Oxidation pathway and kinetics of titania slag powders during cooling process in air

The oxidation pathway and kinetics of titania slag powders in air were analyzed using differential scanning calorimetry(DSC) and thermogravimetry(TG). The oxidation pathway of titania slag powder in air was divided into three stages according to their three exothermic peaks and three corresponding mass gain stages indicated by the respective non-isothermal DSC and TG curves. The isothermal oxidation kinetics of high titania slag powders of different sizes were analyzed using the ln-ln analysis method. The results revealed that the entire isothermal oxidation process comprises two stages. The kinetic mechanism of the first stage can be described as f(α) = 1.77(1-α) [-ln(1-α)]~((1.77-1)/1.77),f(α) = 1.97(1-α) [-ln(1-α)]~((1.97-1)/1.97), and f(α) = 1.18(1-α) [-ln(1-α)]~((1.18-1)/1.18). The kinetic mechanism of the second stage for all samples can be described as f(α) = 1.5(1-α)~(2/3)[1-(1-α)~(1/3)]~(-1). The activation energies of titania slag powders with different sizes(d_1 0.075 mm, 0.125 mm d_2 0.150 mm, and 0.425 mm d_3 0.600 mm) for different reaction degrees were calculated. For the given experimental conditions, the rate-controlling step in the first oxidation stage of all the samples is a chemical reaction. The rate-controlling steps of the second oxidation stage are a chemical reaction and internal diffusion(for powders d_1 0.075 mm) and internal diffusion(for powders 0.125 mm d_2 0.150 mm and 0.425 mm d_3 0.600 mm).     

湖南树木三新种

<正> 1.石门鹅耳枥 新种 图版I∶1 Carpinus shimenensis C. J. Qi, sp. nov. Species insignis, ab omnibus speciebus generis foliis late ellipticis, vel late ovatooblongis, minoribus, 3-5 cm longis, 2-3 cm latis, margine acute dentato-duplica-to-serratis, nervis lateralibus 11-13 jugis, supra manifeste impressis, subtus conspicueelevatis, dense villosis, bracteis frucferis semiovatis vel semiovato-rotundis, extra marginedentato-lobatis, intra margine basi auritis facile distinguibilis. Arbor decidua alta 5 m, trunco 20 cm diametro; ramuli juvenales atro-grisei, deindelaete brunnei, internodiis brevissimis. Folia papyracea, elliptica, vel ovato-elliptica, 3-5cm longa, 2-3 cm lata, apice abrupte acura, obtusa vel aliquantum rotunda, basi cordata,aliquantum obliqua, supra adpresse byssaceo-villosa, nervis lateralibus utrinsecus 11-13,distantioni nervi 2-3 mm, cum costis supra impressis, subtus manifeste elevatis, margineirregulariter dentato-duplicato-serratis, serraturis abrupte acutis; petioli breves, crassi,4-11 mm longi, dense villosi; stipulae persistentes, circ. 7 mm longae, rubrobrunneae.Spica fructifera 3-3.5 cm longa, in rhachidi villosae; nuculae ovato-rotundae, circ. 4 mm     

重庆主城区冬春季降水强度对大气污染物影响

利用重庆主城区2004-2008年1-3月和11-12月的日平均降水资料和空气污染资料,分析了重庆主城区大气污染物浓度分布和不同等级降水对污染物浓度清除能力,结果表明:当降雨量在5mm以上时,大气污染物浓度明显减少,且大气污染物浓度随雨量增加而增加,但污染物下降幅度与雨量增加幅度的对应关系一般.连续降水的第1天和第2天有较好的湿清除能力,第3天和第4天湿清除能力较差.雨量在1～9.9 mm区间,每增加1 mm降水对大气污染物的清除率变化最大,10～15 mm区间,每增加1 mm降水清除率变化最小,几乎没有增加.15 mm以上,每增加1 mm降水,清除率变化增加.     

