Fe_2O_3/TiO_2复合纳米管阵列的制备及其可见光催化性能研究

在氟化铵-乙二醇体系中,采用阳极氧化法在铁基体上制备Fe_2O_3纳米管阵列,然后以氟钛酸铵为钛源,利用水热法在Fe_2O_3纳米管阵列上负载TiO_2纳米片,制得Fe_2O_3/TiO_2复合纳米管阵列,利用SEM、EDS、XRD、TEM、UV-Vis等手段,对所制Fe_2O_3/TiO_2纳米管阵列的表面形貌、物相结构及光催化性能进行表征,并分析Fe_2O_3/TiO_2纳米结构对亚甲基蓝的可见光降解能力。结果表明,Fe_2O_3/TiO_2复合纳米管阵列具有良好的可见光响应;NH_4F浓度为0.4%、水热反应3h制备的Fe_2O_3/TiO_2复合结构具有最佳的光催化性能,对亚甲基蓝的降解率可达90%。     

Ag/α-Fe_2O_3/g-C_3N_4光催化降解罗丹明B

为了使g-C_3N_4光生电子和空穴容易复合,改善可见光响应低等缺点,该实验中采用溶胶-凝胶法将g-C_3N_4和α-Fe_2O_3进行复合形成g-C_3N_4异质结光催化剂,再采用光沉积法将Ag沉积在α-Fe_2O_3/g-C_3N_4上,构建Z型机制Ag/α-Fe_2O_3/g-C_3N_4催化剂材料,改善光生电荷的分离和传输能力及可见光响应,进一步增强其光催化降解污染物活性.最后通过XRD、FT-IR、XPS、SEM、TEM、紫外-可见漫反射光谱表征光催化剂结构和性能,并以染料罗丹明B溶液模拟废水,研究催化剂的降解动力学特性,通过活性基团捕获实验探究光催化机制.实验结果表明:(1)α-Fe_2O_3和g-C_3N_4复合形成异质结,当α-Fe_2O_3负载量为3%时,α-Fe_2O_3/g-C_3N_4光催化性能比纯的g-C_3N_4有了明显的提高,光催化性能降解罗丹明B达到79%.(2)Ag负载在α-Fe_2O_3/g-C_3N_4,当Ag的负载量为3%时,在可见光下3.5 h能够对罗丹明B达到95%以上的降解.(3)Ag/α-Fe_2O_3/g-C_3N_4增强的光催化剂性归因于α-Fe_2O_3和g-C_3N_4形成异质结以及Ag加入后形成Z型异质结结构.     

核壳结构Fe3O4@SiO2纳米粒子的制备及表征

为丰富Fe_3O_4磁性纳米粒子在生物医学领域的应用,通过共沉淀法制备Fe_3O_4纳米粒子,经柠檬酸三钠修饰后,采用改进的Stber法成功在Fe_3O_4纳米粒子表面包覆上SiO_2,制备出核壳结构Fe_3O_4@SiO_2纳米粒子。使用扫描式电子显微镜、X射线衍射仪、傅里叶变换红外光谱仪、振动样品磁强计对制备的Fe_3O_4@SiO_2纳米粒子进行表征。结果表明:制备的Fe_3O_4@SiO_2纳米粒子较Fe_3O_4纳米粒子分散性有明显的提高,平均粒径在65 nm左右,饱和比磁化强度为10.26 A·m^2/kg,仍具有良好的超顺磁性。     

磁性Fe3O4/In2S3可见光催化剂的制备及其性能

采用简单的油浴法制备出磁性Fe_3O_4/In_2S_3可见光催化剂,利用XRD、SEM、FTIR、BET、UV-Vis DRS以及磁滞回线等手段对其进行表征,以可见光(λ≥420 nm)为光源,以罗丹明B的光催化降解为模型反应,考察不同Fe_3O_4/In_2S_3复合比的磁性Fe_3O_4/In_2S_3可见光催化剂的催化性能及循环使用性能.结果表明,当物质的量n(Fe_3O_4)与n(In_2S_3)之比为6∶5时制备的磁性Fe_3O_4/In_2S_3可见光催化剂具有最好的光催化活性.光照90 min后,罗丹明B的降解率高达96%;磁性Fe_3O_4/In_2S_3可见光催化剂的饱和磁化强度达10.31 A·m2·kg-1,在外加磁场作用下,5 s内可以快速从水相中分离,具有良好的磁分离效果;样品经3次循环使用后其催化活性基本保持不变.     

