挤压工艺对AK4-1ч合金棒材晶粒大小的影响

通过调整合金成分分别配制了添加Zr,AlTiB,AlTiC和RE的AK     

稀土在Al-Ti-B-RE中间合金中的作用

采用氟盐法制备了Al-Ti-B-RE中间合金,并对其进行了细化效果实验,利用扫描电镜研究了Al-Ti-B-RE中间合金的微观组织特征.研究结果表明:加入稀土对TiAl3晶粒的大小、形貌及分布有显著影响;稀土增大了铝熔体与TiB2之间的润湿角,使TiB2不易聚集和沉淀,增强了中间合金的细化性能;稀土易聚集在晶界和相界面,减少晶核与液体间的接触面积,增大形核率,对TiAl3合金晶粒的细化效果明显.     

稀土对铝钛硼中间合金组织及细化性能的影响

采用氟盐铝热反应法制取不同稀土含量的Al-Ti-B-RE中间合金,并对其微观组织和细化效果进行了分析,讨论了稀土元素对Al5Ti1B组织及性能的影响。X射线衍射及能谱分析证明:稀土元素和TiAl3结合生成了Ti2Al20RE,同时TiAl3尺寸减小、数量减少;TiB2尺寸、形态不受影响,但分布更加均匀弥散。细化效果试验表明稀土元素确实可以提高Al5Ti1B中间合金的细化效果。在5Ti1B系Al-Ti-B-RE中间合金中,稀土元素的最佳质量分数为3.53%,此时能取得最理想的微观组织和细化效果。     

稀土对铝钛硼中间合金组织及细化性能的影响

采用氟盐铝热反应法制取不同稀土含量的Al-Ti-B-RE中间合金,并对其微观组织和细化效果进行了分析,讨论了稀土元素对Al5Ti1B组织及性能的影响。X射线衍射及能谱分析证明,稀土元素和TiAl3结合生成了Ti2Al20RE,同时TiAl3尺寸减小、数量减少;TiB2尺寸、形态不受影响,但分布更加均匀弥散。细化效果试验表明稀土元素确实可以提高Al5Ti1B中间合金的细化效果。在5Ti1B系Al-Ti-B-RE中间合金中,稀土元素的最佳质量分数为3.53%,此时能取得最理想的微观组织和细化效果。     

Al5Ti1B中间合金细化剂研制及同类产品对比

利用氟盐铝热反应法制备了Al5Ti1B中间合金细化剂,制定出完整的工艺路线和参数,并对其反应过程和原理进行了分析.制取的中间合金化学成分(质量分数)为:Ti,4.64%;B,0.84%.通过与荷兰KBM、英国LSM、国内某厂生产的同类产品进行化学成分、微观组织和细化效果三项指标对比分析,结果表明:自行开发的中间合金细化剂质量优于国内同类产品;同等条件下细化效果(TiAl3＜50 μm,TiB2＜1 μm)与KBM公司的同类产品接近,达到进口同类产品水平.     

超声制备Al-5Ti-1B中间合金中TiB2粒子尺寸分布及其晶粒细化性能

在连续高能超声作用下,制备出一种新型的Al-5Ti-1B中间合金,研究了该中间合金的微观组织、形核相TiB2粒子尺寸分布以及它对工业纯铝的晶粒细化效果.结果表明,与常规制备方法相比,在4 min连续高能超声振动作用下,可使Al熔体对混合氟盐的吸收率达到100%,大大缩短了制备反应时间.Al-5Ti-1B中间合金中,TiAl3相呈现10~20μm小团块状;TiB2粒子为规则多边状,并有清晰的外形轮廓,呈松散聚集团状分布;TiB2粒子的平均尺寸以及尺寸跨度大大降低,分别为646.9 nm、1.2μm.该中间合金的优良组织特性显著提高了其晶粒细化性能,用此中间合金可将工业纯铝的铸态晶粒尺寸细化至45μm.     

挤压工艺对AK_(4-1ч)合金棒材晶粒大小的影响

通过调整合金成分分别配制了添加Zr,AlTiB ,AlTiC和RE的AK4 1ч实验铝合金 ,经过 2种不同的工艺生产棒材 ,在室温下测量其淬火时效态抗拉强度 ,用金相显微镜和扫描电镜观察和分析了合金在不同加工工艺状态下的显微组织和结构 ,并判定其晶粒度 .结果表明 :在设计合金成分时 ,要精确控制Cu的含量在 2 .0 %～ 2 .6 % ,以免生成难溶的含Cu相 ,降低合金的强度 ;多向强应变可细化晶粒 ,提高合金的力学性能 ;随变形程度的增加 ,晶粒尺寸减小 ;制定挤压工艺时 ,为避免产生周期性裂纹 ,建议挤压比取为 2 5左右     

超声波对AlTiC细化剂的活化机理研究

采用AlTiC作为7050铝合金的细化剂,并在铸造中引入高频超声波,通过比较不同试样表面微观组织的晶粒尺寸以及试样中Ti和C元素的分布等特征,研究超声波对AlTiC细化剂细晶效果的影响及其作用机理.研究结果表明:施加高频超声波能够加速TiAl3相的溶解,提高TiC粒子团与铝溶液的润湿性;粗大晶粒的内部存在一个或多个Ti原子偏聚区;而细小晶粒中Ti原子的偏聚则集中在晶界上,其晶内保持着一个相对较低的质量分数;施加高频超声波能够抑制TiC粒子团间的融合,减小Ti原子偏聚区的面积以及质量分数,进而提高TiC粒子团的形核能力,使所得的金属凝固组织更为细小、均匀.     

