Influence of Ag doping on the microstructure and electrical properties of ZnO-Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-based varistor ceramics

Silver in the form of AgNO₃ was added to ZnO-based varistor ceramics prepared by the solid-state reaction method. The effects of AgNO₃ on both the microstructure and electrical properties of the varistors were studied in detail. The optimum addition amount of AgNO₃ in ZnO-based varistors was also determined. The mechanism for grain growth inhibition by silver doping was also proposed. The results indicate that the varistor threshold voltage increases substantially along with the AgNO₃ content increasing from 0 to 1.5mol%. Also, the introduction of AgNO₃ can depress the mean grain size of ZnO, which is mainly responsible for the threshold voltage. Furthermore, the addition of AgNO₃ results in a slight decrease of donor density and a more severe fall in the density of interface states, which cause a decline in barrier height and an increase in the depletion layer.     

Preparation and radar-absorbing properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>/TiO<Subscript>2</Subscript>/Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>/Yb<Subscript>2</Subscript>O<Subscript>3</Subscript> composite powder

Al₂O₃/TiO₂/Fe₂O₃/Yb₂O₃ composite powder was synthesized via the sol-gel method. The structure, morphology, and radar-absorption properties of the composite powder were characterized by transmission electron microscopy, X-ray diffraction analysis and RF impedance analysis. The results show that two types of particles exist in the composite powder. One is irregular flakes (100-200 nm) and the other is spherical Al₂O₃ particles (smaller than 80 nm). Electromagnetic wave attenuation is mostly achieved by dielectric loss. The maximum value of the dissipation factor reaches 0.76 (at 15.68 GHz) in the frequency range of 2-18 GHz. The electromagnetic absorption of waves covers 2-18 GHz with the matching thicknesses of 1.5-4.5 mm. The absorption peak shifts to the lower-frequency area with increasing matching thickness. The effective absorption band covers the frequency range of 2.16-9.76 GHz, and the maximum absorption peak reaches -20.18 dB with a matching thickness of 3.5 mm at a frequency of 3.52 GHz.     

Effect of the synthesis route on the structural and dielectric properties of SrBi<Subscript>1.8</Subscript>Y<Subscript>0.2</Subscript>Nb<Subscript>2</Subscript>O<Subscript>9</Subscript> ceramics

This work is devoted to the synthesis and characterization of yttrium-doped SrBi₂Nb₂O₉ ceramics prepared by three methods: solid state reaction, co-precipitation, and hydrothermal. Multiple characterizations, specifically scanning electron microscopy (SEM), X-ray powder diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR), were used to validate the structural feature. The crystallite size was estimated by Scherrer’s formula and the Williamson–Hall plot. The effect of the process on the band intensities of the FTIR spectra was investigated. The crystallite size and microstructure of ceramics prepared from different synthesis processes were strongly influenced by the sinterability. SEM images revealed nanograin ceramics for materials prepared by co-precipitation and hydrothermal methods and micrograin ceramics prepared by the solid state method. The synthesized compounds underwent phase transitions at 480–465°C. The dielectric and electrical properties of these Y-doped SrBi₂Nb₂O₉ ceramics appear to be dependent on the grain size.     

Effects of Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> on the properties of ceramics from steel slag

Ferric oxide is one of the key factors affecting both the microstructure and the properties of CaO-MgO-SiO₂-based ceramics. Research on this effect is significant in the utilization of iron-rich solid wastes in ceramics. Ceramic samples with various Fe₂O₃ contents (0wt%, 5wt%, and 10wt%) were prepared and the corresponding physical properties and microstructure were studied. The results indicated that Fe₂O₃ not only played a fluxing role, but also promoted the formation of crystals. Ceramics with 5wt% of Fe₂O₃ addition attained the best mechanical properties with a flexural strength of 132.9 MPa. Iron ions were dissolved into diopside, consequently causing phase transformation from diopside and protoenstatite to augite, thereby contributing to the enhancement of its properties. An excess amount of Fe₂O₃ addition (10wt% or more) resulted in deteriorated properties due to the generation of an excess volume of liquid and the formation of high-porosity structures within ceramics.     