RGO/TiO_2/Fe_3O_4复合纳米材料的制备及其对甲基橙废水的脱色效果

通过水热法制备Fe_3O_4磁性纳米微球,以此为核包覆TiO_2,并将核壳结构的TiO_2/Fe_3O_4附着在还原氧化石墨烯(RGO)片层结构上;利用扫描电镜(SEM)、透射电镜(TEM)、N2吸附-脱附、X射线衍射仪(XRD)、震动样品磁强计(VSM)和X射线光电子能谱(XPS)表征了RGO/TiO_2/Fe_3O_4磁性复合纳米材料的形态结构、包覆情况、磁性和元素种类,同时考察了该催化剂在紫外光照射下催化脱色甲基橙的效果。实验结果表明,TiO_2均匀地包覆在Fe_3O_4表面,RGO/TiO_2/Fe_3O_4磁性复合纳米材料的比饱和磁化强度为19.0emu/g。以甲基橙的水溶液为模拟污染物,紫外光照射90min后RGO/TiO_2/Fe_3O_4复合纳米材料对甲基橙的脱色率达到91%。     

Bi2O3/电气石复合催化剂的制备及其光催化性能

以电气石为载体,采用化学沉淀法制备Bi_2O_3/电气石复合光催化材料。通过XRD、SEM、UV-Vis等方法对制备的复合型催化剂进行了表征,并在可见光照射下对催化剂的光催化活性进行了测试。结果表明:复合型催化剂扩展其光响应范围,且复合后的Bi_2O_3比纯的Bi_2O_3比表面积更大,在处理酸性红B实验中表现出良好的可见光催化活性。实验发现复合物含5%电气石的制备比例就可以显著提升Bi_2O_3降解有机物活性,60 min时降解率达到97.32%,明显优于单纯Bi_2O_389.77%降解率,提高了光催化剂的降解效率。     

氨基硅烷修饰的荧光磁性复合纳米粒子的合成

以共沉淀法制备得到了Fe_3O_4磁性纳米粒子,以溶胶-凝胶法得到了包裹罗丹明6G的氨基硅烷修饰的荧光磁性复合纳米粒子(Fe_3O_4/R6G)@SiO_2-APTES,以动态光散射法(DLS)测定了复合纳米粒子的水合粒径,以IR光谱、荧光光谱等手段对得到的复合纳米粒子进行了表征,并以琼脂糖凝胶电泳研究了(Fe_3O_4/R6G)@SiO_2-APTES对DNA的损伤行为。研究结果表明这类氨基硅烷修饰的荧光磁性复合纳米粒子在水中具有很好的分散性和稳定性,且有良好的生物相容性,有望成为一种新的抗癌药物载体。     

ZnO@(Fe_3O_4/ZnS:Mn~(2+))复合空心药物载体的生物相容性研究

通过自组装的方法制备ZnO@(Fe_3O_4/ZnS:Mn~(2+))复合空心药物载体,考察ZnO@(Fe_3O_4/ZnS:Mn~(2+))复合纳米微球对HepG2、HK2和大鼠原代肝细胞活性的影响,同时考察ZnO@(Fe_3O_4/ZnS:Mn~(2+))复合纳米微球在ICR小鼠体内对小鼠脏器比、血生化指标的影响.结果表明,ZnO@(Fe_3O_4/ZnS:Mn~(2+))复合纳米微球具有很好的生物相容性.     

