Microstructure, crystalline phase and electrical properties of Li0.06(Na0.5K0.5)0.94Nb(1−2x/5)Mg x O3 lead-free piezoelectric ceramics

MgO-modified Li_0.06(Na_0.5K_0.5)_0.94NbO₃ (L₆NKN) lead-free piezoelectric ceramics were synthesized by normal sintering at a relatively low temperature of 1000°C. The crystalline phase, microstructure, and electrical properties of the ceramics were investigated with a special emphasis on the influence of MgO content. The addition of MgO effectively improves the sinterability of the L₆NKN ceramics. X-ray diffraction analysis indicates that the morphotropic phase boundary (MPB) separating orthorhombic and tetragonal phases for the ceramics lies in the range of Mg doping content (x) from 0.3at% to 0.7at%. High electrical properties of the piezoelectric constant (d ₃₃=238 pC/N), planar electromechanical coupling coefficient (k _p=41.5%), relative dielectric constant (? _r=905), and remanent polarization (P _r=38.3 μC/cm²) are obtained from the specimen with x=0.5at%, which suggests that the Li_0.06(Na_0.5K_0.5)_0.94Nb_(1?2x/5)Mg _x O₃ (x=0.5at%) ceramic is a promising lead-free piezoelectric material.     

Effect of CuO addition on the sintering temperature and microwave dielectric properties of CaSiO3– Al2O3 ceramics

CuO-doped CaSiO3–1 wt% Al2O3 ceramics were synthesized via a traditional solid-state reaction method, and their sintering behavior,microstructure and microwave dielectric properties were investigated. The results showed that appropriate CuO addition could accelerate the sintering process and assist the densification of CaSiO3–1 wt% Al2O3 ceramics, which could effectively lower the densification temperature from1250 1C to 1050 1C. However, the addition of CuO undermined the microwave dielectric properties. The optimal amount of CuO addition was found to be 0.8 wt%, and the derived CaSiO3–Al2O3ceramic sintered at 1100 1C presented good microwave dielectric properties of εr?7.27,Q f?16,850 GHz and τf? 39.53 ppm/1C, which is much better than those of pure CaSiO3 ceramic sintered at 1340oC(Q f?13,109 GHz).The chemical compatibility of the above ceramic with 30 Pd/70 Ag during the cofiring process has also been investigated, and the result showed that there was no chemical reaction between palladium–silver alloys and ceramics.& 2014 Chinese Materials Research Society. Production and hosting by Elsevier B.V. All rights reserved.     

Optical properties of NdxGd1−xAl3(BO3)4 crystal

The optical properties of Nd x Gd 1-x Al\-3(BO\-3)\-4 (NGAB) crystal are reported. The refractive index of it were mesured by V_prism method. The absorption spectra and the flourescence specra of NGAB were also obtained. The optical parameters of NGAB were calculated following J_O theory, the three optical parameters are Ω 2 =1 805×10 -20 , Ω 4=1 85×10 -20 , Ω 6=3 793×10 -20 (RMS=1 4×10 -7 ) and β c( 4F 3/2 → 4I 11/2 ) is about 0 53.     

Effect of Ti and Ta content on the oxidation resistance of Co–Ni-based superalloys

Co–Ni-based superalloys are known for their capability to function at elevated temperatures and superior hot corrosion and thermal fatigue resistance. Therefore, these alloys show potential as crucial high-temperature structural materials for aeroengine and gas turbine hot-end components. Our previous work elucidated the influence of Ti and Ta on the high-temperature mechanical properties of alloys. However, the intricate interaction among elements considerably affects the oxidation resistance o...     

