带镀层300M超高强度钢应力腐蚀行为与机理研究

利用慢应变速率拉伸试验（ＳＳＲＴ）和预裂纹平面应变（ＷＯＬ）试样,研究了电镀Ｃｒ、Ｃｄ－Ｔｉ及真空离子镀Ａｌ对国产３００Ｍ高强度钢的力学行为和应力腐蚀断裂行为的影响,揭示了带镀层３００Ｍ钢应力腐蚀开裂（ＳＣＣ）机制。结果表明,电镀过程中钢基体渗氢与镀层的缺陷使３００Ｍ钢基体的塑性受损失,真空离子镀Ａｌ对３００Ｍ钢的力学性能无明显影响;阴极镀层加速的电偶腐蚀,对镀Ｃｒ３００Ｍ钢的ＳＣＣ过程有明显的促     

18Mn5Cr护环钢的应力腐蚀开裂

用慢应变速率拉伸试验方法研究了１８Ｍｎ５Ｃｒ护环钢在９０℃去离子水和２２％ＮａＣｌ水溶液以及饱和和ＮａＮＯ３水溶液中的应力腐蚀开裂行为。结果表明，１８Ｍｎ５Ｃｒ钢在三种介质中对ＳＣＣ都较敏感，电位对该钢的ＳＣＣ抗力有明显影响，溶液的ｐＨ值对影响不大。     

不锈钢Ⅲ型试样的氢致开裂和应力腐蚀

研究了奥氏体不锈钢Ⅲ型试样的氢致开裂和应力腐蚀。结果表明,动态充氢时Ⅲ型试样也能发生氢致滞后断裂,且裂纹沿原缺口平面形核和扩展。从而可获得宏观平滑的扭转断口,但断口上存在少量沿45°面的二次裂纹,一系列实验表明动态充氢能促进奥氏体不锈钢室温蠕变,故在恒扭矩下充氢能使扭转角不断增大,直至试样被扭断。奥氏体不锈钢Ⅲ型试样在42％沸腾MgCl_2溶液中也能发生应力腐蚀开裂,且裂纹在与缺口平面成45°的平面上形核和扩展。实验表明,无论是Ⅰ型还是Ⅲ型,应力腐蚀的门槛值均比氢致滞后断裂门槛值要低,例如K_(ⅠSCC)/K_(ⅠX)=0.18,K_(ⅠH/K_(ⅠX)=0.58,K_(ⅢSCC)/K_(ⅢX)=0.13 K_(ⅢH)/K_(ⅢX)=0.62。     

应力腐蚀的电化学研究

应力腐蚀开裂(SCC)是一种应力与腐蚀的协同作用,它广泛存在于工业生产中。国外有人认为,保守地讲每年由于SCC所造成的材料结构破坏至少占15％以上。在与之有关的各种因素中,电化学起十分重要的作用,它是研究SCC过程的有力工具。本文就SCC研究中的电化学方面做一简单的归纳。     

铝合金应力腐蚀开裂的研究进展

应力腐蚀开裂作为一种局部腐蚀形式,是指金属材料在拉应力和特定介质的共同作用下所引起的破坏。针对近10年来文献报道的纯Al、AlLi合金、AlCu合金、AlMg合金、AlZnMg合金的应力腐蚀开裂的研究情况,从开裂机理、冶金效应、环境效应三个方面进行了总结。     

AP1轨钢的应力腐蚀试验研究

本文首先阐述了研究轨钢应力腐蚀的意义。在国内首次开展了对轨钢应力腐蚀门槛应力强度因子K_(ISCC)的测定研究,并取得了AP1轨钢在蒸馏水和3.5％盐水下的K_(ISCC)值。从而为轨道的设计和维修提供了依据。     

