双碳纤维束－Ag／AgCl组合电极的制备、性质和应用

提出了由两束碳纤维和Ａｇ／ＡｇＣｌ丝制备组合电极的方法和处理方法，系统地讨论了电化学条件对组合电极响应的影响，利用该组合电极，测定国家标准物质锌（ＣＲＭＧＢＷ０２７０３）中微量钢，相对标准偏差２．０％．相对误差０．５％，结果令人满意．     

Effect of La0.8Sr0.2Co0.2Fe0.8O3-δ morphology on the performance of composite cathodes

In the present work,one dimensional La0.8Sr0.2Co0.2Fe0.8O3 δ(LSCF) nanofibers with the mean diameter of about 100 nm prepared by electrospinning were deposited on Gd0.2Ce0.8O1.9(GDC) electrolyte followed by sintering to form one dimensional LSCF nanofiber cathode. And LSCF/GDC composite cathodes were formed by introducing GDC phases into LSCF nanofiber scaffold using infiltration method. The polarization resistances for the composite cathode with an optimal LSCF/GDC mass ratio of 1/0.56 are 0.27,0.14 and 0.07 Ω cm2at 650,700 and750 1C,respectively,which are obviously smaller than 2.26,0.78 and 0.29 Ω cm2of pure LSCF nanofiber cathode. And the activation energy is1.194 eV,which is much lower than that of pure LSCF nanofiber cathode(1.684 eV). These results demonstrate that the infiltration of GDC into LSCF nanofiber scaffold is an effective approach to achieve high performance cathode for solid oxide fuel cells(SOFCs). In addition,the performance of composite cathode in this work was also compared with that of our previous nanorod structured LSCF/GDC composite cathode.     

(La,Sr)(Co,Fe)O_3与(La,Sr)MnO_3阴极材料的表征与性能

采用氨水沉淀法分别制备La0.6Sr0.4Co0.2Fe0.8O3-δ(LSCF)与La0.8Sr0.2MnO3-δ(LSM)两种阴极材料,并用X射线衍射(XRD)、场发射扫描电子显微镜(FESEM)和比表面积(BET)对所制备材料的结构、晶粒大小、形貌及比表面积进行表征.结果表明,LSCF和LSM前驱体分别在900℃和1200℃煅烧5h后产物均形成单一正交的钙钛矿结构,但LSCF具有较小的粒径和较大的比表面积.电化学性能测试结果表明,LSCF阴极比LSM阴极的过电位低,且LSCF为阴极单电池的输出功率较高.     

基于Ag+金属中心的硅钨杂多酸配位聚合物的合成及其电化学性能研究

本文利用水热合成法得到了一种基于银离子金属中心的硅钨杂多酸(H₃SiW₁₂O₄₀)配位聚合物材料([Ag₄(BPB)₄SiW₁₂O₄₀])(简称，化合物1).单晶X-射线衍射分析表明，结构中存在Ag1、Ag2和Ag3三种银离子，分别采用2、3、4配位的方式通过Ag-N键连接有机配体，又通过Ag-O键连接多酸分子. Ag1连接有机配体形成左手、右手螺旋链，并连接多酸分子形成梯形链. Ag2连接有机配体和多酸分子形成二维4,4-sql拓扑格子层，梯形链与格子层共用多酸分子. Ag3连接有机配体形成一维链贯穿于二维层，最终形成整体的三维结构.此外，利用复合改性玻碳电极(GCE)作为工作电极对材料的电化学性能进行了研究.电化学分析结果表明，材料可作为还原NaNO₃的电催化剂.     

δ-MnO2/Ti2CTx复合材料的制备与电化学性能研究

以Ti₂AlC为前驱体、LiF-HCl的水溶液为刻蚀液、KMnO₄为氧化剂和锰源,采用溶液-沉积法制备了δ-MnO₂/Ti₂CT_x复合电极材料.分别采用X-射线衍射仪、扫描电子显微镜、拉曼光谱等方法对试样进行了表征; 以镍网为对电极、银/氯化银为参比电极、2 mol·L^-1 KOH溶液为电解质溶液,在3电极体系中采用循环伏安、恒流充放电和交流阻抗等电化学方法研究了复合材料的电化学性质.结果表明:当δ-MnO₂/Ti₂CT_x复合电极材料在电流密度为1 A·g^-1时,复合材料的比电容高达227 F·g^-1.δ-MnO₂/Ti₂CT_x是一种性能良好的电化学电极材料,具有潜在的应用前景.     

