低真空对电渣重熔工艺和铸锭质量的影响

脱氧和夹杂物控制是电渣重熔钢锭质量提升的关键.分别在氩气保护的常压和低真空(10 kPa)条件下重熔H13电极,结合热力学计算,分析了低真空对电渣重熔工艺过程和铸锭质量的影响.结果表明,相比常压,低真空条件下渣池含气率升高,熔速波动更剧烈,所得电渣锭表面质量较差.常压和低真空条件制得电渣锭中总w_O分别为24×10^-6和18×10^-6,碳脱氧反应随压力降低而加强,并逐渐取代铝脱氧.相比Al-O平衡,10 kPa条件下与电极中w_C平衡的溶解w_O更低,因而能够进一步降低钢锭中w_O.碳脱氧产物是CO气体,不会引入新的夹杂物.常压和低真空条件制得电渣锭中夹杂物的类型没有明显区别,最大夹杂物尺寸从14.9μm分别减小到10.5μm和8.3μm,等效直径小于3μm的夹杂物检出比分别为63.85%和75.91%.低真空条件能够进一步细化夹杂物,提高钢锭洁净度.     

Effect of austenitizing temperature on microstructure in 16Mn steel treated by cerium

The change of inclusions and microstructure of 16Mn steel treated by Ce were observed, and the effect of austenitizing temperature on the microstructure was also examined. The results show that the inclusions are transformed from Si-Mn-Al composite oxide and MnS into AlCeO₃, Ce₂O₂S, and MnS composite inclusions after being treated by Ce. Plenty of intragranular ferrites are formed in 16Mn steel containing ～0.017wt% Ce. A large amount of intragranular acicular ferrites are formed after being austenitized for 20 min at 1473 K. The prior austenite grain size fit for the formation of intragranular acicular ferrites is about 120 μm.     

A coupled model of TiN inclusion growth in GCr15SiMn during solidification in the electroslag remelting process

TiN inclusions observed in an ingot produced by electroslag remelting (ESR) are extremely harmful to GCr15SiMn steel. There-fore, accurate predictions of the growth size of these inclusions during steel solidification are significant for clean ESR ingot production. On the basis of our previous work, a coupled model of solute microsegregation and TiN inclusion growth during solidification has been estab-lished. The results demonstrate that compared to a non-coupled model, the coupled model predictions of the size of TiN inclusions are in good agreement with experimental results using scanning electron microscopy with energy disperse spectroscopy (SEM-EDS). Because of high cooling rate, the sizes of TiN inclusions in the edge area of the ingots are relatively small compared to the sizes in the center area. Dur-ing the ESR process, controlling the content of Ti in the steel is a feasible and effective method of decreasing the sizes of TiN inclusions.     

Determination of inclusions in liquid steel after calcium treatment

Nozzle blocking was eliminated by calcium-treated liquid steel through changing the chemical and phase composition of alumina inclusions in aluminium-killed steel. Three different methods were applied to determine the composition of inclusions in liquid steel: total oxygen content samples, sampling spoon samples, and “lollipop” steel samples. The results show that calcium modification of liquid steel influences the inclusion composition varying from 2wt% to 14wt% depending on the method used. The composition of inclusions contains mainly Al₂O₃-CaO only, or is associated with SiO₂ or MgO depending on the initial input. The methods used in this study are indicators of the inclusion composition but can be improved to quantify the inclusion size.     

电流强度对电渣重熔304不锈钢中夹杂物特征的影响

利用实验室规模电渣炉在大气气氛下重熔304不锈钢,考察了不同电流强度(1500、1800、2100A)下电渣锭中夹杂物的特征及全氧含量、硫含量变化,并对钢中硫化物的析出行为进行了热力学分析。结果表明,电渣重熔过程可以有效去除钢中的夹杂物,但随着电流强度的增大,电渣锭的全氧含量和硫含量增加,夹杂物数密度及尺寸增大,电渣锭的洁净度恶化。当电流强度较低(1500A)时,电渣锭中夹杂物主要是以氧化铝为核心、外表裹有硫化物的双层结构,未发现单个的(Mn,Cr)S夹杂;而1800A和2100A重熔时,电渣锭中不仅有以Al-Si-Ca-Ti-Cr-Mn氧化物为核心、外围包裹着(Mn,Cr)S的双层结构夹杂,而且由于电渣锭中硫含量高和凝固过程中残余液相中溶质的富集,其中还有单个(Mn,Cr)S夹杂物存在。本试验条件下,在1500A下重熔更有利于提高304不锈钢电渣锭的洁净度。     