Electrochemical properties of LiNi<Subscript>0.5</Subscript>Mn<Subscript>1.3</Subscript>Ti<Subscript>0.2</Subscript>O<Subscript>4</Subscript>/Li<Subscript>4</Subscript>Ti<Subscript>5</Subscript>O<Subscript>12</Subscript> cells

Spinel compounds LiNi_0.5Mn_1.3Ti_0.2O₄ (LNMTO) and Li₄Ti₅O₁₂ (LTO) were synthesized by different methods. The particle sizes of LNMTO and LTO are 0.5–2 and 0.5–0.8 μm, respectively. The LNMTO/LTO cell exhibits better electrochemical properties at both a low current rate of 0.2C and a high current rate of 1C. When the specific capacity was determined based on the mass of the LNMTO cathode, the LNMTO/LTO cell delivered 137 mA·h·g⁻¹ at 0.2C and 118.2 mA·h·g⁻¹ at 1C, and the corresponding capacity retentions after 30 cycles are 88.5% and 92.4%, respectively.     

Influence of post-annealing on the properties of Ta-doped In<Subscript>2</Subscript>O<Subscript>3</Subscript> transparent conductive films

Ta-doped In₂O₃ transparent conductive oxide films were deposited on glass substrates using radio-frequency (RF) sputtering at 300°C. The influence of post-annealing on the structural, morphologic, electrical and optical properties of the films was investigated using X-ray diffraction, field emission scanning electron microscopy, Hall measurements and optical transmission spectroscopy. The obtained films were polycrystalline with a cubic structure and were preferentially oriented in the (222) crystallographic direction. The lowest resistivity, 5.1×10⁻⁴ Ω cm, was obtained in the film annealed at 500°C, which is half of that of the un-annealed film (9.9×10⁻⁴ Ω cm). The average optical transmittance of the films was over 90%. The optical bandgap was found to decrease with increasing annealing temperature.     

Effect of Al2O3 and Y2O3 on the corrosion behavior of ZrO2-benzotriazole nanostructured coatings applied on AA2024 via a sol-gel method

zirconia-based nanostructured coatings were deposited on AA2024 to improve the corrosion resistance properties. Three different nanostructured coatings, namely, zirconia-benzotriazole, zirconia-alumina-benzotriazole, and zirconia-yttria-benzotriazole, were applied on AA2024 via a sol-gel method using the dip-coating technique. Next, the coatings were annealed at 150℃ after each dipping period. The phases and morphologies of the coatings were investigated using grazing incidence X-ray diffraction (GIXRD), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FESEM), and atomic force microscopy (AFM). The corrosion properties were evaluated using electrochemical methods, including polarization and electrochemical impedance techniques in 3.5wt% NaCl solution. The obtained results confirm the formation of homogeneous and crack free zirconia-benzotriazole-based nanostructured coatings. The average roughness values for zirconia-benzotriazole, zirconia-alumina-benzotriazole, and zirconia-yttria-benzotriazole nanostructured coatings were 30, 8, and 6 nm, respectively. The presence of alumina as a stabilizer on zirconia coating was found to have a beneficial impact on the stability of the corrosion resistance for different immersion times. In fact, the addition of alumina resulted in the dominance of the healing behavior in competition with the corrosion process of zirconia-benzotriazole nanostructured coating.     