低温烧结多层片式ZnO压敏电阻内电极 Ag含量对电性能的影响

研究了低温烧成多层片式ZnO压敏电阻的内电极中Ag扩散进入ZnO晶格对电性能的影响．研究发现内电极中Ag含量严重影响低温烧结多层片式压敏电阻的电性能．当内电极含Ag量为70％时,具有最好的电性能;而内电极为纯Ag时,电性能最差,压敏电压和限制电压过分地升高,漏电流增大,非线性系数减小．反映晶界势垒电容的电容量随内电极中Ag含量的升高而减小．伏安特性和复数阻抗分析表明,随着内电极中Ag含量的升高,Ag扩散进入ZnO晶格加剧,降低了施主浓度Nd,导致ZnO晶粒电阻增大,以及晶界势垒高度和耗尽层宽度增加,使得多层片式ZnO压敏电阻的电性能变差．     

锂离子电池三维多孔硅/银复合材料负极设计及性能

以商品单质硅为原料,利用金属辅助化学刻蚀方法结合化学镀方法制备了三维多孔硅/银复合负极材料,采用X射线粉末衍射仪、场发射扫描电镜及比表面与孔隙度分析仪对其组成、结构、比表面积及孔隙率进行研究,随后对其电化学性能进行研究.结果表明,三维多孔硅呈现狭缝型的介孔,平均孔径宽度为12.5 nm,比表面积达到6.083 m2/g...     

氧化锌/银双层膜负反馈阴极电极的制备及性能研究

提出了一种可显著改善碳纳米管(CNTs)场致发射性能的ZnO/Ag双层膜负反馈阴极电极的制备方法.在条形银电极上溅射沉积一定厚度的Zn膜,经热氧化和湿法刻蚀制备成ZnO/Ag双层膜电极.同单层的Ag或氧化铟锡电极相比,该电极不仅具有足够的负反馈电阻(限流电阻)阻止CNTs场发射中过流的发生,而且降低了条形阴极电极的线性电阻,确保了场发射的均匀性.当溅射沉积Zn膜的厚度从40 nm增到120 nm时,热氧化形成的ZnO由孤岛状的颗粒变为连续体的薄膜,ZnO/Ag双层膜电极的表面光洁度比单层的Ag电极有很大的提高,负反馈电阻层的电阻增大,负反馈的能力增强.CNTs薄膜阴极场发射特性曲线证明,ZnO/Ag双层膜电极能明显降低场发射电流的波动,有效提高器件的稳定性和寿命.     

Ag与Ag20粉末微电极的循环伏安和电化学阻抗对比研究

在Ag电极化成为AgO时,发现只有Ag粉末电极可以氧化得到AgO,而Ag20则不行．分别将Ag和Ag20制作成粉末微电极,对它们进行了循环伏安（CV）和电化学阻抗谱（EIS）测试．通过对测试结果的分析可知,Ag被氧化为Ag20后,Ag电极分为内外两层,外层为富舍离子通道的Ag2O,便于OH-的进入;内层为导电性良好的Ag,便于Ag20氧化为AgO时电子的输出．而Ag20电极所含的离子通道较少,不利于OH-的进入;另外Ag2O的电阻较大,也不利于电子向外输出．这两方面原因使得Ag20电极不能被氧化为AgO．     

碳包覆Ti3AlC2增强银基复合材料的制备与性能

Ti₃AlC₂-reinforced Ag-based composites, which are used as sliding current collectors, electrical contacts, and electrode materials, exhibit remarkable performances. However, the interfacial reactions between Ag and Ti₃AlC₂ significantly degrade the electrical and thermal properties of these composites. To diminish these interfacial reactions, we fabricated carbon-coated Ti₃AlC₂ particles (C@Ti₃AlC₂) as reinforcement and prepared Ag–10wt%C@Ti₃AlC₂ composites with carbon-layer thicknesses ranging from 50–200 nm. Compared with the uncoated Ag–Ti₃AlC₂ composite, Ag–C@Ti₃AlC₂ was found to have a better distribution of Ti₃AlC₂ particles. With increases in the carbon-layer thickness, the Vickers hardness value and relative density of Ag–C@Ti₃AlC₂ gradually decreases. With a carbon-layer thickness of 150 nm, we obtained the lowest resistivity of Ag–C@Ti₃AlC₂ of 29.4 135.5×10?9 Ω·m, which is half that of Ag–Ti₃AlC₂ (66.7 × 10?9 Ω·m). The thermal conductivity of Ag–C@Ti₃AlC₂ reached a maximum value of 135.5 W·m?1·K?1 with a 200-nm carbon coating (~1.8 times that of Ag–Ti₃AlC₂). These results indicate that the carbon-coating method is a feasible strategy for improving the performance of Ag–C@Ti₃AlC₂ composites.     