两相UASB反应器相分离

以蔗糖为基质 ,采用连续进水的方式 ,研究两相 UASB反应器的相分离 .结果表明 ,控制酸化相 p H值为 5 .5 0～ 6.0 0 ,可得到满意的相分离效果 .运行 80 d后 ,酸化相颗粒污泥直径为 2～ 8mm ,污泥浓度为 73.61kg.m-3,COD去除 的产气率 74 0 .0 m L .g-1,COD容积负荷为 116.0 6kg.(m3.d) -1;产甲烷相颗粒污泥直径为 1～ 3mm,污泥浓度为 5 3.73kg.m-3,COD去除 的产气率 614 .4 m L .g-1,COD的容积负荷为 19.91kg.(m3.d) -1.两相 UASB反应器的 COD总去除率达 93.3%,COD容积负荷为 2 0 .82 kg.(m3.d) -1.     

快速高效地板辐射供暖特性影响因素的数值模拟

数值计算了夏热冬冷地区不同的结构层厚度、地暖管导热性能以及超导模块特性对快速高效地板辐射供暖特性的影响。结果表明:当地暖进水温度为318 K、室内初始温度为279 K、开启地暖10 min后,结构层厚度从0 mm增加到15 mm时,室内温度最高相差13. 2 K;地暖管导热系数从0. 4 W·m~(-1)·K~(-1)增加到3. 6 W·m~(-1)·K~(-1)时,室内温度最多相差6. 4 K;比较是否铺设导热模块两种情况,相同供暖时间下,最大相差13 K。为了综合评价快速供暖的影响,提出室内温度不均匀系数,并发现当结构层厚度δ5 mm、地暖管导热系数λ1. 2 W·m~(-1)·K~(-1)、有超导模块工况下,室内平均温度在289. 6～296. 5 K之间,温度不均匀系数在3. 77×10~(-3)～5. 89×10~(-3)之间,有较好的室内温度舒适性和均匀性,可以满足快速供暖需求。     

高压辊磨超细碎对攀西钒钛磁铁矿分选的影响

对攀西钒钛磁铁矿进行了高压辊磨超细碎及其选别试验.当入料d80为155mm时,辊压中料-32mm产率为9105%,-0074mm产率为1529%,P80降低至155mm,边料及闭路循环工艺对粉碎产品粒度特性的影响也非常明显.采用“铁钛平行分选”工艺对高压辊磨超细碎的-32mm攀西钒钛磁铁矿进行了选别试验.结果表明,选铁流程在磨矿细度为-0074mm占45%时,铁精矿Fe品位可达5505%,回收率7064%;选钛流程在-0074mm占80%时,钛精矿TiO2品位4778%,回收率3516%.     

辽西地区水分亏缺与树木生长关系

利用修正的Thornthwaite最大蒸发力公式,计算了辽西地区不同市的水分亏缺量.各市最大潜在蒸发散计算结果是:朝阳1 180.6 mm,锦州1 146.0 mm,葫芦岛1 140.1 mm,阜新1 030.3 mm;水分亏缺量计算结果为:朝阳-658.3 mm,锦州-538.4 mm,葫芦岛-544.8 mm,阜新-626.9 mm.利用美国spss数理统计软件计算了油松与蒙古栎的胸径连年生长量和对应的各年1-12月份的月均温、月降雨量、平均相对湿度的回归关系,表明油松生长与温度紧密,蒙古栎生长与水分关系紧密.     