Photoluminescence and cathodoluminescence properties of CaLaGa<Subscript>3</Subscript>O<Subscript>7</Subscript>:Eu<Superscript>3+</Superscript> phosphors

The CaLaGa₃O₇:Eu³⁺ phosphor was prepared by a chemical co-precipitation method. Field emission scanning electron microscopy (FE-SEM), laser particle size analysis, X-ray diffraction (XRD), photoluminescence (PL), and cathodoluminescence (CL) spectra were utilized to characterize the synthesized phosphor. The results revealed that the phosphor was composed of microspheres with a slight agglomerate phenomenon and was spherically shaped. The average grain size was about 1.0 μm. Eu³⁺ ions, as luminescent centers, substituted La³⁺ ions into the single crystal lattice of CaLaGa₃O₇ with the sites of C_s. Although the CL spectrum was greatly different from the PL spectrum, it had the strongest red emission corresponding to the ⁵D₀ →⁷F₂ transition of Eu³⁺. Under the excitation of UV light (287 nm) and electron beams (1.0–7.0 kV), the chromaticity coordinates of the phosphor were found to be in the nearly red and orange light regions, respectively.     

Preparation of Al<Subscript>72</Subscript>Ni<Subscript>8</Subscript>Ti<Subscript>8</Subscript>Zr<Subscript>6</Subscript>Nb<Subscript>3</Subscript>Y<Subscript>3</Subscript> amorphous powders and bulk materials

Amorphous Al₇₂Ni₈Ti₈Zr₆Nb₃Y₃ powders were successfully fabricated by mechanical alloying. The microstructure, glass-forming ability, and crystallization behavior of amorphous Al₇₂Ni₈Ti₈Zr₆Nb₃Y₃ powders were investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM), and differential scanning calorimetry (DSC). The isothermal crystallization kinetics was analyzed by the Johnson–Mehl–Avrami equation. In the results, the supercooled liquid region of the amorphous alloy is as high as 81 K, as determined by non-isothermal DSC curves. The activation energy for crystallization is as high as 312.6 kJ·mol?1 obtained by Kissinger and Ozawa analyses. The values of Avrami exponent (n) imply that the crystallization is dominated by interface-controlled three-dimensional growth in the early stage and the end stage and by diffusion-controlled two- or three-dimensional growth in the middle stage. In addition, the amorphous Al₇₂Ni₈Ti₈Zr₆Nb₃Y₃ powders were sintered under 2 GPa at temperatures of 673 K and 723 K. The results show that the Vickers hardness of the compacted powders is as high as Hv 1215.     

Microstructure and properties of Ga-modified 0.7BiFeO3-0.3BaTiO3 solid solution

Binary solid solutions 0.7Bi (GaxFe1-x)O3-0.3BaTiO3 (x = 0, 0.025, 0.05, 0.1) ceramics were prepared by traditional ceramic process. All the ceramic samples showed single perovskite phase except the sam- ple with x = 0.1. The effects of gallium doping on microstructure, ferromagnetic, ferroelectric, dielectric properties and conductivity were investigated. The results indicated that Ga-dopant could improve the sintering ability of the solid solution when the Ga content x was below 0.05. When x was over 0.05, the sintering ability of the solid solution was weakened, and the phase structure of 0.7BiFeO3-0.3BaTiO3 solid solution changed from rhombohedral phase into tetragonal ferroelectric phase. The electrical resistivity increased with the Ga content increasing. Both ferroelectricity and ferromagnetism were observed in all the ceramic samples. With the Ga content increasing, the remanent magnetization Mr increased and the magnetic coercive field Hc decreased. However, the remanent polarization Pr fluctu- ated, increasing firstly and decreasing later.     

Preparation and luminescence properties of YeO3：Er^3＋/TiO2 with high specific surface area

The three composites Y2O3 :Er3+ , Y2O3 :Er3+ /Yb 3+ andY2O3 :Er3+ /TiO2 were prepared using coprecipitation and sol-gel techniques. Their morphology, specific surface area, porosity, UV-vis. absorption spectra and fluorescence spectra were measured using SEM, TEM, surface analysis, UV-vis. absorption and photoluminescence spectrophotometry. SEM and TEM showed that samples prepared using coprecipitation were dispersed, while Y2O3 :Er3+ /TiO2 particles possessed a mesoporous surface and average diameter of ab...     

