Fabrication and spectra characteristics of high efficiency white organic light-emitting diodes with single emitting layer

High-efficiency white organic light-emitting devices with single emitting layer are demonstrated. N,N‘-diphenyI-N,N‘-bis(1,1‘-biphenyl)-4,4‘-diamine (NPB) is used as hole transport layer, while 4,7-diphenyl-l,10-phenan-throline (BPhen) as electron transport layer and 9,10-di-(2-naphthyl)-2-terbutyl-anthracene (TADN) doped with the fluorescent dye 4-(dicyanomethylene)-2-t-buty1-6-(1,1,7,7-tetramethyljulolidyl-9-enyl) (DCJTB) as single emissive layer. The effects of performance by the concentration of DCJTB and the thickness of emissive layer are studied. The device with a structure of indium tin oxide/NPB (50 nm)/TADN: 0.2% DCJTB (15 nm)/BPhen (40 nm)/Mg: Ag shows a maximum brightness of 11400 cd/m^2, a peak current efficiency of 5.6 cd/A and power efficiency of 4.1 Ira/W, while the low turn-on voltage of 3.1 V and the stability of the Commission International De L‘Eclairage coordinate. The spectra through color filter of the device are also studied.     

含有咔唑-噁二唑双极性单元的阳离子型有机铱(Ⅲ)配合物的合成及其发光性能

合成了一个新颖的含有咔唑-噁二唑双极性单元的阳离子型有机铱(Ⅲ)配合物[(CPPO)Ir(ppy)2]PF6(CPPO:2-(4-(3-(9-(2-乙基己基)-9H-咔唑-3-基)-1-(吡啶-2-基甲基)-1H-吡唑-5-基)苯基)-5-苯基-1,3,4-噁二唑;ppy:2-苯基吡啶).并对其紫外-可见吸收、光致发光和热稳定性进行了研究,结果显示该配合物固态时可被蓝光激发,其热分解温度为270℃,可适用于发光二极管、发光电化学池等发光器件.     

基于八羟基喹啉铝有机发光二极管的研制

以八羟基喹啉铝(Alq3)和芳香二胺(TPD)为有机原材料,用热蒸发方法把它们蒸镀成薄膜并制作成有机发光器件．原子力显微镜观测得到Alq3和TPD薄膜为均匀、规整的不定形结构．研制的有机发光二极管(OLEDs)具有良好的整流特性、发光特性和稳定性,发光亮度随外加电压增加而逐渐增大,发光亮度最高达1813cd／m^2。     

基于苝的非掺杂荧光白色有机电致发光器件

采用两种经典传统荧光材料作为发光层,制备了非掺杂白色有机电致发光器件(WOLEDs).在器件中两层苝(perylene)以薄层的方式分别置于双极性主体材料CBP(4,4’-di (N-carbazole)biphyenyl)两侧作为蓝光发射体,一层超薄的红荧烯(rubrene)插入CBP中作为橙光发射体.通过改变rubrene在CBP中的插入位置获得了高效率白色荧光器件,最高电流效率为6.6 cd/A(外量子效率为2.6%),最高亮度为18 480 cd/m²,且其中一种器件在200 mA/cm²的高电流密度下,CIE(commission internationale de l’eclairage)色坐标可达理想白光平衡点(0.33,0.33).     

正相微乳液法制备负载染料的二氧化硅荧光纳米粒子

采用正相微乳液法制备了负载油溶性染料2,5-二[4-(2-N,N-二苯胺苯乙烯基)苯基]-1,3,4-噁二唑(PASPO)的二氧化硅荧光纳米粒子.透射电子显微镜和红外光谱表征结果显示,荧光纳米粒子呈单分散球形,平均粒径约为30 nm.利用紫外光谱和荧光光谱对染料PASPO和荧光纳米粒子的光学性能进行表征,发现其光谱基本...     

芳胺取代二(苯乙烯基)芳烃制备的单层有机电致发光器件

合成了具有双极载流子传输性能的有机发光材料BPAVB,制备了绿色单层有机电致发光器件。     

LiF用作阴极注入层的有机发光二极管制备

使用真空热蒸发方法,制备了结构为ITO/TPD/Alq3/LiF/Al的有机发光二极管,其中LiF用作阴极注入层,LiF超薄层的加入,增强了电子注入,降低了启亮电压,提高了器件的发光效率和亮度. 实验结果表明:当加入LiF层的厚度为0.5 nm时,器件性能的改善最好,和不含LiF的器件相比,启亮电压由原来的9 V降低到5 V,效率由1.5 cd/A增加到3.3 cd/A,提高了近1倍,然而随着加入LiF层厚度的增加,器件性能的改善效果降低.     

