镁合金性能与熔炼的探究

介绍了镁合金的分类和组织与性质特点,并介绍了镁合金的主要熔炼方法。熔炼设备,熔剂及气体保护熔炼技术,保护性气体有SF6、CO2、SO2、N2等或它们的混合气体,SF6和CO2是有害气体科学家研究用氩气替代SF6和CO2作为镁合金熔炼保护气体。     

AZ31镁合金及其焊接接头疲劳性能的研究

研究了AZ31镁合金母材、TIG非承载焊接接头试件在脉动循环载荷作用下的疲劳性能,并与铝合金的疲劳性能进行了比较.     

一步水热法构筑镁合金超疏水表面及其性能研究

利用一步水热法在镁合金表面构筑了超疏水表面.通过扫描电子显微镜(SEM)、傅里叶变换红外(FT-IR)、X射线光电子能谱分析(XPS)、X射线衍射(XRD)、接触角测量仪对其表面形貌、组成和润湿行为进行了研究,采用电化学极化曲线测试对超疏水涂层的耐腐蚀性能进行了考察.结果表明,一步水热法构筑的镁合金超疏水涂层由微/纳米二级结构组成,最优条件下改性表面接触角和滚动角分别为163.3°和2.8°,具有良好的耐腐蚀性能、耐酸碱性能和稳定性.     

AZ31B镁合金板料热拉深性能研究

通过实验研究了成形温度对AZ31B交叉轧制镁合金板料成形性能的影响.结果表明:随着温度的升高(T≤240 ℃),镁合金板料的成形能力提高,在210～240 ℃时,AZ31B镁合金板料具有很好的拉深成形性能,为最佳成形温度范围.     

镁合金AZ91D性能探究

随着现代工业的飞速发展,镁合金显得越来越重要。从汽车、航空工业到个人计算机、手机其制成品日益走进我们的生活。本文通过对镁合金特征趋势,重量轻、硬度高、防电磁波干扰、防震性等优良机械性能的介绍,从而对镁合金广阔的应用前景有一个很好的认识。     

锡酸钠添加剂改善镁合金腐蚀及放电性能的研究

采用电化学方法探究了不同浓度锡酸钠添加剂对AZ31B镁合金在MgSO4-Mg(NO3)2(0.14 mol/L MgSO4,1.86 mol/L Mg(NO3)2)电解液中的腐蚀以及电化学放电行为的影响.结果表明,镁合金在含有1 mmol/L锡酸钠添加剂的溶液中具有最大的极化电阻值、最短的滞后时间和最低的电压降.采用电...     

镁合金深冷处理研究

在液氮温度(-196℃)对工业用镁合金AZ31,AM60进行深冷处理,处理时间分别为2 h,4 h,8 h,24 h,48 h,72 h,并进行了力学性能测试、金相组织观察、XRD衍射测试和SEM断口扫描测试.结果发现:深冷处理可以明显提高镁合金的力学性能,改善其显微组织,同时深冷处理可以引起镁合金的晶粒转动现象.研究结果为提高镁合金性能提供了一种简单有效的方法.     

镁合金磷化工艺及耐蚀性研究

采用磷酸盐体系对镁合金表面进行磷化处理,并对磷化配方进行优化．利用扫描电镜（SEM）观察膜层形貌,用极化曲线方法对不同工艺下得到的磷化膜进行耐腐蚀性能分析．结果表明,镁合金表面经过优化配方处理后,磷化膜均匀、细小、致密,膜层主要由锰的磷酸盐构成,富含氧、磷、锰等元素,完全不合Mg和Al．优化配方磷化后的镁合金表面在3．5％NaCl溶液中浸泡24h,耐腐蚀性能显著提高,并确定了最佳工艺条件为：温度60℃、时间60min、pH值3．     

变形镁合金的研究及开发

综述了变形镁合金材料的力学性能和应用领域,介绍了变形镁合金材料加工技术的发展方向,较系统地介绍了镁合金塑性加工技术以及镁合金的开发应用领域和前景,认为变形镁合金将成为重要的商用轻质结构材料。     

消失模镁合金铸件的腐蚀行为

对消失模镁合金铸件的表面成分与耐腐蚀能力进行了研究，发现消失模镁合金铸件比其他铸造方法获得的铸件的耐腐蚀性更好．在50g／L的NaCl盐浴中腐蚀，聚苯乙烯(EPS)消失模镁合金试样的耐腐蚀性能比普通铸造得到的镁合金试样耐腐蚀性提高了约3倍．其主要原因是以EPS为模样的镁合金消失模铸造得到的铸件表面有一层MgO-Al2O3-SiO2-无定型C粒子等组成的薄膜，该薄膜对镁合金起到了保护作用．因此，消失模铸造非常适用于镁合金的成形。     

镁合金材料的应用及其加工成型技术

综合介绍了镁合金材料的基本性能、产品优越性和典型产品的应用,着重分析讨论了镁合金材料加工成型技术和存在的问题,以及我国镁合金材料研究和应用的发展现状。并就镁合金材料的应用前景、开发潜力和尚需解决的问题等方面进行了探讨。     

