微胶囊膜厚对芯料释放速率的影响

采用光学显微镜二次聚焦法测定出微胶囊膜厚,通过理论公式计算出微胶囊芯料的释放速率,从而揭示出微胶囊膜厚对芯料释放速率的影响规律,结果表明:在实验范围内,甲醛用量、复凝聚次数、芯料用量、搅拌速度、乳化时间等工艺条件发生变化时微胶囊膜厚、表观扩散系数对芯料的释放速率影响极大,尤其膜厚对释放速率起着决定作用     

香精微胶囊的制备及其性能研究

以香精为芯料,以明胶-阿拉伯胶为囊材,通过复凝聚法制备出一系列不同工艺条件下的微胶囊,分别测得微胶囊的内径、外径和膜厚,从而揭示出微胶囊制囊工艺对微胶囊性能的影响规律。     

α－淀粉酶的微胶囊化与酶缓释的研究

用乙基纤维素微胶囊包埋α－淀粉酶，研究了膜相乙基纤维素浓度、芯材与膜相体积比、明胶浓度和干燥温度对芯材包坦率及微胶囊粒径分布的影响。根据芯材释放动力学方程探讨了α－淀粉酶通过微胶囊壁微孔的缓释性能，测定了渗透系数。     

壳聚糖亚微粒稳定的Pickering乳液制备pH响应微胶囊

采用离子凝胶法制备了壳聚糖-三聚磷酸钠(CS-TPP)亚微米颗粒,并以其为稳定剂,制备了内含聚乳酸-羟基乙酸共聚物(PLGA)和布洛芬(IBU)药物的o/w型Pickering乳液;采用溶剂挥发法制备了CS-TPP亚微米颗粒包覆的载药微胶囊,并通过静电作用包覆羧甲基纤维素钠(CMC).利用SEM、光学显微镜、荧光共聚焦显微镜、红外光谱等对载药微胶囊进行了表征.以IBU为模型药物,在模拟胃液(SGF,pH=1.2)和模拟肠液(SIF,pH=6.8)中进行载药微胶囊的体外药物释放实验.结果表明:所得载药微胶囊在SIF中释放速率为其在SGF中的约12倍,表现出良好的pH响应性.     

基于非离子复合乳化剂自修复微胶囊的制备

提出采用低起泡性的OP-10/AEO非离子复合乳化体系解决微胶囊制备过程中乳化缺陷问题。以改性环氧树脂E-51为芯材修复剂,通过原位聚合法制备脲醛树脂自修复微胶囊。采用光学显微镜、傅里叶红外光谱仪、同步热分析仪分别对形成过程、化学结构及热稳定性进行分析。利用Gauss拟合研究粒径分布,并探讨了乳化剂体系选择、乳化剂用量、芯壁比、搅拌速率等因素对微胶囊性能的影响。结果表明,该体系能有效改善乳化剂起泡效果,用量为5.0%,芯壁比为0.8∶1,搅拌速率为1 200 r/min,微胶囊包封率达到80%,粒径分布相对集中,具备良好的室温贮存性及热稳定性。     

智能自修复高分子材料用高稳定性微胶囊的制备

针对高分子材料的自修复,选取双环戊二烯（DCPD）作为芯材,采用三聚氰胺-尿素-甲醛树脂为壁材,对其进行微胶囊化包裹。通过激光粒度分析仪、光学一摄影显微镜、微机差热天平和傅里叶变换红外光谱仪对微胶囊的粒径分布、表面形貌、热性能和化学结构等进行了表征。讨论了芯材投料量、乳化剂用量以及乳化速率对微胶囊物性的影响。结果表明：所得微胶囊的平均粒径和囊芯含量可以通过选择不同工艺参数得到控制,其囊芯含量最高约90wt．％,体积平均粒径为50～70μm。     

密胺树脂包覆甲基丙烯酸正丁酯微胶囊的制备

以甲基丙烯酸正丁酯（BMA）为囊芯,密胺树脂为高分子囊壁材料,采用原位聚合法制备具有自修复功能的微胶囊.利用激光粒径分布仪、光学显微镜、微机差热天平和傅里叶变换红外光谱仪分别研究了微胶囊的粒径分布、表面形态、热性能和化学结构.讨论了乳化剂用量、搅拌速度以及芯材与壁材的投料质量比对微胶囊制备工艺的影响.结果表明：所得微胶...     

脲醛树脂包覆双环戊二烯微胶囊的制备

以双环戊二烯为芯材,脲醛树脂为壁材,采用原位聚合法制备了脲醛树脂微胶囊。通过扫描电子显微镜（SEM）、热失重分析（TGA）、光学显微镜（OM）和傅里叶变换红外光谱（FT-IR）等对微胶囊进行了测试和表征。结果表明,所制备的微胶囊平均粒径为150μm,脲醛树脂囊壁的厚度为10μm,微胶囊分解温度为150℃,囊芯质量分数可达65%左右,且囊壁有良好的密封性。     

喷雾干燥法制备A群链球菌微胶囊

采用喷雾干燥法制备A群链球菌微胶囊,以明胶、阿拉伯胶为壁材,以A群链球菌为芯材,将芯材与壁材按照1：12．5的比例进行喷雾干燥。经SEM和显微镜测定表明,制备的A群链球菌微胶囊外形比较圆整。     

负载萃取剂的微胶囊膜的构筑与传输性能研究

以聚苯乙烯(PS)为膜材料,磷酸三丁酯(TBP)为载体,采用复乳-液中干燥法构筑了负载萃取剂的微胶囊膜,并以Cr~(6+)的废水模拟溶液考察微胶囊膜的传输性能。结果表明:微胶囊膜的传输性能随着载体TBP在微胶囊膜中的浓度的增加而增强,随着微胶囊膜膜厚的增加而减弱。微胶囊的富集容量随外相中的Cr_2O_7~(2-)浓度的增加而加大。Cr_2O_7~(2-)在微胶囊膜中的传输,在初始阶段是化学吸附和浓差渗透共同作用的结果,后期逐渐为单纯的浓差渗透的结果。     

DETERMINATION OF MEMBRANE THICKNESS OF MICROCAPSULE

A new optical microscope duplex focus method is proposed to determine membrane thickness through direct measuring the interior and outer diameters of microcapsules by optical microscope duplex focusing.     

