新型节镍奥氏体耐热钢的亚动态再结晶行为

在Gleeble-3800热模拟试验机上利用双道次热压缩实验,研究新型节镍奥氏体耐热不锈钢21Cr-11Ni-N-RE在变形温度950~1 150℃、应变速率0.1~10 s-1,道次间保温时间为0.5~30 s的亚动态再结晶行为。建立亚动态再结晶的动力学模型,并将预测值与试验值进行比较。研究结果表明:试验钢易发生亚动态再结晶,随着道次间保温时间的延长、应变速率的增大和变形温度的升高,材料亚动态再结晶体积分数迅速增大;预应变超过峰值应变后,应变继续增大对亚动态再结晶体积分数的影响十分有限。21Cr-11Ni-N-RE耐热不锈钢的亚动态再结晶激活能Qmdrx为130.417 k J/mol,模型预测值与试验值吻合较好。     

AZ31镁合金加工图研究

采用加工图理论系统的分析了AZ31镁合金在高温变形过程中的变形行为。结果表明:AZ31镁合金在塑性变形行为过程中发生动态再结晶,温度的升高和应变速率的降低有利于动态再结晶形核的形成与长大。采用加工图理论分析AZ31镁合金高温下的塑性变形行为并至关反映变形后AZ31镁合金材料的组织演化以及性能变化规律。由加工图可知材料的最佳变形条件:压缩变形过程温度为320℃~360℃、应变速率为0.5~0.05 s-1;拉伸变形过程温度为350℃~400℃、应变速率为0.001~0.000 33 s-1.     

Ti微合金化汽车大梁钢510L动态再结晶行为

采用单道次压缩实验和阶梯试样热轧-淬火实验研究了低成本的Ti微合金化汽车大梁钢510L的动态再结晶行为.结果表明,应变速率为0.1s^-1时,变形温度为850~1050℃时均发生动态再结晶,应变速率为0.2s^-1时,只有在变形温度高于950℃时发生动态再结晶.变形温度的升高和变形量的增大会逐渐细化奥氏体晶粒,并使再结晶体积分数趋于增大.回归得到实验钢的动态再结晶激活能仅为211.43kJ/mol,说明Ti的添加几乎没有抑制高温奥氏体的动态再结晶,并建立了动态再结晶临界应变模型和动力学模型.     

Q345B钢动态再结晶动力学模型研究

在Gleeble 1500热模拟机上进行Q345B钢单道次压缩变形实验,得到其真应力-真应变曲线,结合加工硬化率曲线,确定了Q345B钢动态再结晶临界应变εC、峰值应变εP和稳态应变εS。根据实验结果得到Zener-Hollomon方程和动态再结晶状态图,利用Johnson-Mehl-Avrami(JMA)方程法得到再结晶体积分数实际值,采用3种不同的再结晶体积分数预报模型对实验数据进行回归,并对再结晶体积分数实测值和预报值进行对比。结果表明,Epsilon-S/Epsilon-C模型精度最高,Epsilon-S模型精度次之,Epsilon-P模型精度最差。     

高强钢300M静态再结晶动力学研究

为研究高强钢300M静态再结晶行为,采用Gleeble-3800型热模拟试验机对300M钢进行单/双道次热压缩试验.通过双道次热压缩试验分析了变形温度、应变速率、变形量和初始晶粒尺寸对静态再结晶体积分数的影响.变形温度越高,应变速率越大,变形量越大,初始晶粒尺寸越小,则静态再结晶体积分数越大.其中变形温度、变形量和应变速率对静态再结晶体积分数影响较大,初始晶粒尺寸的影响相比较小.基于双道次热压缩试验结果建立了300M钢的静态再结晶体积分数模型,基于单道次热压缩试验结果建立了300M钢完全静态再结晶晶粒尺寸模型,并验证了静态再结晶体积分数模型的正确性.     

