合金元素对PrFeB永磁合金结构和磁性能的影响

本文简述了Co、Nb、Zr、Ga、Cu、Si等合金元素的加入对PrFeB永磁合金的结构和磁性能的影响情况。以上合金元素的加入,均能不同程序地提高PrFeB的磁性能;但含量超过一定比例后,永磁合金性能则有所下降。Co、Cu、Si的加入还有助于PrFeB合金居里温度的提高。     

Nb对快淬Nd10Fe84B6合金微观组织和磁性能的影响

研究了添加Nb对快淬Nd10Fe84B6合金磁性能、微观组织和晶化温度的影响.结果表明:添加Nb可以提高快淬态合金中非晶相的热稳定性,减小最佳退火温度和晶化起始温度之间的温度差,抑制热处理时α-Fe和Nd2Fe14B晶粒的预先析出和长大,有效细化了晶粒,提高磁性能.快淬Nd10Fe83Nb1B6合金经过715℃热处理10 min,磁性能达到Br=0.90 T,iHc=750 kA/m,(BH)max=120 kJ/m3,较之Nd10Fe84B6合金,内禀矫顽力提高了25%,最大磁能积提高了14%.     

C覆盖层对FePt纳米薄膜微结构的影响

使用对靶直流磁控溅射和原位退火方法在普通玻璃基底上制备了C/FePt/Fe纳米颗粒薄膜.通过表征分析表明,加入C覆盖层对FePt薄膜的微结构有较大的影响.经过退火处理后C颗粒渗透到磁性层中,起到了隔离磁性颗粒和减弱颗粒间结合能的效果,并且减弱了磁性颗粒间强的交换耦合作用,最终使颗粒和磁畴减小,增加了L10结构的有序程度;样品获得了1 089kA/m的矫顽力.     

快淬速度对Nd2Fe14B/α-Fe纳米晶双相复合稀土永磁材料相结构和磁性能的影响

采用熔体快淬法在不同快淬速度下制备了Nd8Fe86B6合金中Nd2Fe14B/α-Fe双相复合纳米晶薄带．用X射线衍射仪（XRD）和振动样品磁强计（VSM）测量了薄带的相结构和磁性能．结果表明：Nd8Fe86B6合金的最佳快淬速度为18m/s，在此条件下制备的合金薄带平均晶粒尺寸细小．综合磁性能好；合金薄带的平均晶粒尺寸为24．4nm，磁性能为Br=0．69T。Br/Bs=0．66。Hc=296．1kA/m．     

Nd-Fe-B-Sn合金的显微组织及其对磁性能的影响

 用粉末冶金烧结法制备了Nd-Fe-B,Nd-Fe-B-Sn和Nd-Dy-Fe-B-Sn永磁合金,用SEM和TEM分析了合金的显微形貌及相结构,并用永磁参量测量仪和振动样品磁强计(VSM)测量了合金的磁性能.研究表明,添加在合金中的Sn元素主要分布在富钕相中,且改善了富钕相与基体相(Nd2Fe14B)的润湿性.合金的相组成仍然是Nd2Fe14B相(Φ相)、富钕相、富硼相(η相),添加锡没有导致合金中析出新相.但是,添加锡使Nd-Fe-B系合金的室温磁性受到损害,然而却使合金在较高温时的矫顽力温度系数和开路磁通不可逆损失明显减小.锡元素对合金显微组织的改善,可能是合金高温磁性能改善的根本原因.     

Fe含量对FePt磁性薄膜的微结构和磁特性的影响

用直流磁控溅射方法和原位退火工艺在玻璃基片上制备了FexPt100-x纳米颗粒膜.研究发现,Fe含量对FePt纳米颗粒膜的微结构和磁特性有很大的影响.矫顽力随Fe含量的增加而增大,当x=48时矫顽力Hc达到了1 040 kA/m,样品出现很好的有序化L10结构扫描探针显微镜(SPM)观察结果显示,所有样品具有横跨数个晶粒的粒状磁畴,Fe48Pt52的粗糙度Ra大约0.6 nm.     

