25Cr5MoA钢/Q235钢固-液复合轴界面Cr元素扩散行为

提出了金属梯度结构轴的概念.研究了固-液复合的25Cr5MoA钢/Q235钢复合轴的组织、Cr元素的扩散以及结合界面附近显微硬度的变化规律.结果表明:经过挤压变形后,25Cr5MoA钢/Q235钢界面形成了良好的冶金结合,二者结合紧密,除了组织结构的差别外,二者的结合界面已经难以区分.结合界面附近Cr元素在固-液复合时得到充分扩散,并呈现出连续分布的形态.从界面向Q235钢和25Cr5MoA钢两侧±100μm范围内,硬度呈现出均匀、连续分布.经过热处理后,随着加热温度的升高和加热时间的延长,Cr元素在结合界面附近的分布更加均匀,分布曲线在界面的斜率进一步降低,使结合界面附近25Cr5MoA钢的一侧的显微硬度大幅度降低,这有利于形成化学成分、组织以及性能的梯度变化.     

25Cr5MoA钢/微合金钢/Q235钢的复合轧制

将25Cr5MoA钢/微合金钢/Q235钢板复合板坯加热到轧制温度950～1100℃,经保温后轧制1道次,压下量为50%～65%,制成25Cr5MoA钢/微合金钢/Q235钢热轧复合板试样.利用剪切实验方法测定了复合板材的界面结合强度,通过光学显微镜观察结合界面的组织.结果表明:当轧制温度为1000～1100℃时,25Cr5MoA钢/微合金钢/Q235钢能有效复合;压下量对25Cr5MoA钢/Q235钢复合板界面结合强度有一定的影响,当压下量达到一定程度后,随着压下量的增加,复合板的结合强度逐渐降低;轧制温度对25Cr5MoA钢/微合金钢/Q235钢复合板界面结合强度影响很大,在道次压下量一定的情况下,随着轧制温度的升高,复合板的结合强度逐渐升高.在1100℃的轧制温度和50%压下量的轧制条件下结合强度达到最大值.     

25Cr5MoA/Q235钢复合板的结合性能

将25Cr5MoA/Q235钢板复合板坯加热到800～1 100 ℃,经保温后轧制1道次,压下量为50%～70%,制成25Cr5MoA/Q235钢热轧复合板试样. 用材料力学性能试验机测试复合板试样复合界面的剪切强度,用光学显微镜和扫描电镜观察界面的组织. 结果表明:当轧制温度在900～1 000 ℃时,有利于25Cr5MoA/Q235钢的复合;道次压下量对25Cr5MoA/Q235钢复合板界面结合强度影响非常大,道次压下量大,有利于形成更多洁净、活化的新生表面,并且可以细化晶粒,提高复合板的结合强度;金属组织中晶粒的梯度变化,有利于提高双金属复合材料的结合强度.     

钢-半固态Al-7石墨复合界面特性

为了开发高温钢铝轴瓦材料,采用铸轧技术进行了钢板与Al-7石墨半固态浆料的复合实验,得到了不同于常规钢铝复合产品的界面结构。结果表明:在钢板预热温度为510℃、Al-7石墨半固态浆料固相率(体积分数)为32%的条件下,随着扩散时间的增加,复合界面上生成的铁铝化合物逐渐增多;当扩散时间大于35s时,复合界面完全由铁铝化合物构成;当扩散时间为22.5s时,可形成由铁铝化合物和铁铝固溶体交替构成的新型结构,其界面力学性能较好。     

铜／钢液固相复合界面冶金行为的研究

以液固相复合法生产的铜包钢线为研究对象,利用光学显微镜和扫描电镜的能谱等手段分析了铜／钢界面区的组织形态和成分组成。结果表明：在界面区发生了互扩散,形成了Fe、Cu固溶体,无脆性的金属间化合物产生,这使得该复合材料具有较好的微观结合力。     

TA1/Q235钢复合板累积叠轧焊界面特性

对TA1/Q235钢复合板累积叠轧焊进行了研究.研究结果表明:采用累积叠轧焊方法能够制备出结合性能较好的钛/碳钢复合板,其结合强度随着累积变形量与首道次变形量的增加而提高,叠轧过程中经磨床打磨与喷丸处理获得洁净、新鲜并具有一定加工硬化程度的结合界面,会促进复合板结合强度的提高.800℃以下热轧后,Q235钢的组织呈明显的条带状;而850℃以上热轧后,Q235钢条带状变形组织逐渐转化为等轴状,界面附近的Q235钢脱碳,出现明显的排列整齐且粗大的铁素体晶粒带.钛侧的组织主要有等轴α组织和魏氏α组织.综合考虑轧制温度对钛与Q235钢组织与界面结合性能的影响,累积叠轧温度应控制在800～850℃之间.     