Effect of B2O3 on the aqueous tape casting and microwave properties of Li2O–Nb2O5–TiO2 ceramics

The effect of B2O3 addition on the aqueous tape casting, sintering, microstructure and microwave dielectric properties of Li2O-Nb2O5-TiO2 ceramics has been investigated. The tape casting slurries exhibit a typical shear-thinning behavior without thixotropy, but the addition of B2O3 increases the viscosity of the slurries significantly. It was found that doping of B2O3 can decrease the tensile strength, strain to failure and density of the green tapes. The sintering temperature could be lowed down to 900℃ with the addition of 2 wt% B2O3 due to the liquid phase effect. No secondary phase is observed. The addition of B2O3 does not induce much degradation on the microwave dielectric properties. Optimum microwave dielectric properties of εr 67, Q×f 6560 GHz are obtained for Li2O-Nb2O5-TiO2 ceramics containing 2 wt% B2O3 sintered at 900 1C. It represents that the ceramics could be promising for multilayer low-temperature co-fired ceramics (LTCC) application.     

Influence of Ga-doping on the thermoelectric properties of Bi(2−x)GaxTe2.7Se0.3 alloy

Bi(2-x)GaxTe2.7Se0.3(x=0, 0.04, 0.08, 0.12) alloys were fabricated by vacuum melting and hot pressing technique. The structure of the samples was evaluated by means of X-ray diffraction. The peak shift toward higher angle can be observed by Ga-doping. The effects of Ga substitution for Bi on the electrical and thermal transport properties were investigated in the temperature range of 300–500 K. The power factor values of the Ga-doped samples are obviously improved in the temperature range of 300–440 K. Among all the samples, the Bi(2-x)GaxTe2.7Se0.3(x=0.04) sample showed the lowest thermal conductivity near room temperature and the maximum ZT value reached 0.82 at 400 K.     

Effect of light response on the photocatalytic activity of BiOCl x Br1−x in the removal of Rhodamine B from water

BiOClxBr1-x catalysts were synthesized through an alcoholysis method and characterized by X-ray diffraction （XRD）, transmission electron microscopy （TEM）, high-resolution transmission electron microscopy （HRTEM）, and diffuse reflectance spectroscopy （DRS）. The as-prepared photocatalysts were found to be tetragonal crystal structure and lamellar plate morphology. Their band gaps were between 3.44 and 2.83 eV. The effect of light response on the photocatalytic activity of BiOClxBrl-x was investigated by degradation of Rhodamine B （RhB）. Complete removal of RhB from water was realized under simulated sunlight irradiation for 50 min with BiOC10.5Br0.5. Mechanism studies showed that photo- generated holes and superoxide anion radicals played important roles in RhB photodegradation. The results of chemical oxygen demand （COD） confirmed RhB mineralization. The effect of light response on the activity of BiOClxBr1-x was further investigated under monochromatic light irradiation, and BiOCl0.5Br0.5 catalyst exhibited the highest activity. Furthermore, BiOC10.5Br0.5 exhibited high stability, suggesting its practical application for the removal of RhB pollutant from water.     

Preparation and optical properties of solid solution semiconductor (Zn x Cd1−x S) doped silica glasses

Semiconductor(Zn_xCd_1−x S) doped silica glasses were prepared by Sol-Gel process andin situ growth technique. The structure of the materials was characterized by X-ray diffraction technique, the particle size of semiconductor crystallites from X-ray patterns was estimated less than 10 nm. From absorption spectra, it is obtained that the absorption edges shifted to short wavelength direction when Zn contents increased, and the absorption edge can be adjusted from 2.46 eV to 2.96 eV by controlling Zn contents. The third-order nonlinear optical susceptibility was studied at 532 nm with 8 ns pulse laser by degenerate four wave mixing (DFWM) technique.     

Effect of Mn content on the microstructure and mechanical properties of Mg–6Li–4Zn-xMn alloys

The as-cast Mg–6Li–4Zn-x Mn alloys were prepared and extruded at 280℃ with an extrusion ratio of 25:1. The effects of Mn content on the microstructure and mechanical properties of Mg–6Li–4Zn-x Mn alloys were investigated in this study. The XRD results show that Mg–6Li–4Zn–x Mn alloys consisted of α-Mg(hcp) + β-Li(bcc)duplex structured matrix, Mg Li₂Zn and Mn phases. The grains of the extruded Mg–6Li–4Zn–x Mn alloys were refined by dynamic recrystallization during the extrusion process...     

