二氧化硫复合盐雾环境下2024-T351铝合金应力腐蚀开裂

通过SO2复合盐雾试验模拟工业污染海洋大气环境,结合有限元模拟分析、扫描电镜/能谱仪、光电子能谱分析等技术研究2024-T351铝合金在弹性应力区间的应力腐蚀开裂行为.结果表明:应力腐蚀开裂行为优先发生在2024-T351铝合金C型环的顶部应力集中区域;疏松的腐蚀产物层的形貌经历了由细棒状、团絮状到板块状的变化;试验6h就可以监测到裂纹,进行到480h的时候有贯穿裂纹形成,720h的时候试样完全断裂;裂纹为穿晶和沿晶混合机制,主裂纹以穿晶机制沿C型环法线扩展,二次裂纹沿晶界扩展.     

涡轮叶片用GH4033高温低周疲劳特性实验研究

采用总应变控制方法,在INSTRON8032上对镍基高温合金GH4033在400、500、600、700 ℃温度下的疲劳行为进行了研究,用扫描电镜观察了疲劳断口.采用Manson-Coffin方程对实验结果进行了分析,得到了该材料的高温低周疲劳特性参数.从断口的扫描电镜照片中看出:高温疲劳失效断口的萌生区断裂机制为沿晶断裂,扩展区为沿晶和穿晶断裂的混合断裂,失稳断裂区为穿晶断裂.     

应力集中对2024铝合金高周疲劳寿命的影响

研究了2024铝合金常温下的高周疲劳性能,获得了2024铝合金在不同应力状态下的S-N曲线.分析了疲劳试样的断口形貌和裂纹萌生/扩展机理,以及疲劳试样的组织结构与疲劳性能之间的关系.结果表明,疲劳极限随着应力集中系数的增加而降低,当应力集中系数相同时,疲劳极限随着应力比的减小而降低;2024铝合金的疲劳断口以穿晶断裂为主;第二相颗粒起到了阻碍疲劳裂纹扩展的作用,使2024铝合金的高周疲劳强度得到了明显提高.     

应力比对6082T651铝合金疲劳裂纹扩展行为影响

利用液压伺服疲劳试验机对6082T651铝合金进行疲劳裂纹扩展速率测试,研究不同应力比R对疲劳裂纹扩展行为的影响以及疲劳裂纹稳定扩展区断口观察。结果表明:应力比对疲劳裂纹扩展行为有显著影响,较高应力比下的疲劳裂纹扩展速率要高于较小应力比下的疲劳裂纹扩展速率。应力比对Paris公式中的C值影响较大,对m值影响相对较小。稳定扩展区断口形貌特征以疲劳台阶、韧窝和疲劳辉纹为主。     

22Si2MnCrNi2MoA钎杆断裂失效分析

运用金相观察、扫描电镜观察和能谱定量分析等实验手段,从组织状态、夹杂物、断口形貌等方面分析了22Si2MnCrNi2MoA钎杆内螺纹处断裂原因,同时对其疲劳裂纹起源和扩展进行了探讨.22Si2MnCrNi2MoA钎杆内螺纹处断裂破坏并不是由组织异常和夹杂物引起的,而是由于22Si2MnCrNi2MoA钎杆存在明显的壁厚不均,在高频应力、严重的内外耗同时存在的应力状态下持续工作,壁厚较薄处极易成为受力薄弱区,疲劳裂纹更倾向于在此处优先形成,从而致使壁厚较薄处优先断裂,最终导致钎杆断裂失效.该钎杆疲劳破坏起源于内表面,属于多源的疲劳断裂.起源区微观形貌为韧窝形貌,扩展区的微观形貌为韧窝和沿晶的混合形貌.     