硫酸盐还原菌对16Mn钢在海泥中应力腐蚀开裂敏感性的影响

采用慢应变速率拉伸、氢渗透实验方法对16Mn钢在含不同浓度硫酸盐还原菌(sulfatereducingbacteria,SRB)海泥中的应力腐蚀开裂敏感性进行了研究。结果表明SRB的存在,使得16Mn钢的慢应变速率拉伸断裂延伸率变小,拉断所需时间缩短,拉断所需最大压力变小,拉伸曲线下的面积变小;氢渗透电流密度明显增大,因此海泥中SRB的存在能够使16Mn钢的应力腐蚀开裂敏感性增加。     

Effect of hydrogen on the stress corrosion cracking behavior of X80 pipeline steel in Ku'erle soil simulated solution

Hydrogen was a key factor resulting in stress corrosion cracking (SCC) of X80 pipeline steel in Ku'erle soil simulated solution. In this article, the effect of hydrogen on the SCC susceptibility of X80 steel was investigated further by slow strain rate tensile test, the surface fractures were observed using scanning electron microscopy (SEM), and the fracture mechanism of SCC was discussed. The results indicate that hydrogen increases the SCC susceptibility. The SEM micrographs of hydrogen precharged samples presents a brittle quasi-cleavage feature, and pits facilitate the transgranular crack initiation. In the electrochemical impedance spectroscopy (EIS) measurement, the decreased polarization resistance and the pitting resistance of samples with hydrogen indicate that hydrogen increases the dissolution rate and deteriorates the pitting corrosion resistance. The potentiodynamic polarization curves present that hydrogen also accelerates the dissolution rate of the crack tip.     

Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking

The hydrogen permeation behavior and stress corrosion cracking (SCC) susceptibility of precharged 7075-T6 Al alloy were investigated in this paper. Devanthan–Stachurski (D-S) cell tests were used to measure the apparent hydrogen diffusivity and hydrogen permeation current density of specimens immersed in 3.5wt% NaCl solution. Electrochemical experiment results show that the SCC susceptibility is low during anodic polarization. Both corrosion pits and hydrogen-induced cracking are evident in scanning electron microscope images after the specimens have been charging for 24 h.     

Investigation of stress corresion cracking under anodic dissolution control

This review is about stress corrosion cracking (SCC) under anodic dissolution control. The section 1 is the methods distinguishing SCC controlled by anodic dissolution from those by hydrogen. The section 2 presents hydrogen-enhanced corrosion and SCC under anodic dissolution control. The section 3 demonstrates corrosion-enhanced localized plasticity and corrosion-induced deformation localization, which are the fundaments of new mechanism of SCC. The section 4 is an overview of the proposed mechanisms of SCC under anodic dissolution control. The last section proposes a new mechanism of SCC.     

16Mn(HIC)钢硫化物应力腐蚀开裂实验研究

采用恒应变和慢应变速率拉伸实验的方法,研究了16Mn(HIC)和16Mn钢母材、焊缝在H2S环境中应力腐蚀开裂.结果表明:两种材料在酸性H2S介质中均发生穿晶型硫化物应力腐蚀开裂(SSCC);与16Mn钢相比,16Mn(HIC)钢有更好的抗SSCC性能,钢中的C,Mn,P和S的含量降低有利于提高钢的抗SSCC性能.焊缝及热影响区在焊接过程中,产生的粗大魏氏组织、偏析、缩孔和夹杂等缺陷,降低了焊缝的抗SSCC能力.但是,通过焊后热处理可以适当提高焊缝的抗SSCC能力.     

高强钢300M静态再结晶动力学研究

为研究高强钢300M静态再结晶行为,采用Gleeble-3800型热模拟试验机对300M钢进行单/双道次热压缩试验.通过双道次热压缩试验分析了变形温度、应变速率、变形量和初始晶粒尺寸对静态再结晶体积分数的影响.变形温度越高,应变速率越大,变形量越大,初始晶粒尺寸越小,则静态再结晶体积分数越大.其中变形温度、变形量和应变速率对静态再结晶体积分数影响较大,初始晶粒尺寸的影响相比较小.基于双道次热压缩试验结果建立了300M钢的静态再结晶体积分数模型,基于单道次热压缩试验结果建立了300M钢完全静态再结晶晶粒尺寸模型,并验证了静态再结晶体积分数模型的正确性.     