Synthesis, crystal structure and thermal behavior of Rb(NTO) · H2O

The Rb(NTO)·H₂O crystal has been synthesized by reaction of 3-nitro-1,2,4-triazole-5-one (NTO) with Rb₂CO₃ in aqueous solution. Its crystal structure has been determined. The crystal belongs to monoclinic system. Crystal structure data: space group P2₁ / n; a = 0.633 0(1), b = 0.824 1(2), c =1.296 4(3) nm; β= 97.90(1)°; V = 0.669 9 (2) nm³ , Z = 4, D_c = 2.306 g/cm³, μ= 7.365 nm^-1, F (000) = 448. An eight coordinated compound is formed between Rb⁺ with oxygen atoms and nitrogen atoms. A layer structure is formed by coordination bonds and hydrogen bonds. The thermal decomposition mechanism of this coordination compound is discussed .     

Effect of Mg substitution for La on microstructure, hydrogen storage and electrochemical properties of La1−xMgxNi3.5 (x=0.20, 0.23, 0.25 at%) alloys

The effect of Mg substitution for La on microstructure, hydrogen storage and electrochemical properties of the annealed La_(1-x) Mg_x Ni_3.5(x=0.20, 0.23, 0.25 at%) alloys have been studied. All the samples were mainly composed of(LaMg)_2Ni_7,(LaMg)Ni_3, and LaNi_5 phases. Mg substitution for La changed the phase abundance, but did not change the constitution of all phases, which is con fi rmed by the results of backscattered SEM images and EDS analysis. The P–C isotherms indicated that the La_(1-x) Mg_x Ni_3.5alloys reversibly absorbed and desorbed hydrogen smoothly at 298 K. The hydrogen absorption cyclic stabilities of La_(1-x) Mg_x Ni_3.5alloy after 5 hydrogen absorption/desorption cycles reached the maximum values of91.9% and 96.0% at 298 K and 323 K, respectively. The hydrogen desorption capacity and plateau pressure for the La_(1-x) Mg_x Ni_3.5alloy reached the maximum values of 1.055 H/M and 0.074 MPa, respectively. The desorption capacities of La_(1-x) Mg_x Ni_3.5reached 0.193 H/M and 0.565 H/M in the fi rst minute at 298 K and 323 K, respectively. Electrochemical property measurement indicated that La_(1-x) Mg_x Ni_3.5(x=0.20,0.23, 0.25 at%) alloys possessed excellent activation capability and were completely activated within3 cycles. Discharge capacities of La_(1-x) Mg_x Ni_3.5alloys reached 378.2 m A h/g(x = 0.20 at%), 342.7 m A h/g(x = 0.23 at%), and 369.6 m A h/g(x = 0.25 at%), respectively. Moreover, energy density of La_(1-x) Mg_x Ni_3.5alloy was much larger than that of La_0.80Mg_0.20Ni_3.5 alloy and nearly approaches the maximum value of La0.75Mg0.25Ni3.5. Thus, the La_(1-x) Mg_x Ni_3.5alloy exhibits optimum comprehensive properties of hydrogen storage and electrochemistry.     

Effect of bromization on the properties of a series of sub-stituted 1,8,15,22-tetra(2,4-ditertbutylphenoxy) phthalocyanines

As a novel kind of functional dyes, phthalocyanines and metallophthalocyanines have been attracting the at-tention of many scientists for many years. Recently, the chemistry of Pcs has been undergoing a renaissance because Pcs and many of their derivatives exhibit theirproperties for potential application in materials science[1,2 One of the main questions in the field of phthalocya-nines research is to modify the molecular structure re-placing the benzene-spherical hydrogen atoms by various s…     

Investigation of the electronic structure and photoluminescence properties of Eu3＋ in Sr2Mgl_xZnxSi207 （0 〈x 〈 1）

