羊毛的变性处理

纯毛粗绒线的原料一般用４８ｓ～５８ｓ半细毛．将４６ｓ羊毛进行变性处理，若在不损伤纤维的情况下，使得羊毛的细度下降约３μｍ，便可用于纺粗绒线．本文优选了羊毛变性处理的最佳工艺，测试了变性羊毛的主要物理机械性质和染色性能，从变性羊毛的表面形态和结构变化，初步探讨羊毛的变性机理．结果表明，用优选工艺进行羊毛变性处理，基本上脱掉了羊毛表面的鳞片，细度下降３μｍ，不损伤羊毛皮质层；变性羊毛手感柔软，光泽增强，具有良好的防毡缩性；羊毛纤维的染色速度加快，得色鲜艳度提高，物理机械性质变化不大．     

改善羊毛对酸性染料吸附性能的研究

用阳离子剂对羊毛做变性处理后，可在羊毛中引入阳离子基，提高它在酸性液中的阳荷性，增加染座，增强对匀染性酸性染料的吸附能力，从而提高羊毛的上染率和染色牢度．试验结果表明，匀染性酸性染料对变性羊毛的染色深度和湿处理牢度在一定程度上均有提高．但碱性阳离子变性处理液对羊毛有一定损伤，需进一步研究改善措施．     

羊毛的化学改性及其阳离子染料染色性能研究

合成了一种阴离子型羊毛改性剂,测定了羊毛纤维经改性剂处理后的白度、碱溶解度、断裂强度及伸长率等性能,讨论了改性羊毛对阳离子染料上染率的影响因素,测定了改性羊毛染色后的皂洗牢度和磨擦牢度。实验结果表明,羊毛经阴离子改性剂处理后机械性能基本不变,在100℃、pH=5、染色60 m in后阳离子染料的上染率达到80%以上,并且具有较高的染色牢度。     

抗菌性阳离子活性染料对不同纤维的染色及抗菌性能

采用合成的抗菌性阳离子活性染料对尼龙66、羊毛和腈纶纤维进行了染色和抗菌性能研究.该染料对3种纤维均具有良好的染色性能,3种纤维染色织物具有良好的耐水洗和耐摩擦色牢度,但上染速率和上染率具有一定的差异,染色后的3种纤维织物具有良好的抗菌性能.同时,采用该染料对棉、尼龙66、羊毛和腈纶纤维织物进行了同浴染色性能研究,结果表明:该染料对4种纤维在同浴染色时具有不同的上染速率,同色性具有一定的差异.该染料在水溶液中具有良好的抗菌性能,对大肠杆菌(E.coli)和金黄色葡萄球菌(S.aureas)的最小抑菌浓度(MIC)为10×10-6g/L.     

糜蛋白酶预处理羊毛的低温染色性能

用正交试验法研究了糜蛋白酶对羊毛纤维的预处理情况,再用染料酸性大红BS在较低温度下对预处理后的羊毛进行染色,测定了羊毛的上染率、表观色深值、断裂强力等性能。实验结果表明：在糜蛋白酶用量为2％（owf）、pH值为7、温度为40℃、时间为60min的预处理条件下,酸性大红BS在80℃下染羊毛的上染率达到95．1％,色深值（K／S）达到15．05,强力下降率只有5．78％,与常规染色工艺条件下的染色性能相比,上染率和色深值均有提高,而纤维强力损失较小。     

羊毛低温染色的研究

本文采用乙醇胺予处理(简称MEA)及染浴助剂相结合的方法,对媒介染料羊毛染色进行了探讨。文中分析了MEA予处理羊毛对染色的影响;讨论了低温促染剂GF在媒介染料染色中的作用机理;确定了在85℃条件下进行低湿染色的工艺。该工艺与常规染色相比,提高了上染率,减少了纤维损伤,同时改善了纤维性能,提高了折皱回复角。     