粗镁直接炼制镁阳极合金的研究

利用山西峰华鲜厂现有的生产设备，由粗镁直接炼制镁阳极合金，试验获得成功，本文对阳极合金熔炼工艺过程，合金产品质量，技术经济效益以及镁阳保护合金的使用进行了分析、研究     

氩气保护条件下碳对AM60镁合金组织性能的影响

在氩气保护精炼条件下研究了煤粉、石墨粉、碳纤维等形态的碳元素对AM60镁合金组织与性能的影响,探讨了C元素对其合金组织的细化机理。研究结果表明,在AM60镁合金中加入少量不同形态的碳元素能有效地改善其显微组织,使AM60镁合金的铸态室温力学性能有了不同程度的提高;当碳以纤维状态加入时,合金室温铸态力学性能的提高幅度最大,其抗拉强度和延伸率分别达到了242.4 MPa和13.2%,分别在原合金的基础上提高了23%和2.5倍。     

Study on vertical mandibular distraction osteogenesis using magnesium alloy on canine

The bone formation feasibility by a novel magnesium alloy device was evaluated using a canine vertical mandibular distraction osteogenesis(DO) model. Osteotomies were performed in the area where last 3 star’s teeth of left mandibular were pulled out before 3 months. Both AZ31 magnesium alloy(n ? 6) and 316 L stainless steel(n ? 6) distraction devices were implanted. The distraction osteogenesis was carried out with a latency of 5 days after mandibular osteotomy. Distraction proceeded at a rate of 0.3 mm/8 h for 7 days and followed by 4 weeks of consolidations. The evaluations were conducted by scanning electron microscopy(SEM) and histological examinations. There were osteoblasts and trabecular bones formations manifestly in both groups. There was no significant difference in the bone mineral density between the two groups. The surface of the magnesium alloy was much more cracked and uneven, resulting from the surface pitting corrosion. The crew nails were closely combined with the surrounding bone tissue. AZ31 magnesium alloy exhibited a certain degradation rate in mandibular and did not post a negative effect on the kidney and liver. The observations in magnesium alloys group is consistent with the stainless steel group.     

In vitro and in vivo studies on biodegradable magnesium alloy

The microstructure, mechanical property, electrochemical behavior and biocompatibility of magnesium alloy(Bio De MSM^TM) were studied in the present work. The experimental results demonstrated that grain refining induced by extrusion improves the alloy strength significantly from162 MPa for the as-cast alloy to 241 MPa for the as-extruded one. The anticorrosion properties of the as-extruded alloy also increased.Furthermore, the hemolysis ratio was decreased from 4.7% for the as-cast alloy to 2.9% for the as-extruded one, both below 5%. Bio De MSM^TMalloy shows good biocompatibility after being implanted into the dorsal muscle and the femoral shaft of the New Zealand rabbit, respectively, and there are no abnormalities after short-term implantation. In vivo observation indicated that the corrosion rate of this alloy varies with different implantation positions, with higher degradation rate in the femur than in the muscle.     

镁合金环保型阳极氧化工艺研究

采用Na284O7,Na2SiO3,有机羧酸盐及有机胺等组成的环保型碱性电解液,对AZ91D镁合金的阳极氧化进行了研究．实验结果表明：在这种无铬、无氟、无磷的环境友好电解液中,镁合金表面可形成一层光滑致密、具有较高硬度和优良耐蚀性的阳极氧化膜．探讨了电解液中各组分在成膜过程中的作用及电解工艺参数对成膜过程和膜层性能的影响,研究表明：Na284O7为促进成膜、增加膜层厚度的主要物质;Na2SiO3具有细化膜层、改善膜层耐蚀性的作用;有机羧酸盐可以有效提高膜层的硬度;有机胺可有效抑制阳极发生弧光放电．另外峰值电流密度、电解液温度以及pH值对成膜过程和膜层性能也有明显的影响．     

AZ91D镁合金半固态浆料制备工艺

采用自行设计制造的半固态镁合金机械搅拌装置,制备了镁合金半固态浆料,研究了搅拌工艺参数对半固态镁合金组织的影响.结果表明:搅拌速率、静置时间和搅拌温度对半固态组织影响很大,搅拌速率在900r/min时,静置时间为5-10 min,搅拌温度在565～575℃时,获得的组织均匀细小;搅拌速率过大,晶粒尺寸反而有所增大;静置时间影响半固态组织中固相晶粒的长大;搅拌温度影响固相率,从而也影响到固相晶粒的圆整度.     

稀土Gd对AZ系列镁合金压铸件性能的影响

研究了添加稀土元素Gd(0～3.0%)对AZ镁合金压铸件力学性能的影响,试验结果表明:随稀土Gd加入量的增加,AZ镁合金抗拉强度和屈服强度先有提高,过量的稀土Gd反而使AZ铁合金抗拉强度和屈服强度下降.稀土Gd加入量为1.5%时,稀土对AZ镁合金的力学性能强化效果最好,在室温及150 ℃温度条件下AZ-Gd镁合金综合性...