TiAl基合金晶粒细化重要影响因素研究进展

目的 TiAl基合金密度小,高温下具有很高强度以及很好抗蠕变性和抗氧化性,但是其属于金属间化合物型合金,晶粒细化有助于提高它的塑性和韧性。总结TiAl基合金在晶粒细化方面的研究进展,为TiAl基合金的进一步研究提供参考。方法在参考国内外近40篇文献的基础上,仔细研究有关TiAl基合金晶粒细化的实验方法、结果及分析,最后进行综合归纳和总结。结果从添加合金元素、粉末冶金、热处理、热机械加工、氢化处理等方面,对于TiAl基合金组织细化研究进展进行了简要总结;尽管各种工艺的机理有所不同,但是均能实现TiAl基合金组织细化,有助于改进TiAl基合金材料的相关性能。结论在已有研究的基础上,晶粒细化对TiAl合金焊接接头综合性能的改善研究有待进一步深化和加强。     

Al—Ti—CN中间合金的研制

纯铝的晶粒细化一直是铝生产厂家和科研工作者不断研究的课题,Al—Ti和Al—Ti—B作为中间合金细化铝已经相对成熟,Al—Ti—C中间合金还在开发中.本文详细论述了在Al—Ti—C中间合金基础上新开发的Al—Ti—CN中间合金的试验全过程,试验证明Al—Ti—CN中间合金细化工业纯铝效果优于Al—Ti和Al—Ti—B中间合金,有望成为新型纯铝晶粒细化中间合金.     

In-situ study on γ phase transformation behaviour of γ-TiAl alloys at different cooling rates

γ-TiAl-based alloys are promising lightweight high-temperature structural materials, and the transformation from the α parent phase to γ lamellae during the cooling process has a great influence on the microstructures and mechanical properties of TiAl alloys. In this paper, an in-situ observation technique, high-temperature laser scanning confocal microscopy (HTLSCM), was utilized to investigate the continuous cooling transition (CCT) from the α phase in three compositions. The nucleation and growth behaviors of γ lamellae were studied at several moderate cooling rates. In addition, the processes of helium gas quenching for three alloys were investigated, and the massive transformation was observed in Ti–49Al. CCT diagraphs were concluded for three alloys. The Vickers hardness of TiAl alloys subjected to different cooling rates was tested, and it was found that the hardness of alloys was enhanced with increasing cooling rate due to the refinement of lamellar spacing.     

ZLD11铝合金晶粒细化分析

以ZLD11铝合金为研究对象,通过添加Sr来改变ZLD11铝合金的晶粒度,以达到细化晶粒的目的.介绍了ZLD11铝合金中元素的性质及作用,ZLD11铝合金的熔炼方法.以AlSr合金的形式加入熔体中,按照Sr的加入量占成品合金的0.04%,0.06%,0.08%以及0.10%来改变ZLD11铝合金的晶粒度,通过观察金相照片和测定晶粒度,来寻求合理的Sr的加入量,结果表明:采用X金属模铸造和用AlSr作为变质剂可以使ZLD11的晶粒细化,当Sr的加入量为0.08%时,细化晶粒效果最好.     

Grain refinement of Mg-Li-Al cast alloys by adding typical master alloys

Commercial Al-3Ti-1C and Al-5Ti-1B master alloys were added in order to refine the grains of Mg-Li-Al alloys.The effects of their addition levels on grain refinement of Mg-Li-Al cast alloy were investigated and the mechanism of the grain refinement was discussed.The results showed that the addition of Al-3Ti-1C master alloy reduced the grain size of LA141 cast alloy from 900μm to 400μm,while the addition of Al-5Ti-1B master alloy reduced the grain size of LA51 cast alloy from 500μm to 240μm.The grain ref...     

TiAl基合金断裂情况的研究现状及发展趋势

对TiAl基合金断裂情况的研究现状进行了论述 .从显微结构的控制提高其断裂韧性及其它性能 ,加载率、温度和环境对TiAl基合金的断裂及韧化机理的影响 ,变形和断裂行为 ,韧化机理和断裂机理的研究情况等五个方面对前人的工作进行了分析与比较 ,有助于对TiAl合金的变形与断裂 ,断裂过程及其韧化机理更进一步的理解 .同时进一步提出了TiAl基合金的断裂模型是什么 ,传统的COD法能否合理地测试TiAl合金的断裂韧性 ,用什么方法才能更好地评定此类合金的断裂韧性等需解决的问题 ,并对TiAl基合金发展趋势进行了初步的探讨 .     

添加铬元素对TiAl合金室温延性和微观结构的影响

以0 wt％到5 wt％的金属铬作为第三合金元素,探讨了其对TiAl合金的室温延性和微观结构的影响。研究结果表明,适量铬的添加能够显著地改善TiAl合金的室温延性。合金中退火孪晶的量随着铬添加量的增加而明显增多;变形合金中含有大量的孪晶和层错带。这些表明,TiAl合金的堆垛层错能由于铬的添加而降低了,由此可以断定孪生变形和超位错运动对TiAl Cr合金的塑性变形作出了贡献。研究结果还表明,合金的晶粒度以及所含有的少量 Ti_3Al第二相都对其室温延性有着影响。     

Al-Ti-B在Al-Si合金中的晶粒细化行为的研究进展

Al-Ti-B是目前Al合金中应用最为广泛的晶粒细化剂,其晶粒细化行为受到细化剂组织状态、细化工艺、合金成分等因素的影响;尤其是应用于Al-Si系合金时,毒化效应的存在削弱了细化效果,成为制约Al-Si合金晶粒细化效果的重大瓶颈。总结了Al-Ti-B在Al-Si合金中晶粒细化的研究进展,重点阐述了毒化效应的影响及其作用机制,归纳了外加超声能量场对细化行为的影响作用,最后展望了未来的研究方向。