草酸作用下不同粒径纳米Fe3O4的光催化氧化合成及其磁性能

采用空气氧化法,在可见光和微量草酸作用下,室温条件进行了不同粒径(10.5～30.2 nm)纳米Fe3O4的制备及其磁性能研究.结果表明:在可见光作用下,随草酸络合剂的添加,纳米Fe3O4的粒径减小,均匀性及分散性有所提高;在微量草酸存在下,随光照度的增强,纳米Fe3O4的粒径有所减小;Fe2+与草酸的络合增强了对可见光的利用率,加快了体系的氧化速率,高的反应速率使纳米Fe3O4晶粒减小;不同粒径纳米Fe3O4分别呈现出不同的磁性能.     

纳米Fe_3O_4颗粒的制备及磁性能

采用X-ray衍射、高能X-ray衍射、透射电子显微镜及振动样品磁量计等表征手段,研究了不同制备工艺对Fe3O4纳米粒子的平均晶粒尺寸及磁性能的影响.结果表明多元醇方法所制备的Fe3O4粉体平均粒径为32 nm,其饱和磁化强度为6.8×10-3A/m(该值比块体Fe3O4的饱和磁化强度约降低了8%),剩磁Mr=4.2×10-3A/m,矫顽力Hc=1.43×10-2T;通过共沉淀方法得到的Fe3O4粉体平均粒径显著减小为7 nm,但是其饱和磁化强度也明显降低为3.3×10-4A/m,比块体Fe3O4的饱和磁化强度减小约96%,剩磁及矫顽力也下降为零.这是由于小尺寸效应导致出现超顺磁现象,说明Fe...     

磁性聚四氟乙烯密封材料的制备及性能

以纳米Fe3O4为主要增强填料,采用冷压成型和烧结固化工艺制备磁性聚四氟乙烯(PTFE)密封材料.分析不同纳米Fe3O4填充量对材料抗拉强度、断裂伸长率、硬度、线膨胀系数等性能的影响.结果表明:纳米Fe3O4填充量对材料性能具有显著影响,随填充量的增加,硬度增大,抗拉强度先增大后减小,断裂伸长率和线膨胀系数迅速下降.当纳米Fe3O4质量分数为5%时,填料在PTFE基体中分散性较好,硬度和拉伸强度均有所提高,断裂伸长率下降38%,线膨胀系数下降18%,PTFE密封材料性能得到提高.     

溶剂热法制备纳米Fe3O4粉体

通过溶剂热法,以FeOOH作为前驱体,以油酸作为表面活性剂,以十八烯为溶剂,制备了纳米Fe3O4颗粒,研究了油酸和FeCl3用量、反应时间对纳米Fe3O4粒子的大小以及分散性的影响.结果显示,FeCl3用量的增加和反应时间的延长均可使Fe3O4粒子粒径增大,油酸用量的增加会导致Fe3O4粒子粒径先减小再增大.利用XRD、TEM等手段对所制备颗粒的结构、形貌进行了表征,结果表明,所制备的纳米Fe3O4粒子属于反尖晶石结构.FeCl3用量为0.003mol,油酸用量为13.5mL时(即Fe3+/油酸约为1/15),在230℃反应12h得到结晶度较高,分散性良好,平均粒径比较小的纳米Fe3O4粒子.     

EDTA对Mn（OH）2空气氧化反应的影响

用X -射线衍射法(XRD)研究了EDTA 络合剂对Mn(OH)2 空气氧化反应的影响.结果表明:在30 ℃条件下,Mn(OH)2 的氧化产物为Mn3O4 晶体;当EDTA 在反应液中的浓度为2.5m m ol·L- 1情况下,氧化时间由原来不加EDTA 时的4h 缩短为50m in,EDTA可提高氧化反应速率,并且使Mn3O4 晶粒度减小,沿垂直于(211)面方向晶粒度的减小最明显.对EDTA 的作用机理做了简要讨论     

环氧化物溶胶凝胶路线制备近单分散尺寸可控Fe3O4纳米粒子

以二价铁盐为原料,利用环氧化物的胶凝或沉淀作用,以乙醇或水作为反应介质,在较低的温度下制备Fe3O4纳米粒子.表征结果表明,以H2O为溶剂可得到粒径在25～83 nm之间粒度分布较宽的Fe3O4纳米颗粒,而以乙醇为介质时,可得到粒度分布窄近单分散Fe3O4纳米粒子.由于该路线在制备纳米氧化物方面具有反应条件温和、工艺简单、原料价廉和易于规模化制备等优点,显示出其具有工业化前景.     

