Preparation and magnetic properties of CoFe2O4/TiO2 composite films

Using （Ti（OC4H9）4） and metal chlorates as starting materials, CoFe2O4/TiO2 composite films were prepared by sol-gel method. The effects of heat treatment temperature and pH of the precursor on microstructure and magnetic properties were studied. The phase structure of the samples was examined by X-ray diffraction. The microstructure was examined by scanning electron microscope, atomic force microscope and polarized microscope. The magnetic property was measured by vibrating sample magnetometer. The results show that the crystals of different phases grow up independently. CoFe2O4 is uniformly embedded into the TiO2 matrix in the prepared composite films, and the growth of composite films is dependent on the heat treatment temperatures and PH of the precursor. The average size of CoFe2O4 crystal is 19 nm in Nanocomposite film prepared when the heat treatment temperature is 800℃ and the pH of the precursor is between 2 and 3. The magnetism of the composite films is enhanced as the heat treatment temperature increases.     

Preparation and characterization of CoFe2O4/SiO2 nanocomposites

Recent years see an increasing interest in nanocomposites synthesized by a sol-gel procedure consisting of magnetic nanosized particles embedded in a silica matrix. due to their specific physical and chemical properties[1―4]. Sol-gel derived amorphous si…     

TiO_2透明薄膜的制备与光诱导超亲水性研究

采用溶胶凝胶法和旋涂工艺在普通玻璃表面制备透明的TiO2薄膜,经500℃退火处理后,TiO2薄膜完全晶化为锐钛矿结构,是由一些大小只有约30nm的TiO2粒子组成的多孔颗粒膜.经紫外光照射后,TiO2具有光诱导超亲水性.     

溶胶-凝胶法制备CoFe2O4/TiO2纳米复合薄膜及其磁性能研究

以钛酸丁酯和金属盐酸盐为原料,采用溶胶-凝胶工艺成功制备了磁性CoFe2O4/TiO2复合薄膜.通过X射线衍射仪(XRD) 、拉曼光谱(Raman)、扫描电镜(SEM)分析探讨了复合薄膜相结构和表面形貌,使用振动样品磁场计(VSM)测试样品磁性能.研究发现:复合薄膜中两相组分晶体各自析出长大,没有生成新的物相,薄膜生长过程中TiO2网状结构起到控制CoFe2O4的晶粒大小的作用.对比不同温度下薄膜的形貌,得出薄膜的形貌对热处理温度依赖性较大,前驱液为pH =2-3、热处理温度为800℃时,可得到平整的纳米CoFe2O4/TiO2磁性复合薄膜.随着热处理温度的升高,复合薄膜的磁性增强.     

铁酸锌掺杂纳米二氧化钛的制备及其光催化活性

 以钛酸四丁酯和自制铁酸锌为原料,采用溶胶-凝胶法制备了未掺杂的TiO₂和掺杂不同量的ZnFe₂O₄/TiO₂纳米粉体,通过XRD、TEM对产物的晶体结构、晶粒大小、形貌进行了表征,通过对罗丹明B的光催化降解实验研究了ZnFe₂O₄的掺杂对TiO₂催化活性的影响.结果表明,产物为纳米微粒,ZnFe₂O₄的掺杂能加快TiO₂的晶型转变速度,减小TiO₂的粒径,提高TiO₂的光催化活性.     

电气石/TiO_2复合材料的组成与微观形态

为了揭示电气石/TiO_2复合材料使电气石增白和具有颜料性质的内在机制,采用X射线衍射(XRD)、扫描电镜(SEM)测试和电气石、TiO_2颗粒表面官能团性质的分析等方法,研究了电气石/TiO_2复合材料的组成与微观形态。研究结果表明,电气石/TiO_2复合材料由包核物电气石颗粒和其表面包覆的结晶Ti_O2所组成,Ti_O2在电气石表面形成均匀、牢固的包覆层。研究结论初步反映了电气石和Ti_O2的作用性质,有助于对电气石/Ti_O2复合材料综合性能的认识和应用。     

低温合成TiO2/Fe3O4磁载光催化剂的光催化性能研究

采用化学共沉淀法合成的磁性纳米Fe₃O₄为磁核,以钛酸四丁酯为原料,通过溶胶-凝胶法,在较低温度下合成了TiO₂/Fe₃O₄磁性光催化剂。利用XRD、TEM、SEM-EDX等分析方法对合成催化剂的相组成、形貌、粒度、元素分布等进行了表征;研究了不同焙烧温度及TiO₂/Fe₃O₄比例对降解罗丹明B光催化活性及磁分离回收性能的影响。结果表明,在100、300和450 ℃焙烧温度下磁性光催化剂的催化活性依次降低,较低温度(100 ℃)制备的催化剂具备较高的催化活性;当TiO₂质量分数处于67.3%～73.0%时,催化剂既具有较高的光催化降解活性也具有较好的磁分离回收性能;光催化剂TiO₂/Fe₃O₄（100 ℃,TiO₂质量分数70%）在循环使用5次后,在降解75 min时仍能达到对罗丹明B 99%的脱色率和90%的回收率。     

