NH_4Cl-NH_3-H_2O体系浸出氧化锌矿

介绍了氯化铵 氨配合浸出法直接从氧化锌矿提取锌新工艺 .该工艺采用氯化铵 氨水溶液作浸出剂 ,使之与氧化锌矿反应得锌氨配合离子 ,在浸出的同时将杂质砷、锑、铁、硫酸根和碳酸根除去 .实验结果表明 :时间、液固比对锌浸出率影响显著 ,而温度对锌浸出率影响不大 ;在综合浸出条件下 ,锌浸出率大于 6 8% ,氨溶锌浸出率大于 93.88% (质量分数 ) ;胶体吸附除砷、锑效果明显 ,浸出液中砷、锑质量浓度可降至 0 .2 5mg·L- 1 ,铁质量浓度可降至 0 .15mg·L- 1 以下 ,氯化钙、氯化钡可将碳酸根和硫酸根几乎除尽 ,其他杂质元素含量也极低 .该浸出液净化容易 ,特别适合制电锌或锌粉 .本法具有工艺简单、能耗低、污染小、原料适应性广等优点 .     

氨法处理氧化锌矿制取电锌

研究了用氯化铵法直接从氧化锌矿提取电锌的新工艺.该工艺采用氯化铵 氨水溶液作浸出剂,氧化锌矿中的锌以锌氨配合物形式进入浸出液,在浸出锌的同时将杂质砷、锑、铁等除去.研究结果表明:氨溶锌浸出率≥93%;浸液中的As和Sb的质量浓度都低于0.25mg/L,Fe的质量浓度低于0.15mg/L,其他杂质质量浓度低;浸出液经锌粉1次净化除杂后进行电积制取电锌.电锌中Zn的质量分数达99.999%,杂质含量极低,其中Fe的质量分数仅为0.00005%;电流效率高达96.35%,直流电耗为2502kW·h;电解废液经补氨后返回浸取.     

含锑难处理金矿选择性脱除锑

为了消除锑对难处理金矿提取金过程的不利影响,提出用硫化钠浸出方法预先从含锑难处理金矿中选择性脱除锑,考察各因素对锑浸出率的影响,查明最优浸出条件下金和砷的浸出率。研究结果表明:硫化钠过量系数、氢氧化钠质量浓度、温度、液固比和洗水比等因素的增加均有利于提高锑的浸出率,但是延长反应时间和增大搅拌速度会使锑浸出率略降低,增大洗水比至4.0可以将浸出渣中锑质量分数降低至0.04%。含锑难处理金矿硫化钠浸出在最优条件下,锑的浸出率可以达到96.64%,金和砷的浸出率分别为1.44%和0.41%。浸出液静置后析出的黑色沉淀为Na2Fe S2,S和Fe S2的混合物,说明会有少量Fe S2矿物首先溶解然后从溶液中沉淀出来。     

氨浸法从含砷石灰铁盐渣中回收锌的动力学研究

采用氨浸法回收含砷石灰铁盐渣中锌,研究了不同浸取剂、浸取剂的组成、总氨浓度、氨水与铵盐配比、液固比等工艺条件对锌浸出效果的影响,分析了锌的浸出动力学.结果表明:以氨水和碳酸铵组成的浸取体系为浸取剂,当总氨浓度为5 mol/L,氨-铵盐摩尔浓度比为2∶3,液固比为4∶1时,锌的浸出率为56.21%.由宏观模型得出锌的浸出在温度为288～323 K内遵循"未反应核缩减"模型,受内扩散控制,浸出动力学方程为:1-2α3-(1-α)2/3=232×exp(-32245/RT)t,浸出表观活化能为32.24 kJ/mol.     

