使用循环放电法，研究在储氢合金中添加适量的钴系添加剂后的电化学性能。结果表明：添加Co、CoO、Co(OH)2的MH电极0．2C放电容量可以从原来的283mAh/g(Alloy)，提高到313ma/g(Alloy Co)、291mAh／g(Alloy CoO)及315mAh／g(Alloy Co(OH)2)，同时在电极中加入Co、CoO、Co(OH）2后，电极在放电过程中发生了Co的氧化反应，为电极提供了容量。     

负极添加剂CoO对储氢合金电极性能的影响

负极添加剂CoO在储氢金合金颗粒表面形成的Co膜有助于抑制合金粉的表面氧化和成分的偏析,进而减少电解液的损耗,因而有助于储氢合金负极和电池性能的提高.本文从电池内阻和容量衰减角度考察了CoO对电池循环寿命的影响.并以溶解—沉积理论为基础,利用循环伏安研究分析了CoO对储氢合金的保护机理..     

负极添加剂CoO对储氢合金电极性能的影响

负极添加剂CoO在储氢金合金颗粒表面形成的Co膜有助于抑制合金粉的表面氧化和成分的偏析，进而减少电解液的损耗，因而有助于储氢合金负极和电池性能的提高。本文从电池内阻和容量衰减角度考察了CoO对电池循环寿命的影响。并以溶解——沉积理论为基础，利用循环伏安研究分析了CoO对储氢合金的保护机理。     

一种改善La-Mg-Ni贮氢电极合金性能的方法

提出用放电等离子烧结技术(SPS)改善La-Mg-Ni贮氢电极合金的综合电化学性能.所选La-Mg-Ni贮氢电极合金为La0.7Mg0.3Ni2.5Co0.5.实验结果表明,用SPS和真空中频感应熔炼制备得到的合金具有近似的最大放电容量.SPS技术增强了合金电极的循环寿命:在经过150次的充放电循环后,用SPS法制备的La0.7Mg0.3Ni2.5Co0.5合金的容量保持率为61.8%;而感应熔炼法得到的合金电极的容量保持率仅为39.6%.同时用SPS技术使合金的放电中值电压增加,放氢平台变宽,平台倾斜度减小.     

稀土Ce对无Co过计量比CaCu_5型合金贮氢和电化学性能的影响

采用单辊甩带快速凝固方法制备过化学计量比稀土贮氢合金La1-xCexNi4.17Mn0.93Al0.1Fe0.4(AB5.6型,x=0~0.5),研究Ce元素部分替代La后对合金微观结构、储氢及电化学性能的影响.XRD分析及储氢性能测试结果表明,快淬过化学计量比合金的相组织均为过饱和CaCu5型结构单相,合金晶胞体积与Ce质量分数基本呈线性关系,其中合金的储氢量随Ce质量分数的增加而减小,而吸放氢平台压力增高.电化学测试和分析结果表明,随Ce质量分数的增加,合金电极的活化性能和放电容量有所降低,但电极循环寿命得到明显提高.当x=0、0.5时,合金电极的最大放电容量为328.9、305.4 mAh/g;当x≥0.3时,经100次循环后,合金电极容量保持率S100由x=0时的80%提高至93%~96%;合金电极的高倍率放电性能(HRD)随Ce质量分数的增加呈先减小后增加的趋势.     

D型MH/Ni电池过放电机理的研究

通过对D型密封MH／Ni电池在放电过程中电池电压和放电容量以及开口MH／Ni电池在放电过程中电池电压、正负极电极电位和放电容量的关系分析，探讨了电池的过放电机理。发现电池在放电全过程中存在着三种反应过程，而当电池深度过放电时，正极上析出氢气，负极上析出氧气。本文还采用循环伏安法对电池正负极的反应过程进行了研究，从而进一步说明了电池的过放电机理。     

Ni/MH电池负极用高容量稀土-镁-镍基储氢合金

通过感应熔炼方法制备了稀土-镁-镍基储氢合金Ml0.88Mg0.12Ni3.0Mn0.10Co0.55Al0.10(Ml代表富镧混合稀土).采用XRD和SEM分析了合金的微观结构,发现该合金主要由CaCu5型相、Ce2Ni7型相和Pr5Co19型相组成.电化学测试结果表明:合金的放电容量可以达到386 mA·h/g,比商品AB5型合金(332 mA·h/g)高出16.3%;在1 100 mA/g的放电电流密度下,合金的高倍率放电性能可以达到62%,高于商品AB5型合金(45%);充放电循环300次后,合金的放电容量降低到315 mA·h/g,为最大放电容量的81.5 %.     