Undoped and Eu 3+-doped Sr 2 Mg 1-x Zn x Si 2 O 7 (0≤x≤1) powder crystals were obtained by conventional solid-state reaction.X-ray diffraction,inductively coupled plasma analysis,and Fourier transform infrared spectroscopy results implied that a complete solid-solution formed between Sr 2 MgSi 2 O 7 and Sr 2 ZnSi 2 O 7 as well as local structural adjustment.Excitation spectra exhibited O 2-Eu 3+ charge transfer (CT) bands centered at 250 nm for Sr 2 MgSi 2 O 7:Eu 3+ and 258 nm for Sr 2 ZnSi 2 O 7:Eu 3+.Emission spectra exhibited a major band around 616 nm,which showed the environment around Eu 3+ was non-centrosymmetric in both Sr 2 MgSi 2 O 7:Eu 3+ and Sr 2 ZnSi 2 O 7:Eu 3+.In addition,first principles calculations within the local density approximation (LDA) of density functional theory (DFT) were used to calculate the electronic structure of Sr 2 MgSi 2 O 7 and Sr 2 ZnSi 2 O 7.Calculated results were correlated with experimental UV-vis reflection spectra and the observed shift of the O 2-Eu 3+ CT band.     

Out-of-plane and In-plane piezoelectric behaviors of [Ba(Zr0.2Ti0.8)O3]–0.5(Ba0.7Ca0.3TiO3) thin films

The piezoelectric properties of [Ba(Zr_(0.2)Ti_(0.8))O_3]–0.5(Ba_(0.7)Ca_(0.3)TiO_3)(abbreviated as BZT-0.5BCT) thin films deposited on Pt/Ti/SiO_2/Si substrates are reported in the present investigation. The effect of the distances between the target and substrate(d) on the morphology and out-of-plane piezoelectric properties was investigated.The experimental results showed that the ferroelectric domains size was dependent on the distance between the substrate and target and the ferroelectric domain growth was constrained by the grains. The samples exhibited well-defined out-of-plane butterfly loops and hysteresis loops and the one with d of 6.5 cm possessed the optimal ferroelectric properties and it exhibited good in-plane piezoelectric properties.     

Effect of MTEC1 on the functional expression of TCRaβ+ 3G11− 6C10− CD4+ CD8− thymocyte subset

A murine CD4⁺ thymocyte subset with phenotype of TCRαβ⁺ 3G11⁻ 6C10⁻ CD4⁺ CD8⁻ CD69^+/- HSA^med/lo contains the cells in relatively functional matured status. The functional property of the cells in this subset is characterized by the unique pattern of cytokine production at transitional stage from Th0 to Th2 type with the latter being the dominant type. After being co-cultured with murine thymic medullary epithelial cell line (MTEC1) cells, a murine thymic medullary type epithelial cell line, the TCRαβ⁺ 3G11⁻ 6C10⁻ CD4⁺ CD8⁻ CD69^+/- HSA^med/lo thymocytes, has exhibited significantly higher levels of proliferation capability and IL-6 production, whereas the production of IL-4 and IL-10 is suppressed after co-culturing with MTECl. By contrast, MTECl could not induce thymocytes to secrete Thl type of cytokines. The results suggest that MTECl can regulate functional status of this thymocyte subset and induce them to develop into a specialized Th2 subset.     

Effect of Y_2O_3 content in the pack mixtures on microstructure and oxidation resistance of B–Y modified silicide coating

B–Y modified silicide coatings were prepared on Nb–Si based alloy by pack cementation at 1300 ℃ for 10 h. The effect of Y_2O_3 content in the pack mixtures on microstructure and oxidation resistance of the coatings was investigated. The results show that the four coatings have similar structures, which possess a(Nb,X)Si_2 outer layer and a(Nb,X)_5Si_3 transitional layer. Y_2O_3 content in the pack mixtures has an obvious effect on the Si content in the coating. The mass gains of the coatings prepared with 0.5, 1, 2 and 3 wt% Y_2O_3 in pack mixtures are 2.33, 1.96, 2.05 and 2.86 mg/cm~2 after oxidation at 1250 ℃ for 100 h, respectively. The coating prepared with 1 wt% Y_2O_3 exhibits the best oxidation resistance due to the formation of a dense glass-like borosilicate scale.     

