347H不锈钢电化学腐蚀行为研究

使用电化学工作站检测热轧态347H不锈钢、固溶态酸洗347H不锈钢和固溶处理态347H不锈钢在3.5wt.%NaCl、5wt.%H₂SO₄和5wt.%NaOH腐蚀介质中的电化学腐蚀行为,绘制极化曲线和电化学阻抗谱研究固溶处理对347H不锈钢电化学腐蚀行为的影响.结果表明:在3.5wt.%NaCl腐蚀介质中,固溶态酸洗347H不锈钢表现出最佳的耐腐蚀性,而固溶处理会降低热轧态347H不锈钢的耐腐蚀性能.在5wt.%H₂SO₄腐蚀介质中,通过1 160 ℃固溶处理2 h,347H不锈钢的耐腐蚀性有所提高.在5wt.%NaOH腐蚀介质中,热轧态347H不锈钢的自腐蚀电流密度和其他状态的347H不锈钢相比要小一个数量级,因此,热轧态347H不锈钢更耐5wt.%NaOH腐蚀介质的腐蚀.     

两种不锈钢在氯化物熔盐环境中的腐蚀行为研究

以盐湖水氯镁石资源化利用为目的,研究了太阳能光热发电系统中,NaCl、KCl、MgCl2?6H2O和CaCl2四种氯化物熔盐储热介质在900℃下对201不锈钢和304不锈钢的腐蚀行为.采用SEM分析手段对腐蚀产物形貌进行表征.结果表明:两种金属材料在4种氯化物熔盐中均有不同程度的腐蚀,在MgCl2?6H2O熔盐中的腐蚀...     

耐浓硝酸铸造不锈钢的研究

In this research work, the structures and properties of four kinds of stainless steel with different Ni contents used for concentrated nitric acid are investigated using optical microscope, X-ray diffractometer, scanning electron microscope and by means of properties testing. Experimental results show that the amount of austenite in the tested steel is increased with the increasing of Ni content, and the toughness and the corrosion-resistant property are improved.     

700℃下TP347H耐热钢水蒸汽下初期氧化行为研究

为研究TP347H奥氏体不锈钢的在高温水蒸汽下的初期氧化行为,采用自行设计的蒸汽氧化实验模拟装置,在700℃下进行了1.5,2,3,4h 4个不同时段的氧化实验。利用SEM与AFM观察了样品表面与截面形貌,结果表明:在700℃下,TP347H快速氧化,表面首先被细小颗粒完全覆盖,随后生出许多岛状结构,且在岛状结构上会长出细小晶须.EDS与Raman结果显示,氧化层为内外两层,主要由Cr2O3、Ni O、Fe Cr2O4、Fe Cr2O4构成.     

静水压力对304不锈钢腐蚀行为的影响

利用自制的腐蚀实验高压釜模拟深海低温高压化学环境,研究静水压力对304不锈钢腐蚀行为影响机制.利用电化学工作站对腐蚀过程进行原位检测和加速实验,得到交流阻抗谱和动电位极化曲线,通过等效电路拟合和Tafel外推法对数据进行处理.分析了腐蚀发生的热力学倾向和动力学过程,讨论了钝化膜状态对腐蚀的影响.常压环境下,自腐蚀电位高,容抗弧半径较小.氧气等气体分子容易在304不锈钢表面吸附,增大腐蚀发生的热力学倾向.随着静水压力的增加,自腐蚀电位变化不大,压力变化不会导致钝化膜性质的改变.但腐蚀电流密度从3.838×10-8 A/cm2增加到1.197×10-7 A/cm2,容抗弧半径减小,金属/钝化膜/溶液之间电位差降低,钝化膜溶解速率大于生长速率,导致钝化膜厚度减小,使304不锈钢腐蚀加剧.     

硝酸熔盐蓄热过程中NO_x的累积排放监测

通过实验对太阳能蓄热用硝酸熔盐是否排放NOx以及45#碳钢对这种排放是否存在影响进行研究.参照国家标准固定污染源中氮氧化物测定方法,通过监测不同指定温度下熔盐尾气中氮氧化物的排放量,以评估熔盐蓄热过程是否对环境造成影响.研究结果表明,空气中二元和三元硝酸熔盐在使用温度范围内会排放出少量氮氧化物,但其平均排放浓度远低于国家大气污染综合排放标准的限值.三元硝酸熔盐在相同温度下的平均排放量比二元熔盐的大.熔盐接触45#碳钢后其平均排放量成倍增加,但仍然符合国家大气污染物综合排放标准的要求.     