STUDY ON THE PERMEABILITY OF MICROCAPSULES

In the present study,microcapsules with disperse dye solutions and a direct dye solution ascore materials were prepared by the complex coaeervation method and the interfacialpolycondensation method respectively.Experiments and theoretical analysis showed that there wasan exponential relationship between the diffusion time and the release rate of the core material intothe surrounding medium.A concise equation to calculate the permeability constant was derivedand verified by the experimental results.By means of duplex focus on the inner and outer diametersof a microcapsule,the average wall thickness of microcapsules was measured.     

Effect of Membrane Thickness on Core Release Rate of Microcapsule

Membrane thickness of microcapsule is measured by op-tical microscope duplex focusing,the core release rate iscalculated by theoretical formula,and the effect of mem-brane thickness on release rate is revealed.As a result,with changes of formaldehyde dosage,complex coacerva-tion times,core dosage,agitation speed and emulsifica-tion time,membrane thickness and apparent diffusioncoefficient are of great importance on core release rate,but membrane thickness is dominant.     

Effect of Membrane Thickness on Permeability Coefficient of Microcap-sule

The effect of membrane thickness of mieroeapsule, measured by optical microseope duplex focusing, on its permeability coefflcient is discussed. The results reveal that the membrane thickness is of great imiportance on the permeabillty coefficient with changes of formaldehyde dosage, complex coacervation times, core dosage, agitation rate and emulsification time.     

羧甲基甲壳素/海藻酸钙固定化双歧杆菌的研究与应用

双歧杆菌是人和动物肠道中一种重要的益生菌,具有许多生理和保健功能。实验使用厌氧培养箱培养筛选获得双歧杆菌;经鉴定为革兰氏阳性菌(G+)。选用海藻酸钠作为成膜材料、羧甲基甲壳素作为保护剂、Ca Cl_2作为固化液,通过挤压法将双歧杆菌包埋在了微胶囊里;将得到的微胶囊分别置于胃液、肠液中并测定其溶解情况,得到了制备微胶囊的配比和最适浓度。使用2.14%海藻酸钠、1.79%羧甲基甲壳素制备双歧杆菌微胶囊,能够得到最好的包埋效果,菌体包埋率可达66.81%;此结果可为双歧杆菌微胶囊的高效生产提供一个参考。     

明胶/海藻酸钠复合体系用于pH敏感智能药物释放体系的研究

用明胶/海藻酸钠聚合物交联互穿网络作为基材 ,以戊二醛和氯化钙溶液为交联剂 ,对质子泵抑制剂药物奥美拉唑进行包覆 ,制备pH敏感型微胶囊药物制剂。测定了不同交联时间及pH值环境下的释放规律 ,研究结果表明 ,此制剂具有在酸性环境中持续释放 ,且释放百分率较小 ,而在碱性环境中为突释型制剂。此包覆体系适用于在酸性环境(如胃)中需要保护药效 ,防止药物失活 ;在碱性环境(如小肠)中发挥药效的药物制剂。     

阿霉素微胶囊的制备及表征

采用三嵌段共聚物聚乳酸-聚乙二醇-聚乳酸（PLA-PEG-PLA）为载体,阿霉素为模型药物,通过双乳化溶剂蒸发法制备出阿霉素微胶囊,考察了稳定剂和制备条件对阿霉素微胶囊的性质及阿霉素的载药率和释放速率的影响。扫描电子显微镜和激光粒度测试表明,阿霉素微胶囊呈类球形或不完全球形,粒径大小为900nm左右。阿霉素微胶囊对阿霉素的包封率为35.7％。通过体外释药实验表明,阿霉素微胶囊可持续释药10天以上。     

黄芩苷缓释微囊的制备方法及稳定性的研究

目的研制黄芩苷缓释微囊并进行稳定性考察。方法运用复凝聚法以明胶和阿拉伯胶为囊材,黄芩苷为囊心物,吐温-80为润湿剂制备微囊。以包封率作为质量判定指标,采用单因素考察和正交试验优化处方工艺。结果得出最优处方是明胶和阿拉伯胶浓度皆为1．33％g／mL,反应温度50℃,pH值3．90,材药比为5：1。按该处方制得的微囊囊型圆整光滑,载药量较高,并具有一定的缓释效果。结论复凝聚法可成功制备出包封率较高的黄芩苷微囊,且产品稳定性良好。该法可操作性强,重复性好,有一定的实用价值。     

囊芯包覆量变化对光热敏微胶囊特性的影响

采用界面聚合技术制备了以囊芯质量为变量的光热敏微胶囊,利用红外光谱及热显影技术对其光聚合及热显影特性进行了检测.红外光谱检测结果表明,光热敏微胶囊中预聚单体三羟甲基丙烷三丙烯酸酯(TMPTA)随囊芯包覆质量的增加聚合速度逐渐加快,聚合程度逐渐增大;从热显影结果可以看出随囊芯质量增加显影密度逐渐增大,且曝光前后的密度反差也同时逐渐增大,热显影检测结果与红外检测具有一致性,根据实验结果得到了囊壁与囊芯最佳质量比为1/2.17.