魔芋葡甘聚糖/纳米四氧化三铁复合溶胶的流变性能

为了研究魔芋葡甘聚糖/纳米Fe_3O_4_静电纺丝膜,运用流变仪分析纳米Fe_3O_4对KGM溶胶流变性能的影响,以期为制备复合的纺丝液的浓度和配比提供了指导。结果表明:KGM/纳米Fe_3O_4复合溶胶是一种假塑性流体;复合溶胶的粘度、线性粘弹区域范畴、屈服应力值、模量等四个指标均与纳米Fe_3O_4掺杂比的掺杂比呈正比关系,从剪切性质分析其体系纳米Fe_3O_4质量浓度不应超过1.2%。通过频率扫描分析,纳米Fe_3O_4与KGM之间存在相互作用,随着纳米Fe_3O_4粒子含量的增加使得与KGM作用增加,从而使体系形成稳定网络结构,使复合溶胶的稳定性更高,因此将魔芋葡甘聚糖/纳米Fe_3O_4制备静电纺丝膜具有一定可行性。     

Yb_2O_3/g-C_3N_4复合光催化剂的制备及光催化性能研究

为了验证可见光下Yb_2O_3/g-C_3N_4光催化剂分别降解水体中的苯酚和盐酸四环素(TTCH)的光催化效果.本研究采用热解和超声混合方法制备Yb_2O_3/g-C_3N_4光催化剂,并用多种仪器进行性能表征.Yb_2O_3/g-C_3N_4在可见光下对20 mg/L苯酚和TTCH的降解率分别为80.83%和85.01%;Yb_2O_3/g-C_3N_4复合光催化剂的光催化性能明显提高,其降解苯酚的速率是g-C_3N_4的3.80倍,降解TTCH的速率g-C_3N_4的6.57倍.结果表明,Yb_2O_3/g-C_3N_4具有更加高效的可见光响应能力,且具备更好的光催化性能.     

Lead-bismuth-free piezoceramics （Na0.5K0.44Li0.06）Nb0.95Sb0.05O3-Na5.6Cu1.2Sb10O29

Newly developed sintering aid Na5.6Cu1.2Sb10O29 (NCS) and lead-bismuth-free piezoceramics (Na0.5K0.44Li0.06) Nb0.95Sb0.05O3 (NKLNS) were prepared by the conventional solid state reaction. The effects of sintering aid NCS on the electrical properties of NKLNS were investigated. It was found that the addition of a proper amount of sintering aid NCS to NKLNS is effective not only on improving the density and the piezoelectric activity, but also on reducing the dielectric loss of NKLNS. The NKLNS doped with 0.4 mol% NCS has a piezoelectric constant d33 as high as 261pC/N and an electromechanical coupling factor k33 above 60%. These results show that NCS-doped NKLNS is a promising and practicable candidate for lead-bismuth-free piezoceramics.     

Single-negative properties of Ba2Co1.8Cu0.2Fe12O22 and Ba3Co2Fe23.4Zn0.6O41 hexagonal ferrites

The electromagnetic properties of Ba₂Co_1.8Cu_0.2Fe₁₂O₂₂ (Co₂Y) and Ba₃Co₂Fe_23.4Zn_0.6O₄₁ (Co₂Z) were studied by measuring microwave scattering parameters. In the transmission spectra of Ba₂Co_1.8Cu_0.2Fe₁₂O₂₂, a forbidden band emerges due to ferromagnetic resonance, and the permeability will turn to negative in the vicinity of the ferromagnetic resonance frequency. In the complex permittivity spectra of Ba₃Co₂Fe_23.4Zn_0.6O₄₁, the negative permittivity can be obtained due to dielectric resonance. Therefore, Co₂Y and Co₂Z can be used to construct left-handed materials possessing negative permeability and negative permittivity simultaneously.     

TiO2/Al2O3-Al2O3-TiO2/Al2O3绝缘结构的真空沿面闪络特性

基于变插入层介电常数的多层绝缘结构能改善电场分布、提高真空沿面闪络特性.通过真空热压烧结制备了TiO2/Al2O3-Al2O3-TiO2/Al2O3(A-B-A)3层绝缘结构,A层w(TiO2)为0.5%到20%.测量了该绝缘结构的真空沿面闪络特性,发现闪络特性随w(TiO2)的增加而提高,当w(TiO2)为20%时,其脉冲初次闪络电压较同等厚度的Al2O3陶瓷提高了63%.研究发现:A层的介电常数可由w(TiO2)调控,介电常数的增大能有效降低真空-绝缘子-阴极三结合点处的电场强度;A层表面存在的TiO2颗粒可以减小二次电子发射系数并改善表面电荷分布;TiO2的电导率虽比Al2O3高,但其仍为绝缘体,即使TiO2含量较高时也不会形成贯穿的导电通道.     