TA2-Q235B爆炸复合板钢侧组织特征

借助光学显微镜、电子背散射衍射和扫描电子显微镜等测试技术和手段,系统地研究热处理温度对TA2--Q235B爆炸复合板钢侧组织转变的影响,并分析了其形成机理.结果表明:在热处理过程中,钢侧界面组织发生脱碳,形成完全由铁素体组织组成的脱碳层,这些铁素体没有织构特征;当热处理温度在850℃及以下时,钢侧界面组织在靠近波头漩涡的地方发生异常长大,形成粗大的铁素体;当热处理温度在900℃及以上时,钢侧界面组织在钛钢复合界面上发生异常长大,产生柱状的铁素体组织.这些组织的形成受到碳元素的扩散和钢侧基体组织相变的共同作用.热处理过程中,界面产生的TiC在界面上分布不均,随温度升高,在界面局部富集,从而加速了碳元素向界面的扩散.     

工艺参数对楔横轧42CrMo/Q235复合材料层合轴界面剪切强度的影响

对楔横轧42CrMo/Q235层合轴进行轧制实验和界面剪切强度试验,研究成形角α、展宽角β、断面收缩率Ψ、轧制温度T、基材直径d等工艺参数对界面剪切强度的影响规律.结果表明:对楔横轧层合轴界面剪切强度的影响主次为:断面收缩率Ψ、轧制温度T、基材直径d、展宽角β、成形角α.层合轴界面剪切强度随着断面收缩率Ψ、轧制温度T和基材直径d的增大而增大,但过高的轧制温度与过大的基材直径将减小界面剪切强度;随着展宽角β和成形角α的增大而减小.研究结果对楔横轧层合轴模具优化设计和增强界面结合性能提供了依据.      

A novel diffusion model considering curvature radius at the bonding interface in a titanium/steel explosive clad plate

This article introduces an element diffusion behavior model for a titanium/steel explosive clad plate characterized by a typical curved interface during the heat-treatment process. A series of heat-treatment experiments were conducted in the temperature range from 750℃ to 950℃, and the effects of heat-treatment parameters on the microstructural evolution and diffusion behavior were investigated by optical microscopy, scanning electron microscopy, X-ray diffraction analysis, and electron-probe microanalysis. Carbon atoms within the steel matrix were observed to diffuse toward the titanium matrix and to aggregate at the bonding interface at 850℃ or lower; in contrast, when the temperature exceeded 850℃, the mutual diffusion of Ti and Fe occurred, along with the diffusion of C atoms, resulting in the formation of Ti–Fe intermetallics (Fe₂Ti/FeTi). The diffusion distances of C, Ti, and Fe atoms increased with increasing heating temperature and/or holding time. On the basis of this diffusion behavior, a novel diffusion model was proposed. This model considers the effects of various factors, including the curvature radius of the curved interface, the diffusion coefficient, the heating temperature, and the holding time. The experimental results show good agreement with the calculated values. The proposed model could clearly provide a general prediction of the elements’ diffusion at both straight and curved interfaces.     

宽带激光熔覆铸造WCp /Ni基合金复合涂层结合界面组织特征

研究了宽带激光熔覆铸造WCp /Ni基合金复合涂层结合界面组织特征。结果表明结合界面微区组织特征为细小的共晶体组织、过渡层组织以及白亮带组织。白亮带及过渡层中主要含有Fe ,Cr,Ni,Si等元素。白亮带主要是单相的γ - (Fe ,Cr ,Ni,Si)固溶体组织。从熔覆区→过渡层→白亮带的平均显微硬度值呈梯度分布。复合涂层结合界面主要元素、微观组织结构和显微硬度呈梯度分布的特征 ,提高了涂层与基材之间的匹配性 ,缓解应力集中 ,避免裂纹形成 ,实现了基材与涂层良好的冶金结合。     

Microstructure and properties of pure iron/copper composite cladding layers on carbon steel

In the present study, pure iron/copper composite metal cladding was deposited onto carbon steel by tungsten inert gas welding. The study focused on interfacial morphological, microstructural, and mechanical analyses of the composite cladding layers. Iron liquid–solid-phase zones were formed at copper/steel and iron interfaces because of the melting of the steel substrate and iron. Iron concentrated in the copper cladding layer was observed to exhibit belt, globule, and dendrite morphologies. The appearance of iron-rich globules indicated the occurrence of liquid phase separation (LPS) prior to solidification, and iron-rich dendrites crystallized without the occurrence of LPS. The maximum microhardness of the iron/steel interface was lower than that of the copper/steel interface because of the diffusion of elemental carbon. All samples fractured in the cladding layers. Because of a relatively lower strength of the copper layer, a short plateau region appeared when shear movement was from copper to iron.