TiO2光催化降解水中喹诺酮类抗生素

研究TiO2光催化降解水中3种喹诺酮类抗生素的动力学特征,探讨TiO2用量、初始浓度、pH和水质对3种喹诺酮类抗生素光催化降解的影响。研究结果表明:当优化参数为TiO2用量1.0 g/L、抗生素初始浓度10 mg/L,pH=7时,反应80 min,3种喹诺酮类抗生素的降解率均在95%以上;光催化降解反应符合假一级反应动力学方程,反应速率常数为0.044 5~0.071 0,半衰期为9.76~15.57 min,降解难易程度从高到低的顺序为诺氟沙星、环丙沙星、洛美沙星;不同水质中诺氟沙星、环丙沙星的降解率从高到低的顺序为高纯水、河水、自来水,而洛美沙星的降解率从高到低的顺序为河水、自来水、高纯水。     

Cu_2O/TNAs的制备及其对VOCs的降解动力学

光催化技术由于反应条件温和,适宜于降解汽车内部的有机挥发性物质(VOCs).为了提高可见光的利用率和自然光照下对VOCs的光催化降解速率,本文采用阳极氧化法+电沉积法制备了掺杂Cu2O的复合钛纳米管阵列(TNAs),并对其进行了SEM、EDX、XRD及UV-Vis表征.结果表明,Cu2O纳米颗粒均布于TNAs的管壁及表层,复合纳米管阵列对可见光的吸收较纯TNAs提高了.通过反应动力学分析发现,Cu2O和O2对TNAs光催化降解VOCs有协同作用,Cu2O/TNAs对VOCs的光催化降解服从一阶反应动力学.研究了反应温度、反应气体中氧含量、催化剂Cu含量及相对湿度对VOCs降解速率常数的影响,拟合了光催化降解VOCs的速率常数函数式,由模型得出,Cu2O/TNAs含Cu量为31.37%,被处理气体中含氧量为36.92%,相对湿度为33.71%时,速率常数最大.建立并验证了VOCs一阶降解模型,模型值与实测值的误差小于20%.     

掺铜TiO_2光催化降解活性艳红X-3B的研究

采用溶胶-凝胶法制备掺铜TiO2光催化剂,以活性艳红X-3B溶液光催化降解反应为模型,研究各种因素对活性艳红X-3B光催化降解的影响.实验结果表明:适量的Cu2+掺杂可明显提高TiO2的活性,本实验中最佳量为0.5%.掺杂Cu2+的TiO2光催化剂最佳用量为1.5g/L,溶液pH为5左右,活性艳红X-3B溶液初始浓度为40mg/L,加入H2O21ml/L,40min左右活性艳红X-3B降解率可达到94.3%.     

自然光条件下Cu~(2+)/TiO_2纳米催化剂降解头孢类抗生素的研究

在高原自然光条件下利用纳米Cu2+/Ti O2复合光催化剂对高原制药废水中阿莫西林进行了光催化降解实验,研究了不同温度煅烧及催化剂中不同Cu2+浓度对水体中阿莫西林降解率的影响。结果表明:在自然光下照射下,催化剂用量为1 g/L,掺入1.0%Cu2+、煅烧温度为700℃的Cu2+/Ti O2纳米催化剂8 h后对水体中阿莫西林的降解率最高达到75%。纳米Cu2+/Ti O2复合光催化剂对制药废水中阿莫西林的降解有一定的效果。     

Cu2O/Bi2MoO6耦合系统增强光催化活性研究

采用乙二醇为溶剂,成功合成了耦合系统Cu2O/Bi2MoO6,分别采用X射线衍射(XRD)、拉曼光谱(Raman)、X射线光电子能谱分析(XPS)和透射电子显微镜(TEM)进行表征.样品的光催化活性通过在可见光下降解结晶紫来获得.结果表明,当Cu与Mo摩尔比为0.08,Cu2 O/Bi2MoO6展示出最高的光催化性能,仅在100 min结晶紫的降解率达到95.6％.同时,研究了耦合系统中Cu2O的量对其光催化活性的影响,并提出了合理的反应机制.     