AZ61镁合金热压缩流变应力的实验

采用Gleeble-1500型热模拟机,对AZ61镁合金进行高温压缩实验,分析该合金在不同变形温度与应变速率条件下的压缩流变应力.研究AZ61镁合金在热变形时,流变应力与变形温度、应变速率之间的关系,并建立相应的流变应力模型.结果表明,AZ61镁合金在高温压缩变形时,当变形温度一定时,流变应力随应变速率的增大而增大;而当应变速率一定时,流变应力随变形温度的升高而降低.AZ61镁合金的热变形过程均表现出较明显的动态再结晶特征,其流变应力的变化规律主要受加工硬化和再结晶软化两者机制的共同作用.在热变形下,AZ61镁合金峰值流变应力可以用双曲正弦模型来进行较好的描述.     

曲轴用非调质钢C38N2的静态再结晶行为

通过热模拟实验、光学金相及透射电镜分析观察,研究了奥氏体化条件、变形温度、变形速率、变形量以及道次间隔时间对曲轴用非调质钢C38N2轧制道次间的静态再结晶体积分数和残余应变率的影响规律.实验结果表明:随着变形温度的升高、变形速率的增大、变形量的增大或道次间间隔时间的增长,静态再结晶的体积分数逐渐升高,道次的残余应变率逐渐降低;原始奥氏体晶粒尺寸增大,静态再结晶体积分数降低,但变化不大;在1250℃以下,随着奥氏体化温度的升高,静态再结晶体积分数降低不明显,但在1250℃以上,奥氏体化温度的升高明显降低了静态再结晶体积分数.通过线性拟合以及最小二乘法,得到静态再结晶体积分数与不同变形工艺参数之间关系的数学模型;对已有残余应变率数学模型进行修正,得到含有应变速率项的残余应变率数学模型,拟合度较好.     

铸态AZ31镁合金热变形行为研究

在Gleeble3500热模拟实验机上,对铸态AZ31镁合金进行热压缩实验,获得了变形温度为250～400℃、应变速率为0.005～0.5 s~(-1)条件下镁合金的流变应力曲线,分析了主要工艺参数对AZ31镁合金流变应力的影响规律。结果表明,随着应变的进行,在硬化软化机制共同作用下,材料的流变应力达到峰值应力后缓慢下降,最后基本保持不变,镁合金发生了动态再结晶,;随着温度的升高,应变速率降低,其峰值应力显著下降,可见镁合金属于温度敏感型材料。在此基础上,基于双曲正弦流动应力本构模型,同时考虑塑性变形热和摩擦热的影响,建立了形式简单且具有较高精度的流动应力预测模型。预测值与实验值的相关系数为0.932,该模型能较好地描述铸态AZ31镁合金热变形过程中的流变应力行为。     

AZ31镁合金热变形过程中的流变应力

在Gleeble-1500热模拟试验机和UTM5305实验机上以不同的变形条件对AZ31镁合金进行高温热变形试验,研究该材料在高温热变形过程中的真应力应变。研究结果证明:在变形过程中的AZ31镁合金的真应力随应变速率增大、变形温度降低而升高。在压缩变形过程中的真应力峰值、真应变和动态再结晶与拉伸变形过程相比有明显差异;该镁合金热变形过程中的真应力为用包含Arrhenius项的Zener-Hollomon参数来描述,其压缩拉伸变形激活能分别为132.38 kJ/mol和Q=255.26 kJ/mol.     

变形参数对AZ31镁合金变形抗力的影响

利用Gleeble-1500热模拟试验机对AZ31镁合金在变形温度为250～400℃、变形速率为0.5～3.0s-1下进行热变形模拟实验,得到了AZ31镁合金真实应力-真实应变曲线,并通过光学显微镜观察了试样在变形中的微观组织.结果表明,动态再结晶是该实验条件下晶粒细化的主要机制,变形参数影响了再结晶的程度.     