室温全固态氢传感器研究

以Sb₂O₅-H₂O-H₃PO₄ 复合氧化物为固态电解质 ,利用混合压膜和蒸发的方法制作传感催化电极和参考电极 ,研制了室温全固态电解质氢气传感器。传感器的组成为:空气 ,Pd(或Ag) |Sb₂O₅-H₂O-H₃PO₄ |Pd ,H₂ (在N₂ 或空气中) ,考察了传感器的电位响应值与氢气体积分数之间的关系 ,以及温度对氢气传感性能的影响;通过测绘极化曲线来研究其应答机理,从而分析传感器电位响应值不同于能斯特值的原因——敏感电极上混合电势的形成。     

Ag/graphene composite based on high-quality graphene with high electrical and mechanical properties

A simple and effective process has been reported to prepare the silver (Ag)/graphene composite with excellent mechanical and electrical properties based on high-quality graphene (HQG). The HQG was fabricated via hot pressing of reduced graphene oxide (RGO) from chemical exfoliation, while the Ag/HQG composite was obtained by using spark plasma sintering (SPS) treatment under high temperature (1500 °C) and moderate pressure (40 MPa). With low oxygen-containing functional groups and defect density, the HQG dispersed homogeneously in the composite after high-energy ball milling. In comparison to pure Ag, the as-prepared Ag/RGO composite exhibited a great enhancement of 11% electrical conductivity and 42% micro-hardness with an optimal RGO adding content (1 wt%). The Ag/HQG composite is expected to open up a new way for the novel Ag-based electrical contact materials, and further to broaden its applications in micro-electronics and switching power.     

磁控溅射制备Ag/TiO2复合薄膜的光催化降解性能

为了提高TiO2薄膜的光催化效率,利用中频交流磁控溅射技术,采用Ti和Ag金属靶制备了Ag/TiO2复合薄膜.利用X射线光电子能谱、 X射线衍射和扫描电子显微镜分析了复合薄膜的成分、结构和表面形貌,并研究了其光催化降解性能.结果发现: Ag在厚度较薄时以聚集颗粒形式存在; 在Ag膜厚度为15 nm时, Ag/TiO2复合薄膜与TiO2薄膜相比其光催化效率可提高2倍; Ag/TiO2复合薄膜对亚甲基蓝的光催化降解效率与复合薄膜的透射率均随Ag膜厚度增加逐渐下降,其原因是Ag膜厚度不断增加,最终完全覆盖TiO2薄膜表面,阻挡了TiO2薄膜与污染物的有效接触, Ag作为光生电子捕获剂的有利影响消失.     

硅胶基衬底表面高分辨复杂可延展电路的印刷制备

 柔性可延展电子因其能够适应非平面工作环境,将突破现有电子器件的应用范围,促进信息与人的融合,在智能穿戴电子、柔性显示、生物医疗等领域具有广阔的应用前景。本文提出利用印刷结合真空抽滤方法实现硅胶基衬底表面高分辨复杂可延展电路的制备;研究了丝网印刷工艺实现微孔滤膜表面银纳米线（Ag NWs）图形化沉积的分辨率;讨论了Ag NWs线长、抽滤真空度等因素对沉积分辨率的影响,实现了Ag NWs图形化50 μm线径分辨率及间隔分辨率。本文还研究了硅胶基衬底表面微电极的电阻均一性及拉伸电阻稳定性,并结合电极表面微结构的变化详细讨论了屈曲褶皱结构的出现对微电极拉伸电阻的影响,实现了100 μm线宽微电极100%拉伸幅度下电阻增加仅为初始值的40%。最后,通过集成LED芯片演示了面料基底表面柔性可延展发光电路。本研究对于柔性可延展电路的制备提供了新的思路。     

Structural and electrical properties of HCl-polyaniline-Ag composites synthesized by polymerization using Ag-coated (NH4)2S2O8 powder

Ag nanoparticles were sputter-deposited on ammonium persulfate ((NH₄)₂S₂O₈) powder to obtain (NH₄)₂S₂O₈-Ag powder, which was used to synthesize the HCl-doped polyaniline-Ag (HCl-PANI-Ag) composite via a polymerization procedure. The Ag nanoparticles were dispersed in the HCl-PANI matrix, and their sizes mainly ranged from 3 to 6 nm. The Ag nanoparticles did not affect the structure of emeraldine salt in the composite, and they increased the ordered crystalline regions in the HCl-PANI matrix. The HCl-PANI-Ag composite had a conductivity of (6.8 ±0.1) S/cm, which is about four times larger than that of the HCl-PANI. The charge transport mechanism in the composite is explained by the three-dimensional Mott variable-range hopping (3D-Mott-VRH).     