冷凝液硫含量对SUS444铁素体不锈钢腐蚀行为的影响

利用冷凝液浸蚀-高温氧化循环腐蚀法模拟汽车排气系统内部服役环境,借助失重分析、腐蚀形貌观察及腐蚀产物分析,研究了SUS444不锈钢在不同硫含量的冷凝液中的腐蚀行为。结果表明,随着腐蚀循环次数的增加,不锈钢表面不断沉积的FeSO_4·7H_2O、Fe(NH_4)(SO_4)_2及Fe_4(SO_4)_5(OH)_2·18H_2O等硫酸盐物质加速了不锈钢的腐蚀进程,其点蚀深度及腐蚀速率均随冷凝液中硫含量的升高而增加。     

Mo-Al_2O_3金属陶瓷在NaCl熔盐中的腐蚀行为

为提高 Mo-Al_2O_3金属陶瓷热电偶保护管在熔盐中的使用寿命,在实验室采用坩埚法,模拟现场实际使用情况,探讨了Mo-Al_2O_3在NaCl熔盐中的腐蚀行为,结果表明,Mo-Al_2O_3金属陶瓷在纯NaCl熔盐中,主要是电化学蚀损,并随Mo含量的增加而加快,Al_2O_3则与此相反;在添加硼砂的熔盐中,除金属相蚀损外,陶瓷相也严重蚀损。如在Mo-Al_2O_3中添加Cr_2O_3则可提高金属陶瓷在含硼砂的NaCl介质中的抗蚀能力,本工作为保护管的研制及其在现场的合理使用提供了依据。     

反应烧结碳化硅材料的Na_2CO_3熔盐腐蚀行为研究

研究了在 10 0 0℃空气中的Na2 CO3 熔盐对反应烧结SiC材料的腐蚀行为 .研究结果表明 ,Na2 CO3 熔盐加速了材料的高温氧化失效 ,其腐蚀动力学过程主要包括 3个阶段 :第 1阶段是SiO2氧化膜快速溶解所造成的快速失重阶段 ;第 2阶段为材料表面液相膜形成所引起的快速氧化 (增重 )阶段 ;第 3阶段是由于熔体底部形成一层保护性SiO2 氧化膜所表现出的慢速氧化 (增重 )阶段 .因此 ,Na2 CO3 熔盐的作用使得材料表面形成大量蚀坑 .     

反应烧结碳化硅材料的Na2CO3熔盐腐蚀行为研究

研究了在1000℃空气中的Na2CO3溶盐对反应烧结SiC材料的腐蚀行为，研究结果表明，Na2CO3熔盐加速了材料的高温氧化失效，其腐蚀动力学过程主要包括3个阶段：第1阶段是SiO2氧化膜快速溶解所造成的快速失重阶段；第2阶段为材料面液相膜形成所引起的快速氧化（增重)阶段；第3阶段是由于熔体底部形成一层保护性SiO2氧化膜所表现出的慢速氧化（增重）阶段，因此，Na2CO3溶盐的使用使得材料表面形成大量蚀坑。     

Effects of chitosan inhibitor on the electrochemical corrosion behavior of 2205 duplex stainless steel

The effects of chitosan inhibitor on the corrosion behavior of 2205 duplex stainless steel were studied by electrochemical measurements, immersion tests, and stereology microscopy. The influences of immersion time, temperature, and chitosan concentration on the corrosion inhibition performance of chitosan were investigated. The optimum parameters of water-soluble chitosan on the corrosion inhibition performance of 2205 duplex stainless steel were also determined. The water-soluble chitosan showed excellent corrosion inhibition performance on the 2205 duplex stainless steel. Polarization curves demonstrated that chitosan acted as a mixed-type inhibitor. When the stainless steel specimen was immersed in the 0.2 g/L chitosan solution for 4 h, a dense and uniform adsorption film covered the sample surface and the inhibition efficiency (IE) reached its maximum value. Moreover, temperature was found to strongly influence the corrosion inhibition of chitosan; the inhibition efficiency gradually decreased with increasing temperature. The 2205 duplex stainless steel specimen immersed in 0.4 g/L water-soluble chitosan at 30℃ displayed the best corrosion inhibition among the investigated specimens. Moreover, chitosan decreased the corrosion rate of the 2205 duplex stainless steel in an FeCl₃ solution.     

TP347H精炼渣二次氧化控制及夹杂物变性处理

研究了采用EF+VOD+IC工艺流程生产TP347H不锈钢时由于精炼渣成分产生的二次氧化及其氧化夹杂物的变性处理过程.试验中VOD精炼过程中采用Al进行终脱氧,降低精炼渣中FeO、SiO2含量,精炼渣四元碱度控制在1.3以上,保证钢中全氧质量分数小于0.003%.脱氧后使用喂Ca-Si线及钢包软吹的精炼手段,可将硬质Al2 O3及MgAl2 O4转变为CaO-Al2 O3夹杂,减少硬质MgAl2 O4夹杂总量并使夹杂物熔点低于1500益.此类夹杂在炼钢温度下呈液态且更易于聚集与上浮,而在后续轧制、锻造过程中低熔点夹杂随基体发生形变,减少钢材裂纹的产生.     