纳米多孔SiO2-TiO2复合薄膜的制备及研究

采用溶胶凝胶技术,以表面活性剂十六烷基三甲基溴化铵CTAB为模板剂,乙酰丙酮作为钛的水解控制剂,通过钛和硅醇盐的分步水解得到均匀的SiO2TiO2复合溶胶,通过提拉制备出具有纳米多孔结构的复合薄膜.实验结果表明,多孔薄膜中的钛离子形成了Si—O—Ti键的孤立四配位形态,使薄膜具有复合型钛离子的催化效果,并且有介孔结构.随TiO2含量的增加,薄膜仍具有较好的透光性(可达到85%以上).通过对实验条件的调节,可实现对薄膜纳米结构的人工控制,形成的多孔薄膜折射率在1.2~1.4之间连续可调.     

纳米硅/P3HT复合薄膜的制备及光学特性

采用等离子体增强化学气相沉积技术和旋涂法相结合制备了纳米硅/P3HT复合薄膜.利用Raman散射、紫外-可见吸收光谱(UV-Vis)和光致发光谱(PL)等技术对复合薄膜的微观结构及光学特性进行了分析.结果表明:氢流量的增加,可以有效钝化硅中的缺陷,提高纳米硅薄膜的晶化度;复合薄膜中纳米硅的引入改善了P3HT在短波长范围的吸收能力,但存在与P3HT辐射发光相竞争的过程;对复合薄膜的光致发光机制进行了分析.     

TiO_2/S_2O_8~(2-)-沸石分子筛催化合成硬脂酸正丁酯的研究

用TiO2/S2O2-8 -沸石分子筛作催化剂,由硬脂酸和正丁醇发生酯化反应来合成硬脂酸正丁酯。考察了各种因素对酯化反应的影响,得到了反应的最佳条件:当醇和酸的物质的量之比为3∶1、TiO2/S2O2-8 沸石分子筛的用量为反应物质量的2.0%、反应温度为85 ℃时,反应仅需约2.5 h,酯化率可达到98.7%,酯的纯度>99.1%。     

高析氧过电位Ti/SnO2+Sb2O4阳极的制备及性能

采用溶胶-凝胶涂层技术,以无机物SnCl2.2H2O,SbCl3为前驱物制备了Ti/SnO2 Sb2O4电极。电极的晶体结构通过XRD进行了表征,得知涂层中的SnO2是金红石结构,并计算出涂层氧化物属于纳米级,平均粒度为6.5 nm。考察了锑的掺入量和烧结温度对电极性能的影响,结果表明:锑原子质量分数为4%,烧结温度600℃为较佳工艺条件;电流密度10mA/cm2时,电极的析氧电位高达2.1182V(vs.NHE),说明Ti/SnO2 Sb2O4电极是一种优良的阳极电催化剂。     

La2O3/Al2O3/TiO2纳米复合粉体的制备及其耐温性能的研究

以TiCl4、La2O3、Al片为原料,采用液相共沉淀法制备了La2O3/Al2O3/TiO2纳米复合粉体,采用DSC-TG、XRD、TEM技术对该纳米复合粉体进行了表征.结果表明纳米TiO2粉体经La2O3掺杂和Al2O3复合后,其耐温性能得到显著提高,该复合粉体经900℃煅烧后,粒径在32nm左右,锐钛矿含量约为77.2%(mol%)     

Fe3O4@SiO2磁性纳米粒子的制备及表征

用多元醇还原法制备出平均粒径为6.0 nm的Fe3O4磁性纳米粒子,并用盐酸溶液(1 mol/L)对其进行酸化处理,然后利用反相微乳液法,在Op-10/正丁醇/环己烷/浓氨水反相微乳体系中制备出Fe3O4@SiO2磁性纳米复合粒子.利用X射线衍射(XRD)仪,透射电子显微镜(TEM),傅立叶-红外光谱仪(FT-IR)和...     