高拉速连铸低碳铝镇静钢铸坯中夹杂物

针对高拉速板坯连铸生产的低碳铝镇静钢铸坯,采用Aspex自动扫描电镜对铸坯表层夹杂物进行大面积的扫描分析,得到不同拉速下夹杂物的变化规律,并探究流场和S含量对夹杂物分布的影响。结果表明：随着拉速增大,钩状坯壳的深度和长度逐渐减小。对拉速大于2 m·min-1的铸坯,由于钩状坯壳不是很发达,铸坯表层没有发现大于200μm的夹杂物。铸坯表层尺寸介于50~200μm的夹杂物主要是由凝固坯壳所捕获,而夹杂物在凝固前沿的受力决定了夹杂物的捕获行为。随着拉速提高,凝固前沿的钢液流速增加,随着冲刷力的增加、捕获力的减少,夹杂物被捕获的数量减少。在高拉速连铸下,如果钢液中S含量较大,夹杂物受到明显的温度Marangoni力,会更容易被凝固坯壳捕获。     

低氧特殊钢中大尺寸DS类夹杂物生成机理

为了探讨低氧特殊钢中大尺寸DS类夹杂物的生成机理,通过ASPEX PSEM explorer自动扫描电镜对比分析国内外低氧特殊钢试样中夹杂物特征(国内、外试样各两个),发现国内试样中夹杂物平均尺寸大于国外试样,夹杂物的最大尺寸则数倍于国外试样：国内试样中夹杂物的最大尺寸分别为24.9和13.1μm,国外试样分别为7.6和7.5μm.对比国内外特钢试样中大尺寸与小尺寸夹杂物可发现二者成分基本相同,推断大尺寸DS类夹杂物可能是细小夹杂物碰撞长大而形成.通过分析大尺寸夹杂物的可能来源,在实验室通过高温共聚焦激光扫描显微镜观察夹杂物在钢中固/液相界面处的行为.结果发现,总氧降低至7×10-6时,尺寸5μm以下的微细夹杂物可被固/液相界面所捕捉,并在固/液相界面处发生碰撞、聚集、长大而生成大尺寸(>12μm) DS类夹杂物.     

高品质轴承钢LF--VD过程非金属夹杂物演变规律

对国内一钢厂EAF→LF→VD→CC工艺生产的高品质GCr15轴承钢进行系统取样,针对DS类非金属夹杂物随机性强的特点,利用能够进行大面积试样检测的ASPEX自动扫描电镜分析统计钢中非金属夹杂物的成分、尺寸、数量等信息。研究发现：GCr15轴承钢冶炼过程中非金属夹杂物主要为MgO- Al2 O3- CaO复合夹杂物和MnS,同时有少量的SiO2- Al2 O3和MgO-Al2 O3复合夹杂物;夹杂物尺寸主要集中在3~8μm,并有少量DS类夹杂物出现且尺寸范围波动很大,最大可以达70μm以上,形貌为圆形或近似圆形;VD有较强的去除夹杂物功能,经过VD真空精炼,夹杂物中CaO含量有增加趋势;吊包至铸坯过程,夹杂物成分向Al2 O3含量增多的区域移动,最终轴承钢铸坯中夹杂物成分位于高Al2 O3含量(≥80%),少量MgO (<20%)和低CaO(<5%)的区域;DS夹杂物的生成和去除具有较强的随机性。     

铝含量对TWIP钢中夹杂物特征及AlN析出行为的影响

采用扫描电镜、X射线能谱仪以及扫描电镜配置的夹杂物自动扫描统计软件(INCAFeature)表征了Fe-Mn-C(-Al)系TWIP钢中夹杂物的成分、形貌和数量,考察了Al质量分数在0.002%~1.590%的四种TWIP钢中夹杂物的特征和Al含量对AlN析出行为的影响.并在此基础上,采用了适合TWIP钢中高锰高铝特点的热力学参数对AlN夹杂物进行了系统的热力学分析.研究表明,在含有相似N质量分数(0.0078%~0.0100%)的TWIP钢中,当钢中Al质量分数升高至0.75%时,AlN夹杂物开始在钢中析出,并在MnS(Se)-Al2O3上局部析出形成MnS(Se)-Al2O3-AlN复合夹杂;当Al质量分数升高至1.07%时,热力学计算表明AlN已经可以在TWIP钢液相中形成,经不断长大后在MnS(Se)夹杂物表面局部析出形成MnS(Se)-AlN复合夹杂物;在Al质量分数为1.59%的TWIP钢中,AlN的平衡析出温度比其液相线温度高出42 ℃,在液相中形成的AlN可以作为异质核心,MnS(Se)夹杂在其表面包裹形成MnS(Se)-AlN复合夹杂物.另外,在Fe-18.21%Mn-0.64%C-1.59%Al体系的TWIP钢中,AlN在液相中析出所需的最低氮的质量分数仅为0.0043%.因此,在TWIP钢的冶炼过程中,应尽可能的降低钢中的氮含量,避免生成过量的AlN夹杂.     

