Ni-W-P-Al_2O_3复合镀层的制备与抗高温氧化性能

采用直流电沉积技术制备了Ni-W-P-Al_2O_3复合镀层,通过控制镀液中Al_2O_3颗粒的质量浓度及颗粒的粒径,研究了Al_2O_3颗粒对复合镀层表面微观形貌、镀层厚度及抗高温氧化性的影响,并对复合镀层的附着力强度进行了测试.结果表明:通过控制镀液中Al_2O_3颗粒的质量浓度可以获得不同成分的复合镀层;一定质量浓度的Al_2O_3颗粒可以细化Ni-W-P合金镀层的胞状组织,并且纳米颗粒对镀层的细化效果明显优于微米颗粒;Al_2O_3颗粒的质量分数和尺寸对Ni-W-P-Al_2O_3复合镀层的厚度有明显的影响;镀液中Al_2O_3颗粒的质量浓度为15g/L时所得镀层的抗高温氧化性最好;镀层附着力达到1级标准,Ni-W-P合金复合镀层与基体结合良好.     

碳纳米管/铅锡新型复合减摩镀层的抗咬合行为

采用复合电沉积技术制备碳纳米管/铅锡合金新型减摩镀层。在干摩擦条件下,采用摩擦磨损试验法,研究镀液中的碳纳米管的质量浓度对复合镀层抗咬合性能的影响和复合镀层摩擦因数的变化,并用扫描电子显微镜观察普通铅锡镀层和复合镀层的咬合后的形貌。实验结果表明:当试验机的转速为500r/min时,在相同的法向载荷下,复合镀层的抗咬合时间比普通铅锡镀层的抗咬合时间明显延长;当镀液中的碳纳米管质量浓度为2g/L时,抗咬合性能显著提高,优于其他复合镀层;当法向载荷为100N时,复合镀层的摩擦因数逐步上升到1.4以上,而普通铅锡合金镀层的摩擦因数在1.4~1.6之间平稳变化;碳纳米管可以显著改善铅锡复合镀层的抗咬合性能。     

电沉积Cr/ZrO_2复合镀层的结构和摩擦性能

采用复合电沉积工艺制备Cr/ZrO2纳米复合镀层,分别用扫描电子显微镜(SEM)、扫描电子显微镜附带能谱仪(EDS)、X线衍射(XRD)等技术较系统地研究了Cr/ZrO2纳米复合镀层的表面形貌、成分、结构和耐磨性。研究结果表明:复合镀层的中ZrO2的复合量质量分数为1.47%,在ZrO2纳米粒子的弥散强化作用下,Cr/ZrO2复合镀层无裂纹,组织致密,结构呈现明显的非晶态特征;在干摩擦条件下,纳米Cr/ZrO2复合镀层的摩擦性能明显优于3价铬镀层的摩擦性能;纳米Cr/ZrO2复合镀层的磨损主要表现为疲劳磨损特征,而3价铬镀层的磨损机制为磨料磨损。     

载荷对纳米晶Co-Ni-Fe合金镀层摩擦磨损性能的影响

用脉冲电沉积技术制备表面平整光亮的纳米晶Co-Ni-Fe合金镀层.采用XRD、TEM、SEM、EDS等方法研究了纳米晶Co-Ni-Fe合金镀层的微观组织结构、表面形貌和合金成分.研究了干滑动摩擦条件下纳米晶镀层的摩擦磨损性能、磨损后的组织结构和硬度的变化.结果表明：纳米晶Co-Ni-Fe合金镀层的晶体结构为单相面心立方结构.镀层的摩擦系数和磨损量随着摩擦载荷的提高而增大,即镀层的耐磨性随载荷的提高而下降.摩擦磨损使纳米晶Co-Ni-Fe合金镀层发生晶粒长大,摩擦载荷越大,磨损后镀层的硬度越低.     

注塑模零件电刷镀纳米镀层的耐磨性能研究

利用电刷镀技术制备了含纳米SiO2和石墨粉的非晶态Ni-P合金复合镀层，并对其摩擦磨损性能进行了研究。研究表明，当纳米粉体在基质镀液中分散良好时，该复合镀层具有较高的显微硬度，较好的耐磨性及减摩性；当分散不良时，镀层的各项性能未见明显改善。模具试验表明，复合镀层有效地降低了干摩擦状态下注塑模推管与摩擦件的表面划伤与金属转移。     

镍基纳米SiC复合镀层的摩擦学性能

为研究镍基纳米 Si C复合镀层的摩擦学性能 ,在A3钢板上制备了该镀层 ,利用扫描电镜对镀层显微组织进行观察 ,通过纳米显微力学探针测量镀层微区硬度 ,在 MM-2 0 0摩擦磨损试验机上对镀层进行磨损试验 ,研究阴极电流密度、温度和镀液中 Si C浓度等主要工艺参数对镀层耐磨性能的影响。结果表明 :Si C颗粒在镀层中分布均匀 ;Si C颗粒附近镀层的硬度是纯镍镀层的 3倍 ,但随着远离 Si C,复合镀层硬度明显下降 ;复合镀层的耐磨性能与普通镍镀层相比有较大幅度的提高 ,在油润滑条件下磨损体积为普通镍镀层的 1/ 8。     