Cu2〖KG-*3〗O/Ag复合催化剂的合成及红外光激发下的光催化性能研究

采用液相还原法合成不同摩尔比的Cu2O/Ag(x)复合型催化剂,应用X-射线粉末衍射(XRD)、扫描电子显微镜(SEM)、紫外可见漫反射(DRS)等分析手段对样品进行表征.结果显示,纳米金属Ag的存在使得Cu2O/Ag(x)样品对光的吸收扩展到了整个可见和近红外区,且随样品中Ag含量的增加,该区域的吸收逐渐增强,证明Cu2O/Ag(x)复合催化剂对太阳光具有高的吸收能力.以甲基橙（MO）为目标降解物,研究催化剂在黑暗条件下的降解性能,结果表明Cu2O/Ag(005)催化剂具有最高的降解能力,在120 min内黑暗条件下MO(30 mg/L) 降解率达到892%.另外对Cu2O/Ag(x)复合催化剂的降解机理进行了探讨.     

Cu2O@Cu4(SO4)(OH)6的制备及黑暗下降解橙黄II

本文采用液相还原法合成出具有不同摩尔比的Cu2O/Ag(x)复合型催化剂,采用XRD、SEM、UV-Vis-NIR漫反射(DRS)分析手段对样品进行表征。结果显示,纳米金属Ag的存在,使得Cu2O/Ag(x)样品对光的吸收扩展到了整个可见和近红外区,且随样品中Ag含量的增加,该区域的吸收逐渐增强,证明Cu2O/Ag(x)复合催化剂对太阳光具有高的光吸收能力。以甲基橙（MO）为目标降解物,研究催化剂在黑暗条件下的降解性能,结果表明Cu2O/Ag(0.05)催化剂具有最高的降解能力,在120 min内黑暗条件下MO (30 mg?L-1) 降解率达到89.2%。同时对Cu2O/Ag(x)复合催化剂的降解机理进行了探讨。     

Ag/石墨烯复合涂层的制备及抗菌性能

首先用改进的Hummers法制备氧化石墨烯（GO）; 其次用原位还原法将银氨溶液中的Ag纳米粒子通过还原剂葡萄糖和GO复合, 获得Ag/GO胶体; 最后在真空干燥条件下得到Ag/GO涂层, 并用真空阶梯热还原技术制备Ag/还原氧化石墨烯(rGO)涂层. 利用X射线衍射、 扫描电子显微镜、 透射电子显微镜等方法对膜样品结构形貌进行表征, 并用润湿角测量仪和抑菌环方法分别检测样品的亲/疏水性和抗菌性能. 实验结果表明: 石墨烯基膜材料与基底结合较好, Ag纳米粒子在石墨烯片层间呈球形均匀分布, 粒径为20~50 nm; 纯GO和rGO膜表面未见菌落, 大肠杆菌与金黄色葡萄球菌均未出现有效抑菌环; 复合Ag纳米粒子后, 涂层的抑菌效果得到显著提高; 与Ag/GO复合膜相比, Ag/rGO复合膜呈更强的抗菌活性, 即低温退火有助于提高石墨烯基复合涂层的抗菌性能.     

丙烯基硫脲与银电极表面相互作用的EQCM研究

运用循环伏安(CV)和电化学石英晶体微天平(EQCM)方法研究了酸性介质中银阳极溶出和阴极沉积过程以及丙烯基硫脲(ATU)对该过程的影响.实验结果表明:在酸性硝酸银溶液中,银阳极溶出和阴极沉积过程的实验测定值M w/n分别为18.3和43.4g/mol,尽管实验测定值与银1-电子过程的M w/n理论值(108g/mol)相差甚大,但考虑到酸性介质中氢电极过程的影响,仍可指认:在酸性AgNO3溶液中,银的阳极溶出和阴极沉积过程均为1-电子过程.在含有丙烯基硫脲(ATU)溶液中,Ag阳极溶出和阴极沉积过程的M w/n实验测定值分别为104.1和106.3 g/mol,与Ag的1-电子过程的M w/n理论值非常接近,指示丙烯基硫脲(ATU)并不改变银阳极溶出和阴极沉积过程的机理,但ATU阻化了氢的析出,促进了银的电极过程,加大了电极过程的可逆程度.本文从电极表面质量定量变化的角度提供了Ag阳极溶出和阴极沉积过程的新数据.     

电极电位对L-蛋氨酸分子吸附构型影响的表面增强拉曼光谱

利用电化学现场表面增强拉曼光谱技术研究了在粗糙化金电极和银电极表面吸附的L-蛋氨酸自组装单分子膜结构随电位改变的特征.实验结果表明:在外加电位0--0.6V范围内,L-蛋氨酸主要是通过硫原子和去质子化羧基2个吸附位点与银电极表面产生相互作用的;而在金电极表面表现为分子中的氨基、去质子化羧基和硫原子3个吸附位点随电位负移而改变的特征;另外,对于金电极表面吸附的L-蛋氨酸单分子膜而言,还伴随着吸附物分子由于分子内旋转等而引致的分子构型的转变.