304不锈钢在模拟压水堆一回路水中高温电化学腐蚀行为

通过模拟压水堆一回路水环境,研究了氯离子浓度和溶解氧对304不锈钢高温电化学腐蚀行为的影响.动电位极化曲线结果表明,氯离子浓度主要影响高电位下的二次钝化效应,低电位下影响效果不明显,结合X射线光电子能谱对氧化膜元素成分的分析发现二次钝化效应与氧化膜中Fe/Cr元素含量比密切相关.电化学阻抗谱和扫描电镜结果表明,随着氯离子浓度增加,氧化膜阻抗逐渐降低,表面外层氧化物颗粒和间隙逐渐增大,耐腐蚀性能降低.随着溶解氧含量的升高,304自腐蚀电位逐渐升高,钝化电流密度降低,钝化区间缩小,表面氧化膜阻抗逐渐增加.     

pH值对高温高压水中304L不锈钢应力腐蚀开裂的影响

在高温高压水环境中,采用慢应变速率拉伸试验方法,研究了不同pH值对304L不锈钢应力腐蚀开裂行为的影响规律,并通过扫描电镜对试样断口形貌进行观察与分析.结果表明:在300℃时,304L不锈钢在弱酸性和弱碱性溶液中的应力腐蚀开裂敏感性较大,且酸性越强,敏感性越大.在中性溶液中,304L不锈钢的强度和塑性损失较小,应力腐蚀敏感性较小,断口分析与之吻合.     

高温水环境下温度对316 L不锈钢应力腐蚀开裂的影响

在高温水环境中,采用慢应变速率拉伸实验方法研究了温度对316 L不锈钢应力腐蚀开裂的影响规律,并通过扫描电镜(SEM)对试样断口形貌进行分析. 结果表明:在高温水环境中,温度为200～345 ℃时316 L不锈钢具有应力腐蚀开裂敏感性;材料脆性指标随温度升高而增大,应力腐蚀开裂敏感性增强,断口分析与之吻合;250 ℃是316 L不锈钢发生应力腐蚀开裂的敏感温度,断口边缘形貌呈现明显脆性断裂特征.     

316L不锈钢应力腐蚀研究进展

316L不锈钢具备良好的力学性能、焊接性能、耐蚀性能,被广泛应用于化工管道、船舶及核电等领域。因其应用环境复杂,316L不锈钢在特定介质环境和拉应力的协同作用下,易发生应力腐蚀开裂,导致严重事故。概述了316L不锈钢应力腐蚀裂纹萌生及扩展的规律,总结了其应力腐蚀的阳极溶解和氢致开裂两种微观主导机制的特点。在此基础上,针对介质环境、材料、表面应力状态3个影响因素,综述了近年来通过调节介质环境的pH、溶液浓度、引入压应力、优化微观结构及涂层工艺等方面,改善316L不锈钢应力腐蚀性能的研究进展。最后,基于316L不锈钢面临的应力腐蚀问题,从应力腐蚀机制和防护措施两方面展望了316L不锈钢应力腐蚀的研究热点和方向。     

管线钢中带状组织与氢致开裂

研究了 6种材料在NACE溶液中的氢致开裂 (HIC)行为 .结果表明 :钢材中Mn ,P ,S的含量高时 ,带状组织明显增多 ,HIC敏感性提高 .为避免带状组织及氢致开裂 ,应控制钢材中的Mn ,P ,S含量 ,给出了Mn ,P ,S含量的推荐值 :wMn≤ 1.3% ,wP≤ 0 .0 10 % ,wS≤ 0 .0 0 1% .