La_(2/3)A_(1/3)MnO_3(A=Ba,Yb,Eu)的巨磁电阻效应

采用溶胶－凝胶工艺制备La2/3A1/3MnO3（A＝Ba,Yb,Eu）化合物．研究烧结温度对La2/3Ba1/3MnO3的磁性、导电性、磁电阻效应的影响．发现La2/3Yb1/3MnO3未成单相但具有巨磁电阻效应;La2/3Eu1/3MnO3为具有正交结构的绝缘体．     

TiO2复合对La2/3(Ca0.65Ba0.35)1/3MnO3电输运和磁电阻效应的影响

利用甘氨酸-硝酸盐（GNP）法合成了La_2/3(Ca_0.65Ba_0.35)_1/3MnO₃纳米颗粒体系, 与TiO₂复合后, 得到La_2/3(Ca_0.65Ba_0.35)_1/3MnO_3/xTiO₂体系（x=0,0.02,0.035,0.055,0.09,0.17）, 通过X射线衍射、 Raman光谱、 扫描电子显微镜和磁电阻效应测试, 对合成产物的结构及性能进行表征. 结果表明, 样品均成立方对称结构, 复合使低场磁电阻增强, 电阻率增大.     

空位掺杂La2/3Ba1/3MnO3/ZnO复合材料的制备和微结构研究

采用传统的固相反应法在La空位的La2/3Ba1/3MnO3粉末中掺入第二相ZnO,制备了一系列La空位的La2/3(1-x)Ba1/3MnO3/0.33ZnO(LBMO/ZnO)和La空位掺Dy的(La(0.6-x)Dy0.4)2/3Ba1/3MnO3/0.33ZnO(LBDMO/ZnO)复合体系.Rietveld方法拟合X射线衍射(XRD)测量结果表明,LBMO/ZnO复合体系中的LBMO为单相的钙钛矿结构,LBMO的结构参数(包括晶格参数,晶胞体积)以及Mn-O键长,Mn-O-Mn键角随空位浓度的增加呈单调变化的趋势;LBDMO/ZnO复合体系中除了形成LBMO相外,还存在DyMnO3杂相,LBDMO的结构参数以及Mn-O键长,Mn-O-Mn键角随空位浓度x的增加几乎没有发生变化.XRD和扫描电子显微镜(SEM)都表明ZnO和锰氧化物没有发生反应,ZnO可能以非晶态的形式存在于复合体系中,这将影响复合体系的电磁输运性质.     

Ca和Ba掺杂对La4/3Sr5/3Mn2O7的磁电阻效应的影响

用溶胶-凝胶法制备了双层钙钛矿锰氧化物La4/3(Sr1-xAx)5/3Mn2O7 (A是Ca或者Ba,x=0,0.1,0.2)系列多晶样品,并对其结构及电、磁输运性质进行了研究.研究结果表明:Ca和Ba的掺入虽然导致绝缘体-金属(I-M)转变温度(TI-M)降低,但可以明显提高低温区的磁电阻效应.对于x=0.2的Ca或Ba掺杂的样品,在60 K以下,磁电阻值接近100 %,且为一恒定值.对于这一实验结果可以作如下解释:Ca或Ba掺杂引起了MnO6八面体的畸变,导致eg电子占据dx2-y2轨道和d3z2-r2轨道的状态偏离了x=0时的优化组合状态,铁磁性被削弱.     

AgNO3对多晶材料La0.6Sr0.05Na0.35MnO3结构和磁性的影响

采用溶胶-凝胶法制备了多晶La0.6Sr0.05Na0.35MnO3粉体样品,用固相反应法制备了La0.6Sr0.05Na0.35MnO3+xAgNO3(x=0.08,0.16)的粉体样品,块体于1 673K烧结得到.结果在样品中发现了Ag和Mn3O4相,对母体样品的晶格常数和晶胞体积都有微小影响;样品的居里温度随掺杂AgNO3含量的增加而增加;在1.8T磁场下La0.6Sr0.05Na0.35MnO3+0.16AgNO3的块体材料在283K出现磁电阻峰值,为27%;La0.6Sr0.05Na0.35MnO3+0.08AgNO3块体也在283K左右出现峰值,为32%,在210～260K时磁电阻随温度变化不大.     

WO3掺杂的La2/3Ba1/3MnO3的晶体结构和磁性质研究

采用La2/3Ba1/3MnO3(LBMO)为母体,选用非磁性的W离子的氧化物WO3作为第二相,用固相反应法合成了复合体系La2/3Ba1/3MnO3/xWO3.研究了该复合物的晶体结构和磁性质,发现W6 离子的注入会引起晶胞体积的增大和居里相变温度的下降,分析了发生这种变化的原因.     