La0.7Mg0.3Ni3.4-x(Al0.3Co0.4)0.2+x(x=0~0.3)合金电极电化学性能研究

在氩气保护下,采用悬浮熔炼法制备La0.7Mg0.3Ni3.4（Al0.3Co0.7）x（x=0,0.2,0.4,0.6）储氢合金,用X射线衍射仪测试相组成,并用MDI Jade 5.0软件分析相组成和晶胞参数,用开口三电极法测试电极电化学性能。结果表明,合金相主要由LaNi5、LaMg2Ni9、La2Ni7和LaNi2.28相组成,随着合金中Al和Co含量的增加,合金放氢平台压下降,最大吸氢量为1.43%（x=0）,合金电极最大放电容量Cmax为381mA.h.g-1（x=0）,合金电极100个充放循环后的容量保持率S100从53.0%（x=0）增加到57.1%（x=0.3）,循环稳定性增强。当x=0.1时,合金电极的电化学动力学性能较好。     

金属Cu对MH/Ni电池储氢合金电极的修饰

为了提高MH/Ni电池储氢合金电极的导电性,运用真空蒸镀法在电极表面镀覆了一层金属Cu膜,利用XRD、XPS、SEM等方法对极片进行了分析,结果表明,在极片表面镀覆一层金属Cu膜不会对储氢合金的体相结构产生影响.电化学性能测试表明:极片经过修饰的电池,内阻降低了32.8%,5 C放电容量增加了190 mA·h, 放电平台电压提高了0.10 V,同时,充电时的内压也有明显降低,充电效率有较大提高.     

La0.7Mg0.3-xTixNi2.8Co0.3(x=0.03,0.06,0.09,0.12)合金的储氢与电化学性能研究

用高频感应熔炼方法制备了La0.7Mg0.3-xTixNi2.8Co0.3(x=0.03,0.06,0.09,0.12)系列合金,并对其储氢和电化学性能进行测试.结果表明x=0.06时,合金储氢性能最好,气态储氢容量达1.2wt%,放电容量和比容量分别为336 mA.h.g-1,70.0%.     

Co/Co3O4双层膜中的交换偏置

在磁控溅射系统中利用Co靶和Co3O4靶制备了Co/Co3O4双层膜.振动样品磁强计(VSM)结果显示在测量温度高于Co3O4的奈耳温度时,交换偏置场HE仍然存在,多功能光电子能谱(XPS)分析表明在靠近Co层一侧Co3O4层被还原成一薄层的CoO.当Co3O4层的厚度低于3.5 nm时,Co3O4完全被还原成CoO.     

Magnetoresistive sensors with hybrid Co/insulator/ZnO:Co junctions

Magnetic tunnel junctions (MTJs), as the seminal spintronic devices, are expected for applications in magnetoresistive sensors due to their large magnetoresistance (MR) and high field sensitivity. Two hybrid Co/insulator/ZnO:Co junctions were fabricated with two different barriers to investigate the magneto-transport properties. Experimental results indicate that, both Co/MgO/ZnO:Co and Co/ZnO/ZnO:Co junctions show the positive and nearly linear MR, and their tunnel magnetoresistances (TMR) are 21.8% and 13.6%, respectively, when the current is applied perpendicular to the film plane under the magnetic field of 2 T at 4 K. The nonlinearity of MR is less than 1% within the magnetic field (H) of 1 kOe < H < 12 kOe at low temperature, making them attractive as magnetoresistive sensors. The higher MR of Co/MgO/ZnO:Co junctions is due to the superior spin filtering effect and larger effective barrier height of the MgO barrier. This linear MR characteristic of Co/insulator/ZnO:Co structures shows a promising future on the applications of diluted magnetic semiconductors in magnetoresistive sensors.     