Kinetics of recrystallization for twin-roll casting AZ31 magnesium alloy during homogenization

The kinetics of recrystallization for twin-roll casting AZ31 magnesium alloy with different thicknesses during homogenization was analyzed. It is shown that fine grains are first formed at the boundaries of deformed bands in the twin-roll casting slab. The recrystallized grains with no strain are gradually substituted for the deformed microstructure of twin-roll casting AZ31 magnesium alloy. The incubation temperature and time for the recrystallization of a twin-roll casting AZ31 magnesium alloy strip with a thickness of 3 mm are lower and shorter than those of the 6-mm thick strip, respectively. The 3-mm thick twin-roll casting magnesium alloy has finer grains than the 6-mm thick strip. The activation energies of recrystallization for twin-roll casting AZ31 magnesium alloy slabs with the thickness of 3 and 6 mm are 88 and 69 kJ/mol, respectively. The kinetics curves of recrystallization for twin-roll casting AZ31 magnesium alloy were obtained.     

Mechanical behavior and microstructure evolution for extruded AZ31 sheet under side direction strain

AZ31 magnesium alloy sheets were prepared by a conventional extrusion (CE) and a novel integrated extrusion with side direction strain (SE). The microstructure characterizations, crystallographic texture and mechanical property tests were carried out and compared between the extruded Mg alloy sheets processed by CE and SE. The results indicated that the SE sheets exhibited an excellent combination of strength and ductility. To reveal the side strain effect, the finite element model was employed to investigate the effective stress and strain behavior of the AZ31 magnesium alloy sheets during CE and SE processes. It was found that the SE process was effective in weakening the stress and strain concentration. This implied that it developed an additional side direction strain through the sheet thickness during the hot extrusion. Meanwhile, the side strain shear paths could promote the local accumulation of dynamically recrystallized grains and increase the random high-angle boundaries to achieve weak (0002) basal texture. Important factors including the side strain path and extrusion parameters need to be taken into account to understand the deformation mechanism and microstructure evolution.     

AZ31镁合金的热变形加工图及其应用

为了确定AZ31镁合金轧制工艺参数,利用Gleeble--3500热模拟试验机进行热压缩试验以测试其热变形行为,并根据动态材料模型理论得到其热加工图.当变形温度为380～400℃、应变速率为3～12 s-1时,功率耗散效率大于30%,属于动态再结晶峰区;在该区域进行异步轧制变形退火处理后得到平均晶粒直径为2.3μm的细晶组织,抗拉强度为322.7MPa,延伸率为19.6%.当应变速率大于15 s-1时,属于流变失稳区,250～300℃低温加工时合金的塑性显著降低,350～400℃高温加工时合金出现混晶组织.     

高挤压比下挤压工艺对AZ31B镁合金组织与力学性能的影响

研究了高挤压比条件下挤压温度、速度对AZ31B镁合金微观组织、力学性能的影响。采用光学显微镜观察了显微组织,拉伸试验测试了力学性能,并配合扫描电镜观察了拉伸试样的断口形貌。结果表明,高挤压比条件下,动态再结晶较为充分,少量晶粒长大,混晶组织消失。低温、高速挤压有助于晶粒细化,并使晶粒尺寸分布均匀,因而可获得高的抗拉强度、屈服强度以及良好的塑性。350 ℃,2 m/min条件下挤压,试样抗拉强度与延伸率最高,为336.5 MPa与 23%。低温、高速下的挤压试样的拉伸断口韧窝较深且细密,呈现明显的韧性断裂特征,而高温、低速的断口为混合断裂。     

稀土Er对ZK60镁合金变形行为的影响

采用Gleeble-1500D热模拟试验机研究了稀土元素Er对ZK60镁合金的热压缩变形行为的影响。通过引入Zener-Hollomon参数和双曲正弦函数构建了ZK60和ZK60-1.0Er镁合金的本构方程,同时采用应变硬化率θ-流变应力σ关系曲线确定动态再结晶发生的临界应力σc值。结果表明:ZK60和ZK60-1.0Er两种镁合金在热压缩变形过程中,随着变形温度T的升高,压缩流变应力σ值均减小;随着应变速率ε?的增加,流变应力σ值均增加。添加稀土元素Er使得ZK60镁合金热压缩变形流变应力σ值和应力指数n值增加,在变形温度为160~320℃时提高了发生动态再结晶的临界应力σc值,稀土相的存在促进了再结晶晶粒的形核,降低了平均变形激活能Qˉ值。     