电沉积镍-磷-纳米金刚石纳米复合镀层性能研究

利用电沉积法制备了镍-磷复合镀层和镍-磷-纳米金刚石纳米复合镀层,对镀层的结构和形貌进行了表征,研究了热处理温度对复合镀层硬度、摩擦性能的影响．研究发现,与电沉积Ni-P合金镀层相比,镍-磷-纳米金刚石复合镀层具有较高的酎磨性和较低的摩擦系数,硬化峰值出现在673K左右．另外,对纳米复合镀层性能改善的机理进行了讨论．     

组合超声场下电沉积Ni-Nd2O3纳米复合镀层的摩擦磨损性能

在组合超声场下利用电沉积方法制备了Ni-Nd2O3纳米复合镀层,利用扫描电镜分析了复合镀层微观形貌和纳米颗粒含量,测试了复合镀层显微硬度,并考察了复合镀层的摩擦学性能和磨损机理。研究结果表明:组合超声对Ni-Nd2O3纳米复合镀层微观组织、颗粒含量、显微硬度和耐磨性均有影响;与无超声和单一超声相比,在组合超声空化效应和协同效应的影响下,复合镀层晶粒得到进一步细化,组织致密性得到提高,纳米颗粒含量和显微硬度得到提升;组合超声作用下制备的Ni-Nd2O3纳米复合镀层摩擦因数小、磨损率低,表现出优良摩擦学性能。     

Ni-P-PTFE复合镀膜摩擦磨损性能的研究

本文采用化学复合镀工艺在钛合金基体上共沉积Ni-P-PTFE复合镀膜,并和传统的Ni-P镀层进行了比对,研究这两种镀层及钛合金基体在相同条件下的摩擦磨损性能。实验结果表明,化学镀Ni-P镀层和化学复合镀Ni-P-PTFE镀膜都具有良好的耐磨和减摩性能,其中Ni-P-PTFE复合镀膜的效果更为明显,可将钛合金表面的摩擦系数降至0.13左右。     

Ni-P-PTFE复合镀膜摩擦磨损性能的研究

本文采用化学复合镀工艺在钛合金基体上共沉积Ni-P-PTFE复合镀膜,并和传统的Ni-P镀层进行了比对,研究这两种镀层及钛合金基体在相同条件下的摩擦磨损性能。实验结果表明,化学镀Ni-P镀层和化学复合镀Ni-P-PTFE镀膜都具有良好的耐磨和减摩性能,其中Ni-P-PTFE复合镀膜的效果更为明显,可将钛合金表面的摩擦系数降至0.13左右。     

自润滑Ni-P-PTFE化学复合镀工艺及镀层性能

研究了Ni-P-PTFE(聚四氟乙烯)复合镀层的制备工艺,筛选出氟碳类阳离子表面活性剂FC4和非离子表面活性剂FC10,该混合表面活性剂使得粒子具有很好的分散性和悬浮性．在此基础上研究了不同PTFE含量对镀速及镀层性能的影响．结果表明,随着PTFE浓度提高,镀速下降,复合镀层中的粒子含量增加,镀层的硬度相应减小,其耐蚀性也有所下降．而PTFE粒子对Ni-P的晶化温度基本没有影响,摩擦磨损试验表明,该复合镀层与GCr15对磨其摩擦系数低至0．1,具有良好的自润滑效果,而且耐磨性也较Ni-P镀层好。     

Cu-Zn-Al2O3 nanocomposites: study of microstructure,corrosion, and wear properties

Alumina nanoparticles were added to a Cu-Zn alloy to investigate their effect on the microstructural, tribological, and corrosion properties of the prepared alloys. Alloying was performed using a mixture of copper and zinc powders with 0vol% and 5vol% of α-Al nanopowder in a satellite ball mill. The results showed that the Cu-Zn solid solution formed after 18 h of mechanical alloying. The mechan-ically alloyed powder was compacted followed by sintering of the obtained green compacts at 750℃ for 30 min. Alumina nanoparticles were uniformly distributed in the matrix of the Cu-Zn alloy. The tribological properties were evaluated by pin-on-disk wear tests, which revealed that, upon the addition of alumina nanoparticles, the coefficient of friction and the wear rate were reduced to 20% and 40%, respectively. The corrosion properties of the samples exposed to a 3.5wt% NaCl solution were studied using the immersion and potentiodynamic polarization methods, which revealed that the addition of alumina nanoparticles reduced the corrosion current of the nanocomposite by 90%.     