22Si2MnCrNi2MoA钎杆断裂失效分析

运用金相观察、扫描电镜观察和能谱定量分析等实验手段,从组织状态、夹杂物、断口形貌等方面分析了22Si2MnCrNi2MoA钎杆内螺纹处断裂原因,同时对其疲劳裂纹起源和扩展进行了探讨.22Si2MnCrNi2MoA钎杆内螺纹处断裂破坏并不是由组织异常和夹杂物引起的,而是由于22Si2MnCrNi2MoA钎杆存在明显的壁厚不均,在高频应力、严重的内外耗同时存在的应力状态下持续工作,壁厚较薄处极易成为受力薄弱区,疲劳裂纹更倾向于在此处优先形成,从而致使壁厚较薄处优先断裂,最终导致钎杆断裂失效.该钎杆疲劳破坏起源于内表面,属于多源的疲劳断裂.起源区微观形貌为韧窝形貌,扩展区的微观形貌为韧窝和沿晶的混合形貌.     

6005A合金搅拌摩擦焊接头疲劳性能的研究

对6005A—T6铝合金FSW接头、母材以及MIG焊接头进行了疲劳性能试验对比研究。结果表明,FSW接头的抗拉强度约是母材抗拉强度的82．5％;MIG焊试样的抗拉强度约是母材抗拉强度的73．4％。当循环周次N〉10^7时,FSW试样的疲劳强度值接近于母材,约为母材疲劳强度值的93％,而MIG焊试样的疲劳强度值仅为母材的67％。FSW接头热影响区的断口疲劳区形貌为准解理和韧窝的组合形貌。准解理型穿晶扩展裂纹与FSW接头热影响区中原母材枝晶结构有关,断口扩展区形貌为韧窝状形貌。     

XCQ16和20Mn2车轴用钢疲劳失效的微观机理

利用扫描电镜(SEM)对XCQ16和20Mn2两种车轴用钢疲劳断口和裂纹扩展断口进行分析,研究疲劳失效过程中的裂纹萌生及扩展机理.结果表明:裂纹均是从试样表面萌生,非金属夹杂和位错是主要的萌生机制;XCQ16钢在疲劳断口中部区的裂纹闭合效应大于20Mn2钢,裂纹扩展较慢;两者在裂纹扩展区的扩展机理不同,XCQ16钢属于塑性断裂,20Mn2钢属于解理断裂;在非金属夹杂上,XCQ16钢多含氧化物和硫化物的混合夹杂,20Mn2钢主要是氧化物夹杂,混合夹杂对材料的疲劳性能影响较小.     

鞍钢1700初轧机蓄势器的断裂控制

利用断裂力学的理论对鞍钢1700初轧机蓄势器确定了疲劳裂纹扩展参数,估算出疲劳裂纹扩展寿命,制成蓄势器的断裂控制图,以达到在延长探伤周期内,蓄势器能够安全服役的目的。可供轧钢厂工程技术人员参考。     

航空铝合金预腐蚀疲劳寿命退化规律

航空铝合金材料在服役过程中常因腐蚀损伤而导致疲劳断裂问题,通过采用扫描电镜及疲劳寿命测试等方法,研究了不同预腐蚀损伤对2xxx铝合金在不同应力比下疲劳寿命的影响,探讨了预腐蚀损伤对疲劳裂纹萌生扩展的影响机理.结果表明:预腐蚀损伤对2xxx铝合金材料疲劳寿命的影响显著,材料的疲劳性能随着腐蚀损伤程度的增加而明显下降.同时建立了预腐蚀损伤对材料疲劳极限的影响系数C-T-R模型,材料疲劳极限的影响系数C随着预腐蚀时间的增加或者应力比R的增加而变大.断口分析表明,预腐蚀损伤的存在导致裂纹萌生寿命大大缩短,裂纹萌生由单源转变为多源,并且均萌生于腐蚀坑处.     