挤压比对AZ31B镁合金组织和室温力学性能的影响

研究了不同挤压比对AZ31B镁合金显微组织?力学性能的影响?采用光学显微镜观察了挤压棒材显微组织,通过材料万能试验测试了拉伸和压缩性能,并配合扫描电镜观察了拉伸试样的断口处显微组织和形貌?结果表明,随着挤压比的增加,组织由部分动态再结晶向完全动态再结晶过渡;合金拉伸断口由混合断裂转变为明显韧性断裂,压缩断口由解理断裂转变为准解理断裂?大挤压比可以获得良好的综合性能和细致均匀的组织,抗拉强度为310MPa,屈服强度为200MPa,延伸率为14%,并且拉伸压缩不对称性得到缓解,有利于镁合金的二次塑性加工?     

镁合金板材温热冲压成形热力耦合数值模拟

采用Gleeble3500热模拟试验机进行单向拉伸试验,获取了材料的力学性能参数,分析了AZ31镁合金板材的力学性能特点.采用热力耦合技术对镁合金板材温热冲压过程中的温度场进行了数值模拟,研究了冲压过程中温度场的分布规律,并对差温拉延工艺进行了分析.结果表明:差温拉延工艺可以提高镁合金板材的温热成形性能;采用热力耦合技术的数值模拟更能反映AZ31镁合金板材的温度敏感特性.     

镁合金AZ31动态再结晶行为的取向成像分析

利用背散射电子衍射(EBSD)取向成像技术分析了具有不同初始织构的镁合金AZ31动态再结晶晶粒的取向特征以及与相邻的形变晶粒的取向关系.结果表明:不同初始织构以及不同应变量下动态再结晶新晶粒与形变晶粒的取向都相近,说明动态再结晶以连续方式进行,即亚晶转动方式.随形变量的增加,不同初始织构试样的晶粒都转向基面取向,但菊池带衬度图像显示大的形变晶粒内部很少有亚晶界存在并且菊池带质量高,说明塑性滑移机制仍在起很大作用但在靠近晶界处发生,形变晶粒是通过平行于压缩面方向剪切晶界而逐渐消失的.动态再结晶晶粒与相邻形变晶粒的取向差表明不同初始织构造成不同的取向差,但总的趋势是相同的.     

Ti-7333合金β锻动态再结晶行为

 利用Gleeble3800热模拟试验机研究了在温度870～970℃和应变速率0.001～10s^-1范围内,近β钛合金Ti-7333 β锻热变形的组织演化规律及动态再结晶行为.实验结果表明,Ti-7333钛合金在温度较高、应变速率较低的情况下变形时,表现出典型的动态再结晶行为,动态再结晶晶粒尺寸和再结晶体积分数均随变形温度升高和变形速率降低而增大,而应变速率对再结晶晶粒尺寸的影响较显著.在变形速率较高(>0.1s^-1)且变形温度较低(<870℃)时,晶粒严重变形拉长,但动态再结晶将很难发生.因子Z决定着动态再结晶晶粒尺寸,二者之间为幂指数关系.通过回归分析方法得出动态再结晶晶粒尺寸的数学表达式为：lnD_r=8.50949-0.31411lnZ.采用该表达式可以对一定变形条件的动态再结晶晶粒尺寸进行精确预测,从而为Ti-7333钛合金热变形条件下的组织控制提供可靠依据.不适当的热变形工艺会造成组织粗大或者不均匀,进而使材料性能恶化.因此,应该从材料组织均匀性和晶粒细化角度选择最佳的热变形参数.