聚合物双层结构实现稳定的白光发射

通过聚乙烯咔唑(PVK)和发绿光的9’9-二辛基芴(DOF)与硒芬(SeH)的共聚物(PFSeH)形成聚合物双层器件结构(ITO/PEDOT/PVK/PFSeH/Ba/A l)实现白光发射.通过优化PVK和PFSeH各层的厚度,得到了光谱稳定的白光发射.在电压为13V时该器件的最大发光效率为0.51 cd/A,相应的亮度为750 cd/m2和色坐标C IE1931为(0.32,0.32).在10~18 V的电压范围内双层器件的白光发射光谱稳定不变.双层器件发白光的原因是由于PVK层的蓝光发射和PFSeH层的绿光发射及PFSeH与PVK双层界面间形成基激复合物的红光发射.     

Robust transfer-printing method for perovskite films and nanostructures

Metal halide perovskites, as a promising semiconductor material, have been successfully used in electroluminescent devices because of their desirable characteristics, such as good conductivity, high color purity, tunable bandgap, low cost and solution process ability. In the past few years, significant progress has been made in the development of high-efficiency perovskite light-emitting diodes (PeLEDs). These efficient PeLEDs are mainly achieved by sophisticated spin-coating methods, which can easily control the perovskite's composition, film thickness, morphology and crystallinity. However, with the continuous development of PeLEDs, commercial production problems have to be solved, such as large area production, high resolution patterning and substrate diversity, which are difficult for the current spin-coating process.     

Red organic light emitting device with improved performance using a novel fluorescent dye codoped with phosphor-sensitizer

Efficient red organic light-emitting device consisted of a compound fluorescent-phosphor-sensitized emission layer was fabricated. A novel red fluorescent dye, 3-(dicyanomethylene)-5,5-dimethyl-1-(4-dimethylamino-styryl) cyclohexene (DCDDC), and a green phosphorescent dye, fac tris(2-phenylpyridine) iridium [Ir(ppy)3] were codoped into a host material 4,4’-N,N’-dicarbazolebiphenyl (CBP). By adjusting the component ratio of doping system, a series of devices with different concentration proportion of Ir(ppy)3:DCDDC were constructed. The results demonstrated that the device with 0.2 wt% DCDDC had a maximum power efficiency (η_p) of 2.12 lm/W at a current density of 0.1 mA/cm², which was about 38% higher than that of conventional fluorescent device. When at a current density of 4 mA/cm2 (100 cd/m²) and 52 mA/cm² (1000 cd/m²), the η_p percentage was about 160% and 143% higher than that of conventional device, respectively. A stable red light emission at a peak of 615 nm with Commissions Internationale de l’Eclairage coordinates near the region of (0.56, 0.42) in a wide bias range was also obtained. The improved performances were attributed to the efficient multiple-stage energy transfer from the host to the guest and the suppression of loss mechanism.     

中位含氯取代环己烯桥环硫三碳菁染料的合成及性能

采用2-甲基噻唑季胺盐与2-氯-1-甲酰基3-羟亚甲基环己烯,合成了五种题示染料。经IR及~1H-NMR谱确认了产物的结构,测定了电子吸收光谱、溶解度及稳定性,发现在染料苯环上引入甲氧基能改进染料溶解度,苯环上有氯取代的染料具有较高的光稳定性。     

新型顶发射有机电致白光二极管的研究

为了提高顶发射白光有机发光二极管(top-emitting white organic light-emitting diodes,TWOLEDs)色谱稳定性，对一种拥有Ag反射镜的新型双蓝光发光单元顶发射器件展开研究，发现结构为Ag/Glass/ITO/MoO₃(5nm)/TAPC(30nm)/TCTA(5nm)/Firpic:TCTA(10%,20nm)/Firpic:TmPyPb(10%,10nm)TPBi(30nm)/LiF(1nm)/Al(0.8nm)/Ag(22nm)/Alq₃(50nm)的蓝光器件具有最佳光电性能，其最高电流效率可以达到9.76cd·A^-1。基于该结构，结合DCJTB荧光染料制备的颜色转换层实现顶发射白光器件。结果表明，当颜色转换层DCJTB浓度为2.5%时，获得了电流效率为2.45cd·A^-1，CIE色坐标为(0.338,0.337)以及显色指数CRI为72的TWOLEDs，器件微腔效应较弱且光谱随电流密度与观测角度改变仅有微弱变化。     

氢氧化镁/可膨胀石墨/聚丙烯复合材料的热降解过程与燃烧行为

以可膨胀石墨(EG)和氢氧化镁(MH)为无卤阻燃剂，通过熔融共混法制备了无卤阻燃聚丙烯(PP)复合材料(EG/PP、MH/PP和MH/EG/PP)，采用热重法研究了复合材料的热降解过程，以氧指数(LOI)和垂直燃烧(UL-94)评价研究了复合材料的阻燃性能，采用锥形量热仪研究了复合材料的燃烧行为.结果表明:MH和EG间存在显著的协同阻燃作用，在阻燃剂质量分数为60%时，MH与EG质量比为5 : 1的MH/EG/PP材料其氧指数可以达到29.7，与MH/PP复合材料相比提高了11.2%；EG与MH协同具有良好的降低热释放作用，与PP和MH/PP相比，MH/EG/PP复合材料的热释放速率峰值(peak-HRR)分别降低了73.9%和34.2%；EG和MH的协同作用大幅度降低了MH/EG/PP的质量损失速率；结合残炭的形貌结果，揭示了EG和MH协同阻燃机理的关键在于增强了炭层的隔热和隔氧作用.     