CHM法合成BaMnO3、Ba1/2Sr1/2MnO3纳米晶体

采用复合碱媒介法(CHM),以BaCl和MnO2为原料在200 ℃、24 h的生长条件下合成了纳米BaMnO3单晶颗粒.采用同样方法,以Sr(NO3)2、BaCO3以及MnO2为原料,在200 ℃、24 h的生长条件下,用50%的Sr替代50%的Ba,成功合成了Ba1/2Sr1/2MnO3.用X射线衍射仪(XRD)、扫描电镜(SEM)及能量散射X射线谱(EDS)对产物的晶相、形貌和成分进行了分析,并且解释了BaMnO3及Ba1/2Sr1/2MnO3的生长机理.     

基于GMR磁性材料设计的热敏体温计

系统阐述了磁性材料在磁传感方面的应用,重点说明了掺杂磁性材料La2/3(Ca0.6Ba0.4)1/3MnO3在磁传感方面的应用,通过实验研究了La2/3(Ca0.6Ba0.4)1/3MnO3的电阻率-温度特性(R-T特性),进一步说明这一材料在体温计应用上的原理及可行性.     

（La1—xSmx）2／3Sr1／3MnO3材料的巨磁致伸缩及磁电阻效应

采用溶胶凝胶法制备了一系列的多晶 (La1 -xSmx) 2 / 3Sr1 / 3MnO3样品 X射线衍射研究表明 ,随Sm含量的增加 ,样品出现从菱面相向正交相结构的转变 在低温下观察到一定Sm含量的样品具有约 -180× 10 - 6大小的磁致伸缩和 32 0 %的磁电阻效应 在室温下 ,样品的磁致伸缩和磁电阻随Sm含量的变化有类似的关系     

（La1-xEux）2／3Sr1／3MnO3室温低场磁电阻效应

采用溶胶凝胶法,以半径较小的Eu3 部分替代离子半径较大的La3 ,制备一系列 (La1xEux)2/3Sr1/3MnO3大块多晶试样(x=0.1、0.2、0.3、0.4、0.5、0.6、0.7),对试样进行X射线衍射表征,分析Eu掺入量对试样晶体结构的影响.测量试样居里温度、电阻率、室温低场磁电阻等电磁行为.结果表明:随着Eu掺入量的增大,A位的平均离子半径减小,试样居里温度降低,电阻率升高,x=0.2试样在室温低场(H=0.87 T)下磁电阻达到-6.53%.室温低场磁滞回线显示Eu掺入量增加,比饱和磁化强度反而降低.     

钙钛矿La2/3Ca1/3MnO3/YBa2Cu4O8/La2/3Ca1/3MnO3三层薄膜的磁输运性能

高温超导材料YBa2Cu4O8(YBCO)和铁磁材料La2／3Ca1／3MnO3(LCMO)形成的三层薄膜LCMO／YBCO／LCMO由对靶溅射技术制得．与YBCO单层薄膜相比，由于超导／铁磁系统中的磁性邻近效应，三层薄膜表现出较低的超导转变温度(Tc,ON)．与LCMO单层膜相比，三层薄膜的金属半导体转变温度(TMS)被提高并且强烈依赖于YBCO层的厚度．随中间层厚度的变化，磁电阻显示出非单调行为，长振荡周期被发现．结果表明，当YBCO处于正常态时两层LCMO膜之间存左着磁性自旋相互作用．     

La2/3Sr1/3MnO3/NiFe2O4复合多晶材料的磁电阻效应

用化学共沉淀法制备了NiFe2O4粉体样品,采用溶胶-凝胶(sol-gel)法制备了La2/3Sr1/3MnO3的多晶样品.用无压烧结制备了名义组分为(La2/3 Sr1/3MnO3)1-x(NiFe2O4)x(x=0,0.05,0.10,0.20)的多晶样品.在1.8×107A/m磁场作用下,当x=0时,样品的磁电阻随温度几乎成线性变化;当x=0.10时,样品在335 K时出现峰值,磁电阻值达35%.     

Preparation and radar-absorbing properties of Al_2O_3/TiO_2/Fe_2O_3/Yb_2O_3 composite powder

Al_2O_3/Ti O_2/Fe_2O_3/Yb_2O_3 composite powder was synthesized via the sol–gel method. The structure,morphology,and radar-absorption properties of the composite powder were characterized by transmission electron microscopy,X-ray diffraction analysis and RF impedance analysis. The results show that two types of particles exist in the composite powder. One is irregular flakes(100–200 nm) and the other is spherical Al_2O_3 particles(smaller than 80 nm). Electromagnetic wave attenuation is mostly achieved by dielectric loss. The maximum value of the dissipation factor reaches 0.76(at 15.68 GHz) in the frequency range of 2–18 GHz. The electromagnetic absorption of waves covers 2–18 GHz with the matching thicknesses of 1.5–4.5 mm. The absorption peak shifts to the lower-frequency area with increasing matching thickness. The effective absorption band covers the frequency range of 2.16–9.76 GHz,and the maximum absorption peak reaches-20.18 d B with a matching thickness of 3.5 mm at a frequency of 3.52 GHz.     