LiF：Co~（2＋）和NaF：Co~（2＋）晶格中的Co~（2＋）－F~－键长

本文从光谱数据出发，用参量化的ｄ轨道理论确定了ＬｉＦ：Ｃｏ２＋和ＮａＦ：Ｃｏ２＋晶体中的Ｃｏ２＋－Ｆ－键长．结果表明：ＬｉＦ：Ｃｏ２＋中，Ｃｏ２＋－Ｆ－键长基本与未掺杂ＬｉＦ晶体中的Ｌｉ＋－Ｆ－距离相同；而ＮａＦ：Ｃｏ２＋中的Ｃｏ２＋－Ｆ－键长则有很大收缩，完全不同于未掺杂ＮａＦ晶格中的Ｎａ＋－Ｆ－键长．从杂质离子半径与被取代离子半径的差别引起的局域畸变及静电平衡机制引起局域畸变出发进行的讨论表明，所得结果是合理的     

具有垂直各向异性的Co/Pt多层膜中各Co层之间铁磁性耦合

使用磁控溅射法制备了一系列具有不同Pt中间层厚度的glass/NiO(1.nm)/[Co(0.4.nm)/Pt(0.5.nm)]3/Pt(xnm)/[Co(0.4.nm)/Pt(0.5.nm)]3样品并对Co层之间的铁磁性耦合强度进行了测量.整体磁滞回线和局部磁滞回线的测量结果表明,上下两层Co/Pt多层膜之间的铁磁性耦合强度随着Pt中间层厚度的增加单调减小,当Pt中间层厚度超过4.nm时铁磁性耦合消失.除了上下两层Co/Pt多层膜之间通过Pt中间层产生的铁磁性耦合作用之外,它们之间也存在弱的次耦合作用,这导致底层出现宽的磁滞.     

单晶样品Pr3Co和Nd3Co的磁化率测量

我们对金属间化合物 Pr3Co和 Nd3Co单晶样品的磁化率在磁场 H=14π× 1 0 7A/M,温度范围为77K～ 3 0 0 K的条件下进行了测量 ,并计算得出它们的有效玻耳磁子     

虚拟社区共创用户体验对用户共创价值的影响

根据服务主导逻辑理念和价值共创理论,构建了共创用户体验、用户共创价值和行为意向的影响关系模型;并进行了结构方程模型实证研究.同时运用层次回归分析法分析了用户共创价值在共创用户体验和行为意向关系中的中介效应.研究结果表明,共创用户体验对用户共创价值具有显著的正向影响;实用价值和享乐价值均对行为意向产生了显著的正向影响,并且享乐价值的影响更为显著;用户共创价值在共创用户体验和行为意向关系中具有部分中介效应作用.     

Co薄膜的磁滞回线标度行为

采用磁控溅射法制备了多晶的Co薄膜,研究了其结构、磁滞行为和标度关系.实验结果表明:Co薄膜具有简单立方结构和沿膜面的易磁化方向;沿Co磁性薄膜的易磁化方向所得到的标度指数值α=0.90,与其它实验和理论计算结果相近;而对于沿难轴方向,Co磁性膜的标度指数(α=1.8)比沿易磁化方向的要大得多,这种差异有待进一步的理论研究.     

Al－Co合金富Co区相图计算与性质

应用经验电子理论和集团变分方法计算了Ａｌ－Ｃｏ合金富Ｃｏ区的相图。研究了无序－有序相的原子状态和相互作用的变化。     

上海商赢商务有限公司

上海商赢商务有限公司成立于2008年.注册资金1000万元,是一家从事电子消费卡平台运营、维护服务及提供银行卡外包业务的专业化服务公司. 公司以自主开发的积分平台为技术依托,以积分累积、积分兑换、积分充值、资源互换等为核心理念,通过金融PAS、专用金融终端及     

华信邮电咨询设计研究院有限公司

华信邮电咨询设计研究院有限公司（原浙江省邮电规划设计研究院有限公司），成立于1984年，是浙江省科技厅认定的高新技术企业，持有国家颁发的甲级通信和建筑工程设计证书，甲级智能建筑工程设计证书，甲级工程咨询证书，甲级通信信息系统集成资质证书和对外承包工程经营资格证书，公司1997年7月在全国邮电设计同行业中首家通过ISO9001国际质量保证体系认证，连续五年被评选为全国勘察设计百强企业，2003年荣获信息产业部先进集体荣誉称号。2006年获全国用户满意企业称号。[第一段]