凤梨内生菌筛选鉴定及拮抗效果评价

以凤梨叶片为筛选材料,通过平板对峙培养法筛选出3株对蔬菜软腐病菌菊迪基氏菌有拮抗效果的生防细菌,结合生理生化及分子生物学鉴定,以及拮抗效果评价试验,结果表明,这3株内生菌分别为:Bacillus amyloliquefaciens F-2,Bacillus megaterium F-3-1,Bacillus subtilis F-3-2,皆为革兰氏阳性菌。其中F-2对菊迪基氏菌和丁香假单胞菌的抑菌效果最好,抑菌圈分别为24. 67 mm和28. 83 mm; F-3-1对病原真菌燕麦镰孢菌、胶孢炭疽菌、互隔交链孢霉,抑菌率分别为70. 83%、91. 67%、65. 56%. F-3-2对丁香假单胞菌和黄单胞菌属的抑菌效果最好,抑菌圈分别为20. 75 mm和20. 00 mm。另外,通过生化鉴定研究发现,这3株优良内生菌还具有很好的解磷固氮和产纤维素酶能力,这对内生菌的筛选及内生菌对植物抗病促生作用的研究提供了一定的参考价值。     

干燥条件对海巴戟天果中水分和蒽醌类化合物含量的影响

在真空干燥、密闭干燥、热风干燥条件下,研究干燥温度为50℃、60℃、70℃和样品厚度(1 mm、2 mm、3 mm)对海巴戟天果的干燥动力学和蒽醌类化合物含量的影响.水分的干燥曲线表明干燥动力学和有效水分扩散率的关系,阿伦尼乌斯方程则表示扩散系数与温度的关系.干燥条件、样品厚度(1 mm、2 mm和3 mm厚度)以及干燥温度影响干燥率和蒽醌类化合物含量.真空干燥条件具有更高的干燥效率,水分扩散率和蒽醌类化合物含量均较高.当样品厚度为3 mm,真空条件下扩散系数8.82×10-10m2/s,活化能为36.52 KJ/mol.     

[Co(2,3-tri)(een)Cl][ZnCl_4]配合物的合成及—异构体的晶体结构

用过氧化物法合成了 [Co(2 ,3 -tri) (een)Cl][ZnCl4](2 ,3 -tri=N - (2 -Aminoethyl) - 1 ,3 - propanediamine ;een =N -Ethylethylenediamine)中的五个异构体 ,解析了其中的一个异构体的晶体结构为顺式 (2 ,3 -tri中仲胺上的氢相对于Cl)经式异构体 (m4[ZnCl4]) 晶体学参数 :单斜晶系 ,空间群P2 1/c,a =0 .9799(3 )nm ,b =2 .681 5(9)mm .c =0 .81 0 7(3 )mm ,β =1 0 7.595(6)° ,V =2 .0 3 0 (1 )nm3,Dc=1 .756g/cm3,Z =4,F0 0 0 =1 1 0 0 .0 0 ,μ(Mo -Ka) =2 6.62cm-1,R =0 .0 660 ,Rw =0 .1 53 6.配位中心离子Co3+为六配位 晶胞中含 2个配合物离子和 2个 [ZnCl4]2 -阴离子 ,配合物中对映体的比例为 1∶1     

MPM管屏焊机研制

1 主要技术参数 1）适应钢管范围为巾32mm-Ф76．2mm,壁厚为3．5-9mm;扁钢宽厚为12．7-110mm,壁厚为4-9mm;材质为低碳钢或低合金钢;管屏最大尺寸：L×B=12m×1．6m。2）工件输送速度：0．1-1m／min变频无级调速;3）焊接速度为600-800mm／min。4）生产能力为V=0．8m／min,每月有效工作时间约240h计算,[第一段]     

薄层色谱法分离测定1,5-苯并硫氮杂α-氨基-β-内酰胺

用薄层色谱法分离测定了反应混合物中的 1 ,5-苯并硫氮杂 艹卓-α-氨基 -β-内酰胺 .扫描条件为 :λ1 =2 80 nm,λ2 =3 54nm,狭缝 1 .2 mm× 1 .2 mm,SX=3 .校准曲线的线性范围是 0 .2 75～ 7.70 μg( γ=0 .990 5,n=9) ,最低检出限为 0 .1 4 0μg.方法的变异系数小于 5% ,平均回收率为 1 0 0 .1 5% ,方法简便、快速     

Φ400数控飞锯机的设计

介绍了一种新型数控飞锯机,它结构合理,能够实现对运动中各种型材的连续切割.其控制系统采用工控机与PLC相结合,及变频器共同控制.试运行表明,该锯机与普通锯机相比,锯切频率由1-3提高到4-6,定尺精度由±8 mm提高到±5 mm.     