兰纳素染料染羊毛工艺浅探

针对采用常规活性兰纳素染料对羊毛纤维进行染色中存在的问题,经过反复实验对比,总结出了两种行之有效的改进方法,即加氯化稀土促进兰纳素染料上染和加助剂米勒兰LTD实现低温染色。     

电晕处理对毛织物表面性能的影响

对羊毛织物的表面进行了电晕处理，用XPS和SEM研究了处理前后纤维袁面化学结构及物理结构的变化，探讨羊毛的润湿性、表面静电性能和对植物染料染色性能的变化．结果表明，经电晕处理后，羊毛表面舍氧量增多，表面漫润性得到改善，增加了纤维表面的亲水性；此外，电晕处理导致鳞片表层胱氨酸的部分二硫键氧化断裂，改善了对植物染料黄连的染色性能，表现为上染速度提高，但上染率变化不大．     

萘系偶氮型通用染料结构与染色性能之间关系

从超分子化学角度研究了双萘环和单萘环通用染料在染色过程中的构效关系.对腈纶纤维染色时,由于双萘环染料分子对相邻阴离子染席的空间屏蔽作用,其上染率下降.对涤纶纤维染色时,染料分子自身的空间结构对上染率的影响不明显.对棉纤维染色时,由于双萘环染料分子对纤维的直接性好、磺酸基在分子中所占的比例低,其上染率提高.对羊毛和丝绸染...     

阳离子丝素助剂改性羊毛及改性纤维染色性能

用自制的阳离子改性丝素助剂整理羊毛纤维，研究整理工艺条件对羊毛纤维染色性能的影响．结果表明，改性的丝素助剂整理的羊毛纤维显著改善了对活性染料的染色性能，同时整理的羊毛织物防缩抗鹱性能提高．     

稀土在毛制品上的应用

近年来，稀土元素作为纺织梁整助剂在羊毛纤维、纱线和织物的应用取得了很大进展，其中包括羊毛散纤维、全毛绒线、毛织物及全毛地毯等的染色和漂白，目前的稀土羊毛漂染是在不改变生产工艺流程，不增加加工设备条件下，将稀土作为一种漂染助剂加入染浴或漂浴中，起到染色增深增浓、缓染匀染，七约染化料，低温、低铬染色，提高颜色鲜艳度以及促进漂白等作用。本文阐述了稀土羊毛漂染的机理，总结了近年来的生产实践经验，以期进一步推动稀土在纺织染整领域中的应用和研究工作。     

乌拉圭羊毛理化性能及其可纺性的研究

着重研究乌拉圭细羊毛和半细羊毛在化学组成、形态结构、纺纱工艺性能和染色性能等方面的特点，并与相当细度的美利奴羊毛有关性能相对比．分析了ＭＩＣ２２．６、ＭＩＣ２６．８、ＭＩＣ２８．８三种毛条的纤维长度和细度分布特性，制定出可纺纱支的纱线规格和相应的加工工艺路线．结果表明，乌拉圭羊毛表面鳞片密度低并紧贴毛干，使羊毛明亮光泽；乌拉圭羊毛强力大，初始模量高，卷曲弹性率较低，表面光滑，摩擦系数小；乌拉圭羊毛含有较少的自由氨基，上染比较缓慢．根据其特性，作者认为乌拉圭羊毛加工过程中需特别注意和毛油剂种类的选择，同时宜采用较低的单纱和股线捻系数，设计色泽鲜艳、要求保形性能好的产品．     

超声波处理对羊毛纤维性能的影响

以未处理、55℃超声波处理和沸水处理的羊毛纤维为研究对象,对比分析两种处理方法对纤维力学性能、表面形态、化学结构的影响,从纤维角度探讨超声波低温染色的机理.试验结果表明,经超声波处理后的羊毛,束纤维强度降低,油脂质量分数减少,纤维表面鳞片张角增大并产生不规则裂纹,部分二硫键断裂,纤维分子有序程度降低,因此,羊毛在染色过程中更易润湿,染料更易进入纤维内部并扩散.     

