、T—Ni、（Fe,Cr）23,C6等物相组成;WC颗粒呈弥散分布,颗粒尺寸为1txm;熔敷涂层可以改善基体的表面硬度,最高显微硬度可达12．6GPa;熔敷涂层在室温冲击磨粒磨损实验条件下,具有优异的耐磨性,磨损机制主要是磨粒磨桶．其耐磨性较35CrMnSi基体提高近12倍。     

镍基纳米Al2O3粉末复合电刷镀镀层的耐磨性

为了进一步提高刷镀层的耐磨性 ,在 4 5 #钢基体上刷镀含有纳米 Al2 O3粉末的镍基复合镀层。通过光学金相显微镜、扫描电子显微镜对镀层显微组织进行分析 ,用显微硬度计测定了镀层和基体的硬度 ,在 SRV磨损试验机上进行了磨损试验 ,用表面形貌仪测量了镀层磨损量。试验结果表明 ,加入纳米 Al2 O3粉末的复合镀层的硬度要比单纯的致密镍镀层的硬度高。随着纳米 Al2 O3粉末加入量的增加 ,复合镀层硬度逐渐提高。含纳米 Al2 O3粉末的镍基复合镀层与单纯致密镍镀层相比 ,具有更高的耐磨性 ,将有广泛的应用前景。     

载荷对纳米晶Co-Ni-Fe合金镀层摩擦磨损性能的影响

用脉冲电沉积技术制备表面平整光亮的纳米晶Co-Ni-Fe合金镀层.采用XRD、TEM、SEM、EDS等方法研究了纳米晶Co-Ni-Fe合金镀层的微观组织结构、表面形貌和合金成分.研究了干滑动摩擦条件下纳米晶镀层的摩擦磨损性能、磨损后的组织结构和硬度的变化.结果表明：纳米晶Co-Ni-Fe合金镀层的晶体结构为单相面心立方结构.镀层的摩擦系数和磨损量随着摩擦载荷的提高而增大,即镀层的耐磨性随载荷的提高而下降.摩擦磨损使纳米晶Co-Ni-Fe合金镀层发生晶粒长大,摩擦载荷越大,磨损后镀层的硬度越低.     

WC的质量分数对喷熔层耐磨性能的影响

在自熔性合金粉末Ni60中机械混合不同质量分数的WC进行火焰喷熔,通过喷熔工艺性能试验、喷熔层宏观硬度测试、喷熔层低应力磨粒磨损试验、喷熔层冲击磨粒磨损试验和显微组织分析,研究了w(WC)对喷焊层耐磨性能的影响。试验证明:随着合金粉中w(WC)的增大,喷焊工艺性能变差,但当w(WC)低于50%时,WC的加入对喷焊工艺性能影响不很明显,喷熔层硬度变化不大,喷熔层低应力磨粒磨损性能随w(WC)的增大而提高;当w(WC)大于50%时,WC的加入使喷熔工艺性能变得极差,喷熔层的硬度和耐低应力磨粒磨损性能降低。由于WC硬而脆的性能和在喷熔层显微组织中起分割基体的作用,喷熔层耐冲击磨粒磨损性能随w(WC)的增大而降低。     

High-temperature frictional wear behavior of MCrAlY-based coatings deposited by atmosphere plasma spraying

Al₂O₃-Cr₂O₃/NiCoCrAlYTa coatings were prepared via atmosphere plasma spraying (APS). The microstructure and phase composition of the coatings were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), laser confocal scanning microscopy (LSCM), and transmission electron microscopy (TEM). The dry frictional wear behavior of the coatings at 500℃ in static air was investigated and compared with that of 0Cr25Ni20 steel. The results show that the coatings comprise the slatted layers of oxide phases, unmelted particles, and pores. The hot abrasive resistance of the coatings is enhanced compared to that of 0Cr25Ni20, and their mass loss is approximately one-fifteenth that of 0Cr25Ni20 steel. The main wear failure mechanisms of the coatings are abrasive wear, fatigue wear, and adhesive wear.