中国宽蛾属分类学研究(鳞翅目:宽蛾科)

本文记述中国宽蛾属昆虫 8种 ,其中包括 3新种和 3中国新记录种 .并绘制了新种和新记录种的外生殖器特征图 ,编制了分种检索表 .模式标本保存在南开大学生物学系 .申氏宽蛾 Depressaria sheni Wang et Li新种 (图 1～ 2 )翅展 2 3.5～ 2 6 .5 mm.正模 ,河南内乡宝天曼 ,1 35 0 m,1 998- -1 3,李后魂采 .副模 :8 ,采集资料同正模 :1 ,1♀ ,黑龙江省黑河市 ,1 70 m,1 997- -2 6 ,李后魂采 .本种与 Depressaria basicostata Matsumura相似 ,但可通过下列特征区别 :雄性外生殖器抱器腹端突端部光裸 ,末端钝尖 ,阳茎中部具微刺 ;雌性外生殖器囊突呈菱形 .考宽蛾 Depressaria koskjuki Lvovsky中国新记录 (图 3～ 4 )研究标本 :1 ,1 993- -4 ,1♀ ,1 987- -9,甘肃榆中兴隆山 ,2 1 2 0 m,李后魂采 .分布 :甘肃 ,俄罗斯 .壮瓣宽蛾 Depressaria valida Wang et Li新种 (图 5～ 6 )翅展 1 3.0～ 2 3.0 mm.正模 ,陕西宁陕火地塘 ,1 6 2 0 m,1 990 - -1 6 ,李后魂采 ;副模 3♀♀ ,采集资料同正模 .本种与 Depressaria basicostalia Matsumura近似 ,但新种的雄性抱瓣宽短 ,抱器腹端突出自腹缘基部 3/5 ;雌性囊突靠近交配囊的一侧 ,形状为不规则长菱形 .新瓣宽蛾 Depressaria varivalvata Wang et Li     

高效液相色谱法测定3-丁酰氨基-1,2,4-苯并三嗪-1,4-二氧化物的含量

建立高效液相色谱法测定3-丁酰氨基-1,2,4-苯并三嗪-1,4-二氧化物的含量。采用Diamonsil C18柱(5μm,4.6 mm×250 mm),流动相为甲醇-水(40∶60),流速:1.0 mL.min-1,检测波长:274 nm,柱温:25℃。结果在所选定的液相色谱条件下,3-丁酰氨基-1,2,4-苯并三嗪-1,4-二氧化物与有关物质完全分离;并且在12～42μg.mL-1(r=0.999 8,n=6)范围内线性关系良好,检测限为1.5 ng,定量限为4.5 ng。说明方法简便、灵敏、重复性好,可用于3-丁酰氨基-1,2,4-苯并三嗪-1,4-二氧化物含量测定。     

抑制型离子色谱法同时测定矿泉水中阴离子的研究

基于化学自动再生抑制型离子色谱电导法,以2.0 mm ol.L-1N a2CO3+1.3 mm ol.L-1N aH CO3+2%CH3COCH3做淋洗液,选择了最佳色谱条件,在10.5 m in内一次进样测定了矿泉水中F-、C l-、NO3-、SO42-4种主要阴离子。测定样品的相对标准偏差(RSD)为2.59%~5.83%,样品回收率在90.6%~107%之间。采用化学抑制模式的离子色谱法是检测矿泉水中阴离子的快速、准确的方法。     