TiO2/Al2O3-Al2O3-TiO2/Al2O3绝缘结构的真空沿面闪络特性

基于变插入层介电常数的多层绝缘结构能改善电场分布、提高真空沿面闪络特性.通过真空热压烧结制备了TiO2/Al2O3-Al2O3-TiO2/Al2O3(A-B-A)3层绝缘结构,A层w(TiO2)为0.5%到20%.测量了该绝缘结构的真空沿面闪络特性,发现闪络特性随w(TiO2)的增加而提高,当w(TiO2)为20%时,其脉冲初次闪络电压较同等厚度的Al2O3陶瓷提高了63%.研究发现:A层的介电常数可由w(TiO2)调控,介电常数的增大能有效降低真空-绝缘子-阴极三结合点处的电场强度;A层表面存在的TiO2颗粒可以减小二次电子发射系数并改善表面电荷分布;TiO2的电导率虽比Al2O3高,但其仍为绝缘体,即使TiO2含量较高时也不会形成贯穿的导电通道.     

纳米Fe2O3-Al2O3复合材料的制备

采用溶胶-凝胶表面包覆法制备了纳米Fe₂O₃-Al₂ O₃复合材料, 利用X射线衍射和透射电镜对样品的物相、 粒度和形貌进行了研 究. 结果表明, α-Fe₂O₃掺杂降低了Al₂O₃相变温度, 在900 ℃可以得到稳定的α-Al₂O₃相.     

CaO-ZrO2-TiO2-Al2O3-B2O3-SiO2玻璃陶瓷的制备及化学稳定性研究

玻璃陶瓷是固化处理中、高放废物和α废物较为理想的候选材料之一。研究了特定条件下制备的CaO-ZrO2-TiO2-Al2O3-B2O3-SiO2体系玻璃陶瓷在水淬和空气中自然冷却的两种冷却制度对其结晶行为和显微结构的影响,用粉末浸泡实验方法测试了其化学稳定性。结果表明:自然冷却形成的玻璃陶瓷晶相主要是ZrSiO4和ZrTiO4;在25～70℃范围内,温度对玻璃陶瓷浸出率无明显影响,90℃下浸出率比25℃,40℃,70℃的浸出率高一个数量级;7 d元素总的归一化浸出为1.87 g/m2。     

Crystallization Mechanism of Na2O-CaO-Al2O3-SiO2-F- Glass Containing Cr2O3

The effect of Cr₂O₃ on the nucleation and crystallization of Na₂O-CaO-Al₂O₃-SiO₂-F- glass has been investigated by means of ESR(Electron Spin Resonance), SEM(Scanning Electron Microscope), EDS(Energy Dispersive Specrometer) and so on. Computer pattern recognition is applied to optimize the heat-treatment schedules. The experimental results show that the base glass containing more than 1.5 % (mass fraction) Cr₂O₃ can be nucleated internally and converted to spheroidal crystal glass materials. The spheroidal crystal consisted of fibrous wollastonite crystals radiating from a center. The residual glass phase filled in the interstices between the fibers and between the spherulites. During heat treatment process, the valence states ofchromium changed from Cr6- to Cr3-, and the Cr-spinel solidsolution [CaCr₂O₄] precipitated followed this valence change. At the primary stage of crystallization, the Cr-spinel could act as a nucleating center on which the principal or}stalline phase β-CaSiO₃ grew epitaxially.     

La2/3Sr1/3MnO3的室温磁电阻效应

采用溶胶-凝胶法制备了La2／3Sr1／3MnO3多晶样品．X射线衍射测试结果表明样品具有钙钛矿结构．利用振动样品磁强计测量了粉体样品在室温下的磁性能,样品表现为铁磁性．对不同烧结温度下形成的块体样品的导电性以及磁电阻的研究表明,随着烧结温度的提高材料的金属-绝缘体转变温度有所增加,说明材料的烧结温度对其电导性有很大的影响．     

TiO2微粉对Al2O3-MgO-Cr2O3浇注料性能的影响

马克思的市民社会决定国家理论的形成,经历了一个思想交锋、自我批判、绵延提升直至最终导出唯物史观之创建的逻辑进程。马克思立足于《莱茵报》时期的感性经历,先后运用哲学、历史学和政治经济学的方法和知识对黑格尔理性国家观进行系统的理论清算,纠正了黑格尔的市民社会与国家关系的“历史错位”,首次确立了“社会本体论”原则。市民社会决定国家理论的形成是标志着唯物史观开始诞生的第一命题。分析马克思市民社会决定国家理论的发展脉络和演进逻辑,有利于澄清马克思市民社会理论与唯物史观的内在关联,科学评价市民社会理论在历史唯物主义中的历史地位。     

Na原子3p2P3/2态超精细结构的计算

采用SIC-Xα方法,计算了Na原子3p2P3/2态的磁性超精细相互作用耦合系数A,理论计算与实验结果符合得较好。对于电超精细结构,通过理论计算给出电场梯度值q,再由电性超精细相互作用常数B的实验值,得出原子核的电四极矩Q,由此计算出Na原子核的大致结构。这是用原子物理的方法研究原子核问题的有益尝试。