合金成分对Nd2Fe14B/α-Fe纳米双相复合稀土永磁材料结构和性能的影响

采用熔体直接快淬(DRQ)工艺制备了成分为NdxFe94-xB6(x=7,8,9,10at%)和Nd8Dy1Fe85-xNbxB6(x=0,0.5,1,1.5at%)两组合金的最佳快淬薄带.用X射线衍射(XRD)和振动样品磁强计(VSM)测量了薄带的相结构和磁性能.结果表明:NdxFe94-xB6(x=7,8,9,10)合金在x=8时综合磁性能最佳;同时添加少量的Dy和Nb元素,可有效的提高纳米双相复合永磁合金的磁性能.     

新型铁基纳米晶合金的微组织和磁性能

研究了纳米晶Fe85.2Cu1Al1Zr3.3Nb3.5B3Si3合金淬火态和退火态的微组织和磁性能．研究表明，样品经673～873K退火0．5h后，体心立方结构的纳米晶态α—Fe(Si)析出，晶粒尺寸呈线性增长，最终趋于15nm左右．合金的微组织是典型的纳米晶相，残余非晶相和粒问相的混合，其中各种相的体积分数变化都会影响其磁性能．在813K等温退火0．5h后，纳米晶相体积分数为40％，饱和磁感应强度为1．56T，矫顽力为1．787A．m^-1．     

强磁场退火对FePt薄膜结构与磁性能的影响

为减少FePt纳米薄膜退火过程中晶粒团聚长大,进行了在外加强磁场条件下的退火实验。对化学法制备的FePt纳米薄膜,经热处理后外加磁场,并使用X射线衍射仪、透射电子显微镜、扫描电子显微镜、振动样品磁强计表征薄膜的结构、晶粒尺寸和磁性能。实验发现:外加7.96MA.m-1磁场450℃退火,样品即开始有序化相变;外加7.96MA.m-1磁场600℃退火,样品有序度要高于常规退火样品;外加1.59～6.37 MA.m-1磁场550℃退火,样品晶粒明显细化、矫顽力明显提高。因此,强磁场退火能降低FePt薄膜有序化相变温度,提高有序度、细化晶粒和提高矫顽力。     

热处理对Fe83Ga17合金磁致伸缩和有序-无序的影响

实验研究了热处理对〈110〉取向多晶Fe83Ga17合金磁致伸缩性能和有序-无序度的影响.发现冷却速度的不同直接影响着合金的有序程度和磁致伸缩性能,部分有序的Fe83Ga17合金样品磁致伸缩性能最好,水中淬火处理后,在20 MPa预压力作用下,Fe83Ga17饱和磁致伸缩系数λs达到298×106.     

混合稀土对高铝锌基合金组织与性能的影响

研究了混合稀土对高铝锌基合金组织与性能的影响，结果表明：稀土的加入，使合金铸态组织细化，强度、塑性、韧性和耐磨性得以提高。在稀土加入量为0．1％时，湿砂型铸态组织中晶界与昌内均可观察到稀土相的存在，而在水冷金属型铸态组织中，却未观察到稀土的存在，稀土元素固溶于基体中。     

Influence of Rare Earth Elements on Mechanical Properties and Corrosion Resistance of Cu-15Ni Alloy

In order to improve the mechanical property and Cl-+S2-corrosion resistance of B15 copper-nickel alloy,Cu-15Ni-xRE(x:0-0.1%by weight)alloy was prepared by adding rare earth(RE)in melted Cu-15Ni alloy using metal mould casting method.Optical microscopy(OM),electronic tensile testing machine,X-ray diffraction(XRD),scanning electron microscope(SEM),and electrochemical testing system were used to analyze mechanical property,corrosion resistance property,and surface microstructure of different treatment samples.The results of OM and tensile testing show that the RE addition can effectively deoxidize the alloy melt and the microstructure of the alloy changes from coarse dendrite to small equiaxed grain.By addition of 0.05%RE,the tensile strength and elongation of Cu-15Ni alloys are improved from 294 MPa to 340MPa,and 8%to 33.5%respectively.The results of electrochemical testing show that the corrosion resistance of Cu-15Ni alloy is greatly improved by adding proper amount of RE,whereas excess addition of RE worsens the corrosion resistance.The optimum RE content was about 0.05%by weight.In comparison with the alloy without RE,the corrosion potential and corrosion current density of Cu-15Ni alloy containing proper RE decreased by about-0.28 V and 70A/cm2,respectively.     