Al-Cu-Li合金轧制厚板的 疲劳性能及断裂机理研究

利用疲劳试验机、扫描电子显微镜(SEM)和透射电子显微镜(TEM)等设备研究了95 mm厚的Al-Cu-Li合金热轧板材不同方向的组织特征、疲劳性能和断裂机理.结果表明:Al-Cu-Li合金热轧厚板的力学性能和疲劳性能均存在各向异性.LT向(横向)的力学性能和疲劳性能均优于L向(纵向)和ST向(高向),L向(纵向)的力学性能较ST向更好,但疲劳性能较ST向更差.Al-Cu-Li合金厚板的疲劳裂纹源主要出现在试样表面、近表面的夹杂物和晶界处.裂纹扩展过程中,LT向裂纹扩展路径较L向更曲折,ST向具有典型的解理特征,瞬断区形貌与静态拉伸断口相似.晶界越多,裂纹扩展阻力越大,LT向和ST向的未溶第二相能够有效阻碍裂纹扩展,导致其疲劳性能优于L向.     

TA6V钛合金疲劳断口形貌及断口分析

在进行TA6V钛合金疲劳小裂纹实验的基础上,使用KYKY2800B型扫描电镜(SEM)对TA6V钛合金疲劳断口形貌进行疲劳源区及其裂纹扩展形状、扩展区、瞬断区形貌的观察,分析TA6V钛合金疲劳断口形貌形成的原因,为其结构疲劳安全设计及可靠性分析提供科学依据,为今后TA6V钛合金在我国的使用提供参考。     

Aging behavior and fatigue crack propagation of high Zn-containing Al-Zn-Mg-Cu alloys with zinc variation

In the present work, the influence of two-step aging treatments on hardness, electrical conductivity and mechanical properties of two high Zn-containing Al-Zn-Mg-Cu alloys with zinc content variation was investigated and the detailed T76 aging parameters were proposed. The microstructure of the precipitates were studied by transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HREM) and then quantitatively investigated with the aid of an image analysis. The fatigue performances were researched by the fatigue crack propagation (FCP) rate test and fracture morphology was observed with scanning electron microscopy (SEM). The results show that the matrix precipitate size distributions of both alloys had significant difference, so as to fatigue crack propagation rates and fracture appearance. The shear and bypass mechanisms of dislocation-precipitate interactions were employed to explain the difference. Among the shearable precipitates, the proportion of larger size precipitates for the higher zinc content alloy is bigger than that for the lower zinc content alloy. The coarse shearable precipitates hinder the propagation of the fatigue cracks, leading to inferior FCP rate. For both alloys, the shear mechanism possesses the dominant factor, finally causing a preponderance in the FCP resistance for the higher zinc content alloy than the lower one.     

6N01-7N01铝合金T型焊接接头的微观组织与性能的研究

6N01和7N01铝合金是高铁列车车体上大量使用的2种重要的轻量化结构材料.本文利用EBSD、光学显微镜、维氏硬度测试和加速腐蚀实验研究了典型6N01-7N01铝合金T型焊接接头的微观组织、硬度分布和腐蚀特性.结果表明:焊缝、熔合区和热影响区的晶粒组织特征存在显著差异.焊缝组织为等轴晶,熔合区组织为等轴晶和柱状晶.靠近焊缝处的6N01合金存在部分晶粒异常长大现象,而7N01合金仅发生了回复和部分再结晶.6N01合金一侧的热影响区会出现硬度比焊缝更低的硬度谷,即软化区,这是由析出相受焊接热的影响发生明显的粗化导致的.经腐蚀实验后,焊缝的硬度显著降低,焊缝和热影响区为焊接接头腐蚀最严重的区域.     

Ti6Al4V高锁螺栓疲劳断口形貌及断口分析

在进行Ti6Al4V高锁螺栓疲劳实验的基础上,使用扫描电镜(SEM)对Ti6Al4V高锁螺栓疲劳断口形貌进行疲劳源区、裂纹扩展区和瞬断区形貌的观察,分析高锁螺栓疲劳断口形貌形成的原因,为其结构疲劳安全设计提供科学依据,为今后Ti6Al4V高锁螺栓的国产化提供参考。     