金属酞菁配合物的合成及其在光催化应用中的研究进展

金属酞菁（MPcs）可用于提纯、工厂排水、农业排水等,是一种优良的环保材料.文章概述了MPcs的结构、特点以及合成方法,并介绍了光催化的原理,总结了其在光催化中的研究进展,重点介绍了其在降解染料罗丹明B、甲基橙（MO）、亚甲基蓝和降解抗生素四环素类抗生素、磺胺类抗生素、β-内酰胺类抗生素中的应用,展望了未来MPcs在光催化相关工作中的应用前景.     

Cu_2O/Bi_2MoO_6耦合系统增强光催化活性研究(英)

采用乙二醇为溶剂,成功合成了耦合系统Cu2O/Bi2MoO6,分别采用X射线衍射(XRD)、拉曼光谱(Raman)、X射线光电子能谱分析(XPS)和透射电子显微镜(TEM)进行表征.样品的光催化活性通过在可见光下降解结晶紫来获得.结果表明,当Cu与Mo摩尔比为0.08,Cu2O/Bi2MoO6展示出最高的光催化性能,仅在100min结晶紫的降解率达到95.6%.同时,研究了耦合系统中Cu2O的量对其光催化活性的影响,并提出了合理的反应机制.     

溶液共存阳离子对CdS光催化降解罗丹明B性能的影响

采用水热方法制备了纳米硫化镉光催化剂.借助粉末X-射线衍射(XRD),固体紫外可见漫反射光谱(DRS)对合成产物进行了表征.以纳米CdS和本体CdS作为可见光的光催化剂,用难降解的离子型染料罗丹明B为探针分子,讨论了溶液常见的共存金属离子种类、质量分数对CdS光催化降解罗丹明B的影响.结果表明:共存离子Cu2+对CdS光催化降解罗丹明B起抑制作用,Ag+对CdS光催化降解罗丹明B没有显著影响,而共存离子Fe3+ 和Pr3+ 能显著地提高纳米、本体CdS光催化剂降解罗丹明B的降解速率,最佳的离子质量分数分别为催化剂用量的0.5% 和10%.     

掺铜方法对二氧化钛光催化氧化还原性能的影响

采用浸渍法、水解沉淀法、机械混合法制备了铜掺杂的TiO2光催化剂.利用XRD,XPS,TPR等手段对不同样品进行了表征,以乙酸水溶液的光催化氧化降解及二氧化碳光催化还原为反应探针,对3种催化剂光催化活性进行了评价.结果表明,不同方法掺铜影响催化剂表面性质如吸附氧、元素价态及分布,进而影响光催化性能.吸附氧的性能以及存在合适比例的氧化还原对Cu+/Cu2+导致浸渍法制备的掺铜TiO2光催化剂具有最好的光催化活性.     

TiO2光催化降解水体中抗生素的研究进展

本文综述了近十多年来多种不同抗生素在水体中的光催化降解行为,从水体中的抗生素的光催化降解环境影响因素,降解中间产物和降解途径,光催化降解动力学,光催化降解机理几个方面进行了阐述,展望了光催化降解水体中的抗生素类污染物的研究前景．     

TiO2/SiO2纳米粒子光催化降解庚烯/二氧化硫

以TiO₂/SiO₂纳米粒子为催化剂, 研究了催化剂不同焙烧温度对二氧化硫与庚烯光催化反应的影响. 结果表明, 经600 ℃焙烧的催化剂对庚烯的降解最好. 同时研究了庚烯和二氧化硫的初始浓度、 氧气和水蒸气的不同含量及光强等因素对其光催化氧化降解的影响. 庚烯的降解速率随着二氧化硫浓度的增加而增加, 最终趋于稳定. 在二氧化硫浓度一定时, 庚烯的反应速率分别随着氧气和水分子含量的增加而不断增大, 氧含量为20%时速率最大; 水分子含量为444 μmol/L时速率最大. 庚烯的反应速率随着光强的增加而增大, 光强增至8.32 mW/cm²时, 反应速率趋于定值. 通过FT-IR和GC-MS测定初步确定了反应产物.     