HPLC法测定蒙药复方述达格-4中1-苯基-7-(3-甲氧基-4-羟基)苯基-5-醇-3-庚酮的含量

建立测定蒙药复方述达格-4药材中1-苯基-7-(3-甲氧基-4-羟基)苯基-5-醇-3-庚酮含量的方法.色谱柱为InertsilODS-3(4.6mm×250mm,5μm),以乙腈(B)-0.5%磷酸水溶液(A)为流动相,梯度洗脱(0~20min,0%B→45%B;20~25min,45%B→55%B;25~40min,55%B→100%B),流速1.0ml·min-1,检测波长为210nm,柱温30℃,进样量20μL.结果表明蒙药复方述达格-4药材中1-苯基-7-(3-甲氧基-4-羟基)苯基-5-醇-3-庚酮在0.102-1.02μg(r=0.99999)质量范围内与色谱峰面积呈良好的线性关系,精密度、稳定性、重复性试验的RSD≤2%,平均加样回收率(n=6)为99.63%(RSD=1.77%).本法简便、快速、准确,可为蒙药复方述达格-4的质量控制提供依据.     

在线测量Sn-3.5Ag焊点蠕变的电阻应变

以焊料(Sn-3.5Ag)在薄铜基片之间制作截面积约为1 mm2,厚度分别为0.42 mm 和0.10 mm 的试样(其面积与电子封装中的无铅焊点面积大体相同)为对象,利用特制的电子测试系统实时、在线测量试样焊点的微电阻及其剪切应力,并通过串行接口将相关数据传输至计算机.数据经计算机处理后,拟合成实时微电阻和测试时间的关系曲线.基于经典的Griffith 断裂模型,建立一个简易数学模型,从理论上论证电阻应变与焊点机械蠕变裂纹之间的关系.研究结果表明该关系曲线反映焊点的裂纹连续生长、蠕变失效过程,变化趋势与经典结果吻合;在24 MPa 应力作用下,厚度为0.42 mm 的试样最大电阻应变为0.18,最大电阻应变率为2.2×10-3 s-1;在25 MPa应力作用下,厚度为0.10 mm 试样的最大电阻应变为0.036,最大电阻应变率为3.5×10-3 s-1,实验持续时间较厚度为0.42 mm 的试样短.     

三级配混凝土及湿筛混凝土单轴动态拉伸性能试验研究

考虑大骨料特性的混凝土动态拉伸性能研究是混凝土坝抗震特性研究的一个突出问题.进行了大坝迎水面常用的三级配混凝土及湿筛混凝土在10-5、10-4、10-3、10-2 s-1四种应变速率下的单轴动态直接拉伸强度试验.试验采用尺寸为250mm×250mm×400mm和150mm×150mm×300mm的棱柱体试件.试验测得不同应变速率下试件的单轴动态拉伸应力和应变.基于试验数据探讨了三级配混凝土及湿筛混凝土的破坏形态、单轴抗拉强度、峰值应力点的应变随应变速率的变化规律.此外,还建立了三级配混凝土与相应湿筛二级配混凝土的动态强度关系.试验结果可为混凝土大坝、海洋平台等的抗震设计提供理论依据.     

广东省蓝藻新种

在整理和编写中国蓝藻志广东省蓝藻的工作中,我们发现并鉴定了下述新种. 1.广州片藻新种图版Ⅰ,图3—4;图版Ⅱ,图9—14;图版Ⅲ,图3—4. Merismopedia cantonensis W. J. Zhu, sp. noy. Thallus libere natans, membranaceo-sublaminiformis, alivaceus, 0.5-2 mm latus, I.5-6 mm longus (oculis nudis visibili), margine laterali bi-vel tri-lobatus, lobis plicatis-convolutis; familiae multae, cum cellulis numerosis compositis; cellulae aspectu frontali oblongae, 5-6μ latae, 6-8μ longae, aspectu laterali cylindricae, 5-6μ latae, 10-12μ altae, contento pallide aerugineo, non granuloso. Guangdong: Xin-f.eng-huang Cun, Henan., Guangzhou, in fossis, aqua