苛性碱溶液氧压浸出高砷锑烟尘

对苛性碱溶液氧压浸出高砷锑烟尘进行研究,考察NaOH浓度、O2分压、温度、浸出时间和液固质量比等因素对砷、锑和铅浸出行为的影响。研究结果表明:在火法处理铅阳极泥产出的高砷锑烟尘中,砷、锑的主要物相分别为As2O3和Sb2O3,锑也有少量以Sb2O5存在;在苛性碱溶液氧压浸出高砷锑烟尘过程中,As(Ⅲ)氧化为溶解度更大的As(Ⅴ)进入溶液,同时Sb(Ⅲ)氧化为Sb(Ⅴ),并形成难溶化合物Sb2O3·2Sb2O5、Pb2Sb2O7和NaSb(OH)6,进入浸出渣中;实验确定的最佳工艺条件为:NaOH质量浓度40 g/L,O2分压2.0 MPa,浸出温度140℃,浸出时间2 h,液固质量比10。在此条件下,As的浸出率可达95%以上,而Sb和Pb的浸出率均小于1.0%。     

用AC法处理高锑低银类铅阳极泥--氯化浸出和干馏的扩大试验

为提高银的回收率和解决环境污染问题,用AC法进行了处理高锑低银类铅阳极泥流程中氯化浸出、干馏和蒸馏等过程的扩大试验;并用氯气再生的A#CA为氧化剂,循环氯化浸出,以实现"贵、贱"金属彻底分离.实验结果表明贱金属锑、铜、铋、锡的浸出率大于98%,银入渣率大于97%;用聚四氟乙烯筒内衬干馏筒,用热风直接加热和用搪瓷冷凝管冷凝干馏气体,干馏装置运转正常;锑馏出率为84.09%,锑和银的回收率分别为98.55%及98.97%,并产出含Sb高达650 g/L的纯SbCl3,杂质元素Cu,Bi,Sn,Fe,Pb与Sb的质量比为3.5×10-6～3.4×10-4的纯SbCl3溶液,蒸馏脱砷后液As与Sb的质量比为1.3×10-4,适合于对锑进行深度加工.     

砷碱渣中砷锑碱梯级分离及金属砷回收工艺

针对当前砷碱渣处理过程砷碱分离效果差、分离的砷酸钠或钙砷渣安全处置难等问题,提出“水浸-水热沉砷-碳热还原”回收金属砷新工艺。以湖南某冶炼厂砷碱渣为对象,开展砷碱渣水浸砷锑分离、氧化钙水热沉砷砷碱分离、沉砷渣碳热还原回收金属砷等环节的工艺研究。研究结果表明：在浸出时间30 min、液固比3:1、浸出温度45℃、搅拌速度600 r/min的水浸条件下,砷、锑浸出率分别为95.3%和1.6%。在初始pH=11、水热温度180℃、反应时间6 h、Ca/As物质的量比为24:1的水热沉砷条件下,沉砷率达95.3%,沉砷渣主要为碳酸钙、氢氧化钙和砷酸钙。在碳粉添加量10%、温度1 000℃、还原时间3 h条件下,砷挥发率为93.1%,挥发产物砷质量分数达92.0%。砷碱渣“水浸-水热沉砷-碳热还原”新工艺,具有可实现砷锑碱梯级分离、砷以无毒的单质砷回收、沉砷剂氧化钙可循环使用、全流程未引入难处理的阴阳离子等优点。     

无污染砷碱渣处理技术工业试验

以锑冶炼产生的砷碱渣为原料,在80 ℃下,搅拌约2 h浸出脱锑;在脱锑后液中通入二氧化碳气体,脱除碳酸盐;调整脱碱后液的pH值,在酸性条件下加入适量的硫化钠脱除砷."无污染砷碱渣处理技术"工业试验结果表明:锑和铅的回收率分别达到99.0%和99.6%;砷、碱和硫酸钠的浸出率分别达到90%,99%和100%;碳酸盐中碱含量达到95%,砷含量在1%左右;砷硫化物中砷含量达到37%;在脱砷过程中产生的少量硫化氢采用氢氧化钠溶液吸收,吸收液返回脱砷系统;水溶液闭路循环,无废水外排;锑精矿、碳酸盐返回锑冶炼;砷硫化物、硫酸钡作为产品销售.采用该技术无废气、废水、废渣产生,工艺流程简单,操作条件容易控制,设备投资少.     