Cu2+和Zn2+对模拟胃液中NDMA形成的影响

【目的】在模拟胃液条件下研究重金属Cu~(2+)和Zn~(2+)对内源致癌性N-二甲基亚硝胺(NDMA)形成的影响,并进一步探讨其作用机理。【方法】分别用气相色谱-质谱联用法(GC-MS)和离子色谱法(IC)来测定NDMA、二甲胺(DMA)和亚硝酸根(NO_2~-)含量。【结果】在模拟胃液条件下,Cu~(2+)和Zn~(2+)浓度高于50mg/L时,可以促进NDMA的形成,且当浓度由50mg/L增大到200mg/L时,Cu~(2+)促进率由1.16%增大到94.56%,Zn~(2+)促进率由21.32%增大到45.86%。在重金属浓度为符合或接近符合水质基准值1.0mg/L时,Cu~(2+)和Zn~(2+)对NDMA的形成也分别有16.88%和13.42%的促进率;而当重金属浓度为10mg/L时,两种离子却均抑制NDMA的形成。机理研究表明Cu~(2+)、Zn~(2+)促进NDMA的形成主要是由于其与DMA发生相互作用,进而导致NDMA形成。【结论】高浓度的Cu~(2+)和Zn~(2+)通过与DMA相互作用,形成活性中间体从而促进NDMA的生成。     

含Sr2+和Bi3+有机杂化体的合成及其光降解罗丹明B

采用溶剂热法在N,N-二甲基甲酰胺溶液中合成了不同摩尔比例的SrCl_2和Bi(NO_3)_3(分别为5%,10%,30%,50%,80%)与对苯二甲酸形成的含Sr~(2+)和Bi~(3+)有机杂化体,并在紫外可见光照射下对其进行了罗丹明B降解活性的评价.结果表明:杂化体在紫外可见光下对RhB降解活性良好,其中SrCl_2摩尔比例10%掺杂的催化剂光降解活性最佳,这归结于其在紫外区域对光有很好的吸收及光生电子和空穴能有效地分离.双金属离子能协同调节有机杂化体的光催化活性.     

Preparation and photocatalytic activity of Cu-doped TiO2/SiO2

Cu²⁺-doped nanostructured TiO₂-coated SiO₂ (TiO₂/SiO₂) particles were prepared by the layer-by-layer assembly technique and their photocatalytic property was studied. TiO₂ colloids were synthesized by the sol-gel method using TiOSO₄ as a precursor. The experimental results showed that TiO₂ nanopowders on the surface of SiO₂ particles were well distributed and compact. The amount of TiO₂ increased with the increase in coating layers. The shell structure appeared to be composed of anatase titania nanocrystals at 550°C. The 2-layer coated TiO₂ particles on the surface showed a higher degradation rate compared with all the different-layer samples. The photocatalytic activity of Cu²⁺-doped TiO₂/SiO₂ was higher than that of undoped TiO₂/SiO₂. The optimum dopant content was about 0.10wt%.     

Cu2+对好氧颗粒污泥理化特性的影响分析

以普通活性污泥为接种污泥,葡萄糖和乙酸钠为碳源,在SBR反应器中培养好氧颗粒污泥,考察不同质量浓度Cu2+(0 mg/L、1 mg/L、3 mg/L、5 mg/L和10 mg/L)冲击作用对好氧颗粒污泥理化特性的影响。结果表明,随着Cu2+质量浓度从0 mg/L上升至10 mg/L,好氧颗粒污泥的理化特性均受到不同程度的影响。质量浓度为1 mg/L和3 mg/L的Cu2+对COD和NH+4-N的去除率影响较小,而质量浓度为5 mg/L和10 mg/L的Cu2+对COD和NH+4-N的去除率影响较大。随着Cu2+质量浓度的增加,好氧颗粒污泥的丝状菌逐渐增多,污泥浓度不断下降,沉降性能急剧恶化;密实度降低,结构越来越松散,粒径出现两极分化的现象,而且在质量浓度为10 mg/L的Cu2+作用下颗粒污泥解体。     

非活性马尾藻对水中Cd2+和Ni2+的生物吸附及脱附研究

【目的】以马尾藻粉为生物吸附剂,研究其在静态实验中对Cd2＋ 和Ni2＋ 的吸附及脱附能力,并对吸附速度、动力学、重金属选择性和吸附剂再生等问题进行探讨.【方法】采用单因素法分析pH 值、初始浓度、平衡离子类型等条件因素对重金属吸附容量的影响,采用准一级和准二级动力学模型对Cd2＋ 、Ni2＋ 的吸附数据进行拟合.【结果】Cd2＋ 的最佳吸附条件为pH 值4.5、初始浓度500mg/L、平衡离子为NO3ˉ,Ni2＋ 的最佳吸附条件为pH 值3.0、初始浓度900mg/L、平衡离子为Clˉ;Cd2＋ 、Ni2＋ 的吸附平衡到达时间分别为50min和25min;准二级动力学模型对吸附数据的拟合效果更好,相关系数（犚2 ）均大于0.99;对混合溶液中不同重金属的选择性吸附顺序为Pb2＋ 〉Ni2＋ 〉Cd2＋ 〉Mn2＋ ;1.0mol/L HCl对Cd2＋ 、Ni2＋ 的理论洗脱率均可达到99%.【结论】马尾藻粉对Cd2＋ 和Ni2＋ 的吸附容量大,吸附条件温和,重金属脱附率高,是一种性能良好的生物吸附剂.     