聚吡咯-Fe3O4纳米复合材料的制备与表征及性能

用共沉淀方法制备出平均粒径在10 nm左右的Fe3O4纳米粒子,然后在阳离子表面活性剂的引导下采用原位化学氧化聚合法,合成出聚吡咯-Fe3O4纳米复合材料.同时对此纳米复合材料的结构和性能进行了研究.结果表明Fe3O4纳米粒子和聚吡咯之间存在着一定的相互作用,从而有利于吡咯单体在Fe3O4纳米粒子的表面发生聚合反应,进而Fe3O4纳米粒子被聚吡咯所包覆.聚吡咯/Fe3O4纳米复合材料同时具有导电性和磁性,其导电性随着Fe3O4纳米粒子含量的增加先增大后减小,磁性则始终随着Fe3O4纳米粒子含量的增加而增大.     

Fe3O4纳米粉体的制备与表征

化学共沉淀法制备了纳米Fe3O4粉体,采用无水乙醇和水按体积比6:1作为溶剂,研究了溶剂中乙醇同时作为溶剂和分散剂对纳米Fe3O4粉体制备的作用.考查了氢氧化钠、氢氧化钾等强碱和氨水作为沉淀剂对纳米Fe3O4粉体制备的影响;pH值对产物的影响;Fe3+与Fe2+的摩尔比对产物的影响.采用X射线衍射仪、高分辨透射电镜、差热分析仪及傅立叶红外仪等对产品的成分、形貌及热效应等进行了表征.结果表明制得的立方晶体纳米Fe3O4粉体平均粒径在20nm之内,而且粒径分布比较均匀.     

壳聚糖/Fe3O4复合纳米颗粒的制备

以柠檬酸为改性剂,制备水基Fe3O4磁性纳米粒子,基于静电自组装作用,使壳聚糖分子在水溶液中包覆Fe3O4纳米晶粒,获得壳聚糖/Fe3O4复合纳米颗粒液溶胶。扫描电子显微镜（SEM）分析结果表明,复合纳米颗粒平均粒径为49.0 nm,标准差为11.0 nm。X射线衍射（XRD）和红外光谱（FT-IR）分析结果表明,复合纳米颗粒由壳聚糖分子和Fe3O4晶体粒子构成。     

Fe3O4/SiO2磁性微球的制备研究

报道了Fe3O4/SiO2纳米复合材料的可控合成方法.研究并探讨了乙醇-水体系配比及氨水和硅酸四乙酯的用量对纳米粒子形貌的影响,利用柠檬酸作分散剂,控制反应条件对Fe3O4纳米粒子进行表面修饰改性后,又对其进行SiO2包覆.然后运用X射线衍射仪（XRD）、透射电子显微镜（TEM）、红外（IR）对合成的纳米微粒的粒径、结构进行了表征.实验结果表明,产物为粒径均匀的单分散Fe3O4/SiO2复合纳米粒子,平均粒度约为100 nm.     

(LiFe)xZn1-2xFe2O4铁氧体的吸波性能研究

采用固相烧结工艺,按不同配方分别制备了(LiFe)xZn1-2xFe2O4(x=0.1、0.2、0.3、0.4、0.45、0.5),用Agilent8510c矢量网络分析仪测试,在0.5～13GHz频段内材料的吸波性能.实验发现(LiFe)0.45Zn0.1Fe2O4有较强的吸波性能,然后再对(LiFe)0.45Zn0.1Fe2O4进行不同搀杂,并在0.5～18GHz频段内测试材料的吸波性能,发现掺入1wt%的Al2O3对增加-10dB带宽非常有效果.     

Synthesis and characterization of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>@SiO<Subscript>2</Subscript> magnetic composite nanoparticles by a one-pot process

Fe₃O₄@SiO₂ core–shell composite nanoparticles were successfully prepared by a one-pot process. Tetraethyl-orthosilicate was used as a surfactant to synthesize Fe₃O₄@SiO₂ core–shell structures from prepared Fe₃O₄ nanoparticles. The properties of the Fe₃O₄ and Fe₃O₄@SiO₂ composite nanoparticles were studied by X-ray diffraction, transmission electron microscopy, energy dispersive spectroscopy, and Fourier transform infrared spectroscopy. The prepared Fe₃O₄ particles were approximately 12 nm in size, and the thickness of the SiO₂ coating was approximately 4 nm. The magnetic properties were studied by vibrating sample magnetometry. The results show that the maximum saturation magnetization of the Fe₃O₄@SiO₂ powder (34.85 A·m2·kg–1) was markedly lower than that of the Fe₃O₄ powder (79.55 A·m2·kg–1), which demonstrates that Fe₃O₄ was successfully wrapped by SiO₂. The Fe₃O₄@SiO₂ composite nanoparticles have broad prospects in biomedical applications; thus, our next study will apply them in magnetic resonance imaging.     

