溶胶—凝胶法制备SnO2气敏薄膜的研究

以SnCl2.2H2O及乙醇为原料,利用溶胶－凝胶法制备SnO2纳米薄膜,探讨了制膜的工艺条件用XRD,SEM,TEM,AES以及XPS等研究了所得薄膜的结构性质,同时考察了薄的晶相结构、晶粒尺寸,表面形貌以及薄膜中元素的化学状态与热处理条件之间的相互关系。     

用Sol-Gel法制备气敏传感器SnO2薄膜的研究

采用无机试剂（ＳｎＣｌ４．５Ｈ２Ｏ）为原料,用溶胶－凝胶（Ｓｏｌ－Ｇｅｌ）法制备研制气敏传感的ＳｎＯ２薄膜,研究了ＳｎＯ２薄膜的电阻随掺杂和温度的变化关系,并且用ＸＲＤ对ＳｎＯ２薄膜进行分析,结果表明,掺杂和热处理温度对薄膜晶粒尺寸的大小、薄膜的结构形态均有较大的影响,进而影响薄膜的电导及传感器的灵敏度。     

二氧化锡超微粒子气敏薄膜的复数阻抗谱研究

用直流气体放电活化反应蒸发法制备了二氧化锡超微粒子薄膜，测量了薄膜的阻抗谱，验证了超微粒子薄膜的内部模拟等效电路。研究了温度、还原性气体以及热处理对阻抗谱的影响，并用氧吸附理论和晶界热垒理论定性地解释了这些现象。     

粉末溅射SnO2：Pt薄膜和SnO2／SnO2：Pt双层膜的气敏特性

用粉末溅射方法制轩了体掺杂型ＳｎＯ２：Ｐｔ薄膜和表面层掺杂ＳｎＯ２／ＳｎＯ２;Ｐｔ双层膜。实验结果表明,由室温至２００℃,这两种薄膜对ＣＯ气体均显示了较高的灵敏度和选择性。单层膜厚度和双层膜导电层及气敏层厚度对灵敏度有明显的影响。通过对掺杂单层膜和双层膜所敏特性的比较,对粉末溅射ＳｎＯ２薄膜的气敏响应机理进行了探讨。     

SnO2光透射率气敏薄膜的制备和研究

采用溶胶-凝胶技术，利用旋转涂膜法制备二氧化锡薄膜。结果发现，常温下在含有CO的气氛中光通过薄膜的透射率变大，对CO有较高的灵敏度。并对制备过程中出现的实验现象、制备机理及薄膜的结构和特性进行了分析和研究。     

粉末溅射SnO2：Pt薄膜及SnO2／SnO2：Pt薄膜电导在CO中的振荡现象

采用粉末溅射方法制备了体掺杂型ＳｎＯ２：Ｐｔ薄膜和ＳｎＯ２／ＳｎＯ２：Ｐｔ双层膜,这两种薄膜材料不仅对ＣＯ气体有很高的灵敏度,良好的选择性和较低的工作温度,而且其电导在ＣＯ气体中均出现了振荡现象,本分析了电导振荡温区、振幅和频率与ＣＯ气体浓度及膜厚的关系,介绍了其振荡特性并对有关问题进行了讨论。     

粉末溅射SnO2:Pt薄膜及SnO2/SnO2:Pt薄膜电导在CO中的振荡现象

采用粉末溅射方法制备了体掺杂型SnO2 :Pt薄膜和SnO2 /SnO2 :Pt双层膜 .这两种薄膜材料不仅对CO气体有很高的灵敏度 ,良好的选择性和较低的工作温度 ,而且其电导在CO气体中均出现了振荡现象 .本文分析了电导振荡温区、振幅和频率与CO气体浓度及膜厚的关系 ,介绍了其振荡特性并对有关问题进行了讨论     

用PECVD制备的薄膜H2敏元件研究

用ＰＥＣＶＤ法制备了具有较高灵敏度与选择性的Ｈ２薄膜元件。     

SnO2:Sb:Ni低温气敏薄膜的制备及性能研究

以无机盐SnCl4·5H2O,SbCl5,NiCl2·     

SnO2薄膜光透过率气体敏感机理的研究

以掺杂SnO2薄膜为例，推导了薄膜上透射光的消光系数与薄膜内极化电子数和极化电子迁移率的关系式。得出当环境气氛中待测气体的浓度变化时，将导致穿过薄膜的光的透射率与之发生响应，从理论上说明研制新式的气敏－光信号类型的传感器是可行的。     

MO-PECVD SnO2气敏薄膜的制备及表征

目的 探索制备SnO2薄膜的最佳工艺，研究氧分压与其薄膜元件气敏性能间的关系。方法 以金属有机化合物(MO)四甲基锡[Sn(CH3)4]为源物质，采用等离子体增强化学气相沉积技术(PECVD)。利用X射线衍射仪和扫描电镜(SEM)对薄膜的晶体结构、SnO2晶体的颗粒度进行了表征，对不同样品的气敏性能做了测试分析。结果 优化出制备SnO2薄膜的最佳工艺。结论 氧分压是影响SnO2颗粒尺寸大小及薄膜元件气敏性能的重要因素。     

射频反应溅射纳米SnO2薄膜气敏特性研究

采用射频反应溅射在瓷管上制备了SnO2气敏薄膜元件,以及用传统方法制备了SnO2厚膜元件.两种元件经测试表现出对乙醇较高的灵敏度,对两种元件进行了性能对比测试.测试表明,无论在灵敏度、响应恢复时间,还是在检测浓度范围上,SnO2气敏薄膜元件都比传统的厚膜元件性能优越.SnO2气敏薄膜元件经过表面修饰,在200×10-6体积浓度下接近30.对薄膜元件加热温度及选择性进行了研究,初步探讨了元件稳定性及其敏感机理.     