离子型红光铱配合物的合成、表征与光电性能

设计、合成了新型的基于联吡啶衍生物的离子型铱配合物,并通过1H-NMR、元素分析和质谱进行了结构分析,详细研究了其光物理和电化学性质.结果发现,配合物[Ir(piq)2(FbpyF)](PF6)具有较高的发光量子效率和很好的成膜性.通过旋涂成膜,制备了以配合物[Ir(piq)2(FbpyF)](PF6)为发光层的非掺杂的单层红光电致发光器件.     

共缩聚型可溶性耐高温聚芳酰胺合成及表征

采用1,2－二氢－2－（4-氨基苯基）－4－[4－（4－氨基苯氧基）－苯基]－二氮杂萘－1－酮（A）、4,4′－二氨基二苯醚（B）、4,4′－二氨基二苯甲烷（C）为共缩聚二胺单体与对苯二甲酸进行共缩聚反应,制备共缩聚型聚酰胺。当A与B或C的物质的量比为10：0－5：5时,所得聚酰胺溶于强极性溶剂,在NMP中的特性粘度为0．91－1．43dL/g。它们的玻璃化转变温度均高于300℃,具有优异的耐热性能,在氮气中5％的热失重温度为450℃左右,并且在研究范围内与共聚二胺的结构及比例无关。     

nano-MH/MPB膨胀型纳米复合阻燃剂的制备及性能研究

以MgCl2.6H2O、磷酸三聚氰胺硼酸盐(MPB)为原料,NaOH为沉淀剂,通过原位生成法制备了膨胀型纳米复合阻燃剂nano-MH/MPB。通过IR、EDAX、XRD对其进行了表征。研究了反应温度、反应时间对MH/MPB晶粒尺寸及mMH/mMPB对MH/MPB阻燃性能的影响。反应温度低于75℃、反应时间为30 min时,MH/MPB晶粒尺寸较小,通过谢乐公式计算,MH达到纳米级;mMH/mMPB为0.25时,MH/MPB阻燃性能最好。并通过热重分析(TG)以及nano-MH/MPB/EP燃烧炭渣的红外分析,初步探讨了阻燃机理。     

N,N’- 双(2- 氨基苯基)草酸二酰胺的合成——兼论其与Cu( )的配位行为

报道一种新的酰胺配体N,N’-双( 2-氨基苯基)草酸二酰胺(简称H₂L)的合成.并合成了它的3种铜配合物,进行了元素分析、摩示电导、红外、热重- 差热等表征实验,结果表明H₂L可以与 Cu(Ⅱ)形成1∶1或1∶2型的配合物.     

一种含有1,2,3-三氮唑基团的罗丹明B衍生物的合成及其金属离子响应

将2-苯基-5-三氟甲基-2H-1,2,3-三氮唑-4-羧酸乙酯(Ethyl 2-phenyl-5-(trifluoromethyl)-2H-1,2,3-triazole-4-carboxylate,简称PTCT)作为反应物,设计与罗丹明B合成了一种新型含有1,2,3-三氮唑基团的罗丹明B化合物.通过核磁共振、高分辨质谱对其结构进行了表征;并应用紫外吸收和荧光分析法研究了此衍生物与15种金属离子的作用.结果表明:在一定浓度范围内,DMF(N,N-二甲基甲酰胺)-水溶液中(p H 7.4),该化合物对Hg~(2+)的特异响应比其他离子灵敏,使其荧光增强,并且反应时间很快.用等摩尔连续变化法测定其与Hg~(2+)的络合比为1∶2,研究结果可为进一步开发利用此类三氮唑化合物提供科学合理的理论指导.     

无镉ZnO缓冲层的柔性CZTSSe太阳电池

针对铜锌锡硫硒（CZTSSe）薄膜太阳电池中CdS缓冲层带隙较小造成光损耗和Cd元素的毒性问题,提出无镉环保型CZTSSe太阳电池,分别采用溅射法和旋涂法来制备ZnO薄膜以替代CdS缓冲层.薄膜形貌表征及器件性能测试表明,相比旋涂法,溅射法制备的ZnO的薄膜质量及其CZTSSe器件性能明显更好,器件的光电转换效率（PCE）从1.0%提升到4.5%.同时,相比于CdS（E_g=2.4 eV）, ZnO具有更大的带隙（E_g=3.3 eV）,去除CdS膜层后,薄膜和器件在蓝光区具有更高的透光率和更好的光吸收.该设计为制备柔性CZTSSe太阳电池提供了一种新策略.     

掺杂对OLED发光效率的影响

概述了掺杂发光的种类、掺杂发光提高OLED发光效率的机制。