表面状态对核级316LN不锈钢电化学腐蚀行为的影响

表征了打磨态和机械抛光态316LN不锈钢表面的粗糙度、表面残余应变和表面电子功函数的分布,并研究了打磨态和机械抛光态样品在硼酸盐溶液中电化学腐蚀行为的差异.与机械抛光态316LN不锈钢相比,打磨处理后样品表面较为粗糙,且表面的微观残余应变较大,近表面产生约50 μm的加工硬化层.表面粗糙度和微观应变的增加引起打磨态表面电化学活性的增大,从而促进316LN不锈钢在硼酸盐溶液中腐蚀.机械抛光处理降低了表面钝化膜的载流子密度(供体和受体),并增大了钝化膜的阻抗,提高了钝化膜的致密性和保护性,能够有效抑制金属的进一步腐蚀.     

Intergranular corrosion behavior of high nitrogen austenitic stainless steel

The intergranular corrosion (IGC) behavior of high nitrogen austenitic stainless steel (HNSS) sensitization treated at 650-950℃ was investigated by the double loop electrochemical potentiodynamic reactivation (DL-EPR) method. The effects of the electrolytes, scan rate, sensitizing temperature on the susceptibility to IGC of HNSS were examined. The results show that the addi-tion of NaCl is an effective way to improve the formation of the cracking of a passive film in chromium-depleted zones during the reactivation scan. Decreasing the scan rate exhibits an obvious effect on the breakdown of the passive film. A solution with 2 mol/L H₂SO₄+1 mol/L NaCl+0.01 mol/L KSCN is suitable to check the susceptibility to IGC of HNSS at a sensitizing temperature of 650-950℃ at a suitable scan rate of 1.667 mV/s. Chromium depletion of HNSS is attributed to the precipitation of Cr₂N which results in the susceptibility to IGC. The synergistic effect of Mo and N is suggested to play an important role in stabilizing the passive film to prevent the attack of IGC.     

304不锈钢在模拟压水堆一回路水中高温电化学腐蚀行为

通过模拟压水堆一回路水环境,研究了氯离子浓度和溶解氧对304不锈钢高温电化学腐蚀行为的影响.动电位极化曲线结果表明,氯离子浓度主要影响高电位下的二次钝化效应,低电位下影响效果不明显,结合X射线光电子能谱对氧化膜元素成分的分析发现二次钝化效应与氧化膜中Fe/Cr元素含量比密切相关.电化学阻抗谱和扫描电镜结果表明,随着氯离子浓度增加,氧化膜阻抗逐渐降低,表面外层氧化物颗粒和间隙逐渐增大,耐腐蚀性能降低.随着溶解氧含量的升高,304自腐蚀电位逐渐升高,钝化电流密度降低,钝化区间缩小,表面氧化膜阻抗逐渐增加.     

热处理对奥氏体不锈钢00 Cr24 Ni13铸坯高温热塑性的影响

采用热处理实验方法,同时结合热模拟压缩和热模拟拉伸试验,研究了热处理对奥氏体不锈钢00Cr24Ni13铸坯高温热塑性的影响。实验结果表明：热处理能够明显改变实验钢铸坯中δ铁素体的形貌;经1200℃保温3 h空冷后,原始铸坯中存在的大面积连续网状δ铁素体完全转变为弥散分布的细小颗粒状组织。具有颗粒状δ铁素体的热处理试样与热处理前相比,不同温度压缩时的变形抗力略有增加,但并没有急剧恶化;热模拟抗拉强度基本保持不变;相同温度下的断面收缩率( Z)显著提高,其中Z≥60%的温度区间由1150~1280℃扩展为1050~1300℃,高塑性(Z≥80%)温度范围在150℃左右(1150~1300℃)。     

氯离子对石油测井仪器用Cr13不锈钢点损伤行为的影响

采用高温高压模拟环境装置和实时动电位极化和交流阻抗技术对石油测井仪器用Cr13不锈钢在模拟井下不同氯离子环境中电极的腐蚀失重和电化学行为进行了研究.实验结果表明,当地层水或者钻井液中氯离子浓度较高时,Cr13不锈钢表面的点损伤难以避免;随着氯离子浓度的升高,Cr13的均匀腐蚀速率增大,试样表面点蚀坑增多;局部氯离子以FeCl2和FeCl3形式吸附是造成钝化膜损伤的主要原因.应尽量减少仪器在含氯离子环境中的停留时间或提高材料等级.     

温度对13Cr不锈钢在高 CO2 分压环境中腐蚀行为的影响

通过高温高压电化学测试,获得不同实验温度下13Cr不锈钢的循环伏安曲线、交流阻抗谱和Mott-Schottky曲线,结合ZSIMPWIN软件和扫描电子显微镜分析,研究高温高CO2 分压环境下,温度对13Cr不锈钢腐蚀电化学行为的影响. 在高温高CO2 分压环境下,随温度升高,13Cr不锈钢发生腐蚀的倾向增加,表面钝化膜稳定性下降,点蚀敏感度增加.