Microstructures and mechanical properties of as-extruded Mg–5Sn–1Zn–xAl(x=1, 3 and 5) alloys

As-extruded Mg–5Sn–1Zn–xAl alloys(x=1, 3, and 5) were fabricated by hot extrusion. The experimental results revealed that the yield strength of alloys initially decreased and then increased with the increase of Al content. These changes were mainly attributed to the difference in crystallographic texture and volume fractions of second phases. The ultimate tensile strength, yield strength, and elongation of the alloys were greater than 310 MPa, 227 MPa, and 11%, respectively. The strain hardening ability of the alloys was also discussed.     

Effect of the CaO/SiO2 mass ratio and FeO content on the viscosity of CaO–SiO2–"FeO"–12wt%ZnO–3wt%Al2O3 slags

An effective process for recycling lead from hazardous waste cathode ray tubes (CRTs) funnel glass through traditional lead smelting has been presented previously. The viscous behavior of the molten high lead slag, which is affected by the addition of funnel glass, plays a critical role in determining the production efficiency. Therefore, the viscosities of the CaO–SiO2–"FeO"–12wt%ZnO–3wt%Al2O3 slags were measured in the current study using the rotating spindle method. The slag viscosity decreases as the CaO/SiO2 mass ratio is in-creased from 0.8 to 1.2 and also as the FeO content is increased from 8wt% to 20wt%. The breaking temperature of the slag is lowered sub-stantially by the addition of FeO, whereas the influence of the CaO/SiO2 mass ratio on the breaking temperature is complex. The structural analysis of quenched slags using Fourier transform infrared (FTIR) spectroscopy and Raman spectroscopy reveals that the silicate network structure is depolymerized with increasing CaO/SiO2 mass ratio or increasing FeO content. The [FeO6]-octahedra in the slag melt increase as the CaO/SiO2 mass ratio or the FeO content increases. This increase can further decrease the degree of polymerization (DOP) of the slag. Furthermore, the activation energy for viscous flow decreases both with increasing CaO/SiO2 mass ratio and increasing FeO content.     

Synthesis, crystal structure and properties of binuclear manganese complex [(bipy)2Mn2(μ-O)(μ-Ac)2(H2O)2](ClO4)2

Binuclear manganese complex [(bipy)₂Mn₂(μ-O)(μ-Ac)₂(H₂O)₂](ClO₄)₂ was synthesized by the reaction of MnAc₃ · 2H₂O with 2,2′-bipyridine in the HAc-NaAc buffer (pH = 4.0). X-ray diffraction result for the single crystal shows that the crystal is monoclinic, space group C₂/C, with a = 3.408 2(7),b = 0.864 4(2),c = 2.174 9(4) nm, β= 105.2∘, V=6.186(2) nm³, Z= 8. There are two very strong peaks of UV-Vis spectrum in the range of 400–600 nm, which are similar to those of Mn catalase and Mn ribonuleotide reductase extracted from organisms. Cyclic voltammogram shows that the complex in CH₃CN undergoes quasi-reversible one-electron reduction and oxidation at E_1/2=1.15V.     

Synthesis, crystal structure and properties of binuclear manganese complex [(bipy)2Mn2(μ-O)(μ-Ac)2(H2O)2](ClO4)2

Binuclear manganese complex [(bipy)2Mn2(μ-O)(μ-Ac)2(H2O)2](ClO4)2 was synthesized by the reaction of MnAc3·2H2O with 2,2′- -bipyridine in the HAc-NaAc buffer (pH = 4.0). X-ray diffraction result for the single crystal shows that the crystal is monoclinic, space group C2/C, with a = 3.408 2(7), b = 0.864 4(2), c = 2.174 9(4) nm, β=105.2°,V =6.186(2) nm3, Z = 8. There are two very strong peaks of UV-Vis spectrum in the range of 400-600 nm, which are similar to those of Mn catalase and Mn ribonuleotide reductase extracted from organisms. Cyclic voltammogram shows that the complex in CH3CN undergoes quasi-reversible one-electron reduction and oxidation at E1/2=1.15 V.