金属离子对钢在没食子酸/硫酸介质中的腐蚀行为研究

 用失重法研究了4种金属离子(Na⁺,Zn²⁺,Cu²⁺,Fe³⁺)在0.5 mol/L H₂SO₄以及500 mg/L没食子酸+0.5 mol/L H₂SO₄介质中在20℃对冷轧钢腐蚀行为的影响.结果表明:Cu²⁺对钢的腐蚀起抑制作用;而其余3种金属离子(Na⁺,Zn²⁺,Fe³⁺)对钢的腐蚀起加速作用.在相同条件下,冷轧钢在0.5 mol/L H₂SO₄溶液中的腐蚀速率顺序为:Cu²⁺2++3+;而在500 mg/L没食子酸+0.5 mol/L H₂SO₄介质中,腐蚀速率顺序为:Cu²⁺2+3++.     

Degradation of 2, 4-D acid using Mn2+ as catalyst under UV irradiation

In this paper, the oxidative degradation of 2, 4-dichlorophenoxyacetic acid (2, 4-D) using Mn²⁺/H₂O₂ reagent under UV irradiation was studied. The results show that 2, 4-D was degraded more completely in Mn²⁺/H₂O₂ solution than traditional Fenton solutions. The effects of the concentration of Mn²⁺, H₂O₂ and pH were also investigated. And under the optimal condition of 1.48×10⁻⁴ mol/L, 8.99×10⁻⁵ mol/L and pH 3.38, the formation of ·OH was the most, both the decomposition rate of H₂O₂ and the degradation rate of 2, 4-D were the fastest. In addition, the photoreaction process was monitored using spin-trapping electron paramagnetic resonance (EPR), and the results indicated that the oxidative process was predominated mainly by the hydroxyl radical (·OH) gennerated in the system. Biography: HUANG Yingping (1964–), Professor, Ph. D., research direction: pollution ecology and water pollution control.     

MoS2/g-C3N4复合光催化剂的构建及其可见光催化性能研究

本研究通过水热合成法和超声法成功构建MoS₂/g-C₃N₄复合型光催化剂。通过X射线粉末衍射（XRD）、扫描电子显微镜（SEM）、红外光谱（IR）以及紫外-可见吸收光谱（UV-Vis）表征技术对复合型催化剂的物理化学特性进行分析。以光催化降解罗丹明B（RhB）为探针反应,探究可见光下不同质量比的MoS₂/g-C₃N₄复合型光催化剂对RhB光催化降解性能的影响。实验结果表明,当MoS₂负载量为30%,光催化降解80 min时,10 mg/L的RhB溶液的降解率为96.7%。MoS₂/g-C₃N₄复合催化剂相比于纯的g-C₃N₄,MoS₂降解RhB的效果有显著地提高。光催化降解性能的提升归因于两半导体间MoS₂和g-C₃N₄异质结界面构筑,有效地抑制光生电子（e^-）和空穴（h⁺）的复合,从而提高复合型光催化剂MoS₂/g-C₃N₄的光催化性能。     

稀土氧化物掺杂对TiO2/沸石光催化性能的影响

以钛酸丁酯和稀土氧化物为原料, 采用溶胶 凝胶法制备了镧、 钕和镱稀土离子掺杂TiO₂/沸石光催化剂. 通过XRD和IR方法对样品进行表征, 研究了不同沸石粒径及不同稀土氧化物掺杂量(质量分数)对农药敌敌畏光催化降解性能的影响. 结果表明, 当沸石最佳粒径为0.15 mm, La³⁺掺杂量质量分数为3.0%时（以TiO₂质量计）, 稀土离子的掺杂可显著提高TiO₂//沸石的光催化降解性能.