Cu-Zn-Al2O3 nanocomposites:study of microstructure,corrosion,and wear properties

Alumina nanoparticles were added to a Cu-Zn alloy to investigate their effect on the microstructural, tribological, and corrosion properties of the prepared alloys. Alloying was performed using a mixture of copper and zinc powders with 0vol% and 5vol% of α-Al nanopowder in a satellite ball mill. The results showed that the Cu-Zn solid solution formed after 18 h of mechanical alloying. The mechanically alloyed powder was compacted followed by sintering of the obtained green compacts at 750℃ for 30 min. Alumina nanoparticles were uniformly distributed in the matrix of the Cu-Zn alloy. The tribological properties were evaluated by pin-on-disk wear tests, which revealed that, upon the addition of alumina nanoparticles, the coefficient of friction and the wear rate were reduced to 20% and 40%, respectively. The corrosion properties of the samples exposed to a 3.5wt% NaCl solution were studied using the immersion and potentiodynamic polarization methods, which revealed that the addition of alumina nanoparticles reduced the corrosion current of the nanocomposite by 90%.     

Fe－Ni－Al_2O_3复合镀层的制备及其性能的研究

在酸性氯化物电解液中进行Ａｌ＿２Ｏ＿３微粒与铁、镍的共沉积试验，对所得Ｆｅ－Ｎｉ－Ａｌ＿２Ｏ＿３复合镀层的摩擦磨损性能进行研究，结果表明，铁镍合金镀层中弥散分布８．５１％重量的Ａｌ＿２Ｏ＿３微粒后，其摩擦系数和磨损率显著降低，镀层的摩擦磨损性能得到改善。     

铝合金表面机械球磨Ni-Al-Mo复合涂层的制备及其摩擦特性研究

通过机械球磨方法在铝合金表面制备了Ni-Al-Mo复合涂层,对涂层微观组织、组成成分和摩擦学性能等进行了分析.结果表明:经过7 h机械球磨制备的Ni-Al-Mo复合涂层内元素均匀分布;550℃退火后涂层中均有Al3 Ni金属间化合物新相生成;复合涂层中Al3 Ni和Mo的存在使得涂层硬度高于铝合金基体和Ni-Al涂层,...     

40Cr表面TiAlN/TiN复合镀层的滑动摩擦试验分析

采用多弧离子镀工艺在40Cr表面制备了TiAlN/TiN复合镀膜,利用UMT-2摩擦磨损实验机考察了TiAlN/TiN膜层的承载能力和摩擦学性能,通过扫描电子显微镜观察了磨损试件的表面形貌,应用X射线能谱仪分析了磨痕中心区元素及其含量,通过40Cr基体和TiAlN/TiN膜在摩擦系数和磨损量方面的比较来评价TiAlN/TiN复合膜层的摩擦学性能。结果表明:TiAlN/TiN涂层与基体间的结合力是影响涂层承载能力的主要因素之一,TiAlN/TiN复合镀层的摩擦学性能优于40Cr基体,TiAlN/TiN复合镀层的减摩、耐磨性能优越,并能成功地抵抗磨粒磨损和粘着磨损。     

Cu-TiO2纳米复合镀层的腐蚀和光催化性能

采用纳米复合镀技术在铝表面制备了Cu-TiO2纳米复合镀层,利用扫描电镜、电化学测试系统、分光光度计对其形貌、腐蚀和光催化性能进行了研究.结果表明,TiO2纳米颗粒在铜基复合膜层中的分散均匀;TiO2颗粒的加入可使Cu-TiO2纳米复合镀层腐蚀电位明显增加,膜层的耐蚀性提高;在紫外光照射下,复合镀层对甲基橙溶液有明显的光催化降解作用,且这种作用随时间延长而有所增大.     

纳米碳管化学复合镀层摩擦磨损行为

为了进一步提高Ni-P合金镀层的耐磨性,采用化学镀方法使纳米碳管与镍磷在45#钢上共沉积制得纳米碳管耐磨复合镀层。结果表明：纳米碳管已均匀镶嵌在镍磷晶胞上,在干摩擦条件下,纳米碳管复合镀层的耐磨性明显优于纳米碳化硅复合镀层,更优于普通镍磷镀层,并对纳米碳管复合镀层的磨损机理进行了研究。     

SiO2包覆对爆炸喷涂自敏涂层发光和摩擦性能的影响

采用溶胶-凝胶法在铝酸锶荧光粉表面包覆SiO₂层,以45号钢为基体,采用爆炸喷涂技术制备不同SiO₂包覆质量分数下的SrAl₂O₄∶Eu²⁺, Dy³⁺/Cu-14Al-X自敏复合涂层.对比研究了不同包覆质量分数下铝酸锶粉末与自敏涂层的发射光谱和余辉衰减曲线,复合涂层的摩擦系数与磨损量以及SiO₂包覆质量分数对自敏涂层的发光性能和摩擦学行为的影响.结果表明:SiO₂包覆使得铝酸锶在爆炸喷涂制备过程中得到了保护,提高了涂层的发光性能.随着SiO₂包覆质量分数的增加,复合涂层结构致密度、硬度和耐磨性提高.20%包覆质量分数下铝酸锶粉末硬度为564.5HV,比未包覆铝酸锶粉末的涂层提高了38%.由于破碎后的SiO₂包覆层具有自润滑效果,包覆后复合涂层的摩擦系数相对稳定,15%SiO₂包覆质量分数下复合涂层摩擦系数为0.182,具有最优的摩擦性能.