Chemical quenching and inhibition of positronium in Cr<Subscript>2</Subscript>O<Subscript>3</Subscript>/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> catalysts

The pore structure of Cr2O3/Al2O3 catalysts and the surface chemical properties of these pores were characterized by positron lifetime and coincidence Doppler broadening (CDB) measurements. Four lifetime components could be resolved from the positron lifetime spectrum, with two long lifetime components and two short lifetime components. The two long lifetimes τ4 and τ3 are attributed to ortho-positronium (o-Ps) annihilation in large pores and microvoids, respectively. With increasing Cr2O3 content, both τ4 and its intensity I4 show sharp decrease, while τ3 and its intensity I3 keep nearly unchanged. The Doppler broadening S parameters also show sharp decrease with increasing Cr2O3 content. Detailed analysis of the CDB spectrum reveals that the parapositronium (p-Ps) intensity also decreases with increasing Cr2O3 content. This indicates that the change of o-Ps lifetime τ4 is due to the chemical quenching by Cr2O3 but not spin-conversion of positronium. The decrease of o-Ps intensity I4 indicates that Cr2O3 also inhibits positronium formation.     

Nonlinear optical properties of Eu<Subscript>2</Subscript>O<Subscript>3</Subscript> doped 5ZnO-20Nb<Subscript>2</Subscript>O<Subscript>5</Subscript>-75TeO<Subscript>2</Subscript> glasses

The third-order optical nonlinearities, including third-order nonlinear susceptibility X^(3), nonlinear refractive index (n2) and temporal response, were measured with forward DFWM using Nd:YAG mode-locked pulse laser. The results show that Eu203 doped 5ZnO-20Nb2O5-75TeO2 glasses have large n2 and ultra-fast temporal response. Raman spectra show that Eu2O3 dopant induces the changes in the local structure of glasses. The higher the dopant concentration, the larger the nonlinear refractive n2 and the faster the temporal response. The enhancement on the third-order optical nonlinearities can be attributed to the deformation of the electronic clouds in [TeO4] enhanced by Eu2O3 dopant.     

Effect of Al<Subscript>2</Subscript>O<Subscript>3sf</Subscript> addition on the friction and wear properties of (SiC<Subscript>p</Subscript>+Al<Subscript>2</Subscript>O<Subscript>3sf</Subscript>)/Al2024 composites fabricated by pressure infiltration

Aluminum (Al) 2024 matrix composites reinforced with alumina short fibers (Al₂O_3sf) and silicon carbide particles (SiC_p) as wear-resistant materials were prepared by pressure infiltration in this study. Further, the effect of Al₂O_3sf on the friction and wear properties of the as-synthesized composites was systematically investigated, and the relationship between volume fraction and wear mechanism was discussed. The results showed that the addition of Al₂O_3sf, characterized by the ratio of Al₂O_3sf to SiC_p, significantly affected the properties of the composites and resulted in changes in wear mechanisms. When the volume ratio of Al₂O_3sf to SiC_p was increased from 0 to 1, the rate of wear mass loss (K_m) and coefficients of friction (COFs) of the composites decreased, and the wear mechanisms were abrasive wear and furrow wear. When the volume ratio was increased from 1 to 3, the COF decreased continuously; however, the K_m increased rapidly and the wear mechanism became adhesive wear.     

Preparation of nanocrystalline Co<Subscript>3</Subscript>O<Subscript>4</Subscript> and its properties as supercapacitors

Electrochemical capacitors store the capacitance through faradic reaction, which is generally named psue-docapacitance or supercapacitance. They are currently extensively studied as novel energy storage devices. Due to their superb characteristics of high power density and long cycle life compared to the conventional batteries, their high pulse-power capability is very excellent. Inter-ests in supercapacitor energy-storage systems have arisen in recent years on account of possible applications…     

Reinforcing effect of graphene on the mechanical properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>/TiC ceramics

Multilayer graphene (MLG)-reinforced Al₂O₃/TiC ceramics were fabricated through hot pressing sintering, and the reinforcing effect of MLG on the microstructure and mechanical properties of the composites was investigated by experiment and simulation. The simulation of dynamic crack initiation and propagation was investigated based on the cohesive zone method. The results show that the composite added with 0.2wt% MLG has excellent flexural strength and high fracture toughness. The major reinforcing mechanisms are the synergistic effect by strong and weak bonding interfaces, MLG pull-out, and grain refinement resulting from the addition of MLG. In addition, the aggravating of crack deflection, branching, blunting, and bridging have indispensable contribution to the improvement of the as-designed materials.     