(NH4)2SO4-NH3-H2O体系浸出高碱性脉石低品位氧化铜矿

以高碱性脉石低品位氧化铜矿为研究对象,针对该矿样钙镁含量高的特点,采用氨水-硫酸铵浸出体系进行了常温常压浸出实验.针对该矿样的主要含铜矿物孔雀石(Cu₂(OH)₂CO₃),基于质量和电荷的双守恒的条件下构建的浸出体系中建立Cu₂(OH)₂CO₃-(NH₄)₂SO₄-NH₃-H₂O的热力学模型,采用Matlab的拟合功能与diff和solve函数算出不同硫酸铵浓度时氨浸出孔雀石的最佳氨浓度和总铜离子浓度.实验考察了浸出氨水浓度、氨铵比、液固比对铜浸出率的影响.实验结果表明,高碱性脉石氧化铜矿石适宜浸出条件为氨水浓度1.2mol/L,氨铵比2∶1,液固比3∶1,该条件下铜浸出率较高,达到约70%.实验结果与热力学计算结果基本吻合.     

复杂银铜精矿的沸腾焙烧综合回收工艺

采用沸腾焙烧综合回收工艺对呷村复杂银铜精矿难浸出问题进行实验,以沸腾焙烧脱硫、脱砷→硫酸浸出铜、锌→氯盐浸出锑、银→NaClO3氧化浸金→碳铵转化铅的工艺进行处理,实现铜、锌、银、锑、铅、金、砷和硫等有价元素的综合回收.在硫酸化沸腾焙烧过程中控制1·1倍空气过剩系数、0·25~0·35m·s-1的工况炉膛线速度以及600~630℃的焙烧温度,可以避免高铅复杂银铜精矿的烧结,脱硫率为49·68%,烟气中SO体积分数为5·5%可满足制酸要求.     

Lead-bismuth-free piezoceramics （Na0.5K0.44Li0.06）Nb0.95Sb0.05O3-Na5.6Cu1.2Sb10O29

Newly developed sintering aid Na5.6Cu1.2Sb10O29 (NCS) and lead-bismuth-free piezoceramics (Na0.5K0.44Li0.06) Nb0.95Sb0.05O3 (NKLNS) were prepared by the conventional solid state reaction. The effects of sintering aid NCS on the electrical properties of NKLNS were investigated. It was found that the addition of a proper amount of sintering aid NCS to NKLNS is effective not only on improving the density and the piezoelectric activity, but also on reducing the dielectric loss of NKLNS. The NKLNS doped with 0.4 mol% NCS has a piezoelectric constant d33 as high as 261pC/N and an electromechanical coupling factor k33 above 60%. These results show that NCS-doped NKLNS is a promising and practicable candidate for lead-bismuth-free piezoceramics.     

Single-negative properties of Ba2Co1.8Cu0.2Fe12O22 and Ba3Co2Fe23.4Zn0.6O41 hexagonal ferrites

The electromagnetic properties of Ba₂Co_1.8Cu_0.2Fe₁₂O₂₂ (Co₂Y) and Ba₃Co₂Fe_23.4Zn_0.6O₄₁ (Co₂Z) were studied by measuring microwave scattering parameters. In the transmission spectra of Ba₂Co_1.8Cu_0.2Fe₁₂O₂₂, a forbidden band emerges due to ferromagnetic resonance, and the permeability will turn to negative in the vicinity of the ferromagnetic resonance frequency. In the complex permittivity spectra of Ba₃Co₂Fe_23.4Zn_0.6O₄₁, the negative permittivity can be obtained due to dielectric resonance. Therefore, Co₂Y and Co₂Z can be used to construct left-handed materials possessing negative permeability and negative permittivity simultaneously.     

TiO2/Al2O3-Al2O3-TiO2/Al2O3绝缘结构的真空沿面闪络特性

基于变插入层介电常数的多层绝缘结构能改善电场分布、提高真空沿面闪络特性.通过真空热压烧结制备了TiO2/Al2O3-Al2O3-TiO2/Al2O3(A-B-A)3层绝缘结构,A层w(TiO2)为0.5%到20%.测量了该绝缘结构的真空沿面闪络特性,发现闪络特性随w(TiO2)的增加而提高,当w(TiO2)为20%时,其脉冲初次闪络电压较同等厚度的Al2O3陶瓷提高了63%.研究发现:A层的介电常数可由w(TiO2)调控,介电常数的增大能有效降低真空-绝缘子-阴极三结合点处的电场强度;A层表面存在的TiO2颗粒可以减小二次电子发射系数并改善表面电荷分布;TiO2的电导率虽比Al2O3高,但其仍为绝缘体,即使TiO2含量较高时也不会形成贯穿的导电通道.     