低温制备光活性纳米晶二氧化钛薄膜

在传统溶胶凝胶法基础上,改进陈化及凝胶工艺,并采取破胶、回流、重新分散等手段,得到稳定无异味光催化溶胶,在玻璃基体上涂布该溶胶制备透明TiO2薄膜．物相分析表明,样品主要为锐钛矿型,平均晶粒尺寸为16．6nm．通过甲醛气体光催化降解实验,评价了TiO2薄膜的光催化性能．结果表明,在8W紫外灯照射下,该薄膜能有效降解甲醛．     

TiSiW12O40／TiO2催化合成葡萄糖五异丁酸酯

报道了新型催化剂ＴｉＳｉＷ１２Ｏ４０／ＴｉＯ２催化酯化合成葡萄糖五异丁酸酯的糖酸比，催化剂用量，反应时间，反应温度褚因素对产率的影响。实验表明：ＴｉＳｉＷ１２Ｏ４０／ＴｉＯ２具有良好的催化活性，糖酸摩尔比为１：５．５，催化剂的用量为反应液的２％，酯化反应时间为２ｈ，反应温度１００￣１０５℃，反应产率可达８９．６％。     

溶胶－凝胶法制备TiO_2－CeO_2薄膜

采用溶胶－凝胶法制备了鲜黄色的高反射ＴｉＯ＿２－ＣｅＯ＿２薄膜。研究了环境湿度和醋酸添加剂对薄膜形成的影响。研究表明：醋酸加入能显著提高薄膜质量，得到均匀透明的高质量薄膜；涂膜环境温湿度对薄膜质量有决定性作用。     

溶胶-凝胶法制备的Co0.7Fe2.3O4纳米晶薄膜结构与磁性

采用柠檬酸溶胶-凝胶法在玻璃衬底上制备了钴铁氧体Co0.7Fe2.3O4纳米晶薄膜.用X射线衍射仪、振动样品磁强计对不同热处理温度样品的结构及磁性进行了测量与分析.测量结果表明,退火400℃时样品已生成单一的尖晶石结构,晶粒尺寸变化范围在15~33 nm之间,样品的磁性能强烈地依赖于退火温度的变化;550℃时退火样品获得最大矫顽力1475 Oe.Co0.7Fe2.3O4薄膜还具有平行膜面方向的择优取向.     

选择性加氢脱硫催化剂Co-Mo/TiO_2-Al_2O_3的制备与表征

采用溶胶-凝胶法获得TiO2-Al2O3复合载体,研究了该复合载体负载Co、Mo后制备的Co-Mo/TiO2-Al2O3催化剂在FCC汽油重馏分加氢脱硫反应中的催化性能,重点考察了复合载体TiO2/(TiO2+Al2O3)对催化剂加氢脱硫活性和选择性的影响,并对催化剂和载体进行了BET、IR和NH3-TPD表征.实验结果表明:催化剂加氢脱硫活性和选择性均随载体中TiO2含量的增加而增加.表征结果表明催化剂的比表面积、孔容和平均孔径均随载体中Ti O2含量的增加而减小;随着TiO2含量的增加,催化剂酸中心强度和酸量有所增大,但变化量不大;催化剂载体的L酸量逐渐增大.载体表面仅有微量的B酸.     

新型固体酸SO_4~(2-)/TiO_2-La~(3+)-Al_2O_3-Al催化合成乙酸乙酯

研究一种新型的催化酯化专用催化剂。采用铝阳极氧化法制备Al2O3-Al载体,通过引入SO42-/TiO2-La3 固体酸,制得催化精馏专用的填料型固体酸催化剂,并应用于乙酸乙酯合成反应。最佳反应条件:反应时间为6 h,原料摩尔比(酸∶醇)为1∶8,催化剂用量为2 g,反应酯化率可达50.4%,选择性为100%,催化剂可重复使用。     

纳米TiO2／SiO2固相萃取剂的制备及对重金属离子吸附性能的研究

以钛酸四丁酯、正硅酸乙酯作为前驱体,溶胶—凝胶法制备了纳米TiO2／SiO2复合物。采用x射线衍射（XRD）、透射电镜（TEM）、X射线能谱（EDS）等手段对所制得的TiO2／SiO2复合材料进行表征。以纳米TiO2／SiO2复合材料作为填料制成固相萃取小柱,对重金属离子Cu^2＋、Cr^3＋、Pb^2＋和Hg^2＋进行吸附,硝酸洗脱后,采用ICP—MS进行检测。考察了吸附剂对不同pH值溶液中金属离子的吸附性能。自制SPE小柱与ICP—Ms联用测定Cu^2＋、Cr^3＋、pb^2＋和Hg^2＋的最低检出限分别为0．031,0．010,0．041,0．025μg／L。