IF 钢铸坯厚度方向洁净度演变

采用夹杂物原貌分析、扫描电镜和能谱分析、氧氮分析等手段系统分析了 IF 钢铸坯全厚度方向的洁净度变化及夹杂物分布规律.铸坯厚度方向全氧(T. O)和 N 质量分数平均值均为17×10-6.内、外弧表层1/16内 T. O、N 均高于平均值5%~10%,存在夹杂物聚集带;内弧1/4至外弧1/4区域 T. O、N 水平低于平均值5%~10%;表层1/16至1/4区域接近平均水平.共统计夹杂物963个,夹杂物平均粒径5.7μm,<5μm 占60%, < 10μm 占90%;Al2 O3夹杂主要存在表层5 mm 内,尺寸在2~10μm;TiN- Al2 O3和 TiN 粒子主要在距离表层5 ~ 80 mm,尺寸随深度增加而增大;TiN- TiS 和 TiS 夹杂主要在距离表面80~130 mm,尺寸1~5μm.从铸坯表层到中心主要夹杂物的分布依次是 Al2 O3、Al2 O3- TiN、TiN、TiN- TiS、TiS 和 MnS.     

Modification of MgO·Al<Subscript>2</Subscript>O<Subscript>3</Subscript> spinel inclusions in Al-killed steel by Ca-treatment

The modification of MgO·Al₂O₃ spinel inclusions in Al-killed steel by Ca-treatment has been studied by industrial trials and thermodynamic calculations. In the industrial trials, samples were taken systematically during the refining process in which the molten steel was treated by calcium, and the characters of the inclusions were analyzed using scanning electron microscopy (SEM) and energy dispersive spectra (EDS). The effects of Ca-treatment were evaluated by tracking the compositions of the inclusions. The results show that the modification of MgO·Al₂O₃ spinel inclusions by Ca-treatment is effective and the transformation sequence of the inclusions during the refining is Al₂O₃→MgO·Al₂O₃→liquid complex inclusions. The modification of spinel inclusions by Ca-treatment was calculated by FactSage6.0 utilizing its free-energy minimization routines. The results of thermodynamic calculations indicate that spinel inclusions are easier to be modified than Al₂O₃ inclusions and the spinel inclusions in 30CrMo steel would transform to liquid complex inclusions when the content of dissolved Ca in the molten steel exceeds 1×10⁻⁶. Also, the results show that adding more calcium into the molten steel would lower the contents of Al₂O₃ and MgO and increase the CaO content of the inclusions, while the change in SiO₂ content is little.     

电渣重熔与连铸轴承钢中的夹杂物

研究了电渣熔前后钢中氧及夹杂物的变化。结果表明，用电渣重熔工艺生产同承钢，虽然氧含量比连铸钢高，但其大颗粒夹杂物数量少，尺寸较小，分布均匀，因此疲劳寿命高。     

低温取向硅钢中第二相粒子的析出行为及热轧组织

研究了不同工艺生产的低温取向硅钢热轧板中第二相粒子的析出行为及其组织。结果表明,热轧板中的析出物除了弥散分布的纳米级球形或椭球形的Mn S、Cu2S外,还观察到与其形貌相似的Si O2、Al N和Si3N4及其复合在一起的复杂化合物。试样中微米级析出物主要为Si O2、Mn S、Cu2S和Al N的复合物,纳米级析出物主要为Al N、Si3N4、Mn S、Cu2S的复合物。热轧板中0.01~0.2μm的析出物数量最多,约占总数的99%。与常规热轧板相比,CSP试样中夹杂物面积密度较小,在大于1μm范围内其平均尺寸较大,会使得后期退火过程中二次再结晶不完整,影响产品磁性能。热轧板在垂直于轧向横截面上组织分布具有很大的差别,其中CSP试样组织相对比较均匀,不利于后续处理工艺中发展完善的二次再结晶织构从而获得良好的磁性能。     

Variation of Zr/Rb ratios on the Loess Plateau of Central China during the last 130000 years and its implications for winter monsoon

To find a new index of winter monsoon without effects of chemical weathering and pedogenesis is an important task in loess research. Chemical analysis of five grain size fractions (i.e. >32 μm, 32–20 μm, 20–8 μm, 8–2 μm and <2 μm) show that Zr is enriched in coarser grain size, while Rb is concentrated in finer fractions. An excellent correlation occurs between Zr/Rb ratios and mean grain size in loess units (L₁LL₁ and L₁LL₂) from Huanxian and Xifeng sections, reflecting that Zr/Rb ratios increase when grain size is coarser. Due to immobility of the two elements during the postdepositional process, Zr/Rb ratios can eliminate the effect of weathering and pedogenesis and serve as an excellent proxy on winter monsoon variation. The Zr/Rb ratio curves of the Huanxian, Xifeng and Luochuan sections during the last 130000 years show that the winter monsoon strength was very weak during MIS 3, which corresponded to the intensity during MIS 5.     