稀土元素La,Ce对93WNiFe合金力学性能的影响

通过粉末冶金方法制备了添加稀土元素La,Ce的93W-4.9Ni-2.1Fe合金,研究了稀土元素对高密度93钨合金静、动态力学性能的影响. 结果表明,添加少量的稀土元素La,Ce可以显著提高93钨合金的力学性能. La,Ce的加入使合金断口上钨-钨界面分离和钨-粘结相界面开裂的比例减少,钨颗粒解理断裂和基体相韧性撕裂的比例增加. 稀土元素La,Ce改变了氧和硫在合金中的存在与分布状态,减小了其在钨-粘结相界面的偏聚,从而改善了合金的力学性能.     

退火温度对FePt薄膜物性的影响

用直流磁控溅射方法和原位退火工艺在玻璃基片上制备了Fe48Pt52纳米薄膜.研究发现,退火温度对FePt膜的微结构和磁特性有很大的影响,退火可以减小颗粒间的磁相互作用,矫顽力随退火温度的升高先急剧增大后减小,600℃退火处理的FePt样品平行膜面方向的矫顽力略大于垂直方向,分别达到了684.4,580.9 kA/m;650℃退火处理的FePt样品在2个方向上都获得了巨大的矫顽力,最大值达到了986.8 kA/m.     

稀土对激光重熔合金化层组织与性能的影响

本文研究了加稀土与不加稀土的FeBSi非晶粉末涂层经激光重熔后的组织与性能。结果发现,两者相比,前者合金化层的硬度和耐磨性均比后者提高一倍左右。显微组织分析表明,加入稀土的激光重熔合金化层有马氏体相变发生,其组织为奥氏体及部分马氏体枝晶,碳化物、合金化合物与奥氏体及马氏体枝晶,碳化物、合金化合物与奥氏体及马氏体共晶组成。层内晶粒细小,共晶化合物多,形态规整、分布均匀。未加稀土的激光重熔合金化层中没有马氏体相变发生,其组织为奥氏体枝晶和枝晶间的枝杈状、锯齿状碳化物和合金化合物等共晶组成,层内晶粒粗大,共晶化合物大小不等且分布不均。     

稀土对Al-Zn-Mg合金力学性能和应力腐蚀的影响

将0.06%稀土加入到Al-Zn-Mg合金中, 固溶处理后在150 ℃下时效. 在峰时效条件下 , 观察稀土对其力学性能和抗应力腐蚀断裂性能的影响. 结果表明, 稀土的加入使硬度峰值出现的时间提前, 并使硬度峰值、 屈服强度、 抗拉强度、 延伸率和抗应力腐蚀断裂的能力增加. 金相观察和X射线衍射结果表明, 稀土的加入减小了晶粒尺寸, 促进了强化相MgZn₂的析出, 此外稀土还能够明显减少合金中的 氢含量.     

富Nd混合稀土MR-Fe-B永磁合金的性能

本文研究了廉价高性能富Nd混合稀土MR-Fe-B永磁合金的成分及其工艺因素对磁性能的影响。确定了这种铁基稀土永磁合金的最佳成分及最佳工艺制度。该永磁合金磁性能达到:B_r=1.15—1.28T(11.5—12.8 kGs),i~Hc=573—796kA/m(7.2-10.0kOe);(BH)_(max)=247—270kJ/m~3(31—34MGOe),在20—100℃范围内开路磁通可逆温度系数为-0.098%/℃,居里温度T_c=310℃,维氏硬度HV≥520。对其高矫顽力的机制进行了探讨,认为烧结态磁体的矫顽力主要来源于富 MR相的作用,而后烧态磁体的矫顽力的提高主要是反磁化校数目减少的缘故。     

热浸镀富铈稀土铝合金的耐腐蚀性研究

研究了富铈稀土对碳钢热浸镀铝合金组织及耐腐蚀性的影响.结果表明,在稀土含量为0.1%～0.5%范围内随着稀土含量的增加热浸镀层组织均匀,当稀土含量超过0.5%时扩散层厚度明显减小,稀土含量0.3%的热浸镀层具有最好的组织,并且在酸性介质腐蚀条件下具有最好的耐腐蚀性.含0.3%稀土的热扩散层的耐腐蚀性比纯铝提高2～3倍.     

碳酸稀土变质铝硅合金的研究

将配有熔剂的碳酸稀土直接加入共晶铝硅合金，可使共晶硅完全变质，机械性能大幅度提高，并且变质具有极好的长效性。从理论上分析了碳酸稀土的变质行为。