TiAl＋Ca合金断裂及变形亚结构研究

运用ＳＥＭ和ＴＥＭ等分析手段研究了ＴｉＡｌ＋Ｃａ三元合金的室温断裂行为和变形亚结构．结果表明，少量Ｃａ的添加可以大幅度提高Ｔｉ－３４％Ａｌ合金的室温力学性能．合金断裂时不再表现为单纯的穿晶解理断裂而在γ单相中出现了河流状的解理纹，断口上还出现较多的撕裂梭；ＴＥＭ分析表明，Ｃａ的添加有助于１／２＜１１０］正常位错的启动；Ｔｉ－３４％Ａｌ－１．０％Ｃａ合金压缩变形时产生大量的位错环，当Ｃａ含量达到２．０％时，在γ相中出现了由于位错分解而产生的层错．     

固溶处理对2E12铝合金组织及疲劳断裂行为的影响

通过对2E12铝合金进行493 ℃/20 min和503℃/20 min固溶处理,研究固溶处理对2E12合金室温拉伸及疲劳性能的影响.采用X线衍射分析、扫描电镜和金相分析对合金组织及疲劳断口进行观察.研究结果表明:提高固溶处理温度对合金拉伸性能影响不大,但可明显减少合金中残留相(Al2Cu,A12CuMg)的含量;经503 ℃/20 min处理后合金的拉伸强度较经493℃/20 min处理后合金的拉伸强度略有提高,但其疲劳寿命延长约20％;合金中残留相在疲劳过程中容易开裂形成微小二次裂纹,在主裂纹扩展过程中起到桥接作用,从而加速疲劳裂纹扩展,降低合金疲劳性能.     

碳纤维增强镁合金层合板拉伸性能和层间断裂韧性

玻璃纤维增强铝金属层合板,已广泛应用于航空、航天等领域。现采用密度更小的镁合金板取代铝合金板,并用抗拉强度更高、弹性模量更大的碳纤维来代替玻璃纤维,会得到一种新型的复合材料——碳纤维增强镁合金层合板。通过对不同纤维/树脂复合材料体积比的碳纤维增强镁合金层合板进行拉伸以及单悬臂梁试验,分别得到其强度、刚度及界面断裂韧性等机械性能。并与工程实际中广泛使用的玻璃纤维增强铝合金层合板进行比较。结果表明,碳纤维增强镁合金层合板具有比玻璃纤维增强铝合金层合板更高的比强度、比刚度以及界面断裂韧性。碳纤维增强镁合金层合板是一种非常有前途的新型复合材料。     

Near-microscopic grain boundary facilitates fatigue crack propagation in a polycrystalline Al–Zn–Mg–Cu alloy

In present study, grain characteristics with sizes within 10–30 μm were fabricated from a same Al–Zn–Mg–Cu alloy, FCP behaviors of the alloys with small grain(SG alloy), medium grain(MG alloy) and large grain(LG alloy)were investigated and related fatigue fracture morphology was analyzed. With the enhancement of stress intensity factor range(ΔK), the alloy with larger grains possessed faster FCP rate, which were successively arranged as SG alloy > MG alloy > LG alloy at initial stage while...     

HRB500E高强度抗震钢筋焊接性能

国内某厂通过铌微合金化和控冷工艺开发试制HRB500E高强度抗震钢筋,采用金相显微镜、维氏硬度计、闪光焊接、疲劳试验机及力学性能测试,对HRB500E钢筋焊接样力学性能、HV5硬度、金相显微组织、焊接接头强度及疲劳强度进行了试验研究。结果表明:焊接前后焊件和母材强度变化小于5 MPa,强度变化不大,焊件拉伸断口远离焊缝,为延性断口,焊接性能良好;在焊接热循环作用下,焊接接头焊缝、热影响粗晶区、热影响细晶区的表层和芯部经历奥氏体化后再结晶,其组织和硬度变化不大;混晶区至母材表层和芯部则经历不完全奥氏体化后的再结晶,母材芯部组织为F+P+B、表层组织为S,表层硬度HV5高于芯部硬度30 HV5,其组织和硬度变化较大;焊接接头的抗拉断负荷从焊缝到混晶区逐渐减小,焊缝和热影响粗晶区的抗拉断负荷比母材的高;采用国际焊接学会推荐的FAT75疲劳设计曲线对钢筋焊接接头疲劳强度设计是安全的。