CaO-ZrO2-TiO2-Al2O3-B2O3-SiO2玻璃陶瓷的制备及化学稳定性研究

玻璃陶瓷是固化处理中、高放废物和α废物较为理想的候选材料之一。研究了特定条件下制备的CaO-ZrO2-TiO2-Al2O3-B2O3-SiO2体系玻璃陶瓷在水淬和空气中自然冷却的两种冷却制度对其结晶行为和显微结构的影响,用粉末浸泡实验方法测试了其化学稳定性。结果表明:自然冷却形成的玻璃陶瓷晶相主要是ZrSiO4和ZrTiO4;在25～70℃范围内,温度对玻璃陶瓷浸出率无明显影响,90℃下浸出率比25℃,40℃,70℃的浸出率高一个数量级;7 d元素总的归一化浸出为1.87 g/m2。     

在Na3AlF6-AlF3-CaF2-LiF-Al2O3体系中低温铝电解

Based on the main physico-chemical properties of Na₃AlF₆-AlF₃-CaF₂-LiF-Al₂O₃ system studied, including liquidus temperature、electrical conductivity and bath density, a laboratory scale vertical discharging aluminum type electrolysis cell of about 100A capacity was run with TiB₂ cathodes and low molar ratio(1.5～2.0) electrolytes at 800～930℃ range. Aluminum metal was obtained with 84.6%～88.3% current efficiencies and 11.54～11.83 kW^.h/kg specific energy consumption.     

关于Euler-致型方程x^2-D1y^2=2s^2和x^2-D2y^2=-2t^2

设D1，D2是无平方因子正整数，该文给出了方程组x^2-D1y^2=2s^2和x^2-D2y^2=-2t^2有本原整数解(x，y，s，t)的必要条件。     

Crystallization Mechanism of Na2O-CaO-Al2O3-SiO2-F- Glass Containing Cr2O3

The effect of Cr₂O₃ on the nucleation and crystallization of Na₂O-CaO-Al₂O₃-SiO₂-F- glass has been investigated by means of ESR(Electron Spin Resonance), SEM(Scanning Electron Microscope), EDS(Energy Dispersive Specrometer) and so on. Computer pattern recognition is applied to optimize the heat-treatment schedules. The experimental results show that the base glass containing more than 1.5 % (mass fraction) Cr₂O₃ can be nucleated internally and converted to spheroidal crystal glass materials. The spheroidal crystal consisted of fibrous wollastonite crystals radiating from a center. The residual glass phase filled in the interstices between the fibers and between the spherulites. During heat treatment process, the valence states ofchromium changed from Cr6- to Cr3-, and the Cr-spinel solidsolution [CaCr₂O₄] precipitated followed this valence change. At the primary stage of crystallization, the Cr-spinel could act as a nucleating center on which the principal or}stalline phase β-CaSiO₃ grew epitaxially.     

二维磁性NbSi2N4-WSi2N4-NbSi2N4异质结的光生电流效应

采用量子输运方法研究了二维(2D)磁性NbSi₂N₄-WSi₂N₄-NbSi₂N₄面内异质结的光生电流效应.该异质结具有C2v非空间反演对称性,在可见光范围内,用线偏光垂直及倾斜照射时,均能激发显著的光生电流效应,产生自旋极化且偏振敏感的光电流.光电流与偏振角(θ)和入射角(α)均为余弦依赖(cos(2θ),cos(2α))关系.两种照射方式下均能产生纯自旋流及完全自旋极化的光电流.在垂直照射时,能取得完美的自旋阀效应.这些结果表明,二维磁性NbSi₂N₄-WSi₂N₄-NbSi₂N₄异质结在低能耗自旋电子学及低维光电探测领域具有应用潜力.