CaO-ZrO2-TiO2-Al2O3-B2O3-SiO2玻璃陶瓷的制备及化学稳定性研究

玻璃陶瓷是固化处理中、高放废物和α废物较为理想的候选材料之一。研究了特定条件下制备的CaO-ZrO2-TiO2-Al2O3-B2O3-SiO2体系玻璃陶瓷在水淬和空气中自然冷却的两种冷却制度对其结晶行为和显微结构的影响,用粉末浸泡实验方法测试了其化学稳定性。结果表明:自然冷却形成的玻璃陶瓷晶相主要是ZrSiO4和ZrTiO4;在25～70℃范围内,温度对玻璃陶瓷浸出率无明显影响,90℃下浸出率比25℃,40℃,70℃的浸出率高一个数量级;7 d元素总的归一化浸出为1.87 g/m2。     

在Na3AlF6-AlF3-CaF2-LiF-Al2O3体系中低温铝电解

Based on the main physico-chemical properties of Na₃AlF₆-AlF₃-CaF₂-LiF-Al₂O₃ system studied, including liquidus temperature、electrical conductivity and bath density, a laboratory scale vertical discharging aluminum type electrolysis cell of about 100A capacity was run with TiB₂ cathodes and low molar ratio(1.5～2.0) electrolytes at 800～930℃ range. Aluminum metal was obtained with 84.6%～88.3% current efficiencies and 11.54～11.83 kW^.h/kg specific energy consumption.     

关于Euler-致型方程x^2-D1y^2=2s^2和x^2-D2y^2=-2t^2

设D1，D2是无平方因子正整数，该文给出了方程组x^2-D1y^2=2s^2和x^2-D2y^2=-2t^2有本原整数解(x，y，s，t)的必要条件。     

Crystallization Mechanism of Na2O-CaO-Al2O3-SiO2-F- Glass Containing Cr2O3

The effect of Cr₂O₃ on the nucleation and crystallization of Na₂O-CaO-Al₂O₃-SiO₂-F- glass has been investigated by means of ESR(Electron Spin Resonance), SEM(Scanning Electron Microscope), EDS(Energy Dispersive Specrometer) and so on. Computer pattern recognition is applied to optimize the heat-treatment schedules. The experimental results show that the base glass containing more than 1.5 % (mass fraction) Cr₂O₃ can be nucleated internally and converted to spheroidal crystal glass materials. The spheroidal crystal consisted of fibrous wollastonite crystals radiating from a center. The residual glass phase filled in the interstices between the fibers and between the spherulites. During heat treatment process, the valence states ofchromium changed from Cr6- to Cr3-, and the Cr-spinel solidsolution [CaCr₂O₄] precipitated followed this valence change. At the primary stage of crystallization, the Cr-spinel could act as a nucleating center on which the principal or}stalline phase β-CaSiO₃ grew epitaxially.     

二维磁性NbSi2N4-WSi2N4-NbSi2N4异质结的光生电流效应

采用量子输运方法研究了二维(2D)磁性NbSi₂N₄-WSi₂N₄-NbSi₂N₄面内异质结的光生电流效应.该异质结具有C2v非空间反演对称性,在可见光范围内,用线偏光垂直及倾斜照射时,均能激发显著的光生电流效应,产生自旋极化且偏振敏感的光电流.光电流与偏振角(θ)和入射角(α)均为余弦依赖(cos(2θ),cos(2α))关系.两种照射方式下均能产生纯自旋流及完全自旋极化的光电流.在垂直照射时,能取得完美的自旋阀效应.这些结果表明,二维磁性NbSi₂N₄-WSi₂N₄-NbSi₂N₄异质结在低能耗自旋电子学及低维光电探测领域具有应用潜力.