Hydrogen storage properties of MgH<Subscript>2</Subscript> co-catalyzed by LaH<Subscript>3</Subscript> and NbH

To improve the hydrogen storage properties of Mg-based alloys, a composite material of MgH₂ + 10wt%LaH₃ + 10wt%NbH was prepared by a mechanical milling method. The composite exhibited favorable hydrogen desorption properties, releasing 0.67wt% H₂ within 20 min at 548 K, which was ascribed to the co-catalytic effect of LaH₃ and NbH upon dehydriding of MgH₂. By contrast, pure MgH₂, an MgH₂ + 20wt%LaH₃ composite, and an MgH₂ + 20wt%NbH composite only released 0.1wt%, 0.28wt%, and 0.57wt% H₂, respectively, under the same conditions. Analyses by X-ray diffraction and scanning electron microscopy showed that the composite particle size was small. Energy-dispersive X-ray spectroscopic mapping demonstrated that La and Nb were distributed homogeneously in the matrix. Differential thermal analysis revealed that the dehydriding peak temperature of the MgH₂ + 10wt%LaH₃ + 10wt%NbH composite was 595.03 K, which was 94.26 K lower than that of pure MgH₂. The introduction of LaH₃ and NbH was beneficial to the hydrogen storage performance of MgH₂.     

Microwave absorption properties of SiC@SiO2@Fe3O4 hybrids in the 2-18 GHz range

To enhance the microwave absorption performance of silicon carbide nanowires (SiCNWs), SiO₂ nanoshells with a thickness of approximately 2 nm and Fe₃O₄ nanoparticles were grown on the surface of SiCNWs to form SiC@SiO₂@Fe₃O₄ hybrids. The microwave absorption performance of the SiC@SiO₂@Fe₃O₄ hybrids with different thicknesses was investigated in the frequency range from 2 to 18 GHz using a free-space antenna-based system. The results indicate that SiC@SiO₂@Fe₃O₄ hybrids exhibit improved microwave absorption. In particular, in the case of an SiC@SiO₂ to iron(Ⅲ) acetylacetonate mass ratio of 1:3, the microwave absorption with an absorber of 2-mm thickness exhibited a minimum reflection loss of -39.58 dB at 12.24 GHz. With respect to the enhanced microwave absorption mechanism, the Fe₃O₄ nanoparticles coated on SiC@SiO₂ nanowires are proposed to balance the permeability and permittivity of the materials, contributing to the microwave attenuation.     

High-temperature synthesis in nonpolar solvent for CsPbBr<Subscript>3</Subscript> and CH<Subscript>3</Subscript>NH<Subscript>3</Subscript>PbBr<Subscript>3</Subscript> perovskite nanocrystals with high-efficient luminescence

We report a method to synthesize both organicinorganic CH₃NH₃PbBr₃ and all-inorganic CsPbBr₃ perovskite nanocrystals in nonpolar solvent at high temperature. The cesium oleate and CH₃NH₃Br (MABr) are prepared and then injected into the nonpolar solvent of octadecene including oleic acid, oleylamine, and lead halide. In the synthesis of organic-inorganic perovskites of CH₃NH₃PbBr₃, the frequently-used polar solvent of dimethylformamide or other polar solvents are not used. The prepared CsPbBr₃ nanocrystals are spherical nanoparticles with the diameter of 250 nm. The CH₃NH₃PbBr₃ perovskites are micro- scale hexagonal nanoplatelets. The colloidal perovskites exhibit high-efficient fluorescence and excellent stability.