The Study of Top Dyeing Damage by Bundle Tensile Testing

It is well known that top dyeing is an Important step in wool processing, but it will result in the damage of fibre in normal dyeing. How to measure the damage quickly and to evaluate it quantitatively are vital important for wool industry and also interested for wool researchers. For the purpose, nineteen tops dyed in normal condition from three wool textile mills in China were tested with TENSOR, a bundle fibre tensile tester. The experimental results showed that the dyeing damage rate of bundle strength of these tops is 6% - 7% in average and some tops were higher than 10% dyeing damage. Meanwhile, the dyeing damages for different wool mills were discussed . It is obvious that bundle tensile test is an efficient and quick method to evaluate the damage caused by top dyeing and to identify the difference between wool mills in quality and quantity.     

Study on the Dyeing Behaviors of Low Temperature Glow Discharge Treated Wool

Wool tops was modified by low temperature glow discharge (LTGD). The inputted power, the treating time and the pressure or vacuum were found to play an important role. The wool tops were dyed with reactive dye under a constant dyeing temperature after plasma treatment. Then the dyeing behaviors were studied based on the data of uptake, fixation, dyeing rate and fixing rate. The results revealed the possibility of low temperature dyeing and the suitable parameter of LTGD treatment.     

散毛染色损伤分析

本文对酸性媒介染料散毛染色前后的羊毛性能做了测试和分析,发现纤维受到严重损伤,表现为强力、伸长、膨松度大大降低。纤维损伤主要是以化学损伤、局部损伤、毡缩损伤3种形式出现的。为减少纤维损伤,提高染色毛的纺纱性能,进行了一些探讨。     

四乙烯五胺交联染料在羊毛上的吸附及染色性能研究

吸附动力学和吸附热力学可以指导染色理论和染色工艺的建立.考察了pH、温度和时间对四乙烯五胺交联染料在羊毛纤维上吸附性能的影响,研究了四乙烯五胺交联染料的吸附动力学和吸附平衡模型.研究显示四乙烯五胺交联染料的染色pH在羊毛的等电点以上,染料吸附过程遵循准二级动力学方程,并且活化能为130.3kJ/mol,以化学吸附为主.染色温度的提高可以加快染色速率但降低了染料的平衡吸附量,吸附平衡为Langmuir型,吸附的各项热力学参数均为负值,说明吸附过程是自发放热的过程.另外,测定了染料的交联反应性能和各项色牢度,结果表明四乙烯五胺交联染料在羊毛纤维上可得到近100%的交联反应率和优良的色牢度.     

Sorption Behaviour of Acid Dyes by Soybean Protein/Poly （vinyl alcohol） Blend Fibre

The sorption behaviour of acid dyes by soybean protein/poly（vinyl alcohol） blend fibre was studied. The quantity of dye sorbed by the fibre increased markedly with the decrease in the pH of dyebath and reduced with the addition of neutral electrolyte when the pH was below 4.5, Acid dyes exhibited higher sorption rate constant and lower half dyeing time for the fibre than for spun silk and wool, which was related to the special morphological structure of the fibre, At pH 4, the sorption of disulphonated acid dyes with higher molecular weight followed the dual sorption mechanism of Langmuir plus Nernst-type partitioning well as they interacted with the fibre through electrostatic forces, hydrophobic forces and hydrogen bonds. It is considered that soybean protein and PVA components should be simultaneously dyed by disulphonated acid dyes with higher molecular weight.     

Research on the Dyeing and Finishing Properties of Wool Treated with Chitosan

The dyeing and finishing properties of wool treated with chitosan were studied. It was shown that chitosan can be absorbed by wool in an acetic acid bath, both dyeing rate and equilibrium dye uptake of wool treated with chitosan increase in a wide pH range from strong acid to neutral conditions. This work also indicated that chitosan could be used to achieve feltproofing of wool.