纳米Fe3O4颗粒及其磁流体的制备与研究

以氨水为沉淀剂,利用改进的化学共沉淀法制备粒径分布均匀的超顺磁性纳米Fe3O4颗粒.采用X射线粉末衍射仪(XRD)、傅里叶红外光谱仪(FT-IR)、振动样品磁强计(VSM)及透射电子显微镜(TEM)等方法对试样进行了结构与性能表征.结果表明:当n(Fe3+)/n(Fe2+)=1.75,温度为60℃,pH值为9时,超声波预处理制备的Fe3O4颗粒平均粒径在23 nm左右,饱和磁化强度(Ms)达到61.63 emu/g,具有超顺磁性.同时利用油酸钠和聚乙二醇4000(PEG 4000)的协同作用制得了稳定分散的纳米Fe3O4磁流体,当二者加入量与纳米Fe3O4颗粒质量比均为2.00∶3.48时,制备的纳米Fe3O4磁流体最稳定.     

表面巯基化Fe3O4纳米粒子的一步合成及表征

以FeCl3为铁源,在生物小分子L-半胱氨酸(L-Cys)、水和丙三醇的混合体系中,采用溶剂热法一步合成L-Cys包覆的Fe3O4复合纳米粒子Fe3O4/L-Cys.通过粉末X射线衍射(XRD)、红外光谱(IR)、热重-差热分析(TG-DTA)等表征Fe3O4/L-Cys复合纳米粒子的晶体结构;采用Zeta电位测量和酸...     

纳米Fe3O4磁流体的制备及表征

采用化学沉淀法制备纳米Fe3O4颗粒,并以聚乙二醇为改性剂,蒸馏水为载液,制备出固体质量分数为10%的纳米Fe3O4磁流体.用XRD研究Fe3O4纳米粒子的结晶情况;用FT-IR研究聚乙二醇改性前后Fe3O4粒子表面官能团的变化;用TEM研究Fe3O4颗粒的粒径大小及改性情况;用VSM研究Fe3O4粒子的磁性能.结果表明,制备的纳米Fe3O4为立方晶型,平均粒径在15 nm左右,聚乙二醇物理吸附在Fe3O4表面,Fe3O4颗粒几乎没有磁滞,具有超顺磁性.     

高分散Fe3O4磁性液体的制备和表征

制备高分散稳定的磁性颗粒是研究磁性液体的磁性、流变性能以及其它物理性质的实验基础.用化学共沉淀法制备了高分散的Fe3O4煤油基磁性液体,通过X射线衍射、透射和扫描电镜等实验技术,对纳米Fe3O4 颗粒的形态和结构进行了表征,并用Bayesian统计理论计算了颗粒的尺寸分布,静态磁场下磁性液体显示了良好的超顺磁性和胶体系统的稳定性.     

Bi2Fe4O9的制备及光催化性能研究

用Bi(NO3)3.5H2O和Fe(NO3)3.9H2O为基本原料,采用共沉淀法合成了Bi2Fe4O9粉体,用XRD和SEM测试了不同制备条件下得到的Bi2Fe4O9粉体的晶体结构和形貌,XRD结果表明在650℃～750℃直接煅烧2h可得到纯相Bi2Fe4O9粉体,SEM结果表明随着灼烧温度的提高,晶粒的尺寸增加,750℃时晶粒呈片状,UV-Vis分析表明,Bi2Fe4O9在可见光区域有较强的吸收,光催化性能表明,Bi2Fe4O9粉体对甲基橙降解效果较好。     

磁性纳米TiO2/Fe3O4的制备及光催化去除甲基紫的研究

采用溶胶-凝胶法,在磁性纳米Fe3O4表面包覆TiO2制备磁性纳米TiO2/Fe3O4复合光催化剂.用XRD、SEM、FTIR对其表面结构进行表征,结果显示Fe3O4表面被锐钛型的TiO2包覆,该磁性纳米光催化剂颗粒分布均匀,平均粒径为80～100 nm.将纳米TiO2/Fe304用着光催化剂去除水中的甲基紫染料,在紫...     

PEG为软模板水热法合成NiFe2O4

以聚乙二醇(PEG)为软模板,采用水热法合成了尖晶石型NiFe2O4纳米晶,考察了PEG分子量对样品的影响,并对样品进行了X射线衍射,振动样品磁强计,扫描电镜,低温氮吸脱附和原子发射光谱表征.结果表明合成的NiFe2O4纳米晶具有尖晶石结构且粒度分布较为均匀.以PEG-400为软模板水热合成的样品粒度小、比表面积较大、饱和磁化强度较高；PEG-1500合成的样品粒度稍大、饱和磁化强度较高.