沉淀法制备纳米氧化锌的研究

通过实验和理论分析,对均匀沉淀法和直接沉淀法制备纳米ZnO进行了比较,结果表明：以硝酸锌为原料,尿素为均匀沉淀剂制得的纳米ZnO粒径小,分布窄,分散性好,收率大体相等,远优于直接沉淀法制备的纳米ZnO.     

Influence of laser doping on nanocrystalline ZnO thin films gas sensors

The effect of laser doping of Al on the gas sensing behavior of nanocrystalline ZnO thin films is reported. The doping of Al was carried out by the spin-coating of Al-precursors on nanocrystalline ZnO films followed by a pulsed laser irradiation. The laser-doped films were characterized as a function of laser power density by measuring the optical, structural, electrical, morphological and gas sensing properties of ZnO films. It was found that the laser doping process resulted in an increase of electrical conductivity of ZnO films. The performance of gas sensor was investigated for different concentrations of H2 and NH3 in the air. The results indicate that the laser doping process can be utilized to improve the sensor characteristics such as sensitivity and response time by optimization of laser power density. The optimum laser power is interpreted as the critical power level required to compete the effective doping versus developing the effective grain boundaries. Also, the selectivity of laser-doped ZnO sensors for H2 was studied for a likelihood practical gas mixture composed of H2, NH3 and CH4. It is found that these films can be optimized to develop H2 and NH3 sensors in PPM level with a higher selectivity over other reducing gases.     

溶胶-凝胶法制备纳米薄膜技术应用研究进展

溶胶-凝胶法制备的纳米薄膜材料除了具有某些普通膜材料的基本特性外,还具有许多新性能,如水质净化、光催化剂、自清洁、防尘、防雾、可见光透过率高和电阻率低等,这些性能在工业上都得到了广泛地应用。本文综述了近5年溶胶-凝胶法制备纳米薄膜技术应用的研究进展。     

溶胶-凝胶法制备纳米TiO2研究

采用溶胶-凝胶法制备纳米TiO2，讨论了反应过程中各影响因素对纳米TiO2粒度的影响，并设计正交实验优化出制备纳米TiO2实验条件，用透射电镜对制得的纳米TiO2粉末进行了表征．     

射频溅射法研制SnO2纳米薄膜

采用射频溅射工艺制得细小均匀的β－Sn纳米锡膜,然后通过氧化处理工艺获得组织非常细小均匀的纳米级二氧化锡薄膜。X－衍射实验结果表明Sn和SnO2晶粒尺寸分别约为6nm和5nm,采用该工艺获得的SnO2纳米薄膜结构比较稳定,为薄膜型SnO2气敏元件新工艺研究提供了基础性资料。     

钯催化三氧化钨薄膜对氢气的感应特性

以对氢气易于反应的钯为催化材料、钯的沉积厚度和热处理条件为变量,研究三氧化钨薄膜的物理化学性能及气体反应特性。结果表明,三氧化钨在500 ℃以上时呈现四方晶体的多晶态,钯沉积对三氧化钨的晶体结构没有影响,但是随着钯的添加抑制了三氧化钨的晶粒生长。500 ℃以上热处理时钯在薄膜表面呈现小球状,600 ℃以上热处理时钯粒子在薄膜表面凝结或扩散到材料内部。沉积钯 2 nm的薄膜在工作温度250 ℃时反应灵敏度和恢复特性对氢气的检测特性最好。     

磁控溅射制备In掺杂ZnO薄膜及NO2气敏特性分析

利用射频磁控溅射技术在玻璃衬底上成功制备了In掺杂的ZnO(ZnO∶In)薄膜。X射线衍射(XRD)和原子力显微镜(AFM)的研究结果显示所制备的ZnO∶In为纤锌矿的多晶薄膜,具有高度C轴择优取向。气敏研究结果表明ZnO∶In薄膜对NO2气体有较强的敏感性,最佳工作温度为273℃,其敏感度与薄膜的厚度和NO2气体的体积分数有关。ZnO∶In薄膜对较高体积分数的NO2气体的灵敏度较高,而薄膜比厚膜的灵敏度高,厚度为90 nm的薄膜在273℃时对体积分数为2×10-5的NO2气体的敏感度高达16,表明ZnO∶In薄膜具有检测较低体积分数NO2的能力。     

厚膜二氧化锡材料的气敏特性研究

用液相结晶和高温分解法制备偏离化学计量比的二氧化锡材料，对此二氧化锡进行掺杂，制成由一定原料配方组成的厚膜浆料，以此浆料用丝网印刷技术制备ＳｎＯ２厚膜气敏元件。然后，对系列元件进行气敏特性测试，所制备的ＳｎＯ２气敏元件表现出对乙醇气体的选择敏感性。