钙处理过程夹杂物演变及热力学分析

通过检测分析钙处理前后钢中夹杂物的形貌和成分的变化,探讨钢液钙处理过程中夹杂物演变规律.利用热力学计算,优化钙处理工艺.结果表明,钙处理可以将钢液中不规则固态夹杂物改性为球形液态夹杂物;1873 K下,当[ Al ]为0.030%时,[O]控制在5×10-6~17×10-6,[Ca]控制在0.7×10-6~30×10-6,钢中夹杂物变性效果良好;当[Al]为0.030%时,[ S]控制在6×10-6~19×10-6,既能使钢中Al2 O3夹杂生成液态铝酸钙夹杂物,同时又可以减少CaS生成.     

不同碱度精炼渣系对弹簧钢夹杂物的影响

哈贝马斯对《启蒙辩证法》的否定性解读,使得该著中的拯救逻辑遭到歪曲。由哈贝马斯的解读所延伸出的对《启蒙辩证法》拯救逻辑的美学化和精神分析化的重构与阿多尔诺的哲学思想相矛盾,由此我们必须重新反思哈贝马斯的解读模式。《启蒙辩证法》并非仅仅局限于工具理性批判,它通过有规定的否定达到了对现代启蒙当中现实权力因素的内在批判,它因此并没有彻底否定启蒙也没有重新树立新的乌托邦。对自然的回忆的拯救逻辑意味着思想必须对自身展开批判,以达到重新正视社会现实中的苦难现象,从而解构抽象主体的优先地位。     

Preparation of protein-loaded microspheres with size≤10 μm by electrostatic droplet generation technology

AT PRESENT, ALMOST ALL PROTEIN DRUGS HAVE TO BE CLINI- CALLY ADMINISTERED VIA INJECTION ROUTES SUCH AS INTRAVE- NOUS INJECTION. ONE OF THE IMPORTANT PROBLEMS CON- FRONTED IS THAT THESE DRUGS SHOULD BE INJECTED REPEATEDLY DUE TO SHORT HALF-LIFE IN BLOOD. I…     

Glass melt inclusion in clinopyroxene from Linqu Cenozoic basalt, Shandong Province, China

Melt inclusions or glasses usually occur in spinel- facies peridotitic xenoliths entrained in the global ba- salts[1―4], and olivine phenocrysts and/or xenocrysts carried in the intermediate-mafic volcanic rocks (such as basalts, basaltic andesites and h…     

Behaviors of different inhibitors during secondary recrystallization of a grain-orientated silicon steel

The behaviors of different inhibitors including their composition, size, distribution, coalescence and coarsening were experimentally studied. It was observed that during secondary recrystallization of the tested steel, the key inhibition effect was produced by Cu₂S and AlN, but not MnS. With the increase of temperature, the size distributions of AlN and Cu₂S were changed to some extent. However, significant changes in particle size were not observed. The initial temperature of abnormal growth was determined by measuring the evolution of particle sizes and their distribution density during heat treatment. AlN and Cu₂S are the dominant inhibitors and both are necessary, which is verified by calculating the Zener factor.     

Characteristics of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>, MnS,and TiN inclusions in the remelting process of bearing steel

The Al₂O₃, MnS, and TiN inclusions in bearing steel will deteriorate the steel's mechanical properties. Therefore, elucidating detailed characteristics of these inclusions in consumable electrode during the electroslag remelting process is important for achieving a subsequently clean ingot. In this study, a confocal scanning violet laser microscope was used to simulate the remelting process and observe, in real time, the behaviors of inclusions. The obtained images show that, after the temperature exceeded the steel solidus temperature, MnS and TiN inclusions in the specimen began to dissolve. Higher temperatures led to faster dissolution, and the inclusions disappeared before the steel was fully liquid. In the case of an observed Al₂O₃ inclusion, its shape changed from angular to a smooth ellipsoid in the region where the solid and liquid coexisted and it began to dissolve as the temperature continued to increase. This dissolution was driven by the difference in oxygen potential between the inclusion and the liquid steel.